Enhanced performance and improved interfacial properties of polymer electrolyte membrane fuel cells fabricated using sputter-deposited Pt thin layers

For this study, catalyst layers for polymer electrolyte membrane fuel cells (PEMFC) were prepared by spraying and sputtering to deposit Pt amount of 0.1 and 0.01 mg cm⁻², respectively. These Pt layers were then assembled to fabricate membrane electrode assemblies (MEA) having either single- or double-layered catalysts. The PEM fuel cell with double layers showed a current density of 777 mA cm⁻² at a cell voltage of 0.6 V, which is a higher current density than state-of-the-art fuel cells at 643 mA cm⁻². These results indicate that Pt loading in state-of-the-art PEMFCs could be reduced by approximately 50% with no performance loss by using both spraying and sputtering method in the MEA fabrication process.     

Optimization of the sputter-deposited platinum cathode for a direct methanol fuel cell

The electrodes prepared by a sputtering method were evaluated as the cathodes for direct methanol fuel cells (DMFCs). Pt loading below 0.25 mg cm⁻² achieved higher mass activities than that of 0.5 mg cm⁻² prepared by the paste method, which was general conventional method. However, an increase in Pt loading reduced the catalyst activity for the oxygen reduction reaction (ORR). This result may suggest an increase in only electrochemically inactive Pt. Pt utilization efficiency can be found about ten times higher at Pt loading of 0.04 mg cm⁻². Moreover, addition of Nafion to sputter-deposited Pt cathodes is found possible to improve the catalyst activity for the ORR, but the excess Nafion over the optimum condition reduces the active sites.     

Development and characterization of a silicon-based micro direct methanol fuel cell

A silicon-based micro direct methanol fuel cell (μDMFC) for portable applications has been developed and its electrochemical characterization carried out in this study. Anode and cathode flowfields with channel and rib width of 750 μm and channel depth of 400 μm were fabricated on Si wafers using the microelectromechanical system (MEMS) technology. A membrane-electrode assembly (MEA) was specially fabricated to mitigate methanol crossover. This MEA features a modified anode backing structure in which a compact microporous layer is added to create an additional barrier to methanol transport thereby reducing the rate of methanol crossing over the polymer membrane. The cell with the active area of 1.625 cm² was assembled by sandwiching the MEA between two micro-fabricated Si wafers. Extensive cell polarization testing demonstrated a maximum power density of 50 mW/cm² using 2 M methanol feed at 60 °C. When the cell was operated at room temperature, the maximum power density was shown to be about 16 mW/cm² with both 2 and 4 M methanol feed. It was further found that the present μDMFC still produced reasonable performance under 8 M methanol solution at room temperature.     

The influence of a new fabrication procedure on the catalytic activity of ruthenium-selenium catalysts

A new procedure has been introduced to enhance catalytic activity of ruthenium-selenium electro-catalysts for oxygen reduction, in which materials are treated under hydrogen atmosphere at elevated temperatures. The characterisation using scanning electron microscopy, energy dispersive spectroscopy or energy dispersive X-ray spectroscopy exhibited that the treatment at 400 °C made catalysts denser while their porous nature remained, led to a good degree of crystallinity and an optimum Se:Ru ratio. The half cell test confirms feasibility of the new procedure; the catalyst treated at 400 °C gave the highest reduction current (55.9 mA cm⁻² at −0.4 V) and a low methanol oxidation effect coefficient (3.8%). The direct methanol fuel cell with the RuSe 400 °C cathode catalyst (2 mg RuSe cm⁻²) generated a power density of 33.8 mW cm⁻² using 2 M methanol and 2 bar oxygen at 90 °C. The new procedure produced the catalysts with low decay rates. The best sample was compared to the Pt and to the reported ruthenium-selenium catalyst. Possible reasons for the observations are discussed.     

A study on the dissymmetrical microporous layer structure of a direct methanol fuel cell

The effect of carbon type, carbon loading and microporous layer structure in the microporous layer on the performance of a direct methanol fuel cell (DMFC) at low temperature was investigated using electrochemical polarization techniques, electrochemical impedance spectroscopy, scanning electron microscope and other methods. Vulcan XC-72 carbon was found to be most suitable as a microporous layer for low temperature DMFC. Maximum fuel cell performance was obtained utilizing a microporous layer with carbon loading of 1.0 mg cm⁻² when air was used as an oxidant. A membrane electrode assembly with 1.0 mg cm⁻² Vulcan XC-72 carbon with 20 wt.% Teflon in the cathode and no microporous layer in the anode showed a maximum power density of 36.7 mW cm⁻² at 35 °C under atmospheric pressure. The AC impedance study proved that a cell with a dissymmetrical microporous layer structure had lower internal resistance and mass transfer resistance, thus obtaining better performance.     

