Catalytic effect of carbon nanostructures on the hydrogen storage properties of MgH2–NaAlH4 composite

The present investigation describes the hydrogen storage properties of 2:1 molar ratio of MgH₂–NaAlH₄ composite. De/rehydrogenation study reveals that MgH₂–NaAlH₄ composite offers beneficial hydrogen storage characteristics as compared to pristine NaAlH₄ and MgH₂. To investigate the effect of carbon nanostructures (CNS) on the de/rehydrogenation behavior of MgH₂–NaAlH₄ composite, we have employed 2 wt.% CNS namely, single wall carbon nanotubes (SWCNT) and graphene nano sheets (GNS). It is found that the hydrogen storage behavior of composite gets improved by the addition of 2 wt.% CNS. In particular, catalytic effect of GNS + SWCNT improves the hydrogen storage behavior and cyclability of the composite. De/rehydrogenation experiments performed up to six cycles show loss of 1.50 wt.% and 0.84 wt.% hydrogen capacity in MgH₂–NaAlH₄ catalyzed with 2 wt.% SWCNT and 2 wt.% GNS respectively. On the other hand, the loss of hydrogen capacity after six rehydrogenation cycles in GNS + SWCNT (1.5 + 0.5) wt.% catalyzed MgH₂–NaAlH₄ is diminished to 0.45 wt.%.     

Nanoconfined 2LiBH4–MgH2–TiCl3 in carbon aerogel scaffold for reversible hydrogen storage

Nanoconfinement of 2LiBH₄–MgH₂–TiCl₃ in resorcinol–formaldehyde carbon aerogel scaffold (RF–CAS) for reversible hydrogen storage applications is proposed. RF–CAS is encapsulated with approximately 1.6 wt. % TiCl₃ by solution impregnation technique, and it is further nanoconfined with bulk 2LiBH₄–MgH₂ via melt infiltration. Faster dehydrogenation kinetics is obtained after TiCl₃ impregnation, for example, nanoconfined 2LiBH₄–MgH₂–TiCl₃ requires ∼1 and 4.5 h, respectively, to release 95% of the total hydrogen content during the 1st and 2nd cycles, while nanoconfined 2LiBH₄–MgH₂ (∼2.5 and 7 h, respectively) and bulk material (∼23 and 22 h, respectively) take considerably longer. Moreover, 95–98.6% of the theoretical H₂ storage capacity (3.6–3.75 wt. % H₂) is reproduced after four hydrogen release and uptake cycles of the nanoconfined 2LiBH₄–MgH₂–TiCl₃. The reversibility of this hydrogen storage material is confirmed by the formation of LiBH₄ and MgH₂ after rehydrogenation using FTIR and SR-PXD techniques, respectively.     

Improved hydrogen storage performance of MgH2–NaAlH4 composite by addition of TiF3

In a previous paper, it was demonstrated that a MgH₂–NaAlH₄ composite system had improved dehydrogenation performance compared with as-milled pure NaAlH₄ and pure MgH₂ alone. The purpose of the present study was to investigate the hydrogen storage properties of the MgH₂–NaAlH₄ composite in the presence of TiF₃. 10 wt.% TiF₃ was added to the MgH₂–NaAlH₄ mixture, and its catalytic effects were investigated. The reaction mechanism and the hydrogen storage properties were studied by X-ray diffraction, thermogravimetric analysis, differential scanning calorimetry (DSC), temperature-programmed-desorption and isothermal sorption measurements. The DSC results show that MgH₂–NaAlH₄ composite milled with 10 wt.% TiF₃ had lower dehydrogenation temperatures, by 100, 73, 30, and 25 °C, respectively, for each step in the four-step dehydrogenation process compared to the neat MgH₂–NaAlH₄ composite. Kinetic desorption results show that the MgH₂–NaAlH₄–TiF₃ composite released about 2.4 wt.% hydrogen within 10 min at 300 °C, while the neat MgH₂–NaAlH₄ sample only released less than 1.0 wt.% hydrogen under the same conditions. From the Kissinger plot, the apparent activation energy, E_A, for the decomposition of MgH₂, NaMgH₃, and NaH in the MgH₂–NaAlH₄–TiF₃ composite was reduced to 71, 104, and 124 kJ/mol, respectively, compared with 148, 142, and 138 kJ/mol in the neat MgH₂–NaAlH₄ composite. The high catalytic activity of TiF₃ is associated with in situ formation of a microcrystalline intermetallic Ti–Al phase from TiF₃ and NaAlH₄ during ball milling or the dehydrogenation process. Once formed, the Ti–Al phase acts as a real catalyst in the MgH₂–NaAlH₄–TiF₃ composite system.     

