Synthesis and electrochemical properties of LiAl0.05Mn1.95O4 by the ultrasonic assisted rheological phase method

Pure-phase and well-crystallized spinel LiAl_0.05Mn_1.95O₄ powders were successfully synthesized by a simple ultrasonic assisted rheological phase (UARP) method. The structure and morphology properties of this as-prepared powder compared with the pristine LiMn₂O₄ and LiAl_0.05Mn_1.95O₄ obtained from the solid-state reaction (SSR) method were investigated by powder X-ray diffraction (XRD) and scanning electron microscopy (SEM). The electrochemical properties focused on the LiAl_0.05Mn_1.95O₄ by this new method have also been investigated in detail. According to these tests results, it is obviously to see that the newly prepared sample delivers a relatively high initial discharge capacity of 111.6 mAh g⁻¹, presents excellent rate capability and reversibility, and shows good cycling stability with capacity retention of 90.6% after 70 cycles. Meanwhile, the electrochemical impedance spectroscopy (EIS) investigations were employed to study the electrochemical process of Li⁺ ions with the synthesized LiAl_0.05Mn_1.95O₄ electrode in detail.     

Electrochemical and thermal studies of Li[NixLi(1/3−2x/3)Mn(2/3−x/3)]O2 (x = 1/12, 1/4, 5/12, and 1/2)

Samples of the layered cathode materials, Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ (x = 1/12, 1/4, 5/12, and 1/2), were synthesized at 900 °C. Electrodes of these samples were charged in Li-ion coin cells to remove lithium. The charged electrode materials were rinsed to remove the electrolyte salt and then added, along with EC/DEC solvent or 1 M LiPF₆ EC/DEC, to stainless steel accelerating rate calorimetry (ARC) sample holders that were then welded closed. The reactivity of the samples with electrolyte was probed at two states of charge. First, for samples charged to near 4.45 V and second, for samples charged to 4.8 V, corresponding to removal of all mobile lithium from the samples and also concomitant release of oxygen in a plateau near 4.5 V. Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples with x = 1/4, 5/12 and 1/2 charged to 4.45 V do not react appreciably till 190 °C in EC/DEC. Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples charged to 4.8 V versus Li, across the oxygen release plateau, start to significantly react with EC/DEC at about 130 °C. However, their high reactivity is similar to that of Li_0.5CoO₂ (4.2 V) with 1 μm particle size. Therefore, Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples showing specific capacity of up to 225 mAh/g may be acceptable for replacing LiCoO₂ (145 mAh/g to 4.2 V) from a safety point of view, if their particle size is increased.     

Synthesis of spinel LiMn2O4 with manganese carbonate prepared by micro-emulsion method

Micro-spherical particle of MnCO₃ has been successfully synthesized in CTAB-C₈H₁₈-C₄H₉OH-H₂O micro-emulsion system. Mn₂O₃ decomposed from the MnCO₃ is mixed with Li₂CO₃ and sintered at 800 °C for 12 h, and the pure spinel LiMn₂O₄ in sub-micrometer size is obtained. The LiMn₂O₄ has initial discharge specific capacity of 124 mAh g⁻¹ at discharge current of 120 mA g⁻¹ between 3 and 4.2 V, and retains 118 mAh g⁻¹ after 110 cycles. High-rate capability test shows that even at a current density of 16 C, capacity about 103 mAh g⁻¹ is delivered, whose power is 57 times of that at 0.2 C. The capacity loss rate at 55 °C is 0.27% per cycle.     

Cathodic performance of LiMn1−xMxPO4 (M = Ti, Mg and Zr) annealed in an inert atmosphere

To improve the cathodic performance of olivine-type LiMnPO₄, we investigated the optimal annealing conditions for a composite of carbon with cation doping. Nanocrystalline and the cation-doped LiMn_1−xM_xPO₄ (M = Ti, Mg, Zr and x = 0, 0.01, 0.05 and 0.10) was synthesized in aqueous solution using a planetary ball mill. The synthesis was performed at the fairly low temperature of 350 °C to limit particle size. The obtained samples except for the Zr doped one consisted of uniform and nano-sized particles. The performance of LiMnPO₄ was much improved by an annealing treatment between 500 and 550 °C with carbon in an inert atmosphere. A small amount of metal-rich phosphide (Mn₂P) was detected in the sample annealed at 900 °C. In addition, 1 at.% Mg doping for Fe enhanced the rate capability in our doped samples. The discharge capacity of LiMn_0.99Mg_0.01PO₄/C was 146 mAh/g at 0.1 mA/cm² and 125 mAh/g even at 2.0 mA/cm².     