Effects of membrane electrode assembly preparation on the polymer electrolyte membrane fuel cell performance

This paper presents results of recent investigations to develop an optimized in-house membrane electrode assembly (MEA) preparation technique combining catalyst ink spraying and assembly hot pressing. Only easy steps were chosen in this preparation technique in order to simplify the method, aiming at cost reduction. The influence of MEA fabrication parameters like electrode pressing or annealing on the performance of hydrogen fuel cells was studied by single cell measurements with H₂/O₂ operation. Toray paper and carbon cloth as gas diffusion layer (GDL) materials were compared and the composition of electrode inks was optimized with regard to most favorable fuel cell performance. Commercial E-TEK catalyst was used on the anode and cathode with Pt loadings of 0.4 and 0.6 mg/cm², respectively. The MEA with best performance delivered approximately 0.58 W/cm², at 65 °C cell temperature, 80 °C anode humidification, dry cathode and ambient pressure on both electrodes. The results show, that changing electrode compositions or the use of different materials with same functionality (e.g. different GDLs), have a larger effect on fuel cell performance than changing preparation parameters like hot pressing or spraying conditions, studied in previous work.     

Preparation of low-platinum-loading electrocatalysts using electroless deposition method for proton exchange membrane fuel cell systems

One promising preparative method that offers the potential for improved platinum (Pt) dispersion of electrocatalysts is electroless deposition (ED). In this study, the effects of multiwalled carbon nanotubes (MWCNTs) pretreatment and synthesis procedure on properties of the four catalysts, synthesized by ED method, have been considered. The results of energy-dispersive X-ray spectroscopy (EDS), X-ray dot-mapping, X-ray fluorescence (XRF) and cyclic voltammetry (CV) analyses showed that using palladium (Pd) precursor during two-step sensitization-activation coating procedure gives uniform Pt particles distribution on MWCNTs with low aggregation and high specific surface area (∼80 m² g⁻¹). In addition, to investigate the performance of the synthesized catalysts in experimental fuel cell system, thin-film method was used to fabricate the membrane electrode assemblies (MEAs). Obtaining the polarization curves for the fabricated MEAs (Pt loading ∼0.4 mg cm⁻²) and a commercial MEA (ElectroChem, Pt loading ∼1 mg cm⁻²) demonstrated that the catalyst prepared by two-step sensitization-activation coating procedure possesses a good performance despite of its lower Pt content.     

Functionalized carbon support with sulfonated polymer for direct methanol fuel cells

Recently electrodes for direct methanol fuel cell (DMFC) have been developed for getting high fuel cell performances by controlling composition of catalysts and sulfonated polymers, developing catalyst particles, modifying carbon supports, etc. The electrodes in DMFCs are porous layers, which are composed of catalyst, which is black or carbon supported, and sulfonated polymers in a blended form. In the present study, carbon support for catalysts was functionalized to play dual roles of a mass transport and a catalyst support. The functionalized carbon support was characterized and compared with pristine one by thermal and spectroscopic analysis, and loading of platinum (Pt) catalysts on modified support was performed by gas reduction. The electrodes with Pt on functionalized carbon support were fabricated, though the conventional electrodes were prepared with sulfonated polymer and Pt catalysts. Membrane electrode assembly with Pt catalyst on functionalized support showed a higher DMFC performance of 30 mW cm⁻² at 50 °C without using additional sulfonated polymer. Integration of electrode components in one body has another advantage of easier and simpler process in preparing electrodes for DMFCs. Improved DMFC performance of the electrode containing functionalized carbon was be attributed to a better mass transport which maximize the catalytic activities.     

