Dielectric, electrical and magnetoelectric characterization of (x)Ni0.8Zn0.2Fe2O4 + (1 − x)Pb0.93La0.07(Zr0.60Ti0.40)O3 composites

The structural, electrical, dielectric, magnetic and magnetoelectric properties of (x)Ni_0.8Zn_0.2Fe₂O₄ + (1 − x)Pb_0.93La_0.07(Zr_0.60Ti_0.40)O₃ (x = 0, 0.15, 0.30, 0.45 and 1) have been studied by means of various experimental techniques. Polycrystalline samples of this series have been prepared by the double sintering ceramic method. X-ray diffraction data analysis revealed purity of the composites. Microstructural analysis using scanning electron microscopy mode depicts the presence of two phases in contact with each other. Dielectric properties were studied at and well above room temperature. Temperature dependent variation of the dielectric constant show diffused phase transition which can be well described by fitting the Lorentz-type relation, . Observation of well-saturated ferroelectric hysteresis loop and magnetic hysteresis loop for composites indicates that ferroelectric and magnetic ordering exist simultaneously at room temperature. The static value of magneto electric voltage coefficient (α_E) has been studied as a function of magnetic field at room temperature for all the composites. The maximum value of α_E is 7.53 mV/(cm Oe) for 85% PLZT-15% NZFO composites.     

Synthesis of nanocrystalline xCuFe2O4-(1 − x)BiFeO3 magnetoelectric composite by chemical method

xCuFe₂O₄-(1 − x)BiFeO₃ spinel-perovskite nanocomposites with x = 0.1, 0.2, 0.3 and 0.4 were prepared using citrate precursor method. X-ray diffraction (XRD) analysis showed phase formation of xCuFe₂O₄-(1 − x)BiFeO₃ calcined at 500 °C. Transmission electron microscopy (TEM) shows formation of nanocrystallites of xCuFe₂O₄-(1 − x)BiFeO₃ with an average particle size of 40 nm. Variation of dielectric constant and dielectric loss with frequency showed dispersion in the low frequency range. Coercivity, saturation magnetization and squareness have been found to vary with concentration of ferrite phase and annealing temperature due to the increase in crystallite size. Squareness and coercivity increased with an increase in annealing temperature up to 500 °C and then decreased with a further increase in temperature to 600 °C. Magnetoelectric effect of the nanocomposites was found to be strongly depending on the magnetic bias and magnetic field frequency.     

Synthesis, low-temperature sintering and the dielectric properties of the ZnO-(1 − x)TiO2-xSnO2 (x = 0.04-0.2)

ZnO-(1 − x)TiO₂-xSnO₂ (x = 0.04-0.2) ceramics were prepared by conventional mixed-oxide method combined with a chemical processing. Fine particle powders were prepared by chemical processing to activate the formation of compound and to improve the sinterability. One wt.% of V₂O₅ and B₂O₃ with the mole ratios of 3:1 were used to lower the sintering temperature of ceramics. The effect of Sn content on phase structure and dielectric properties were investigated. The results show that the substituting Sn for Ti accelerates the hexagonal phase transition to cubic phase, and an inverse spinel structure Zn₂(Ti_1−xSn_x)O₄ solid solution forms. The best dielectric properties obtained at x = 0.12. The ZnO-0.88TiO₂-0.12SnO₂ ceramics sintered at 900 °C exhibit a good dielectric property: ?_r = 29 and tan δ = 9.86 × 10⁻⁵. Due to their good dielectric properties, low firing characteristics, ZnO-(1 − x)TiO₂-xSnO₂ (x = 0.04-0.2) can serve as the promising microwave dielectric capacitor.     

Preparation and electrical properties of xCaRuO3/(1 − x)CaTiO3 perovskite composites

CaRuO₃-CaTiO₃ ceramic composites were prepared by sintering for short times for potential applications in the areas of electronic ceramics. Scanning electron microscopy and energy dispersive X-ray analysis showed two separate phases, CaRuO₃ and CaTiO₃ in the composite. Conductivity data, measured by the four-probe method, showed that the composites have high electrical conductivity when x ≥ 0.19 in xCaRuO₃-(1 − x)CaTiO₃ composites. Furthermore, the nanoparticle of calcium ruthenate prepared by reverse micelle synthesis was used to be conductive agent for the composite. The result shows that the use of nano-sized calcium ruthenate enabled higher electrical conductivity to be maintained down to x = 0.09.     