Hydrothermal synthesis of LiMn2O4/C composite as a cathode for rechargeable lithium-ion battery with excellent rate capability

A spinel LiMn₂O₄/C composite was synthesized by hydrothermally treating a precursor of manganese oxide/carbon (MO/C) composite in 0.1 M LiOH solution at 180 °C for 24 h, where the precursor was prepared by reducing potassium permanganate with acetylene black (AB). The AB in the precursor serves as the reducing agent to synthesize the LiMn₂O₄ during the hydrothermal process; the excess of AB remains in the hydrothermal product, forming the LiMn₂O₄/C composite, where the remaining AB helps to improve the electronic conductivity of the composite. The contact between LiMn₂O₄ and C in our composite is better than that in the physically mixed LiMn₂O₄/C material. The electrochemical performance of the LiMn₂O₄/C composite was investigated; the material delivered a high capacity of 83 mAh g⁻¹ and remained 92% of its initial capacity after 200 cycles at a current density of 2 A g⁻¹, indicating its excellent rate capability as well as good cyclic performance.     

Synthesis and electrochemical characterization of nano-CeO2-coated nanostructure LiMn2O4 cathode materials for rechargeable lithium batteries

LiMn₂O₄ spinel cathode materials were coated with 0.5, 1.0, and 1.5 wt.% CeO₂ by a polymeric process, followed by calcination at 850 °C for 6 h in air. The surface-coated LiMn₂O₄ cathode materials were physically characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray photoelectron microscopy (XPS). XRD patterns of CeO₂-coated LiMn₂O₄ revealed that the coating did not affect the crystal structure or the Fd3m space group of the cathode materials compared to uncoated LiMn₂O₄. The surface morphology and particle agglomeration were investigated using SEM, TEM image showed a compact coating layer on the surface of the core materials that had average thickness of about 20 nm. The XPS data illustrated that the CeO₂ completely coated the surface of the LiMn₂O₄ core cathode materials. The galvanostatic charge and discharge of the uncoated and CeO₂-coated LiMn₂O₄ cathode materials were measured in the potential range of 3.0-4.5 V (0.5 C rate) at 30 °C and 60 °C. Among them, the 1.0 wt.% of CeO₂-coated spinel LiMn₂O₄ cathode satisfies the structural stability, high reversible capacity and excellent electrochemical performances of rechargeable lithium batteries.     

Optimum synthesis of Li2Fe1−xMnxSiO4/C cathode for lithium ion batteries

Li₂Fe_1−xMn_xSi0₄/C cathode materials were synthesized by mechanical activation-solid-state reaction. The effects of Mn-doping content, roasting temperature, soaking time and Li/Si molar ratio on the physical properties and electrochemical performance of the Li₂Fe_1−xMn_xSi0₄/C composites were investigated. The materials were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM), charge-discharge tests and AC impedance measurements. SEM images suggest that the morphology of the Li₂Fe_1−xMn_xSi0₄/C composite is sensitive to the reaction temperature. Samples synthesized at different temperatures have different extent of agglomeration. Being charged-discharged at C/32 between 1.5 and 4.8 V, the Li₂Fe_0.9Mn_0.1Si0₄/C synthesized at the optimum conditions shows good electrochemical performances with an initial discharge capacity of 158.1 mAh g⁻¹ and a capacity retention ratio of 94.3% after 30 cycles. AC impendence investigation shows Li₂Fe_0.9Mn_0.1SiO₄/C have much lower resistance of electrode/electrolyte interface than Li₂FeSiO₄/C.     