Study on the hydrogen storage properties and reaction mechanism of NaAlH4–MgH2–LiBH4 ternary-hydride system

In this paper, we report the hydrogen storage properties and reaction mechanism of NaAlH₄–MgH₂–LiBH₄ (1:1:1) ternary-hydride system prepared by ball milling. It was found that during ball milling, the NaAlH₄/MgH₂/LiBH₄ combination converted readily to the mixture of LiAlH₄/MgH₂/NaBH₄ and there is a mutual destabilization among the hydrides. Three major dehydrogenation steps were observed in the system, which corresponds to the decomposition of LiAlH₄, MgH₂, and NaBH₄, respectively. The onset dehydrogenation temperature of MgH₂ in this system is observed at around 275 °C, which is over 55 °C lower from that of as-milled MgH₂. Meanwhile, NaBH₄-relevant decomposition showed significant improvement, starts to release hydrogen at 370 °C, which is reduced by about 110 °C compared to the as-milled NaBH₄. The second and third steps decomposition enthalpy of the system were determined by differential scanning calorimetry measurements and the enthalpies were changed to be 61 and 100 kJ mol⁻¹ H₂ respectively, which are smaller than that of MgH₂ and NaBH₄ alone. From the Kissinger plot, the apparent activation energy, E_A, for the decomposition of MgH₂ and NaBH₄ in the composite was reduced to 96.85 and 111.74 kJ mol⁻¹ respectively. It is believed that the enhancement of the dehydrogenation properties was attributed to the formation of intermediate compounds, including Li–Mg, Mg–Al, and Mg–Al–B alloys, upon dehydrogenation, which change the thermodynamics of the reactions through altering the de/rehydrogenation pathway.     

Processing analysis of the ternary LiNH2–MgH2–LiBH4 system for hydrogen storage

In this article, we investigate the ternary LiNH₂–MgH₂–LiBH₄ hydrogen storage system by adopting various processing reaction pathways. The stoichiometric ratio of LiNH₂:MgH₂:LiBH₄ is kept constant with a 2:1:1 molar ratio. All samples are prepared using solid-state mechano-chemical synthesis with a constant rotational speed, but with varying milling duration. Furthermore, the order of addition of parent compounds as well as the crystallite size of MgH₂ are varied before milling. All samples are intimate mixtures of Li–B–N–H quaternary hydride phase with MgH₂, as evidenced by XRD and FTIR measurements. It is found that the samples with MgH₂ crystallite sizes of approximately 10 nm exhibit lower initial hydrogen release at a temperature of 150 °C. Furthermore, it is observed that the crystallite size of Li–B–N–H has a significant effect on the amount of hydrogen release with an optimum size of 28 nm. The as-synthesized hydrides exhibit two main hydrogen release temperatures, one around 160 °C and the other around 300 °C. The main hydrogen release temperature is reduced from 310 °C to 270 °C, while hydrogen is first reversibly released at temperatures as low as 150 °C with a total hydrogen capacity of ∼6 wt.%. Detailed thermal, capacity, structural and microstructural properties are discussed and correlated with the activation energies of these materials.     

Enhanced hydrogen storage properties of TiN–LiAlH4 composite

The hydrogen storage properties of LiAlH₄ doped efficient TiN catalyst were systematically investigated. We observe that TiN catalyst enhances the dehydrogenation kinetics and decreases the dehydrogenation temperature of LiAlH₄. The dehydrogenation behaviors of 2%TiN–LiAlH₄ are investigated using temperature programmed desorption (TPD), differential scanning calorimetry (DSC) and fourier transform infrared spectroscopy (FTIR). Interestingly, the onset hydrogen desorption temperature of 2%TiN–LiAlH₄ sample gets lowered from 151.0 °C to 90.0 °C with a faster kinetics, and the dehydrogenation rate reached a maximum value at 137.2 °C. By adding a small amount of as-prepared TiN, approximately 7.1 wt% of hydrogen can be released from the LiAlH₄ at 130 °C. Interestingly, the result of the FTIR indicates that the 2%TiN–LiAlH₄ maybe restore hydrogen under 5.5 MPa hydrogen. Moreover, 2%TiN–LiAlH₄ displayed a substantially reduced activation energy for LiAlH₄ dehydrogenation.     

