温度对高速电弧喷涂FeNiBSi/Cr_3C_2复合涂层热腐蚀性能的影响

采用高速电弧喷涂技术在45钢基体上制备出Fe Ni BSi/Cr3C2复合涂层.采用光学显微镜和扫描电镜分析涂层的显微结构,以及X射线衍射分析涂层相组成.试验选用摩尔比为7∶3的Na2SO4+K2SO4饱和水溶液为腐蚀介质涂刷于试样表面,并以20G钢作对比材料,在550~750℃下研究了涂层的抗热腐蚀性能.结果表明,涂层具有典型的层状结构特征,致密且连续.涂层的抗热腐蚀性能明显优于20G钢.在550和650℃下涂层表面形成了致密的氧化膜(Fe2O3,Cr2O3和Fe Cr2O4)阻碍了熔盐的侵入,提高了涂层抗热腐蚀性能.在750℃下涂层氧化膜变得不完整,不能有效地阻隔熔盐,此时涂层的抗热腐蚀性能较差.     

K452合金表面CVD渗铝涂层制备温度对其750℃硫酸盐热腐蚀行为的影响

采用化学气相沉积(CVD)技术在K452合金表面沉积渗铝涂层,沉积温度分别为850、950和1050℃。研究了沉积温度对CVD渗铝涂层在750℃空气中表面沉积Na₂SO₄及Na₂SO₄+NaCl环境下热腐蚀行为的影响。采用扫描电子显微镜(SEM)、X射线能谱仪(EDS)和X射线衍射仪(XRD)对腐蚀前和后的试样进行截面形貌观察和物相结构分析。结果表明,在750℃下表面沉积Na₂SO₄及Na₂SO₄+NaCl热腐蚀50 h后,3种涂层试样均表现出了较K452合金更好的抗热腐蚀性能,且涂层的抗热腐蚀性能随着涂层沉积温度的增加而增强。     

激光重熔对TiAl合金表面等离子喷涂热障涂层耐热腐蚀性能的影响

分别采用等离子喷涂和等离子喷涂一激光重熔复合工艺在TiAl合金表面制备了热障涂层,研究了两种涂层在850℃：下75％Na2SO4＋25％NaCl（质量分数）熔融盐中的热腐蚀行为,进而分析激光重熔工艺对等离子喷涂热障涂层耐热腐蚀性能的影响。结果表明：激光重熔热障涂层可以有效地阻止熔融盐腐蚀介质进入涂层发生腐蚀,具有更优的抗热腐蚀性能和使用寿命。     

纳米化对K38G合金900℃涂盐热腐蚀行为的影响

通过磁控溅射方法在K38G合金上沉积了一层与其同成分的纳米晶涂层。研究了铸态肥8G合金及其纳米晶涂层在900℃的涂盐(盐的成分为75％Na2SO4 25％K2SO4)热腐蚀行为。结果表明：当涂薄盐膜时(0．8mg／cm^2)，纳米晶涂层表面生成一层连续的Al2O3膜，消除了内硫化；当涂厚盐膜时(3mg／cm^2)，纳米晶涂层表面氧化产物为Al2O3、Cr2O3和TiO2混合氧化物，虽然没有消除内硫化，但纳米晶涂层仍然提高了合金的抗热腐蚀性能。并讨论了纳米晶涂层的抗热腐蚀机理。     

共渗制备NiCrAlY涂层及抗高温腐蚀研究

采用热扩散的方法在高温合金K417G基体上制备了NiCrAlY涂层,经测定,涂层以β–NiAl相为主,Cr以固溶态和AlCr(x)相同时存在。1000和1100℃恒温氧化试验表明,NiCrAlY涂层显著提高了合金的抗氧化性,氧化膜致密稳定的Al2O3为主,300h后氧化膜没有明显的剥落。对基体合金和涂层试样进行了900℃,NaCl/Na2SO4(25:75)融盐环境的热腐蚀试验。结果表明,NiCrAlY涂层氧化膜完整,涂层内硫化物含量低,有效提高了抗热腐蚀性能。     