Lithium-deficient LiYMn2O4 spinels (0.9 ≤ Y < 1): Lithium content, synthesis temperature, thermal behaviour and electrochemical properties

Lithium-deficient Li_YMn₂O₄ spinels (LD-Li_YMn₂O₄) with nominal composition (0.9 ≤ Y < 1) have been synthesized by melt impregnation from Mn₂O₃ and LiNO₃ at temperatures ranging from 700 °C to 850 °C. X-ray diffraction data show that LD-Li_YMn₂O₄ spinels are obtained as single phases in the range Y = 0.975-1 at 700 °C and 750 °C. Morphological characterization by transmission electron microscopy shows that the particle size of LD-Li_YMn₂O₄ spinels increases on decreasing the Li-content. The influence of the Li-content and the synthesis temperature on the thermal and electrochemical behaviours has been systematically studied. Thermal analysis studies indicate that the temperature of the first thermal effect in the differential thermal analysis (DTA)/thermogravimetric (TG) curves, T_C1, linearly increases on decreasing the Li-content. The electrochemical properties of LD-Li_YMn₂O₄ spinels, determined by galvanostatic cycling, notably change with the synthesis conditions. So, the first discharge capacity, Q_disch., at C rate increases on rising the Li-content and the synthesis temperature. The sample Li_0.975Mn₂O₄ synthesized at 700 °C has a Q_disch. = 123 mAh g⁻¹ and a capacity retention of 99.77% per cycle. This LD-Li_YMn₂O₄ sample had the best electrochemical characteristics of the series.     

Spray-drying synthesized LiNi0.6Co0.2Mn0.2O2 and its electrochemical performance as cathode materials for lithium ion batteries

Layered LiNi_0.6Co_0.2Mn_0.2O₂ materials were synthesized at different sintering temperatures using spray-drying precursor with molar ratio of Li/Me = 1.04 (Me = transition metals). The influences of sintering temperature on crystal structure, morphology and electrochemical performance of LiNi_0.6Co_0.2Mn_0.2O₂ materials have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and charge-discharge test. As a result, material synthesized at 850 °C has excellent electrochemical performance, delivering an initial discharge capacity of 173.1 mAh g^− 1 between 2.8 and 4.3 V at a current density of 16 mA g^− 1 and exhibiting good cycling performance.     

Structural and electrochemical behaviors of metastable Li2/3[Ni1/3Mn2/3]O2 modified by metal element substitution

Layered metastable lithium manganese oxides, Li_2/3[Ni_1/3−xMn_2/3−yM_x+y]O₂ (x = y = 1/36 for M = Al, Co, and Fe and x = 2/36, y = 0 for M = Mg) were prepared by the ion exchange of Li for Na in P2-Na_2/3[Ni_1/3−xMn_2/3−yM_x+y]O₂ precursors. The Al and Co doping produced the T^#2 structure with the space group Cmca. On the other hand, the Fe and Mg doped samples had the O6 structure with space group R-3m. Electron diffraction revealed the 1:2 type ordering within the Ni_1/3−xMn_2/3−yM_x+yO₂ slab. It was found that the stacking sequence and electrochemical performance of the Li cells containing T^#2-Li_2/3[Ni_1/3Mn_2/3]O₂ were affected by the doping with small amounts of Al, Co, Fe, and Mg. The discharge capacity of the Al doped sample was around 200 mAh g⁻¹ in the voltage range between 2.0 and 4.7 V at the current density of 14.4 mA g⁻¹ along with a good capacity retention. Moreover, for the Al and Co doped and undoped oxides, the irreversible phase transition of the T^#2 into the O2 structure was observed during the initial lithium deintercalation.     

Effect of synthesis condition on the structure and electrochemical properties of Li[Ni1/3Mn1/3Co1/3]O2 prepared by hydroxide co-precipitation method

The layered Li[Ni_1/3Co_1/3Mn_1/3]O₂ powder with good crystalline and spherical shape was prepared by hydroxide co-precipitation method. The effects of pH value, NH₄OH amount, calcination temperature and extra Li amount on the morphology, structure and electrochemical properties of the cathode material were investigated in detail. SEM results indicate that pH value affected both the morphology and the property of the cathode material, and the highest discharge capacity in the first cycle of 163 mAh g⁻¹ (2.8-4.3 V) was obtained at pH value was 12. On the contrary, the NH₄OH amount, which was used as a chelating agent, only affected the particle size distribution of the material. The calcination temperatures caused great difference in the structure and property of layered Li[Ni_1/3Co_1/3Mn_1/3]O₂, and the best electrochemical properties were obtained at the calcination temperature of 800 °C. Extra Li amount not only caused difference in the material structure, but also affected their electrochemical properties. With increasing Li amount, the lattice parameters (a and c) increased monotonously, and the highest first cycle coulombic efficiency (the ratio of discharge capacity to charge capacity in the first cycle) was obtained with the Li/M of 1.10. Therefore, the optimum synthetic conditions for the hydroxide co-precipitation reaction were: pH value was 12, NH₄OH amount was 0.36 mol L⁻¹, calcination temperature was 800 °C and the Li/M molar ratio was 1.10.     

