Studies on the Hydrogenation of Acetonitrile over Fresh Mo_2C/γ-Al_2O_3 Catalyst by In-situ IR Spectroscopy

The adsorption of acetonitrile, the co-adsorption of acetonitrile with CO, and hydrogenation of acetonitrile on fresh Mo2C/γ-Al2O3 catalyst were studied by in situ IR spectroscopy. It was found out that CH3CN exhibited strong interaction with the fresh Mo2C/γ-Al2O3 catalyst and was adsorbed mainly on Moδ+ sites of fresh Mo2C/γ-Al2O3 catalyst. Moreover, CH3CN could affect the shifting of IR spectra for CO adsorption towards a lower wave number. The IR spectroscopic study on acetonitrile hydrogenation showed that CH3CN could be easily hydrogenated in the presence of H2 on the Mo2C/γ-Al2O3 catalyst. Furthermore, it was observed that CH3 CN could be selectively hydrogenated to imines on fresh Mo2C/γ-Al2O3 catalyst. Additionally, the active sites of fresh Mo2C/γ-Al2O3 catalyst might be covered with coke during the hydrogenation reaction of acetonitrile. The treatment of catalyst with hydrogen at 673 K could not completely remove coke deposits on the surface of the Mo2C/γ-Al2O3 catalyst.     

新鲜态Mo2C/γ-Al2O3 催化剂上丁二烯加氢反应的原位红外光谱研究

The surface species formed from the adsorption of 1,3-butadiene and 1,3-butadiene hydrogenation over the freshMo2C/γ-Al2O3 catalyst was studied by in situ IR spectroscopy. It is found that 1,3-butadiene adsorption on the Mo2C/γ-Al2O3catalyst mainly forms π-adsorbed butadiene （πs and πd） and σ-bonded surface species. These species are adsorbed mainly onthe surface Moδ＋ （0〈δ〈2） sites as evidenced by co-adsorption of 1,3-butadiene and CO on the fresh Mo2C/γ-Al2O3 catalyst.The IR spectrometric analysis show that hydrogenation of 1,3-butadiene over fresh Mo2C/γ-Al2O3 catalyst produces mainlybutane coupled with a small portion of butene. The selectivity of butene during the hydrogenation of 1,3-butadiene overfresh Mo2C/γ-Al2O3 catalyst might be explained by the adsorption mode of adsorbed 1,3-butadiene. Additionally, the activesites of the fresh Mo2C/γ-Al2O3 catalyst may be covered by coke during the hydrogenation reaction of 1,3-butadiene. Thetreatment with hydrogen at 673 K cannot remove the coke deposits from the surface of the Mo2C/γ-Al2O3 catalyst.     

FCC汽油选择性加氢脱硫CoMo/Al2O3催化剂的CO吸附原位红外光谱表征

 采用CO吸附原位红外光谱对系列硫化态CoMo/Al₂O₃催化剂进行表征,获得了加氢脱硫催化剂活性相的信息,并将表征结果与微反加氢脱硫活性和选择性评价结果进行关联分析。结果表明,CoMoS和MoS₂活性中心上吸附的CO数目的比值与HDS选择性具有良好的相关性;催化剂表面CoMoS相相对含量的增多有利于提高HDS的活性和选择性;CoMoS活性中心的强缺电子特性是CoMoS相有助于提高HDS活性和选择性的重要原因。     

喹啉对在Co-Mo/Al2O3及Ni-Mo/Al2O3催化剂上二苯并噻吩加氢脱硫活性的影响

在工业催化剂FHUDS-5(Co-Mo/Al2O3)和FHUDS-6(Ni-Mo/Al2O3)上,模拟工业柴油加氢工艺,考察了喹啉对二苯并噻吩(DBT)加氢脱硫(HDS)活性的影响,还讨论了喹啉抑制DBT加氢脱硫反应的机理。结果表明,喹啉对DBT的HDS反应有强烈抑制作用,对加氢路径(HYD)的抑制作用大于对氢解路径(DDS)的抑制作用;反应温度高于300℃时,在同一温度下,喹啉对在Co-Mo/Al2O3及Ni-Mo/Al2O3催化剂上DBT加氢脱硫反应活性的影响不同;当氢分压大于4.8 MPa时,在同一氢分压下,喹啉对在Co-Mo/Al2O3及Ni-Mo/Al2O3催化剂上DBT加氢脱硫反应活性的影响不同。     

