The relationship between charge passed and the chloride-ion concentration in concrete using steady-state chloride migration test

The accelerated chloride migration test in this study is a modified version of the ASTM C1202-97 or AASHTO T277-96 (RCPT) method. The current, chloride-ion concentration and temperature were measured during the experiment. Four different concretes used for test had a water to cementitious ratio of 0.4, containing various mineral admixtures. The transport properties were investigated using the accelerated chloride migration test. At a steady-state chloride flux, a good correlation was found between the charge passed (obtained by integrating the current-time curve) and the chloride-ion concentration.     

非离子表面活性剂对超细粉的分散作用

商品超细粉团聚现象严重，湿法球磨亦无法破坏粉体的团聚结构．非离子表面活性剂可有效地破坏团聚体，使粉体颗粒在纯水中高度分散，是一种理想的超细粉分散剂．     

超细改性矿物粉体增强硅橡胶

采用材料物理化学和复合材料的方法,系统地研究了８种矿物及其超细粉体和改性粉体与硅本的相互作用。结果表明,湍石、石英和硅灰石对硅橡胶基体具有较好的增强作用。粒径小、比面积大、长径比大等粉体性质好的填料,其增强性能高。界面粘附功与界面张力比值大的复合材料的力学性能好。具有表面活性基团（通过表面改性）、表面缺陷和一的表面羟基是提高粉体增强性能的重要因素。复合粉体的增强性能与粉休性质、混炼胶中的结合橡胶、     

氧化镁部分稳定氧化结超细粉末及其烧结特性

本文对氧化镁部分稳定氧化锆超细粉末的制备工艺和性能进行了实验研究。利用颗粒度分析仪、ＴＧ和ＤＴＡ热分析仪等测定了氧化镁部分稳定氧化锆粉末的性能。研究了粉末的烧结特性，测定了烧结密度随烧结温度及烧结时间的变化。利用热膨胀法对烧结过程中试样的长度变化作了模拟试验，以考察试样的收缩特征。     

矿粉对C40混凝土性能的影响研究

开展了不同矿粉掺量的混凝土试验研究,寻找不同掺量矿粉对混凝土性能(包括坍落度,强度,抗碳化性能,抗冻融性能,水化热)影响规律.经实验研究发现,以C40混凝土为基础,用一定量的矿粉代替水泥,显著优化混凝土水化放热情况,提高混凝土后期强度,增强混凝土的使用性能.     

超细钢渣粉与超细S95矿粉复和性能的研究

利用超细粉磨工艺,制备出比表面积≥700 m2/kg的超细钢渣粉、超细S95矿粉。设计超细钢渣粉与超细S95矿粉按质量比7∶3、6∶4、5∶5复合,制得超细复合粉,并对其活性指数、流动度比、需水量比、初凝时间比、安定性进行测试。结果表明：超细钢渣粉28d活性指数达到100%、流动度比达到130%;各复合比例的超细复合粉7d、28d活性指数分别超过100%、95% ,需水量比均小于95%,流动度比均大于120%,初凝时间比、安定性合格,均能达到S95矿粉要求。     

超细TiC粉体的制备方法及应用研究进展

结合近年TiC材料的研究进展,对超细TiC粉体的制备方法进行了综述,介绍了还原法、自蔓延高温合成法（SHS）、机械合金化法、微波法、气相反应合成法及等离子体法,简述了TiC在增强颗粒、航空航天材料及涂层材料方面的应用。     

高频氢等离子体增强还原制备超细铜粉

利用高频感应热氢等离子体强化还原制备超细铜粉,考察了加料速率、还原氢气流量、氢气分布位置、反应区空间、冷却温度等因素对铜粉颗粒性能的影响,对制备的铜粉颗粒进行氧含量、XRD晶体结构、松装密度、粒度分布和比表面积的表征。结果表明,优化的工艺条件为反应区内径100 mm,加料速率4 g/min,淬火气氩气气量500 L/h,氢气气量500 L/h并通入少量载气,由氢等离子电离产生的氢自由基可强化反应实现瞬时还原,不仅可控制铜粉形貌,还能有效控制铜粉颗粒大小;利用该方法制备出粒径分布100?200 nm、分散性好的超细球形铜粉颗粒。该方法操作简便、产品纯度高、气氛可控、对环境污染小。     

几种超细矿粉抑制混凝土碱骨料反应的试验研究

利用ASTM C441方法检验了矿物质超细粉对混凝土碱硅酸反应ASR的抑制作用，并利用小混凝土柱法检测了其抑制碱碳酸盐反应ACR的效果。试验表明，矿渣、粉煤灰、沸石等混合材掺入混凝土中均可以抑制ASR的发生，且偏高岭土和沸石粉的效果优于粉煤灰，粉煤灰又优于矿渣。矿物质混合材对ACR膨胀也有抑制作用，但效果不明显，掺30％的粉煤灰和30％A型偏高岭土超细粉试件的28d膨胀率为0．0953％和,0.108％，掺加其它混合材的小混凝土柱膨胀率则在0．12％-0．16％之间。     