Effects of the nanostructured SiO2 coating on the performance of LiNi0.5Mn1.5O4 cathode materials for high-voltage Li-ion batteries

LiNi_0.5Mn_1.5O₄ spinels coated with various amounts of fumed silica have been synthesized and investigated as cathode materials for high-voltage lithium-ion batteries at the elevated temperature (55 °C). The morphology and structure of the coated LiNi_0.5Mn_1.5O₄ samples were characterized by XRD, TEM and EDX. It was found that the surfaces of the coated LiNi_0.5Mn_1.5O₄ samples are covered with a porous, amorphous, nanostructured SiO₂ layer. The results of electrochemical experiments showed that the SiO₂-coated LiNi_0.5Mn_1.5O₄ samples display obviously improved capacity retention rate, and the improvement effect enhances with the increase of SiO₂ content. The XPS results revealed that the surfaces of the SiO₂-coated LiNi_0.5Mn_1.5O₄ cathode materials have relatively low content of LiF, and this is mainly responsible for their improved electrochemical cycling stability.     

Improved electrochemical properties of Li1+x(Ni0.3Co0.4Mn0.3)O2−δ (x = 0, 0.03 and 0.06) with lithium excess composition prepared by a spray drying method

Layered Li_1+x(Ni_0.3Co_0.4Mn_0.3)O_2−δ (x = 0, 0.03 and 0.06) materials were synthesized through the different calcination times using the spray-dried precursor with the molar ratio of Li/Me = 1.25 (Me = transition metals). The physical and electrochemical properties of the lithium excess and the stoichiometric materials were examined using XRD, AAS, BET and galvanostatic electrochemical method. As results, the lithium excess Li_1.06(Ni_0.3Co_0.4Mn_0.3)O_2−δ could show better electrochemical properties, such as discharge capacity, capacity retention and C rate ability, than those of the stoichiometric Li_1.00(Ni_0.3Co_0.4Mn_0.3)O_2−δ. In this paper, the effect of excess lithium on the electrochemical properties of Li_1+x(Ni_0.3Co_0.4Mn_0.3)O_2−δ materials will be discussed based on the experimental results of ex situ X-ray diffraction, transmission electron microscopy (TEM) and galvanostatic intermittent titration technique (GITT)     

Evolution of the local structure and electrochemical properties of spinel LiNixMn2−xO4 (0 ≤ x ≤ 0.5)

A series of Ni substituted spinel LiNi_xMn_2−xO₄ (0 ≤ x ≤ 0.5) have been synthesized to study the evolution of the local structure and their electrochemical properties. X-ray diffraction showed a few Ni cations moved to the 8a sites in heavily substituted LiNi_xMn_2−xO₄ (x ≥ 0.3). X-ray photoelectron spectroscopy confirmed Ni²⁺ cations were partially oxidized to Ni³⁺. The local structures of LiNi_xMn_2−xO₄ were studied by analyzing the and A_1g Raman bands. The most compact [Mn(Ni)O₆] octahedron with the highest bond energy of Mn(Ni)O was found for LiNi_0.2Mn_1.8O₄, which showed a Mn(Ni)O average bond length of 1.790 Å, and a force constant of 2.966 N cm⁻¹. Electrolyte decomposition during the electrochemical charging processes increased with Ni substitution. The discharge capacities at the 4.1 and 4.7 V plateaus obeyed the linear relationships with respect to the Ni substitution with the slopes of −1.9 and +1.9, which were smaller than the theoretical values of −2 and +2, respectively. The smaller slopes could be attributed to the electrochemical hysteresis and the presence of Ni³⁺ in the materials.     