Mixed cation effect in xR2O-(40 − x)Na2O-50B2O3-10Bi2O3 (R = Li, K) glasses

Mass density, glass transition temperature and ionic conductivity are measured in xLi₂O-(40 − x)Na₂O-50B₂O₃-10Bi₂O₃ and xK₂O-(40 − x)Na₂O-50B₂O₃-10Bi₂O₃ glass systems with 0 ≤ x ≤ 40 mol%. The strength of the mixed alkali effect in T_g, dc electrical conductivity and activation energy has been determined in each glass system. The magnitudes of the mixed alkali effect in T_g for the mixed Li/Na glass system are much smaller than those in the mixed K/Na glasses. The impact of mixed alkali effect on dc electrical conductivity in mixed Li/Na glass system is more pronounced than in the K/Na glass system. The results are explained based on dynamic structure model.     

(5 − x)BaO-xMgO-2Nb2O5 ceramics prepared using a reaction-sintering process

(5 − x)BaO-xMgO-2Nb₂O₅ (x = 0.5 and 1; 5MBN and 10MBN) microwave ceramics prepared using a reaction-sintering process were investigated. Without any calcinations involved, the mixture of BaCO₃, MgO, and Nb₂O₅ was pressed and sintered directly. MBN ceramics were produced after 2-6 h of sintering at 1350-1500 °C. The formation of (BaMg)₅Nb₄O₁₅ was a major phase in producing 5MBN ceramics, and the formation of Ba(Mg_1/3Nb_2/3)O₃ was a major phase in producing 10MBN ceramics. As CuO (1 wt%) was added, the sintering temperature dropped by more than 150 °C. We produced 5MBN ceramics with these dielectric properties: ?_r = 36.69, Qf = 20,097 GHz, and τ_f = 61.1 ppm/°C, and 10MBN ceramics with these dielectric properties: ?_r = 39.2, Qf = 43,878 GHz, and τ_f = 37.6 ppm/°C. The reaction-sintering process is a simple and effective method for producing (5 − x)BaO-xMgO-2Nb₂O₅ ceramics for applications in microwave dielectric resonators.     

Structural, magnetic and dielectric properties of Bi1−ySryFe(1−y)(1−x)Sc(1−y)xTiyO3 (x = 0-0.2, y = 0.1-0.3) ceramics

In this study, bulk ceramics with general formula Bi_1−ySr_yFe_{(1−y)(1−x)}Sc_(1−y)xTi_yO₃ (x = 0-0.2, y = 0.1-0.3 mol%) were prepared by traditional solid-state reaction method. As a comparison, bulk BiFeO₃ (BF) was also sintered by rapid sintering method. Their structural, magnetic, dielectric properties were investigated. X-ray diffraction analysis indicated that apart from a small amount of secondary phase detected in BF, all other samples crystallized in pure perovskite structure and maintained original R3c space group. The room temperature M-H curves were obtained. While BF had a coercive magnetic field (H_c) of 150 Oe, Bi_1−ySr_yFe_1−yTi_yO₃ solid solutions had a much larger value (for y = 0.1, 0.2, 0.3, H_c were 4537, 5230 and 3578 Oe, respectively). Sc³⁺ substitution decreased the H_c values of these solid solutions remarkably, and resulted in soft magnetic properties, as well as a decrease of the dielectric loss. At 1 MHz, the tan δ of Bi_0.7Sr_0.3Fe_0.7(1−x)Sc_0.7xTi_0.3O₃ with x = 0.05, 0.1, 0.15, 0.2 were 0.1545, 0.1078, 0.1046 and 0.1701, respectively.     

Composition dependent phase connectivity, dielectric and magnetoelectric properties of magnetoelectric composites with Pb(Mg1/3Nb2/3)0.67Ti0.33O3 as piezoelectric phase

Ferrite (Ni_0.6Co_0.4Fe₂O₄) phase, ferroelectric (Pb(Mg_1/3Nb_2/3)_0.67Ti_0.33O₃) phase and magnetoelectric composites of (x)Ni_0.6Co_0.4Fe₂O₄ + (1 − x)Pb(Mg_1/3Nb_2/3)_0.67Ti_0.33O₃ with x = 0.15, 0.30 and 0.45 were prepared using solid-state reaction technique. Presence of Ni_0.6Co_0.4Fe₂O₄ and Pb(Mg_1/3Nb_2/3)_0.67Ti_0.33O₃ was confirmed using X-ray diffraction technique. The scanning electron microscopic images were used to study the microstructure of the composites. Connectivity scheme present in the magnetoelectric (ME) composites are discussed from the microscopic images. Variation of dielectric constant and dielectric loss with temperature for all the composites was studied. Here we report the effect of Ni_0.6Co_0.4Fe₂O₄ mole fraction on connectivity schemes between Ni_0.6Co_0.4Fe₂O₄ and Pb(Mg_1/3Nb_2/3)_0.67Ti_0.33O₃ composite. The variation of magnetoelectric voltage coefficient with dc magnetic field shows peak behaviour. The maximum value of magnetoelectric voltage coefficient of 9.47 mV/cm Oe was obtained for 0.15Ni_0.6Co_0.4Fe₂O₄ + 0.85Pb(Mg_1/3Nb_2/3)_0.67Ti_0.33O₃ composites. Finally we have co-related the effect of Ni_0.6Co_0.4Fe₂O₄ content and dielectric properties on magnetoelectric voltage coefficient.     