Synthesis of Pt nanocatalyst with micelle-encapsulated multi-walled carbon nanotubes as support for proton exchange membrane fuel cells

Micelle-encapsulated multi-walled carbon nanotubes (MWCNTs) with sodium dodecyl sulfate (SDS) were used as catalyst support to deposit platinum nanoparticles. High resolution transmission electron microscopy (HRTEM) images reveal the crystalline nature of Pt nanoparticles with a diameter of ∼4 nm on the surface of MWCNTs. A single proton exchange membrane fuel cell (PEMFC) with total catalyst loading of 0.2 mg Pt cm⁻² (anode 0.1 and cathode 0.1 mg Pt cm⁻², respectively) has been evaluated at 80 °C with H₂ and O₂ gases using Nafion-212 electrolyte. Pt/MWCNTs synthesized by using modified SDS-MWCNTs with high temperature treatment (250 °C) showed a peak power density of 950 mW cm⁻². Accelerated durability evaluation was carried out by conducting 1500 potential cycles between 0.1 and 1.2 V with 50 mV s⁻¹ scan rate, H₂/N₂ at 80 °C. The membrane electrode assembly (MEA) with Pt/MWCNTs showed superior performance stability with a power density degradation of only ∼30% compared to commercial Pt/C (70%) after potential cycles.     

Electrodeposited Pd-Co catalyst for direct methanol fuel cell electrodes: Preparation and characterization

Pd-Co alloy has been recently proposed as a catalyst for the cathode of direct methanol fuel cells with both excellent oxygen reduction activity and methanol tolerance, hence electrodeposition of this alloy is an attractive approach for synthesizing porous metal electrodes with high methanol tolerance in direct methanol fuel cells. In this study, we electrodeposited two types of Pd-Co films onto Au substrates by applying different current density (−10 or −200 mA cm⁻²); and then characterized them in terms of morphology, composition, crystal structure, and catalytic activity. Pd-Co deposited at −10 mA cm⁻² was smooth and possessed smaller particles (ca. 10 nm), while that at −200 mA cm⁻² was dendritic (or rough) and possessed larger particles (ca. 50 nm). Both the Pd-Co alloys were found to be almost the same structure, i.e. a solid solution of ca. Pd₇Co₃ with Pd-skin, and also confirmed to possess comparable activity in oxygen reduction to Pt (potential difference at 1.0 μA cm⁻² was 0.05 V). As for methanol tolerance, cell-voltage was not influenced by addition of 1 mol dm⁻³ methanol to the oxidant solution. Our approach provides fundamental technique for synthesizing Pd-Co porous metal electrodes by electrodeposition.     

Studies of the performance of PEM fuel cell cathodes with the catalyst layer directly applied on Nafion membranes

The performance of a proton exchange membrane fuel cell (PEMFC) with gas diffusion cathodes having the catalyst layer applied directly onto Nafion membranes is investigated with the aim at characterizing the effects of the Nafion content, the catalyst loading in the electrode and also of the membrane thickness and gases pressures. At high current densities the best fuel cell performance was found for the electrode with 0.35 mg Nafion cm⁻² (15 wt.%), while at low current densities the cell performance is better for higher Nafion contents. It is also observed that a decrease of the usual Pt loading in the catalyst layer from 0.4 to ca. 0.1 mg Pt cm⁻² is possible, without introducing serious problems to the fuel cell performance. A decrease of the membrane thickness favors the fuel cell performance at all ranges of current densities. When pure oxygen is supplied to the cathode and for the thinner membranes there is a positive effect of the increase of the O₂ pressure, which raises the fuel cell current densities to very high values (>4.0A cm⁻², for Nafion 112—50 μm). This trend is not apparent for thicker membranes, for which there is a negligible effect of pressure at high current densities. For H₂/air PEMFCs, the positive effect of pressure is seen even for thick membranes.     

Performance of the Direct Methanol Carbonate Fuel Cell Using Anion Exchange Materials and Non‐Noble Metal Cathode Catalyst

A direct methanol fuel cell using a mixture of O₂ and CO₂ at the cathode was evaluated using anion exchange materials and cathode catalysts of Pt and a non‐Pt catalyst. The MEA based on non‐noble metal catalyst Acta 4020 showed superior performance than Pt/C based MEA in terms of open circuit potential and power density in carbonate environment. The fuel cell performance was improved by applying anion exchange ionomer in the catalyst layer. A maximum power density of 4.5 mW cm^–2 was achieved at 50 °C using 6.0 M methanol and 2.0 M K₂CO₃.     