Preparation and characterization of novel spinel Li4Ti5O12−xBrx anode materials

Br-doped Li₄Ti₅O₁₂ in the form of Li₄Ti₅O_12−xBr_x (0 ≤ x ≤ 0.3) compounds were successfully synthesized via solid state reaction. The structure and electrochemical properties of the spinel Li₄Ti₅O_12−xBr_x (0 ≤ x ≤ 0.3) materials were investigated. The Li₄Ti₅O_12−xBr_x (x = 0.2) presents the best discharge capacity among all the samples, and shows better reversibility and higher cyclic stability compared with pristine Li₄Ti₅O₁₂, especially at high current rates. When the discharge rate was 0.5 C, the Li₄Ti₅O_12−xBr_x (x = 0.2) sample presented the excellent discharge capacity of 172 mAh g⁻¹, which was very close to its theoretical capacity (175 mAh g⁻¹), while that of the pristine Li₄Ti₅O₁₂ was 123.2 mAh g⁻¹ only.     

Zr-doped Li[Ni0.5−xMn0.5−xZr2x]O2 (x = 0, 0.025) as cathode material for lithium ion batteries

Layered Li[Ni_0.5−xMn_0.5−xZr_2x]O₂ (x = 0, 0.025) have been prepared by the mixed hydroxide and molten-salt synthesis method. The individual particles of synthesized materials have a sub-microsize range of 200-500 nm, and LiNi_0.475Mn_0.475Zr_0.05O₂ has a rougher surface than that of LiNi_0.5Mn_0.5O₂. The Li/Li[Ni_0.5−xMn_0.5−xZr_2x]O₂ (x = 0, 0.025) electrodes were cycled between 4.5 and 2.0 V at a current density of 15 mA/g, the discharge capacity of both cells increased during the first ten cycles. The discharge capacity of the Li/LiNi_0.475Mn_0.475Zr_0.05O₂ cell increased from 150 to 220 mAh/g, which is 50 mAh/g larger than that of the Li/LiNi_0.5Mn_0.5O₂ cell. We found that the oxidation of oxygen and the Mn³⁺ ion concerned this phenomenon from the cyclic voltammetry (CV). Thermal stability of the charged Li[Ni_0.5−xMn_0.5−xZr_2x]O₂ (x = 0, 0.025) cathode was improved by Zr doping.     

Synthesis and electrochemical characterizations of nano-scaled Zn doped LiMn2O4 cathode materials for rechargeable lithium batteries

The LiZn_xMn_2−xO₄ (x = 0.00-0.15) cathode materials for rechargeable lithium-ion batteries were synthesized by simple sol-gel technique using aqueous solutions of metal nitrates and succinic acid as the chelating agent. The gel precursors of metal succinates were dried in vacuum oven for 10 h at 120 °C. After drying, the gel precursors were ground and heated at 900 °C. The structural characterization was carried out by X-ray powder diffraction and X-ray photoelectron spectroscopy to identify the valance state of Mn in the synthesized materials. The sample exhibited a well-defined spinel structure and the lattice parameter was linearly increased with increasing the Zn contents in LiZn_xMn_2−xO₄. Surface morphology and particle size of the synthesized materials were determined by scanning electron microscopy and transmission electron microscopy, respectively. Electrochemical properties were characterized for the assembled Li/LiZn_xMn_2−xO₄ coin type cells using galvanostatic charge/discharge studies at 0.5 C rate and cyclic voltammetry technique in the potential range between 2.75 and 4.5 V at a scan rate of 0.1 mV s⁻¹. Among them Zn doped spinel LiZn_0.10Mn_1.90O₄ has improved the structural stability, high reversible capacity and excellent electrochemical performance of rechargeable lithium batteries.     