NaCl盐对Ti_2AlNb合金表面渗镀Al层热腐蚀行为影响

为提高Ti_2AlNb合金的实际使用温度,采用加弧辉光等离子渗镀技术在合金表面制备渗镀Al层,研究渗镀Al层在750℃下涂盐Na_2SO_4和Na_2SO_4+25%NaCl的热腐蚀行为。同时利用扫描电子显微镜(SEM)、能谱仪(EDS)对腐蚀产物的形貌进行观察,并结合X射线衍射对相组成进行分析。结果表明:渗镀Al层组织均匀致密,与基体结合良好。涂层可分为明显的3个区域:最外层Al_2O_3薄膜、次表层纯Al沉积层和内层Al-Ti-Nb扩散层。扩散层主要包括Al_3Ti﹑Al_3Nb和AlNb_2等相。渗镀Al层试样在750℃的Na_2SO_4盐热腐蚀100 h后,仅增重约2 mg/cm~2,表现出良好的抗热腐蚀性能;而在Na_2SO_4+25%NaCl混合盐中,试样则先增重后逐渐减重,整个涂层出现明显开裂和剥落,其原因是Cl–的渗入使表面形成的Al_2O_3膜被破坏,进而加速消耗涂层中的Al。     

搪瓷/NiCrAlY复合涂层的抗高温氧化及热腐蚀行为

研究了溅射NiCrAlY及搪瓷/NiCrAlY复合涂层在900℃空气氧化及850℃75mass%Na2SO4＋25mass%K2SO4和75mass%Na2SO4＋25mass%NaCl的热腐蚀行为.结果表明：溅射NiCrAlY涂层900℃表面生成了单一的氧化铝膜,具有良好的抗氧化性能,而搪瓷复合涂层进一步提高了NiCrAlY层的抗氧化性能;850℃两种盐的热腐蚀表明,基体合金没有出现内氧化及内硫化现象,搪瓷层的成分也没有显著变化,表现出优异的抗热腐蚀性能.     

Al-Cr涂层对TC21合金抗氧化和热腐蚀性能的影响

采用双辉等离子表面渗铬和后续多弧离子镀铝处理在TC21合金表面制备Al-Cr涂层;同时研究Al-Cr涂层在850℃下的高温氧化行为和850℃下25%NaCl+75%Na_2SO_4(质量分数)混合盐中的热腐蚀行为。结果表明:Al-Cr复合涂层包括表面富Al沉积层、中间Al-Cr扩散层和内侧Cr-Ti互扩散层。在850℃氧化100 h后,Al-Cr涂层表面生成致密Al_2O_3膜,对基体有很好的保护作用;中间Al-Cr扩散层中Cr元素的存在促进Al的选择性氧化,有利于涂层的后续氧化行为。在850℃混合熔盐中腐蚀100 h后,内部Cr-Ti扩散区仍保持完整,涂层表现出较好的热腐蚀抗力。     

Al-Si涂层在900℃硫酸盐中的热腐蚀行为

采用料浆法在Ni基高温合金上制备了Al-Si扩散涂层，研究了表面涂覆75mass%Na2SO4+K2SO4盐膜的基体合金和Al-Si涂层在900℃空气中的热腐蚀行为.结果表明，铸态合金遭受了灾难性的热腐蚀，合金出现严重的内硫化和内氧化，而Al-Si涂层由于表面生成致密的、保护性Al2O3膜，以及涂层中Cr元素和一些富Si相的有益作用而表现出优异的抗热腐蚀性能.       

Cr25Ni20Si2合金表面复合搪瓷涂层的抗热腐蚀研究

在Cr25Ni20Si2合金上制备了施加Ni中间层的复合搪瓷涂层,研究了Cr25Ni20Si2合金、搪瓷涂层及含镍中间层的复合搪瓷涂层在800℃熔融盐(75%Na2SO4+25%NaCl)下的腐蚀行为和腐蚀机理。试验表明合金在孕育期结束后发生灾难性腐蚀,腐蚀机理主要遵从硫化-碱融模式;未镀镍搪瓷涂层主要以直接脱落丧失保护能力,复合搪瓷涂层则以物理减薄方式缓慢失效。搪瓷涂层使合金的抗热腐蚀能力提高了30%,复合搪瓷涂层可使合金抗热腐蚀能力提高100%以上。这种复合搪瓷涂层是有效的抗热腐蚀涂层。     

纳米 NiCrBSi-TiB2 涂层在硫酸熔盐中的热腐蚀行为研究

目的研究纳米NiCrBSi-TiB2涂层在800℃下的Na2SO4-30%(质量分数)K2SO4熔盐中的热腐蚀行为。方法采用超音速火焰技术在中碳钢表面喷涂纳米NiCrBSi-TiB2涂层,以饱和Na2SO4-30%K2SO4溶液为腐蚀介质,研究该涂层在800℃时的热腐蚀行为。结果微米涂层晶粒粗大,Si的扩散系数低,易出现贫Si富Cr层,形成的Cr2O3膜在碱性熔盐中具有较低的溶解度,对涂层具有良好的保护作用。结论微米涂层在Na2SO4-30%K2SO4熔盐中具有更优的抗热腐蚀性能。     