纳米Pd/Al2O3催化剂的制备及应用

采用氢电弧等离子体法制备的纳米钯粉制备了纳米Pd/Al2O3催化剂,并在重整后加氢反应中研究了其催化活性和选择性。扫描电镜（SEM）和透射电镜（TEM）显示,纳米Pd/Al2O3催化剂的其表面排列有序、呈蜂窝状,其载体的内部没有钯存在,而浸渍法所得的壳型Pd/Al2O3催化剂载体内部有钯的存在。在重整后加氢反应中,纳米Pd/Al2O3催化剂显示出较高的催化活性和优异的选择性能。     

CO_2加氢合成甲醇催化剂中Al_2O_3的作用

研究了ＣＯ２加氢合成甲醇催化剂中载体Ａｌ２Ｏ３的作用。活性评价、ＴＰＲ、ＴＰＤ、ＴＰＳＲ等实验表明，Ａｌ２Ｏ３不但起骨架作用，而且能分散催化剂的活性组分，使ＣＯ２的吸附和转化率提高。铜基催化剂掺中入适量的Ａｌ２Ｏ３能提高ＣＯ２加氢合成甲醇的选择性，过量的Ａｌ２Ｏ３会降低甲醇的收率。     

NiO／SiO_2－Al_2O_3超细催化剂上CO氧化反应的研究

采用溶胶凝胶－超临界干燥法制备的ＮｉＯ／ＳｉＯ２－Ａｌ２Ｏ３催化剂对ＣＯ氧化显示出可与贵金属催化剂相类比的优良活性。以ＣＯ氧化的最低完全转化温度为基准，研究了不同制备参数对反应行为的影响规律，并结合程序升温还原（ＴＰＲ）结果对其活性位进行了探讨。结果表明，在ＮｉＯ／ＳｉＯ２－Ａｌ２Ｏ３系催化剂上ＣＯ氧化反应具有两类不同的活性位：ＮｉＯ及八面体配位的镍；制备参数通过影响活性位从而影响反应行为；优化制备参数为ＮｉＣｌ２前驱物、ＳｉＯ２载体、３％含量及制载体浸渍     

Al2O3晶型对Pt/Al2O3-Cl催化剂物化性质及其催化C5/C6异构化性能的影响

以拟薄水铝石粉和湃水铝石粉为前驱体,通过挤条成型和焙烧制备了3种不同晶型(γ、θ、η)Al₂O₃载体,并分别经负载Pt和氯化制备了3种Pt/Al₂O₃-Cl催化剂(Pt/γ-Al₂O₃-Cl、Pt/θ-Al₂O₃-Cl和Pt/η-Al₂O₃-Cl);采用X射线衍射(XRD)、N₂吸附-脱附(BET)、吡啶红外(Py-IR)、透射电镜(TEM)、NH₃程序升温脱附(NH₃-TPD)等手段表征了3种Al₂O₃载体及Pt/Al₂O₃-Cl催化剂,并通过固定床微反装置考察了Pt/Al₂O₃-Cl催化剂的C₅/C₆异构化性能。结果表明：γ、θ、η型Al₂O₃载体经负载Pt和氯化后,晶型不发生改变,Cl含量和酸量均大幅度提高,Lewis酸酸性显著增强,比表面积和孔体积明显下降;Pt/η-Al₂O₃-Cl催化剂的比表面积和酸量最大,C₅/C₆异构化活性最高,Pt/γ-Al₂O₃-Cl次之,Pt/θ-Al₂O₃-Cl最低;在温度为150 ℃、压力为3.2 MPa、进料质量空速为1.5 h^-1、氢/烃摩尔比为1.0的条件下,Pt/η-Al₂O₃-Cl催化剂作用下,C₅异构化率、C₆异构化率和C₆选择性分别为77.13%、88.68%和31.87%。     

新型Pt/Al_2O_3苯加氢催化剂的研制

开发了一种新型的苯气相加氢制环己烷的Pt/A l2O3催化剂,并在模拟苯加氢制环己烷工业装置建成的催化剂原粒度活性评价装置上评价催化剂的性能。考察了催化剂的制备方法、A l2O3载体物性、催化剂制备时竞争吸附剂对催化剂性能的影响。确定了适用于该新型催化剂的最佳的工艺操作条件。本催化剂具有与参比的工业催化剂类似的催化性能,但侧压强度明显高于参比催化剂。     