Synthesis and tunable thermal expansion properties of Sc2−xYxW3O12 solid solutions

A new series of rare earth solid solutions Sc_2−xY_xW₃O₁₂ was successfully synthesized by the conventional solid-state method. Effects of doping ion yttrium on the crystal structure, morphology and thermal expansion property of as-prepared Sc_2−xY_xW₃O₁₂ ceramics were investigated by X-ray diffraction (XRD), thermogravimetric analysis (TG), field emission scanning electron microscope (FE-SEM) and thermal mechanical analyzer (TMA). Results indicate that the obtained Sc_2−xY_xW₃O₁₂ samples with Y doping of 0≤x≤0.5 are in the form of orthorhombic Sc₂W₃O₁₂-structure and show negative thermal expansion (NTE) from room temperature to 600 °C; while as-synthesized materials with Y doping of 1.5≤x≤2 take hygroscopic Y₂W₃O₁₂·nH₂O-structure at room temperature and exhibit NTE only after losing water molecules. It is suggested that the obvious difference in crystal structure leads to different thermal expansion behaviors in Sc_2−xY_xW₃O₁₂. Thus it is proposed that thermal expansion properties of Sc_2−xY_xW₃O₁₂ can be adjusted by the employment of Y dopant; the obtained Sc_1.5Y_0.5W₃O₁₂ ceramic shows almost zero thermal expansion and its average linear thermal expansion coefficient is −0.00683×10⁻⁶ °C⁻¹ in the 25–250 °C range.     

Sintering behavior and microwave dielectric properties of a new low-permittivity ceramic system Ca(Mg1−xAlx)(Si1−x/2Alx/2)2O6

The diopside ceramics with a formula of Ca(Mg_1−xAl_x)(Si_1−x/2Al_x/2)₂O₆ (x=0.01–0.3) were synthesized via a traditional solid-state reaction method, and their solid solubility, sintering behavior and microwave dielectric properties were investigated. The results revealed that the solubility limit of Al₂O₃ in Ca(Mg_1−xAl_x)(Si_1−x/2Al_x/2)₂O₆, which is defined as x, was between 0.15 and 0.2, and a second phase of CaAl₂SiO₆ presented when the x value reached 0.2. Appropriate Al³⁺ substitution for Mg²⁺ and Si⁴⁺ could promote the sintering process and lower the densification temperature, and a broadened densification temperature range of 1250–1300 °C was obtained for the compositions of x=0.08–0.15. With the increase of the x value, the dielectric constant (ε_r) increased roughly linearly, and the temperature coefficient of frequency (τ_f) showed a rising trend. The Q×f values increased from 57,322 GHz to 59,772 GHz as the x value increased from 0.01 to 0.08, and then they were saturated in the range of x=0.08–0.2. Further increase of the x value (x≥0.25) deteriorated the microwave dielectric properties. Good microwave dielectric properties of ε_r=7.89, Q×f=59,772 GHz and τ_f=−42.12 ppm/°C were obtained for the ceramics with the composition of x=0.08 sintered at 1275 °C.     

Synthesis of spherical spinel LiMn2O4 with commercial manganese carbonate

Spherical spinel LiMn₂O₄ particles were successfully synthesized from a mixture of manganese compounds containing commercial manganese carbonate by sintering of the spray-dried precursor. Different preparation routes were investigated to improve the tap density and to enhance the electrochemical performance of LiMn₂O₄. The structure and morphology of the LiMn₂O₄ particles were confirmed by X-ray diffraction (XRD) and scanning electron microscopy. The results showed that hollow spherical LiMn₂O₄ particles could be obtained when only commercial MnCO₃ was used as the manganese source. These particles had a low tap density (ca.0.8 g/cm³). Perfect micron-sized spherical LiMn₂O₄ particles with good electrochemical performance were obtained by spray-drying a slurry composed of MnCO₃, Mn(CH₃CHOO)₂ and LiOH, followed by a dynamic sintering process and a stationary sintering process. The as-prepared spherical LiMn₂O₄ particles comprised hundreds of nanosize crystal grains and had a high tap density(ca. 1.4 g/cm³). The galvanostatic charge-discharge measurements indicated that the spherical LiMn₂O₄ particles had an initial capacity of 121 mAh/g between 3.0 and 4.2 V at 0.2 C rate and still delivered a reversible capacity of 112 mAh/g at 2 C rate. The retention of capacity after 50 cycles was still 96% of its initial capacity at 0.2 C. All the results showed that the as-prepared spherical LiMn₂O₄ particles had an excellent electrochemical performances. The methods we used for preparing spherical LiMn₂O₄ are energy-saving and suitable for industrial application.