Hot Corrosion Behavior of SiO_2–Al_2O_3–Glass Composite Coating on Ti–47Al–2Cr–2Nb Alloy: Diffusion Barrier for S and Cl

Type Ⅰ hot corrosion behavior of SiO_2-Al_2O_3-glass composite coating based on Ti-47 Al-2 Cr-2 Nb substrate was investigated in the mixture salt of 25 wt%NaCl + 75 wt%Na_2SO_4 at 850 °C. The results showed that there was a bidirectional ion exchange between composite coating and the film of mixed salts, and the sodium ion in the molten salts penetrated into the glass matrix of composite coating, while the potassium ion in the glass matrix dissolved into the molten salts. A decrease in hot corrosion rate was achieved for the coated alloy in comparison with the bared substrate due to the composite coating acting as a diffusion barrier to sulfur and chlorine and preventing the molten salts from diffusing to the coating/alloy interface during the hot corrosion exposure. Additionally, the composite coating decreased the oxygen partial pressure at the coating/alloy interface and promoted the selective oxidation of Al to form a protective Al_2O_3 layer.     

Effect of enamel coating on long-term oxidation and hot corrosion behavior of Ti-24Al-17Nb-0.5Mo alloys

The effect of enamel coating on long-term isothermal oxidation at 700 ℃ and cyclic oxidation at 800 ℃ in air and hot corrosion resistance of Ti-24Al-17Nb-0. 5Mo in 75% (Na2SO4 K2SO4 ) 25% NaCl (mass fraction) molten mixed salts at 700 ℃ was investigated. The results indicate that Ti-24Al-17Nb-0.5Mo alloy exhibits relatively poor long-term oxidation resistance due to the formation of Al2O3 TiO2 Nb2O5 mixed scales and poor hot corrosion resistance due to the spallation of scales formed in molten (Ns, K)2 SO4 NaCl. Enamel coating can effectively protect Ti-24Al-17Nb-0.5Mo alloy from long-term oxidation at high temperature in air and remarkably improve the hot corrosion resistance of Ti-24Al-17Nb-0. 5Mo alloy, and can act as the barrier to suppress the migration of oxygen and corrosive ions into the substrate.     

包铝LY12铝合金表面镀铬层的界面显微组织及耐蚀性能

利用电镀法在包铝LY12铝合金表面上制备约20 μm厚 的Cr镀层，通过对热处理前后镀铬试样的断面显微硬度分布的测试，用扫描电镜对镀铬试样的断面形貌进行观察分析以及电子探针测定镀铬试样界面处的元素线分布状态等分析了镀铬试样的界面显微组织.同时，分别在60℃、Na2CO3(25 g/L)和室温、NaOH(10 g/L)两种溶液中对镀铬层的耐蚀性能进行了考察.结果表明，通过镀铬处理在上述两种腐蚀环境下使包铝LY12铝合金的耐蚀性能得到显著提高.     

电弧离子镀NiCrAlY涂层900℃的热腐蚀行为

采用电弧离子镀技术在镍基单晶合金上沉积Ni28Cr11Al0.5Y涂层,并研究了镍基单晶合金及有Ni28Cr11Al0.5Y涂层镍基单晶合金在900℃的75%Na2SO4+25%K2SO4熔盐中的热腐蚀行为。结果表明,镍基单晶合金遭受了破坏性的热腐蚀,出现了严重的内硫化和内氧化;而由于Ni28Cr11Al0.5Y涂层在熔盐中生成连续的Al2O3氧化膜,阻止了熔盐对单晶合金的腐蚀,有涂层镍基单晶合金表现出优良的抗热腐蚀性能。     

P91钢亚音速喷涂NiCr/Cr3C2涂层的热腐蚀行为研究

采用亚音速火焰喷涂方法在P91钢上制备了NiCr/Cr3C2涂层,研究了样品在600,650和700℃的80 ％Na2 SO4 +10％K2SO4+10％KCl(质量分数,后同)混合熔融盐中的热腐蚀行为,利用XRD和SEM分析了表面成分和结构.结果表明:喷涂NiCr/Cr3 C2涂层样品在热腐蚀过程中,腐蚀产物从样品表...     