Hydrogen storage properties and mechanisms of the Mg(BH4)2–NaAlH4 system

Hydrogen storage properties and mechanisms of the combined Mg(BH₄)₂–NaAlH₄ system were investigated systematically. It was found that during ball milling, the Mg(BH₄)₂–xNaAlH₄ combination converted readily to the mixture of NaBH₄ and Mg(AlH₄)₂ with a metathesis reaction. The post-milled samples exhibited an apparent discrepancy in the hydrogen desorption behavior with respect to the pristine Mg(BH₄)₂ and NaAlH₄. Approximately 9.1 wt% of hydrogen was released from the Mg(BH₄)₂–2NaAlH₄ composite milled for 24 h with an onset temperature of 101 °C, which is lowered by 105 and 139 °C than that of NaAlH₄ and Mg(BH₄)₂, respectively. At initial heating stage, Mg(AlH₄)₂ decomposed first to produce MgH₂ and Al with hydrogen release. Further elevating operation temperatures gave rise to the reaction between MgH₂ and Al and the self-decomposition of MgH₂ to release more hydrogen and form the Al_0.9Mg_0.1 solid solution and Mg. Finally, NaBH₄ reacted with Mg and partial Al_0.9Mg_0.1 to liberate all of hydrogen and yield the resultant products of MgAlB₄, Al₃Mg₂ and Na. The dehydrogenated sample could take up ∼6.5 wt% of hydrogen at 400 °C and 100 atm of hydrogen pressure through a more complicated reaction process. The hydrogenated products consisted of NaBH₄, MgH₂ and Al, indicating that the presence of Mg(AlH₄)₂ is significantly favorable for reversible hydrogen storage in NaBH₄ at moderate temperature and hydrogen pressure.     

Destabilization of LiBH4 by nanoconfinement in PMMA–co–BM polymer matrix for reversible hydrogen storage

Destabilization of LiBH₄ by nanoconfinement in poly (methyl methacrylate)–co–butyl methacrylate (PMMA–co–BM), denoted as nano LiBH₄–PMMA–co–BM, is proposed for reversible hydrogen storage. The onset dehydrogenation temperature of nano LiBH₄–PMMA–co–BM is reduced to ∼80 °C (ΔT = 340 and 170 °C as compared with milled LiBH₄ and nanoconfined LiBH₄ in carbon aerogel, respectively). At 120 °C under vacuum, nano LiBH₄–PMMA–co–BM releases 8.8 wt.% H₂ with respect to LiBH₄ content within 4 h during the 1st dehydrogenation, while milled LiBH₄ performs no dehydrogenation at the same temperature and pressure condition. Moreover, nano LiBH₄–PMMA–co–BM can be rehydrogenated at the mildest condition (140 °C under 50 bar H₂ for 12 h) among other modified LiBH₄ reported in the previous literature. Due to the hydrophobicity of PMMA–co–BM host, deterioration of LiBH₄ by oxygen and humidity in ambient condition is avoided after nanoconfinement. Although the interaction between LiBH₄ and the pendant group of PMMA–co–BM leads to a reduced hydrogen storage capacity, significant destabilization of LiBH₄ is accomplished.     

The hydrogen storage properties and reaction mechanism of the NaAlH4 + Ca(BH4)2 composite system

The hydrogen storage properties and reaction mechanism of the combined NaAlH₄ + Ca(BH₄)₂ (2:1) composite system was investigated in the present study. Analyses show that after 6 h of milling, the NaAlH₄ + Ca(BH₄)₂ combination fully converted to the mixture of Ca(AlH₄)₂ + NaBH₄, and a metathesis reaction occurred between the hydrides. Four major dehydrogenation stages were observed in the system, which corresponds to the decomposition of Ca(AlH₄)₂, CaAlH₅, CaH₂ and NaBH₄, respectively. The onset desorption temperature of the composite system is reduced to 125 °C, which is much lower than a unary component of NaAlH₄ and Ca(BH₄)₂. The de/rehydrogenation kinetics of the composite system had improve at a higher temperature. From the Kissinger plot, the apparent activation energies for the decomposition of CaAlH₅ and NaBH₄ in the composite system were reduced to 142.9 and 146.5 kJ/mol, respectively. It is believed that the formation of AlCa, AlB and CaB alloys during the dehydrogenation process is responsible for the distinct reduction in the onset desorption temperature and kinetics enhancement of the 2NaAlH₄ + Ca(BH₄)₂ composite system.     