Microstructure and microwave dielectric characteristics of (1 − x)Ba(Zn1/3Ta2/3)O3-xBaTi4O9 ceramics

(1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ (0.1 ≤ x ≤ 0.85) composites are prepared by mixing 1150 °C-calcined BaTi₄O₉ with 1150 °C-calcined Ba(Zn_1/3Ta_2/3)O₃ powders. The crystal structure, microwave dielectric properties and sinterabilites of the (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics have been investigated. X-ray diffraction patterns reveal that BaTi₄O₉, ordered and disordered Ba(Zn_1/3Ta_2/3)O₃ phases exist independently over the whole compositional range. The sintering temperatures of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics are about 1240 - 1320 °C and obviously lower than those of Ba(Zn_1/3Ta_2/3)O₃ ceramics. The dielectric constants (?_r) and the temperature coefficient of resonant frequency (τ_f) of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics increase with the increase of BaTi₄O₉ content. Nevertheless, the bulk densities and the quality values (Q × f) of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics increase with the increase of Ba(Zn_1/3Ta_2/3)O₃ content. The results are attributed to the higher density and quality value of Ba(Zn_1/3Ta_2/3)O₃ ceramics, the better grain growth, and the densification of sintered specimens added a small BaTi₄O₉ content. The (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramic with x = 0.1 sintered at 1320 °C exhibits a ?_r value of 31.5, a maximum Q × f value of 68500 GHz and a minimum τ_f value of 4.1 ppm/°C.     

Dielectric properties of a new ceramic system (1 − x)Mg4Nb2O9-xCaTiO3 at microwave frequency

The microstructures and the microwave dielectric properties of the (1 − x)Mg₄Nb₂O₉-xCaTiO₃ ceramic system were investigated. In order to achieve a temperature-stable material, CaTiO₃ (τ_f ∼ 800 ppm/°C) was chosen as a τ_f compensator and added to Mg₄Nb₂O₉ (τ_f ∼ −70 ppm/°C) to form a two phase system. It was confirmed by the XRD and EDX analysis. By appropriately adjusting the x-value in the (1 − x)Mg₄Nb₂O₉-xCaTiO₃ ceramic system, near-zero τ_f value can be achieved. A new microwave dielectric material, 0.5Mg₄Nb₂O₉-0.5CaTiO₃ applicable in microwave devices is suggested and possesses the dielectric properties of a dielectric constant ?_r ∼ 24.8, a Q × f value ∼82,000 GHz (measured at 9.1 GHz) and a τ_f value ∼−0.3 ppm/°C.     

Studies on dielectric and magnetoelectric behavior of 25% CMFO ferrite and 75% BZT ferroelectric multiferroic magnetoelectric composites

In the present work, multiferroic magnetoelectric (ME) composites of ferrite and ferroelectric phases are prepared. Here, the magnetostrictive (ferrite) phase, Co_1.2 − yMn_yFe_1.8O₄ (y = 0.0 to 0.4) i.e. CMFO is synthesized by chemical combustion route and the piezoelectric (ferroelectric) phase, BaZr_0.08Ti_0.92O₃ i.e. BZT is synthesized by conventional ceramic method. Frequency dependent dielectric constant measurement from 20 Hz-1 MHz at room temperature shows usual dielectric dispersion behaviour, which may be attributed to the Maxwell-Wagner type interfacial polarization. Temperature dependent dielectric constant measurement shows two dielectric maxima, one below 100 °C and the second above 500 °C. The dielectric maxima below 100 °C corresponds to the transition temperature of the ferroelectric phase and that of above 500 °C corresponds to the transition temperature of the ferrite phase of the ME composites. It is observed that as Mn content increases in the cobalt ferrite, the phase transition temperature of the ferrite phase decreases. The static magnetoelectric voltage coefficient was measured as a function of intensity of the applied dc magnetic field. These magnetoelectric composites may have possible applications in magnetic field sensing probes and linear ME devices.     