Performance degradation study of a direct methanol fuel cell by electrochemical impedance spectroscopy

A stability test of a direct methanol fuel cell (DMFC) was carried out by keeping at a constant current density of 150 mA cm⁻² for 435 h. After the stability test, maximum power density decreased from 68 mW cm⁻² of the fresh membrane-electrode-assembly (MEA) to 34 mW cm⁻² (50%). Quantitative analysis on the performance decay was carried out by electrochemical impedance spectroscopy (EIS). EIS measurement of the anode electrode showed that the increase in the anode reaction resistance was 0.003 Ω cm². From the EIS measurement results of the single cell, it was found that the increase in the total reaction resistance and IR resistance were 0.02 and 0.05 Ω cm², respectively. Summarizing the EIS measurement results, contribution of each component on the performance degradation was determined as follows: IR resistance (71%) > cathode reaction resistance (24%) > anode reaction resistance (5%). Transmission electron microscopy (TEM) results showed that the average particle size of the Pt catalysts increased by 30% after the stability test, while that of the PtRu catalysts increased by 10%.     

Microfabricated polymer electrolyte membrane fuel cells with low catalyst loadings

Miniaturized fuel cells as compact power sources fabricated in Pyrex glass using standard polymer electrolyte membrane (PEM) and electrode materials are presented. Photolithographic patterned and wet chemically etched serpentine flow channels of 1 mm in width and 250  m in depth transport the fuels to the cell of 1.44 cm² active electrode area. Feeding H₂/O₂ a maximum power density of 149 mW cm⁻² is attained at a very low Pt loading of 0.054 mg cm⁻², ambient pressure, and room temperature. Operated with methanol and oxygen about 9 mW cm⁻² are achieved at ambient pressure, 60 °C, and 1 mg cm⁻² PtRu/Pt (anode/cathode) loading. A planar two-cell stack to demonstrate and investigate the assembly of a fuel cell system on Pyrex wafers has successfully been fabricated.     

A Study on Process Parameters of Direct Ethanol Fuel Cell

Ethanol is one of the promising future fuels of Direct Alcohol Fuel Cells (DAFC). The electro‐oxidation of ethanol fuel on anode made of carbon‐supported Pt‐Ru electrode catalysts was carried out in a lab scale direct ethanol fuel cell (DEFC). Cathode used was Pt‐black high surface area. The membrane electrode assembly (MEA) was prepared by sandwiching the solid polymer electrolyte membrane, prepared from Nafion^® (SE‐5112, DuPont USA) dispersion, between the anode and cathode. The DEFC was fabricated using the MEA and tested at different catalyst loadings at the electrodes, temperatures and ethanol concentrations. The maximum power density of DEFC for optimized value of ethanol concentration, catalyst loading and temperature were determined. The maximum open circuit voltage (OCV) of 0.815 V, short circuit current density (SCCD) of 27.90 mA/cm² and power density of 10.30 mW/cm² were obtained for anode (Pt‐Ru/C) and cathode (Pt‐black) loading of 1 mg/cm² at a temperature of 90°C anode and 60°C cathode for 2M ethanol.     

Membrane electrode assembly with Pt/SiO2/C anode catalyst for proton exchange membrane fuel cell operation under low humidity conditions

In this work, a novel self-humidifying membrane electrode assembly (MEA) with Pt/SiO₂/C as anode catalyst was developed to improve the performance of proton exchange membrane fuel cell (PEMFC) operating at low humidity conditions. The characteristics of the composite catalysts were investigated by XRD, TEM and water uptake measurement. The optimal performance of the MEA was obtained with the 10 wt.% of silica in the composite catalyst by single cell tests under both high and low humidity conditions. The low humidity performance of the novel self-humidifying MEA was evaluated in a H₂/air PEMFC at ambient pressure under different relative humidity (RH) and cell temperature conditions. The results show that the MEA performance was hardly changed even if the RHs of both the anode and cathode decreased from 100% to 28%. However, the low humidity performance of the MEA was quite susceptible to the cell temperature, which decreased steeply as the cell temperature increased. At a cell temperature of 50 °C, the MEA shows good stability for low humidity operating: the current density remained at 0.65 A cm⁻² at a usual work voltage of 0.6 V without any degradation after 120 h operation under 28% RH for both the anode and cathode.     

