Dispersant-free disperse dyes for polyester an eco-friendly approach

Disperse dyes contain around 30–60% of dispersing agents as well as dyeing with disperse dyes requires around 2–5 g/L of dispersing agent for faultless dyeing of polyester and other hydrophobic fibres. Dispersing agents are not absorbed by the fibres and a large quantity of dispersing agent creates unavoidable load on the effluent treatment. Dispersant-free disperse dyes seem to have an acceptable solution to this existing problem. These dyes can work in absence of dispersing agents and thus are called as dispersant free disperse dyes. In this work, dispersant-free disperse dyes were synthesised by coupling diazotised p-nitroaniline with the different components like sulfomethylated aniline and m-toluidine. These synthesised dyes were applied successfully on polyester which resulted into uniform dyeing, good build-up and desired colour yield. The dyeing was dependent on the pH and the optimum pH was 5 similar to that employed in conventional polyester dyeing. The fastness properties obtained were good and comparable with the conventional dyes. Whereas the chemical oxygen demand levels of the dispersant-free disperse dyes were much lower than those from commercial disperse dye.     

超临界流体染色技术的过去、现在和将来(二)

介绍了超临界C02染色技术在世界范围的发展过程及其优于水染色的特点。阐述了超临界C02对纤维性能的影响，诸如润滑效果、C02吸附、结晶、收缩和热机械性能，超临界C02对纤维的玻璃化温度和有效温度以及对纤维损伤的影响。另一重要问题是在超临界C02中纤维与染料之间的平衡分布和影响染料溶解性的参数。文中给出了涤纶纤维的染色步骤、设备和最佳工艺参数，然而天然纤维的染色仍是一个问题。通过浸质溶胀剂和交联剂，或在染色前对纤维改性、添加极性共溶剂，可以提高分散染料的染色性，所有这些方法增加了工艺步骤和设备清洗，若使用有机溶剂则将大大提高机器成本，采用活性分散染料可以避免这种情况。含乙烯矾基团的染料主要适宜于羊毛和聚酰胺纤维的超临界C02，染色，而对于纤维系纤维迄今尚未开发可行的解决方法。预计在不久的将来建造工业化规模的染色设备，努力实现超临界C02染色技术的经济效益。     

细旦涤纶织物高温分散匀染剂SS—97的性能研究

本文着重研究了细旦涤纶织物高温分散匀染剂SS—97的表面特性,以及高温分散性、匀染性、移染性、上染率和染色牢度等染色性能;对不同结构、不同粒径的分散染料以及不同品种织物的适用性,进行了大样试验。试验表明,高温分散匀染剂SS—97能耐高温,对染料有较好的增溶能力和高温分散性;有较强的移染能力,在细旦涤纶织物上具有良好的匀染效果,并有较高的上染率和满意的染色牢度,对不同结构、粒径的染料和不同纤度的纤维均具有良好的适用性。     

涤棉混纺织物一浴法竭染染色用分散／直接交联染料 一

本文介绍了国内外适用于涤棉混纺织物一浴一步法染色的分散／直接交联染料的性能及其染料结构。分散染料染色过程一般分为织物表面吸附，纤维内部扩散，纤维内部达到平衡三个阶段。一浴一步法分散染料则由老品种中筛选拼混而成以获得增效作用，达到快速染色目的。直接交联染料具有较大的直接性，对棉纤维的亲和力应大于冰染料；染料的线性和同平面性愈强，愈能作为交联染料，直接交联染料具有类似于直接染料的性质，但是直接染料不能     

超临界流体染色技术的过去、现在和将来(一)

介绍了超临界CO2染色技术在世界范围的发展过程及其优于水染色的特点。阐述了超临界CO2对纤维性能的影响，诸如润滑效果CO2吸附、结晶、收缩和热机械性能，超临界CO2对纤维的玻璃化温度和有效温度以及对纤维损伤的影响。另一重要问题是在超临界CO2中纤维与染料之间的平衡分布和影响染料溶解性的参数。文中给出了涤纶纤维的染色步骤、设备和最佳工艺参数，然而天然纤维的染色仍是一个问题。通过浸渍溶胀剂和交联剂，或在染色前对纤维改性、添加极性共溶剂，可以提高分散染料的染色性，所有这些方法增加了工艺步骤和设备清洗，若使用有机溶剂则将大大提高机器成本，采用活性分散染料可以避免这种情况。含乙烯砜基团的染料主要适宜于羊毛和聚酰胺纤维的超临界CO2染色，而对于纤维素纤维迄今尚未开发可行的解决方法。预计在不久的将来建造工业化规模的染色设备，努力实现超临界CO2染色技术的经济效益。     