Mg2FeH6–LiBH4 and Mg2FeH6–LiNH2 composite materials for hydrogen storage

Two composite hydrogen storage materials based on Mg₂FeH₆ were investigated for the first time. The Mg₂FeH₆–LiBH₄ composite of molar ratio 1:5 showed a hydrogen desorption capacity of 5.6 wt.% at 370 °C, and could be rehydrogenated to 3.6 wt.% with the formation of MgH₂, as the material was heated to 445 °C and held at this temperature. The Mg₂FeH₆–LiNH₂ composite of 3:10 molar ratio exhibited a hydrogen desorption capacity of 4.3 wt.% and released hydrogen at 100 °C lower then the Mg₂FeH₆–LiBH₄ composite, but this mixture could not be rehydrogenated. Compared to neat Mg₂FeH₆, both composites show enhanced hydrogen storage properties in terms of desorption kinetics and capacity at these low temperatures. In particular, Mg₂FeH₆–LiNH₂ exhibits a much lower desorption temperature than neat Mg₂FeH₆, but only Mg₂FeH₆–LiBH₄ re-absorbs hydrogen.     

TiO2–graphene nanocomposites for photocatalytic hydrogen production from splitting water

TiO₂ (P25)–graphene (P25–GR) hybrids were prepared via solvothermal reaction of graphene oxide and P25 using ethanol as solvent. The as-prepared P25–GR nanocomposites were characterized by X-ray diffraction, Raman spectroscopy, transmission electron microscopy, X-ray photoelectron spectroscopy, photoluminescence emission spectroscopy and ultraviolet-visible (UV–vis) diffuse reflectance spectroscopy. The results indicated that P25–GR nanocomposites possessed enhanced light absorption ability and charge separation efficiency. As photocatalysts, P25–GR hybrids were much better than the bare P25, when they were used in the hydrogen evolution from aqueous methanol solution under Xe-lamp illumination. A significant enhancement in the rate of hydrogen production was achieved through using P25–GR as photocatalysts, comparing to bare P25. The optimum mass ratio of GR to P25 in the hybrids was 0.5 wt%. The higher mass ratio of GR in P25–GR would decrease the photocatalytic activity of P25.     

Improved hydrogen storage properties of LiBH4 doped Li–N–H system

Remarkable improvement of hydrogen sorption properties of Li–N–H system has been obtained by doping with a small amount of LiBH₄. The starting and ending temperatures of hydrogen desorption shift to lower temperatures and the release of NH₃ is obviously restrained by 10 mol% LiBH₄ doping. The kinetics of hydrogen desorption and absorption of Li–N–H system became faster by the addition of LiBH₄. About 4 wt.% H₂ can be released within 30 min and ∼4.8 wt.% H₂ can be reabsorbed within 2 min by LiBH₄ doped sample at 250 °C, while only 1.44 wt.% H₂ is released and 2.1 wt.% is reabsorbed for pure Li–N–H system. The quaternary hydride (LiNH₂)_x(LiBH₄)_(1−x) formed by the reaction between LiBH₄ and LiNH₂ may contribute to the enhancement of the hydrogen sorption performances by yielding a ionic liquid phase and transferring LiNH₂ from solid state to molten state with a weakened N–H bond.     