Graphene-supported platinum and platinum-ruthenium nanoparticles with high electrocatalytic activity for methanol and ethanol oxidation

In this study, Pt and Pt-Ru nanoparticles were synthesized on graphene sheets and their electrocatalytic activity for methanol and ethanol oxidation was investigated. Experimental results demonstrate that, in comparison to the widely-used Vulcan XC-72R carbon black catalyst supports, graphene-supported Pt and Pt-Ru nanoparticles demonstrate enhanced efficiency for both methanol and ethanol electro-oxidations with regard to diffusion efficiency, oxidation potential, forward oxidation peak current density, and the ratio of the forward peak current density to the reverse peak current density. For instance, the forward peak current density of methanol oxidation for graphene- and carbon black-supported Pt nanoparticles is 19.1 and 9.76 mA/cm², respectively; and the ratios are 6.52 and 1.39, respectively; the forward peak current density of ethanol oxidation for graphene- and carbon black-supported Pt nanoparticles is 16.2 and 13.8 mA/cm², respectively; and the ratios are 3.66 and 0.90, respectively. These findings favor the use of graphene sheets as catalyst supports for both direct methanol and ethanol fuel cells.     

The effect of two-layer cathode on the performance of the direct methanol fuel cell

To reduce the effect of methanol permeated from the anode, the structure of the cathode was modified from a single layer with Pt black catalyst to two-layer with PtRh black and Pt black catalysts, respectively. The current density of the direct methanol fuel cell (DMFC) using the two-layer cathode was improved to 228 mA/cm^-2 compared to that (180 mA/cm^-2) of the DMFC using the single layer cathode at 0.3 V and 303 K. From the cyclic voltammograms (CVs), it is indicated that the amount of adsorbates on the metal catalyst in the two-layer cathode is less than that of adsorbates in the single layer cathode after methanol test. In addition, the adsorbates were removed very rapidly by electrochemical oxidation from the two-layer cathode. It is suggested fromex situ X-ray absorption near edge structure analysis that the d-electron vacancy of Pt atom in the two-layer cathode is not changed by the methanol test. Thus, Pt is not covered with the adsorbates, which agrees well with the results of CV.     

Degradation of high temperature MEA with PBI-H3PO4 membrane in a life test

The article reports on the results of a 780 h life test of high temperature MEA with PBI-H₃PO₄ membrane. The MEA was loaded by current density 0.2 A cm⁻² for 763 h at 160 °C in hydrogen-air feed. The load was discontinued 14 times during the life test including three complete shut downs. In the course of the life test MEA characteristics were studied by electrochemical methods. Pt particle size growth was evaluated by ex situ measurements of electrochemical hydrogen adsorption/desorption with the cathode catalyst sampled after the life test and with pristine catalyst. Possible changes of electrochemically active surface area (ESA) of carbon support were monitored by electrochemical impedance studies (EIS) performed in the course of the MEA life test. Average Pt particle diameter was found 3.8 and 7.8 nm for pristine catalyst and for catalyst sampled after the life test, respectively. ESA of carbon support remained unchanged, membrane resistance decreased by ∼20%, hydrogen crossover increased by a factor of 14, although remained insignificant. Voltage loss rate in the life test was ∼25 μV h⁻¹. The major cause of the MEA degradation was identified as a loss of Pt ESA by particle size growth.     

Characterization and performances of cobalt-tungsten and molybdenum-tungsten carbides as anode catalyst for PEFC

The preparation of carbon-supported cobalt-tungsten and molybdenum-tungsten carbides and their activity as an anode catalyst for a polymer electrolyte fuel cell were investigated. The electrocatalytic activity for the hydrogen oxidation reaction over the catalysts was evaluated using a single-stack fuel cell and a rotating disk electrode. The characterization of the catalysts was performed by XRD, temperature-programmed carburization, temperature-programmed reduction and X-ray photoelectron spectroscopy. The maximum power densities of the 30 wt% 873 K-carburized cobalt-tungsten and molybdenum-tungsten mixed with Ketjen carbon (cobalt-tungsten carbide (CoWC)/Ketjen black (KB) and molybdenum-tungsten carbide (MoWC)/KB) were 15.7 and 12.0 mW cm⁻², respectively, which were 14 and 11%, compared to the in-house membrane electrode assembly (MEA) prepared from a 20 wt% Pt/C catalyst. The CoWC/KB catalyst exhibited the highest maximum power density compared to the MoWC/KB and WC/KB catalysts. The 873 K-carburized CoW/KB catalyst formed the oxycarbided and/or carbided CoW that are responsible for the excellent hydrogen oxygen reaction.