稀土对酸性媒介染料上染羊毛的作用研究

本文采用酸性媒介染料对羊毛纤维进行染色,通过加入氯化钆稀土来提高染料的上染率,降低羊毛染色温度,提高纤维强力并减少媒染剂重铬酸钾的用量。实验中确定了稀土的加入时间、稀土用量、重铬酸钾用量、染色温度等主要工艺参数,最终得出稀土用于酸性媒介染料上染羊毛纤维的最佳优化工艺。     

分散染料碱性浴染色

分散染料碱性浴染色是近年来为适应聚酯超细纤维染色而提出的染色新方法，它具有很多在弱酸性条件下染色不可以拟的优点。本文对部分国产分散染料在碱性条件下染色的适应性进行了研究，筛选出一部分适合于碱性浴染色的分散染料。     

SML染色载体对涤纶微细纤维染色的影响

研究了环保型分散染料染色载体ＳＭＬ对涤纶微细纤维染色的影响,从其对涤纶微细纤维上分散染料的上染速度曲线,升温上染速率曲线,提升性,移染率以及染色织物的表观色泽浓度,颜色特性和染色牢度的影响来看,ＳＭＬ具有良好的应用前景。     

交织物、混纺纤维定性鉴别剂PZ

研制能正确认和鉴别纤维材料的定性鉴别剂。根据交织物、混纺纤维的结构特征,选用各种不同上染性能和不同亲和力的染料组成混合染液,对目前常用的22种纤维进行染色鉴别,得到各种不同色相。结果明显,对交织物、混纺纤维的鉴别效果了很好。这是一种简便、快捷（10s)、易于掌握的染色鉴别方法,重演性好,便于推广。     

溶解度参数与涤纶染色

溶解参数理论更清楚地解释了分散染料的染色机理，可用以指导分散染料的染色，有助于选择载体、染料和溶剂等，也可进一步解释染料的升华性和超细涤纶丝的染深性。     

涤纶浸染用高固色率液体分散染料

研究了菲诺CLT型液体分散染料的粒径、扩散性、高低温分散性和储存稳定性等基本性能;分析了液体分散染料的染色上染率、移染性和提升性等应用性能;对比了常规粉状染料和液体分散染料的浸染染色残液。结果表明,CLT型液体分散染料颗粒细致均匀,扩散性、高低温分散性能和存储稳定性优异。三只液体分散染料上染曲线、移染性和提升性相近,染料组合配伍性好。     

The Nature of Coupling between the Crystalline and Amorphous Phases and its Effect on the Properties of Heat-set Poly(ethylene terephthalate) Fibres

Poly(ethylenc terephthalate) (PET) fibres having a wide range of structures and morphologies were prepared by heat-setting commercial PET yarn at fixed temperatures between 100 and 255°C under two conditions, i.e. while the yarn was free to relax and when it was held taut at constant length. The structural and morphological characteristics of the crystalline and amorphous phases of the fibre were obtained by using standard methods. The sonic modulus, boiling-water shrinkage, recovery during an axial load–elongation test, and uptake of disperse dye by the fibre were determined experimentally. The dependence of these physical properties on structure is critically examined in this paper. It is shown that, in addition to the well-known structural characteristics such as the content and orientation of the amorphous phase, size and size distribution of crystallites, birefringence, etc., the nature of coupling between the crystalline and amorphous phases in the fibre, which differs significantly in the two sets of fibres, can play an important role in determining fibre properties.     

晶型对分散染料染色性能的影响

针对疏水性纤维染色过程中分散染料吸尽率低及染色助剂消耗大的问题,采用溶剂法对分散染料进行转晶,获得更易分散吸附上染的分散染料晶体,以提高染色效率。分别采用N, N?二甲基甲酰胺和苯对C．I． 分散红73 染料进行转晶,得到不同于原染料晶型的2 种晶型染料,分别是晶型I和晶型II。采用聚合物分散剂对这2种晶型染料进行研磨分散,将得到的不同种晶型染料分散液对超细涤纶织物进行染色,研究分散染料的晶型对染料研磨效率、染料分散液稳定性以及织物染色性能的影响,并与未转晶的染料做比较。结果表明：不同种晶型染料研磨分散到相同粒径大小时,晶型I 染料的研磨效率最高,且此种晶型染料分散液的离心稳定性最好,染色性能最优。     