TiAl合金表面等离子喷涂MCrAlY涂层热腐蚀行为研究

研究TiAl合金表面等离子喷涂NiCoCrAl-Y2O3涂层在850 ℃下对75%Na2SO4+25%NaCl熔盐的热腐蚀行为,及对TiAl金属间化合物抗高温热腐蚀性能的影响。研究表明,在850 ℃,等离子喷涂NiCoCrAl-Y2O3涂层由于生成Cr2O3,NiO和NiCr2O4等各种氧化物组成的氧化层,显著提高了TiAl基体的抗热腐蚀性能。在热腐蚀过程中,S元素以Ni元素为载体,逐步渗入涂层中,生成过渡产物Ni3S2。随着O分压的升高,反应进入了氧化阶段,生成Cr2O3、NiO等氧化物,随着两种物质含量的增加,最后发生固相反应,生成尖晶石结构的NiCr2O4化合物。过渡产物Ni3S2与腐蚀介质中的Cl-离子形成微电池,可以加快热腐蚀反应速度     

Ti65合金磷酸盐涂层抗高温氧化性能研究

目的通过表面涂层提高高温钛合金Ti65的抗高温氧化性能。方法采用喷涂法在Ti65合金基体上制备以磷酸铝为粘结剂、Al和Al/SiC为填料的两种磷酸盐抗高温氧化复合涂层。研究Ti65合金和涂层样品在650℃准等温、静态空气条件下的氧化动力学行为。用XRD和SEM/EDS分别对涂层样品氧化前后的物相组成、组织形貌和微区成分进行表征分析;用电子探针(EPMA)分析涂层样品的元素分布情况。结果650℃抗高温氧化实验结果表明,磷酸盐涂层样品的准等温氧化动力学曲线均符合抛物线规律,两种涂层样品的抛物线氧化速率常数kp分别为3.922×10^-2、1.768×10^-2 mg/(cm^2·h^1/2)和2.48×10^-2、3.385×10^-4 mg/(cm^2·h^1/2),均小于Ti65合金,氧化增重显著降低。以Al/SiC为填料的磷酸铝涂层的抗氧化性能最好,氧化1000 h,质量增加0.20 mg/cm^2,约为Ti65基体氧化增重(1.13 mg/cm^2)的1/6。微观分析结果表明,两种磷酸盐涂层样品在650℃准等温氧化后,涂层与基体形成扩散层,生成TiAl3金属间化合物,涂层表面均保持完好,没有裂纹和孔隙,有效阻止了氧元素向Ti65基体的扩散,保护基体不受氧化。结论磷酸盐涂层能有效阻止650℃温度下氧向Ti65合金基体的扩散,具有优异的抗高温氧化性能。     

Ti60合金表面电弧离子镀Ti-Al-Cr(Si,Y)防护涂层的热腐蚀行为

采用电弧离子镀技术在Ti60合金表面制备了Ti-48%Al-12%Cr(0.2%Si,0.1%Y,原子分数)防护涂层.利用XRD,SEM和EDS研究了Ti60合金及Ti-Al-Cr(Si,Y)涂层在Na_2SO_4和75%Na_2SO_4+25%K_2SO_4(质量分数)中800及850℃下的热腐蚀行为.结果表明,Ti60合金基体在800和850℃的硫酸盐中发生了严重的腐蚀,腐蚀产物发生了明显剥落.涂层样品在800和850℃的硫酸盐腐蚀介质中,表面形成了保护性的氧化膜,可以有效地保护Ti60合金免受腐蚀破坏.Ti60合金及涂层样品在75%Na_2SO_4+25%K_2SO_4混合硫酸盐中的腐蚀比在纯K_2SO_4中剧烈.Si和Y元素的加入使得Ti-Al-Cr-Si和Ti-Al-Cr-Si-Y涂层在硫酸盐中抗热腐蚀性能优于Ti-Al-Cr涂层.     

一种定向凝固Co基合金的热腐蚀行为

利用箱式电阻炉、SEM等手段,研究了一种定向凝固Co基合金在不同介质中的热腐蚀行为及机理。研究结果表明:合金在Na2SO4中的热腐蚀最为严重,在75%Na2SO4+25%NaCl中的热腐蚀程度最轻。合金在Na2SO4中的热腐蚀过程中主要发生了酸性熔融反应,形成了Al2(SO4)3,Cr2Ni3,Cr4Ni15W和Al4CrNi15等腐蚀产物,而在NaCl中的热腐蚀主要发生了活性氧化反应,合金在75%Na2SO4+25%NaCl中热腐蚀时,部分酸性熔融反应和活性氧化反应受到抑制,主要形成了一系列的Ni-S化合物。