Itinerant ferromagnetism to insulating spin glass in SrRu1−xCuxO3 (0 ≤ x ≤ 0.3)

The ferromagnetic metallic oxide, SrRuO₃ (T_C ∼ 165 K) undergoes structural, magnetic and metal-insulator transitions upon substitution of Cu at the Ru-site. For x = 0.2 in SrRu_1−xCu_xO₃, the structure becomes a tetragonal with the space group I4/mcm and there is a signature of both ferromagnetic (T_C = 65 K) and antiferromagnetic (T_N = 32 K) ordering due to possible magnetic phase separation. The antiferromagnetism arises due to short range ordering of Cu- and Ru-moments. Jahn-Teller distortion of (Ru,Cu)-O₆ octahedra indicates that the copper ions are in 2+ oxidation state with ⁶t2g³eg electronic configuration. For x ≥ 0.1, narrowing of Ru-4d bandwidth by the substitution of Cu ions results in semiconducting behavior. For x = 0.3, the ac and dc susceptibility measurements indicate a spin glass behavior. The origin of spin glass behavior has been attributed to competing ferromagnetic and antiferromagnetic interactions.     

Phase formation, microstructure, and dielectric properties of (1 − x)PZT-(x)PCN ceramics

Ceramics in a PZT-PCN system with the formula (1 − x)Pb(Zr_1/2Ti_1/2)O₃-(x)Pb(Co_1/3Nb_2/3)O₃, where x = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5, and 1.0, were prepared using a solid-state mixed-oxide technique with columbite−CoNb₂O₆ and wolframite−ZrTiO₄ precursors. The crystal structure of the specimens studied with X-ray diffraction (XRD) analysis showed a coexistence between tetragonal and pseudo cubic phases at composition x = 0.2. The SEM micrograph showed that the average grain size significantly decreased with increasing PCN content. A maximum dielectric constant was observed at composition x = 0.2, while the transition temperature strongly decreased with increasing PCN content. All ceramics also showed diffused phase transition behaviors with a minimum diffusivity at x = 0.2. The morphotropic phase boundary (MPB) lay at the 0.8PZT-0.2PCN composition.     

Thermal stability and transport studies of (100 − 2x)TeO2-xAg2O-xWO3 (7.5 ≤ x ≤ 30) glass system

Differential scanning calorimetry (DSC), infrared (IR) and direct current (DC) conductivity studies have been carried out on (100 − 2x)TeO₂-xAg₂O-xWO₃ (7.5 ≤ x ≤ 30) glass system. The IR studies show that the structure of glass network consists of [TeO₄], [TeO₃]/[TeO₃₊₁], [WO₄] units. Thermal properties such as the glass transition (T_g), onset crystallization (T_o), thermal stability (ΔT), glass transition width (ΔT_g), heat capacities in the glassy and liquid state (C_pg and C_pl), heat capacity change (ΔC_p) and ratios C_pl/C_pg of the glass systems were calculated. The highest thermal stability (237 °C) obtained in 55TeO₂-22.5Ag₂O-22.5WO₃ glass suggests that this new glass may be a potentially useful candidate material host for rare earth doped optical fibers. The DC conductivity of glasses was measured in temperature region 27-260 °C, the activation energy (E_act) values varied from 1.393 to 0.272 eV and for the temperature interval 170-260 °C, the values of conductivity (σ) of glasses varied from 8.79 × 10⁻⁹ to 1.47 × 10⁻⁶ S cm⁻¹.     

Synthesis of perovskite-type (La1−xCax)FeO3 (0 ≤ x ≤ 0.2) at low temperature

Gel formation was realized by adding citric acid to a solution of La(NO₃)₃·5H₂O, Ca(NO₃)₂·4H₂O, and Fe(NO₃)₂·9H₂O. Perovskite-type (La_1−xCa_x)FeO₃ (0 ≤ x ≤ 0.2) was synthesized by firing the gel at 500 °C in air for 1 h. The crystallite size (D_1 2 1) decreased with increasing x, while the specific surface area was 6.8-9.4 m²/g and independent of x. The XPS measurement of the (La_1−xCa_x)FeO₃ surface indicated that the Ca²⁺ ion content increased with increasing x, while the Fe ion content was independent of x. Catalytic activity for CO oxidation increased with increasing x.     