Reversible hydrogen storage behavior of LiBH4–Mg(OH)2 composites

The dehydrogenation/hydrogenation properties of LiBH₄-xMg(OH)₂ were systematically investigated. The results show that the LiBH₄-0.3Mg(OH)₂ composite possesses optimal dehydrogenation properties: approximately 9.6 wt% of hydrogen is released via a stepwise reaction with an onset temperature of 100 °C. In the range of 100–250 °C, a chemical reaction between LiBH₄ and Mg(OH)₂ first occurs to give rise to the generation of LiMgBO₃, MgO and H₂. From 250 to 390 °C, the newly developed LiMgBO₃ reacts with LiBH₄ to form MgO, Li₃BO₃, LiH, B₂O₃ and Li₂B₁₂H₁₂ with hydrogen release. From 390 to 450 °C, the decomposition of LiBH₄ and Li₂B₁₂H₁₂ proceeds to release additional hydrogen and to form LiH and B. A further hydrogenation experiment indicates that the dehydrogenated LiBH₄-0.3Mg(OH)₂ sample can take up 4.7 wt% of hydrogen at 450 °C and 100 bar of hydrogen with good cycling stability, which is superior to the pristine LiBH₄.     

Light-weight NaNH2–NaBH4 hydrogen storage material synthesized via liquid phase ball milling

As a light-weight and low-cost hydrogen storage composite, NaNH₂–NaBH₄ (molar ratio of 2:1) was prepared by a liquid phase ball milling (LPBM) method under the co-protection of argon and cyclohexane. The structure evolution and the thermal decomposition performance of the as-prepared sample were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and thermo gravimetric-differential thermal analysis (TG-DTA), respectively. It is found that the interaction of NaNH₂ with NaBH₄ is enhanced by LPBM, thus causes a preferred orientation for the crystal structure of NaNH₂, and the red-shifts of the N–H stretching vibration and the B–H stretching vibration. In addition, the as-prepared NaNH₂–NaBH₄ (2/1) can achieve a low activation energy of 76.4 kJ mol⁻¹ during the main decomposition stage, which is only 47.9% of that of the one synthesized via a solid state ball milling (SSBM) method, and is very close to that of the Co–B catalyst promoted one. This indicates the LPBM method is an efficient way to get high-performance NaNH₂–NaBH₄, whose thermal decomposition kinetics can be greatly improved without any catalyst.     

Improved hydrogen storage performance of the LiNH2–MgH2–LiBH4 system by addition of ZrCo hydride

Significant improvements in the hydrogen absorption/desorption properties of the 2LiNH₂–1.1MgH₂–0.1LiBH₄ composite have been achieved by adding 3wt% ZrCo hydride. The composite can absorb 5.3wt% hydrogen under 7.0 MPa hydrogen pressure in 10 min and desorb 3.75wt% hydrogen under 0.1 MPa H₂ pressure in 60 min at 150 °C, compared with 2.75wt% and 1.67wt% hydrogen under the same hydrogenation/dehydrogenation conditions without the ZrCo hydride addition, respectively. TPD measurements showed that the dehydrogenation temperature of the ZrCo hydride-doped sample was decreased about 10 °C compared to that of the pristine sample. It is concluded that both the homogeneous distribution of ZrCo particles in the matrix observed by SEM and EDS and the destabilized N–H bonds detected by IR spectrum are the main reasons for the improvement of H-cycling kinetics of the 2LiNH₂–1.1MgH₂–0.1LiBH₄ system.     

Effect of SWNTs on the reversible hydrogen storage properties of LiBH4–MgH2 composite

Single-walled carbon nanotubes (SWNTs) were mechanically milled with LiBH₄/MgH₂ mixture, and examined with respect to its effect on the reversible dehydrogenation properties of the Li–Mg–B–H system. Experimental results show that the addition of SWNTs results in an enhanced dehydriding rate and improved cyclic stability of the LiBH₄/MgH₂ composite. For example, the LiBH₄/MgH₂ composite with 10 wt% purified SWNTs additive can release nearly 10 wt% hydrogen within 20 min at 450 °C, with an average dehydriding rate over 2 times faster than that of the neat LiBH₄/MgH₂ sample. Based on the results of phase analysis and a series of designed experiments, the mechanism underlying the observed property improvement was discussed.     

