釉层龟裂的成因及其预防

针对釉层龟裂缺陷，探讨了釉应力与瓷坯残余石英量、釉层厚度及热稳定性的相互关系与规律。希望能对实际生产具有一定的指导作用。     

裂纹釉的研制及残余应力有限元分析

以长石、滑石、方解石、高岭土等为主要原料制备裂纹釉。研究了釉料配方组成对釉面裂纹效果的影响,并用有限元方法对釉层中的残余应力分布特征及残余应力对裂纹产生的作用机理进行了分析。结果表明:在1250～1300℃、保温时间30min,以及坯、釉的物理性能具有合适的差异时,可以得到效果较好的裂纹釉,且有限元对残余应力的分析与实验结果取得了较好的吻合。     

Delayed curvature and residual stresses in porcelain tiles

Most industrial porcelain tiles suffer changes in their curvature after firing: such process is known as delayed curvature. One of the hypotheses used to explain this phenomenon is based on the relaxation of residual stresses by creep. In this study two types of industrial glazed porcelain tiles have been studied. One of them displayed delayed curvature after firing, whereas the other one presented a stable curvature. The main objective was to determine if the delayed curvatures were caused by the residual stresses generated during rapid industrial cooling. Both types of existing residual stresses (thermal stresses, caused by thermal gradients inside the tile during cooling, and body–glaze fit stresses, due to the thermal expansion mismatch between body and glaze) were measured, as well as related samples properties (elastic modulus, creep behaviour, thermal expansion). The results demonstrated that the residual stresses are not the main cause of the delayed curvature phenomenon.     

中温裂纹釉的研究

本文以钠长石、石英、硅灰石、方解石等为主要原料,采用正交实验法制备了一种中温裂纹釉,并探究了配方组成对冰裂纹釉面效果的影响。研究结果表明：坯、釉的膨胀系数差值大,是釉面开裂的重要影响因素。当坯体的膨胀系数为6.52×10-6/℃,釉的膨胀系数为7.29×10-6/℃时,可获得良好的冰裂纹釉。     

分相艺术釉釉泡缺陷形成机理的探讨

论述了分相窑变釉形成的基本原理,分析了分相艺术釉针孔和釉泡形成的原因,得出了除烧成温度太高或太低、素烧坯不到位、坯体挥发所致之外,还有一种新的可能,那就是SiC的落渣所致的结论。     

全抛釉气泡影响因素的研究

针对目前建陶行业全抛釉气泡存在的难题,本文采用单因素实验法研究了全抛釉气泡的主要影响因素及其规律,揭示了坯体、底釉以及全抛釉的相关性能与气泡的关系。结果表明：全抛釉始熔点应与坯体的烧结性能以及底釉的融熔特性相匹配,严格控制全抛釉的高温黏度及表面张力有利于控制抛釉层中的气泡的数量和尺寸。全抛釉中形成一定量的晶体对气泡的控制和稳定有促进作用。     

缩点釉在工艺美术陶瓷上的应用研究

缩点釉是一种釉面会收缩成点粒现象的釉。阐述了缩点釉产生的机理．介绍了研制经过,讨论了几个影响缩点效果的问题。并指出只要合理地选用原料．调整好坯釉配方,掌握好施釉厚度和烧成温度。是可以得到均匀、好看、美观的“缩点釉”的;若能在装饰对象和装饰方法上大傲文章,可以使这一具有“缺陷功能”的釉种产生更好的艺术效果。     

Investigation of Glaze Layer Formation on Green Ceramic Bodies

Using a high‐speed and high‐resolution‐camera system of droplets in glaze sprays and their impact on the surface of a green ceramic body based on silicate tiles have been characterized. The influence of the surface tension of the glaze slips on the droplet size distribution and their wetting behavior on contact with the green silicate body surface have been investigated. The unfired glaze layers have been studied by means of scanning electron microscopy and computer tomography. The impact angle of the droplets as well as the size of the droplets is of great importance for a high glaze surface quality.     