Rietveld refinements of the solid solution Li(1−2x)NixTiO(PO4) (0 ≤ x ≤ 0.50)

Li_(1−2x)Ni_xTiO(PO₄) oxyphosphates with 0 ≤ x ≤ 0.10 crystallize in the orthorhombic system with the space group Pnma, those with 0.10 < x ≤ 0.25 crystallize in the monoclinic system with the space group P2₁/c and compositions with 0.25 < x < 0.50 present a mixture of the limit of the solid solution Li_0.50Ni_0.25TiO(PO₄) and Ni_0.50TiO(PO₄). The structure of the compositions 0 ≤ x ≤ 0.25 is based on a three-dimensional anionic framework constructed of chains of alternating TiO₆ octahedra and PO₄ tetrahedra, with the lithium and nickel atoms in the cavities in the framework. The dominant structural units in the compositions are chains of tilted corner-sharing TiO₆ octahedra running parallel to one of the axis. The oxygen atoms of the shared corners, not implied in (PO₄) tetrahedra, justify the oxyphosphate designation. Titanium atoms are displaced from the geometrical center of the octahedra resulting in alternating long (≈2.25 Å) and short (≈1.71 Å) TiO(1) bonds. The four remaining TiO bond distances have intermediate values ranging from 1.91 to 2.06 Å.     

Dielectric properties of Ba(Ti1 − xZrx)O3 solid solutions

This paper reports the structural and dielectric properties of Ba(Ti_1 − xZr_x)O₃ (x = 0-0.3) ceramics. Single-phase solid solutions of the samples were determined by X-ray diffraction. Microscopic observation by scanning electron microscope revealed dense, single-phase microstructure with large grains (20-60 μm). The evolution of dielectric behavior from a sharp ferroelectric peak (for x ≤ 0.08) to a round dielectric peak (for 0.15 ≤ x ≤ 0.25) with pinched phase transitions and successively to a ferroelectric relaxor (for x = 0.3) was observed with increasing Zr concentration. Compared with pure BaTiO₃, broaden dielectric peaks with high dielectric constant of 25,000-40,000 and reasonably low loss (tanδ: 0.01-0.06) in the Ba(Ti_1 − xZr_x)O₃ ceramics have been observed, indicating great application potential as a dielectric material.     

Synthesis and electromagnetic properties of microwave absorbing material: Cox(Cu0.5Zn0.5)1−xFe2O4 (0 < x < 1) nanoparticles

Spinel ferrite Co_x(Cu_0.5Zn_0.5)_1−xFe₂O₄ over a compositional range 0 < x < 1 was prepared using a simple hydrothermal method. Particle sizes could be varied from 14 to 25 nm by changing the x value. X-ray diffraction results confirmed that all the as-prepared nanoparticles revealed typical spinel structure and transmission electron microscopy images showed that the particle size of the samples increased with increasing x value. The magnetic properties of the as-prepared Co_x(Cu_0.5Zn_0.5)_1−xFe₂O₄ nanoparticles have been systematically examined. The maximum saturation magnetization existed at the highest Co content (x = 1). The electromagnetic properties of all the samples have been measured by an Agilent network analyzer and the results showed that Co_0.1(Cu_0.5Zn_0.5)_0.9Fe₂O₄ possessed the best microwave absorbing properties.     

Dielectric and pyroelectric anisotropy in melt-quenched BaBi2(Nb1 − xVx)2O9 ceramics

The (0 0 l) textured BaBi₂(Nb_1 − xV_x)₂O₉ (where x = 0, 0.03, 0.07, 0.1 and 0.13) ceramics were fabricated via the conventional melt-quenching technique followed by high temperature heat-treatment (800-1000 °C range). The influence of vanadium content and sintering temperature on the texture development and relative density were investigated. The samples corresponding to the composition x = 0.1 sintered at 1000 °C for 10 h exhibited the maximum orientation of about 67%. The Scanning electron microscopic studies revealed the presence of platy grains having the a-b planes perpendicular the pressing axis. The dielectric constant and the pyroelectric co-efficient values in the direction perpendicular to the pressing axis were higher. The anisotropy in the dielectric constant is about 100 (at 100 kHz) at the dielectric maximum temperature and anisotropy in the pyroelectric co-efficient is about 50 μC cm⁻² °C⁻¹ in the vicinity of pyroelectric anomaly for the sample corresponding to the composition x = 0.1 sintered at 1000 °C. Higher values of the dielectric loss and electrical conductivity were observed in the direction perpendicular to the pressing axis which is attributed to the high oxygen ion conduction in the a-b planes.