NiO／SiO_2－Al_2O_3超细催化剂上CO氧化反应的研究

采用溶胶凝胶－超临界干燥法制备的ＮｉＯ／ＳｉＯ２－Ａｌ２Ｏ３催化剂对ＣＯ氧化显示出可与贵金属催化剂相类比的优良活性。以ＣＯ氧化的最低完全转化温度为基准，研究了不同制备参数对反应行为的影响规律，并结合程序升温还原（ＴＰＲ）结果对其活性位进行了探讨。结果表明，在ＮｉＯ／ＳｉＯ２－Ａｌ２Ｏ３系催化剂上ＣＯ氧化反应具有两类不同的活性位：ＮｉＯ及八面体配位的镍；制备参数通过影响活性位从而影响反应行为；优化制备参数为ＮｉＣｌ２前驱物、ＳｉＯ２载体、３％含量及制载体浸渍     

V助剂对CuO/Al2O3上CO2加H2合成甲醇的影响

研究了不同Ｖ含量助剂对ＣuＯ／Ａ１２Ｏ３催化剂上ＣＯ２加Ｈ２合成甲醇的影响,发现 Ｖ助剂在低于５１０Ｋ时能明显提高催化剂的活性和选择性。Ｘ射线衍射 结果表明,Ｖ助剂加入后,ＣuＯ的分散度明显提高。程序升温还原（ＴＰＲ）的“ＲＯＲ”法揭示,在ＣuＯ／Ａ１２Ｏ３催化剂中存在能在室温下被氧化的铜物种,而这种铜物种的含量随Ｖ负载量的增加而增多。     

水热处理对Mo-Ni/Al2O3催化剂活性结构和催化硫醚化反应性能的影响

采用水热处理的方法对Mo Ni/Al2O3催化剂的微观孔结构性质和负载金属的结构性质进行调变,并考察调变后催化剂在硫醚化反应中的催化性能。结果表明,水热处理可增加催化剂的平均孔径,有利于产物中形成的大分子异构硫醚的扩散,维持催化剂的稳定性;还可以降低负载金属与载体间的作用,提高负载金属的硫化度,增加Ni Mo S活性中心数目。然而,这些对催化剂结构性质的促进作用,不仅提高了硫醚化反应过程的硫醚化反应和二烯烃选择加氢反应性能,还大大促进了烯烃的加氢饱和反应,造成反应产物辛烷值的损失。     

CuO/ZnO/活性Al2O3催化剂合成N-异丙基苯胺催化性能的考察

采用浸渍法制备ＣｕＯ／ＺｎＯ／活性Ａｌ２Ｏ３催化剂,用于合成Ｎ－异丙基苯胺的Ｎ－烷基化反应。并且考察了催化剂的制备因素及反应条件对催化剂反应性能的影响。得到了ＣｕＯ／ＺｎＯ／活性Ａｌ２Ｏ３催化剂制备Ｎ－异丙基苯胺的适宜反应条件。     

四氯化碳气相催化加氢脱氯反应Pt-Co/Al_2O_3催化剂研究

采用浸渍法制备了w(Pt)为0.1%的Pt-Co/Al2O3催化剂,考察了其在四氯化碳气相催化加氢中的催化性能,结果表明其在最佳反应温度和空速分别为200℃和1500h-1时表现出很高的催化活性;同时,通过对不同Co前驱体制备的w(Pt)为0.1%的Pt-Co/Al2O3催化剂的催化性能考察,表明以C℃l2·6H2O作为Co前驱体最佳,最适宜的w(Co)为15%;而不同掺杂方法的研究结果显示,V的掺杂量w(V)=0.024%对提高Pt-Co/Al2O3催化剂的催化稳定性有很大帮助。     

CO_2-CH_4重整制合成气Ni-Mg/Al_2O_3催化剂制备与表征

用３ 种浸渍程序制备ＣＯ２ ＣＨ４ 重整制合成气的Ｎｉ Ｍｇ／Ａｌ２Ｏ３ 催化剂,结果表明用二次不等量浸渍法制备的催化剂性能较好,程序升温实验也说明二次不等量浸渍法制备的催化剂其表面活牲Ｎｉ 粒子较多。     