废瓷粉在釉料中的应用

本文对陶瓷工业中的废瓷处理进行了一系列的釉料配方对比试验。通过对比试验发现:在釉料配方中引入一定量的废瓷粉取代长石等釉用原料,可以提高釉面质量及产品良品率。     

素烧坯改素坯施釉用色釉的配制

介绍了素烧坯改素坯施釉用色釉的配制。用配制的色釉可直接施于素坯表面,而不需要在素烧后施釉,使成坯与施釉连续操作,大幅度缩短生产周期,而且形成的釉层也不会出现釉裂和剥釉缺陷。     

无铅碱硼釉的研究分析

通过对无铅碱硼硅酸盐釉的氧化物体系的试验研究，分析了釉组分中SiO2，B2O3及金属氧化物对釉的热膨胀性、表面张力及坯釉结合层形成等方面的影响作用。     

论骨质瓷的坯釉适应性

骨质瓷通常采用高温素烧、低温釉烧二次烧成工艺,其坯釉料组成和生产工艺存在复杂性,在制备过程中,常因坯釉的不适应而影响其性能和釉面质量。本文从四个方面论述了骨质瓷坯釉适应性的影响因素,并提出改善途径。     

自释釉瓷机理的研究

本文集中研究了自释釉瓷胎不同温度阶段的结构特征，从结构的变化分析玻璃相的迁移过程，借助能谱微区探针分析玻璃相和晶相的成份变化．并与实物辅证相对照，从而提出１μｍ左右细微晶体堆集．形成新的毛细管构造，毛细管压力对液相产生驱动的观点。     

釉面分相对无铅CuO-MnO2系金属光泽釉的影响

以钙系生料釉为基础,引入结晶剂CuO、MnO₂制备无铅CuO-MnO₂系金属光泽釉;结合XRD、SEM-EDS进行物相组成定性分析和显微结构表征,系统探究外加TiO₂、V₂O₅以及玻璃粉对金属光泽釉釉面分相的影响。研究表明:一定量的TiO₂、V₂O₅引入能有效促进釉面的分相,将玻璃粉部分替换基础釉中的钾长石能使得釉熔体的高温粘度降低,并进一步加剧釉面分相,促进CuMn₂O₄铜锰尖晶石在釉层表面的析出和富集;当TiO₂引入量为2%,V₂O₅引入量为1%,玻璃粉引入量为25%(同为质量分数)时,金属光泽釉釉面效果最佳。     

薄形陶瓷板釉泡、孔洞影响因素探讨

薄形陶瓷板作为一种可持续发展陶瓷产品越来越受到人们的欢迎.但是,在生产薄形陶瓷板过程中,非常容易产生釉泡、孔洞等缺陷.笔者从各个工序探讨了产生釉泡、孔洞缺陷的影响因素.通过研究发现,产生这些缺陷的主要原因是因为坯体里的硫酸盐和碳酸盐在分解过程中排气不充分导致.最后结果表明:通过在坯体配方中降低高CaO含量的原材料比例原...     

景德镇传统低温黄釉的文化与科技内涵

研究和分析了景德镇传统低温黄釉蕴含的历史文化内涵及社会文化对其的影响,得出传统低温黄釉技术与封建社会文化、制度等的关系;同时借助于科学仪器对其进行了化学成分、显微结构等分析研究。通过分析比较得出了历代低温黄釉制品胎、底釉、黄釉和白釉的化学组成变化规律,以及不同工艺方法对制品外观和显微结构的影响情况。     

金属光泽釉的研究

论述了开展此项目研究的目的．釉料所用原料及配方组成，釉的制作工艺以及与各种坯料的适应性．还对该釉的烧成和呈色效果进行了分析。     

铜红釉

本分析了铜红釉的化学组成，组成与釉呈色的关系；讨论了铜红釉难以烧成的根本原因，分析了生产工艺对铜红釉呈色的影响，介绍了几种现代铜红釉的曲型配方及生产工艺要点；对铜红釉的呈色机理作了初步探讨。     

银鳞釉及高银釉的研究

本文对日本银鳞釉及高银釉进行了系统的研究，选择适合这两种釉的组成系统，确定了其最佳化学组成，釉面效果达到日方产品水平。本文还对影响这两种釉的各种因素进行了较详细的分析讨论，并指出了高银釉的形成机理是熔体液－液分相。     

日用瓷用锆乳浊釉的研制

针对日用瓷工业优质陶瓷原料日趋紧缺 ,使用劣质原料会使坯体产生发黄或发灰的现象 ,研制了可以遮盖坯体颜色的高白度锆乳浊釉 ,并对影响乳浊能力的因素进行了探讨。