Effects of MoS2 addition on the hydrogen storage properties of 2LiBH4–MgH2 systems

A 2LiBH₄–MgH₂–MoS₂ composite was prepared by solid-state ball milling, and the effects of MoS₂ as an additive on the hydrogen storage properties of 2LiBH₄–MgH₂ system together with the corresponding mechanism were investigated. As shown in the TG–DSC and MS results, with the addition of 20 wt.% of MoS₂, the onset dehydrogenation temperature is reduced to 206 °C, which is 113 °C lower than that of the pristine 2LiBH₄–MgH₂ system. Meanwhile, the total dehydrogenation amount can be increased from 9.26 wt.% to 10.47 wt.%, and no gas impurities such as B₂H₆ and H₂S are released. Furthermore, MoS₂ improves the dehydrogenation kinetics, and lowers the activation energy (E_a) 34.49 kJ mol⁻¹ of the dehydrogenation reaction between Mg and LiBH₄ to a value lower than that of the pristine 2LiBH₄–MgH₂ sample. According to the XRD test, Li₂S and MoB₂ are formed by the reaction between LiBH₄ and MoS₂, which act as catalysts and are responsible for the improved hydrogen storage properties of the 2LiBH₄–MgH₂ system.     

Reversible hydrogen storage in the Li–Mg–N–H system – The effects of Ru doped single walled carbon nanotubes on NH3 emission and kinetics

In this study, the LiNH₂–MgH₂ (2:1.1) complex hydride system (Li–Mg–N–H is investigated in terms of hydrogen ab/desorption kinetics and the concomitant NH₃ emission levels. By selecting more intense ball milling parameters, the hydrogen ab/desorption kinetics were improved and the NH₃ emission reduced. However, it is shown that NH₃ emission cannot be completely eliminated during ball milling. Single walled carbon nanotubes (SWCNTs) and 20 wt.% Ru doped SWCNTs are utilized as catalysts to study their effects on NH₃ emission and kinetics characteristics of the Li–Mg–N–H system. The SWCNT doped sample did not show any kinetics improvement, whereas the SWCNT-20Ru doped sample showed similar kinetics performance as that of the base sample. More importantly, the presence of SWCNT increased the NH₃ emission as compared to the base sample. On the other hand, SWCNT-20Ru doping reduced the NH₃ emission compared to the SWCNT doping, but did not eliminate it completely. As revealed from the mass spectrometry signals, the SWCNT-20Ru catalyst starts to decompose NH₃ at a temperature as low as 200 °C.     

Catalytic effect of MgFe2O4 on the hydrogen storage properties of Na3AlH6–LiBH4 composite system

The effect of MgFe₂O₄ on the hydrogen storage properties of the composite Na₃AlH₆4LiBH₄ was studied for the first time, where it was found that MgFe₂O₄ addition decreased the onset desorption temperature of Na₃AlH₆4LiBH₄. Hydrogen (～9.5 wt%) was released in three stages and the dehydrogenation temperatures were reduced to 80 °C, 350 °C, and 430 °C for the first, second, and third stage, respectively. The absorption kinetics of Na₃AlH₆4LiBH₄ was also significantly improved due to the catalytic effect of MgFe₂O₄. Using Kissinger analysis, the apparent activation energies of decomposition of the Li₃AlH₆ and NaBH₄ stages in Na₃AlH₆4LiBH₄-10 wt% MgFe₂O₄ were calculated to be 72 and 141 kJ/mol, respectively. These values were considerably lower than the corresponding values for the undoped composite. X-ray diffraction analysis revealed the formation of new products such as MgO and Fe during the heating process. Our results suggest that MgFe₂O₄ enhanced the hydrogen storage properties of Na₃AlH₆4LiBH₄ through the formation of active species, such as MgO and Fe.     

Electrochemical hydrogen storage of ball-milled MmMg12 alloy–Ni composites

MmMg₁₂–Ni amorphous or nanocrystalline composites (Mm: Ce-rich mischmetal) were prepared through the ball-milling method, and their electrochemical hydrogen storage performance was investigated and compared with that of ball-milled CeMg₁₂–Ni composites. It was found that the ball-milled MmMg₁₂–Ni composites had larger initial discharge capacities and better high rate dischargeability. Analysis of electrochemical impedance spectra (EIS) shows that the reaction resistance and hydrogen diffusion resistance of the ball-milled MmMg₁₂–Ni composites are lower as a result of the decrease in Ce content, and thus can contribute to the larger discharge capacity and better high rate dischargeability. Additionally, the cycle performance of the ball-milled MmMg₁₂–Ni composites is better than those of the ball-milled CeMg₁₂–Ni composites. This may be related to the formation of a Nd oxide or Nd(OH)₃ film on surface of the MmMg₁₂ alloys.