NiMo/Al2O3加氢脱硫催化剂的电镜表征

 采用常规透射电子显微技术（TEM）和扫描透射电子显微技术结合X射线能谱分析的测量技术（简称分析电子显微技术- —AEM）对NiMo/Al₂O₃系工业加氢脱硫催化剂的氧化态和硫化态进行对比研究。结果表明，对于硫化态加氢脱硫催化剂，TEM可以给出清晰的活性相的形貌和分布信息，活性相条纹的长度、堆叠层数等活性相参数特征的统计与其催化活性具有良好的关联。通过AEM的Mapping技术对NiMo/Al₂O₃催化剂氧化态和硫化态活性组分Ni、Mo的微区成分分布的测定，可获得催化剂活性相前体和硫化态活性组分的成分分布信息，克服了单一TEM不能提供成分信息的缺点，增加了对催化剂制备过程中活性组分变化的了解。     

添加组分对Cu/ZnO/Al_2O_3催化剂顺酐加氢合成γ-丁内酯活性的影响

在常压固定床反应装置上研究了不同添加组分对顺酐加氢催化剂催化性能的影响 ,在反应温度 2 70℃ ,氢气与顺酐摩尔比 5 5 ,顺酐空速 0 16h- 1 的条件下 ,考察了添加碱金属、碱土金属、ⅥB族、ⅦB族和Ⅷ族金属元素对顺酐加氢催化剂活性的影响 ,并探讨了引起活性变化的原因。结果表明 ,在所有添加组分中 ,Cr是唯一既不影响催化剂活性又能提高γ -丁内酯选择性的助剂 ,但其添加量应不超过 5 % (摩尔分数 ) ;碱金属元素和Mo、Mg对催化剂有毒害作用 ;Ba对催化剂加氢活性影响不大 ;添加其它金属元素时催化剂的加氢活性虽下降不大 ,但γ -丁内酯的选择性却大幅度降低     

Pt/Al2O3催化剂催化2-丙基-2-庚烯醛选择性加氢

以Pt／Al2O3为催化剂．采用微型固定床反应装置．在液相条件下对正戊醛缩合产物2-丙基-2-庚烯醛进行选择性加氢制取2-丙基庚醛。在0．5～2．0MPa,373～433K,氢气／烯醛摩尔比2．5：1,液时体积空速0．5～Z．0h^1的实验范围内,筛选出合适的反应条件,实现高选择性加氢,制得目的产物2-丙基庚醛。     

沉淀pH对CuO/ZnO/Al_2O_3系催化剂前体性质的影响

用并流共沉淀方法制备了一系列CuO／ZnO／Al2O3催化剂前体及催化剂,用XRD,TG-DTG,TPR及微反活性评价等技术考察了沉淀pH对催化剂前体物相组成及焙烧后物相中CuO-ZnO间的作用情况。研究表明,沉淀pH主要对催化剂前体的物相组成有重要影响,在不同的沉淀pH下,前体中的物相组成不同。在pH为7的情况下,前体中存在碱式硝酸铜Cu2(NO3)(OH)3、碱式碳酸铜Cu2CO3(OH)2、类碱式碳酸锌(Zn,Cu)5(CO3)2(OH)6及类孔雀石(Cu,Zn)2CO3(OH)2等多种物相;在pH为8-9时,前体中主要存在(Cu,Zn)2CO3(OH)2和(Zn,Cu)5(CO3)2(OH)6两种物相,且其结晶度较低,在此范围内催化剂的活性最好,TPR实验表明,此时催化剂中形成了较多的CuO-ZnO固溶体。实验结果表明,(Cu,Zn)2CO3(OH)2和(Zn,Cu)5(CO3)2(OH)6两种物相对提高催化剂的活性至关重要。     

纳米Pd/Al2O3催化剂的表征及其选择性加氢反应性能

 采用氢电弧等离子体法制备的纳米钯粉制备了纳米Pd/Al2O3催化剂，采用X射线粉末衍射（XRD）、扫描电镜（SEM）、透射电镜（TEM）、X光电子能谱（XPS）和程序升温还原（TPR）等物理化学手段对其进行了表征，并在裂解汽油一段加氢反应中考察了其催化活性和选择性。结果表明，纳米Pd/Al2O3催化剂表面的Pd原子排列有序，表面呈蜂窝状，其载体的内部没有Pd元素，而浸渍法所得的Pd/Al2O3催化剂载体内部有Pd元素；纳米Pd/Al2O3的Pd3d5/2结合能比壳型Pd/Al2O3的Pd3d5/2结合能高；前者XRD谱图中未发现Pd和PdO的特征峰。两种样品的程序升温还原研究表明纳米Pd和载体Al2O3发生了强相互作用。在裂解汽油一段加氢选择性反应中，纳米Pd/Al2O3催化剂显示出较高的催化活性和优异的选择加氢性能。