非金属矿物粉体机械力化学研究进展

在球磨过程中,机械力化学使颗粒和晶粒细化产生裂纹,比表面积增大,晶格缺陷增多,晶格发生畸变和结晶程度降低,甚至诱发低温化学反应,可以制备出高活性矿物粉体和性能优异的材料。本文介绍了机械力化学在非金属矿物粉体研究中的最新进展,并对其未来发展进行了展望。     

Very-high-performance concrete with ultrafine powders

The compactness and fluidity of binary and ternary compound paste systems containing ultrafine powders such as pulverized fly ash (PFA), pulverized granulated blast furnace slag (PS) and silica fume (SF) were quantitatively studied with the relative density (d/d₀) index. Through optimization of the proportions of compositions and applying heat treatment to specimens, a very-high-performance concrete (VHPC) including large quantities of ultrafine powders has been made successfully, which offers compressive strength up to 200 MPa. Two methods of overcoming the brittleness of VHPC were investigated.     

超细粉体表征方法及应用进展

介绍了超细粉体的表征方法,同时综述了超细粉体材料在电子信息、军事、轻工、化工、中医药、农业及食品等方面的应用,展望了超细粉体材料的发展前景。     

水泥磨前掺加粗矿粉的实践应用

粒化高炉矿渣粉是水泥生产中的重要活性混合材料,矿粉活性的高低直接影响水泥产品质量。生产过程中存在磨机开停或检修后磨合阶段,此阶段所生产的矿粉存在细度偏粗、比表面积低、早期活性偏低等问题。针对此问题,我公司将该部分矿粉通过水泥磨头物料仓微机计量入磨与熟料、石膏和其它辅助混合材共同粉磨,达到稳定水泥质量,实现最终消化的目的。     

超细碳化钨粉末的制备研究现状及进展

碳化钨是一种重要的硬质合金材料,也是一种性能优良的催化材料,本文对近年来超细碳化钨粉的制备方法分为气相法,液相法和固相法三大类,并围绕碳化钨的颗粒细化,从钨源和碳源的选择,工艺流程等方面进行了归纳,     

超声波在超细粉体分散中的应用

超细粉体具有较大的比表面积及表面活性 ,易于吸附而发生凝聚 ,影响了它在改性聚酯中的应用。研究了通过超声波处理超细粉体 ,打开凝聚体 ,使它均匀地分散在分散剂中 ,从而生产出可纺性好的改性聚酯。     

化妆品用超细结晶蚕丝粉末的制备及表征

用质量分数为85%的磷酸催化水解桑蚕茧,茧与磷酸的质量体积比为1∶4时,在100℃条件下反应,可制得平均粒径为250 nm的结晶性丝粉,收率达70%以上.并对样品进行了扫描电镜、示差热分析、X-射线粉末衍射等表征分析.     

水泥粉磨系统矿粉后掺改造实例

随着水泥市场竞争的日趋激烈,企业要想提高竞争优势和市场占有率,就必须加强内部的挖潜降耗,降低水泥生产成本。前期我公司的矿粉是由磨尾掺入出磨提升机,进入高效选粉机,经过选粉后部分回粉会进入磨机进行粉磨,在粉磨过程中由于矿粉细度过细易形成垫层,影响磨机做功与熟料强度的发挥,制约磨机系统提产降耗。经过试验证明,矿粉后掺后水泥物理性能（细度、比表面积、标稠、凝结时间、适应性、强度）基本不变,不影响项目改造后的水泥性能,遂进行矿粉后掺改造。     

超细粉体粒度测试方法浅析

介绍了超细粉体粒度测试的几种主要方法(激光衍射散射法、离心沉降法、颗粒图像处理仪和库尔特颗粒计数器)的测试原理及性能特点，并进行了比较。讨论了粒度测试中应注意的几个问题，重点分析了测试条件不同对粒度测定的影响，得出分散介质、分散剂、超声功率及超声时间等是影响粒度测定的最主要的因素；指出了重复性、真实性、易操作性、量程和动态范围是评价粒度仪测试性能的几个重要指标。     

超细粉体制备技术的应用和发展

介绍了超细粉体的制备方法,重点对超细粉碎设备,工艺及应用领域作了详细评述。     

Study on the hydration heat of binder paste in high-performance concrete

High-performance concrete (HPC) is a type of new concrete materials developed in the recent 10 years. Compared with normal strength concrete (NSC), HPC is made with lower water-binder ratio (W/B), larger dosage of superplasticizer and addition of different types of mineral admixtures. The objective of the article was to evaluate the effect of W/B, superplasticizer and mineral admixtures on the hydration heat of the binder paste in HPC. The testing results showed that the hydration heat reduced with the decrease of W/B of the binder paste. The total hydration heat did not decrease with the incorporation of superplasticizer containing retarding component, however, the hydration exothermic process was delayed. Mineral admixtures greatly reduced the hydration heat and the exothermic rate and prolonged the arrival time of the highest temperature, particularly when two or three types of mineral admixtures were added at the same time (double adding and triple adding). The influence of these three factors on hydration heat may counteract the deficiency of high hydration heat at early stage due to high cement content and high-strength cement usually used in HPC. This way, the influence of temperature stress is alleviated and the durability of concrete is enhanced.