PBT磨尖丝采用分散染料染色代替色母粒染色的生产试验

通过采用分散染料染色加工能解决因色母粒染色的PBT丝经磨尖加工后毛尖部位泛白、无光泽、粗糙等问题。同时,采用紧式集束方法解决了动态染色造成的毛尖走向混乱和PBT丝加热受外力使用弯曲变形这两个技术难题。     

低熔点皮芯复合纤维分散染料染色机制

以低熔点皮芯复合纤维为主要研究对象,用2种典型结构的分散染料——分散红玉SE-GFL（偶氮型）和分散蓝2BLN（蒽醌型）对其进行染色,研究低熔点皮芯复合纤维分散染料染色动力学和热力学。实验结果表明：分散染料上染低熔点皮芯复合纤维的吸附等温线与分散染料上染普通聚酯纤维一样,都符合Nernst分配型;与普通聚酯纤维分散染料染色相比,分散染料在低熔点皮芯复合纤维上的染色速率常数大大增加,半染时间缩短,扩散系数增大,染色亲和力增加,染色热和染色熵降低。     

分散剂与分散染料上染率

从分散染料后加工所用的各种分散剂的角度,探讨了分散剂的品质,种类,数量等对分散染料上染率的影响,从而提醒生产和研究分散染料后加工的有关厂家和技术人员,在选择使用分散剂时要特别慎重。     

羽毛/棉混纺织物的染色性能研究

对羽毛/棉混纺织物的染色性能进行了研究,通过对不同染料的选择实验,选定了适合于此种织物的混合染料,并对混合染料同浴染色浓度配比进行了探讨.研究表明,对羽毛/棉混纺织物进行染色时,采用分别对棉纤维和羽毛纤维上染性最好而又彼此不沾色的直接染料和中性浴染色的酸性染料作为羽毛纤维织物一浴法染色的复合染料,并选定此复合染料的最佳配比为4/6.     

拼混型黑色分散染料的配伍性及其染色性能

针对涤纶纺织品染色用黑色分散染料拼混各组分配伍性能差,染料提升力低等问题,对筛选的1组中温型拼色分散染料组分的配伍性能及其染色性能进行实验,并对染色样品进行剥色处理以及色牢度测试。结果表明:采用中温型单偶氮类分散染料分散紫SE-E、分散橙SE-G以及分散蓝SE-F进行黑色分散染料拼混,三者拼混比例为0.50∶1.85∶0.65时,可获得比商品液黑分散染料更低的明度值和优良的提升力,实现涤纶纺织品深黑色染色效果;染色样品上各染料组分浓度比值与拼混比例基本吻合,表明拼混黑色分散染料组分间具有良好的配伍性能和染色性能。     

基于粒径分析的分散染料黑浆聚集沉淀

针对分散染料黑浆易聚集沉淀的问题,以150% LB分散黑浆为原料,探究了分散染料浆料经过长时间静置后,发生沉淀且色光发生变化的原因。结果表明：150% LB成品黑浆放置半年后,浆料最上层85%以上的染料颗粒发生沉淀,DC（艳度差）、DH（色相差）明显增大,近似色光变为艳红光;对浆料沉淀及色光变化的各种原因进行了分析,其中分散染料颗粒粒径分布不匀是导致浆料容易发生沉淀的主要原因,并提出了可延缓分散染料浆料沉淀速率的方案,即“粒径控制”--有效控制分散染料的粒径分布,在一定程度上解决了分散染料浆料的聚集沉淀问题,扩大了液态分散染料的应用前景。     

低压无水染色体系中发色母体对分散染料染色性能的影响北大核心CSCD

涤纶传统水浴染色存在高耗水、高排放和高污染的技术难题,以高沸点、非极性的十甲基环五硅氧烷(D5)为染色介质可以实现分散染料在低压条件下对涤纶织物染色。为了研究该体系中发色母体对分散染料染色性能的影响,文章分别以邻氰基对硝基苯胺、3-氨基-5-硝基苯并异噻唑为重氮组分,N-氰乙基-N-乙酰氧乙基苯胺为偶合组分,合成了分散染料D-1(偶氮结构)和D-2(杂环结构)。选用D-1、D-2和C.I.分散红177在低压无水染色体系中对涤纶织物染色,探究了发色母体及促染剂与染料在染色介质中的溶解度、染色性能的关系。结果表明,在无促染剂时,以邻氰基对硝基苯胺为重氮组分的D-1的溶解度最低为0.081 g/L,上染率最高为95%;随着促染剂质量分数的增加,D-1的溶解度及上染率变化较小,而D-2和C.I.分散红177的溶解度明显降低,上染率提高15%;发色母体对染色织物的各项色牢度无显著影响,且均可达到4级或以上。