Ni52.5Mn23.5Ga23.6Tb0.4磁性形状记忆合金马氏体相变和磁感生应变的研究

研究多晶合金Ni52.5Mn23.5Ga24的马氏体相变特征和磁感生应变性能,分析了稀土元素Tb对合金马氏体相变和磁性能的影响.研究结果表明,添加Tb使合金Ni52.5Mn23.5Ga24的马氏体相变温度提高到室温以上,并且降低了合金的温度滞后,在一定压力的作用下合金磁感生应变值增大.     

退火工艺对Ti50.2Ni29.8Cu20合金薄带中马氏体相变的影响

通过快速凝固法制备Ti50.2Ni29.8Cu20合金薄带,并利用XRD(X射线衍射仪)、DSC(差示扫描量热仪)、TEM(透射电子显微镜)等手段研究退火温度和退火时间对Ti50.2Ni29.8Cu20合金薄带马氏体相变的影响.结果表明,退火处理后Ti50.2Ni29.8Cu20合金薄带的室温相主要是B19马氏体和少量...     

制备方法对Ti50.2Ni29.8Cu20合金显微组织和相变行为的影响

采用常规铸造和快速凝固两种合金制备方法,分别制备出化学成分为Ti50.2Ni29.8Cu20的合金体材料和合金薄带,利用XRD(X射线衍射仪)、TEM(透射电子显微镜)、DSC(差示扫描量热仪)等手段研究这两种制备方法对Ti50.2Ni29.8Cu20合金的马氏体相变行为和显微组织方面的影响。实验结果表明,经500℃退火1h处理后,Ti50.2Ni29.8Cu20合金薄带中出现大量B19马氏体和少量Ti2Ni析出相,而固溶后的Ti50.2Ni29.8Cu20合金体材料只存在B19马氏体,同时相比于体材料,薄带的B19马氏体衍射峰强度减小及B19晶格常数a、b增大,而c减小;Ti50.2Ni29.8Cu20合金薄带的马氏体相变温度Ms比体材料的马氏体相变温度Ms低,且薄带的热滞△T也比体材料小。     

退火温度对共晶和单相Al-Co-Cr-Fe-Ni高熵合金显微组织及硬度的影响

采用电弧熔炼法制备了4个铸态为FCC+B2共晶组织和B2单相的Al-Co-Cr-Fe-Ni高熵合金,分析了其相变点,并研究了600,800,1000℃下真空退火10 d对这些合金显微组织及硬度的影响.研究表明:AlCoCrFeNi2.1和Al0.75 Co1.25 CrFeNi合金的共晶反应温度分别为1344℃和1359℃.600～1000℃退火10 d对AlCoCrFeNi2.1高熵合金的显微组织无明显影响;而随着退火温度的增加,Al0.75Co1.25CrFeNi合金中共晶组织的两相层片间距增加.随着Al含量的增加,AlxCo2-xCrFeNi合金的B2相稳定性增加,合金的固相线温度明显升高,显微硬度也明显增加.铸态为B2单相的AlCoCrFeNi合金加热到605.7℃以上会转变为组织细小的FCC+B2+σ三相;继续加热到906.8℃以上,σ相消失,FCC相呈大块状分布.而Al1.75Co0.25CrF-eNi合金需要加热到982.4℃以上才会分解为两种不同成分的B2相.实验发现:退火温度越高,合金的显微硬度越低,这些合金在800℃以下都具有较高的硬度.     

Co部分替代Ni对La_(0.4)Er_(0.4)Mg_(0.2)Ni_(3.3-x)Co_xAl_(0.2)(0.1≤x≤0.4)储氢合金结构和电化学性能的影响

为了改善储氢合金La0.4Er0.4Mg0.2Ni3.3-xCoxAl0.2(0.1≤x≤0.4)的结构和综合电化学性能,采用Co部分替代Ni的方法,实验采用高频感应炉制备La0.4Er0.4Mg0.2Ni3.3-xCoxAl0.2(0.1≤x≤0.4)储氢合金。通过X射线衍射技术和电化学测量方法研究储氢合金的晶体结构和电化学性能。XRD图谱显示样品储氢合金主要由LaNi5和La2Ni7相组成,电化学实验表明,随着Co含量的增高,储氢合金电极的最大放电容量和50次循环后的容量保持率S50基本呈现增加状态,放电容量从x=0.1时的225mA·h/g升高到x=0.4时的254.9mA·h/g,容量保持率S50从57.11%(x=0.1)增加到66.10%(x=0.4),但高倍率性能不断下降。通过交流阻抗(EIS)和线性扫描(LS)对Co替代Ni的合金动力学性能分析发现,Co替代Ni后合金的表面电荷转移能力先降低后升高。     

Fe-Mn-Si合金热循环时γ-ε马氏体相变特征

用Ｘ射线衍射方法对Ｆｅ－３１．６Ｍｎ－６．５Ｓｉ合金在８３－４８０Ｋ温度范围两次热循环时的热诱发γ－ε马氏体相变进行了研究。结果表明,冷却过程中γ→ε相变过程并非终止于Ｔ＾γＮ,而是终止在更低的温度。冷却至８３Ｋ时,γ相表现的还相当稳定。同样,ε马氏体在加热到４８０Ｋ时也显示出较高的稳定性。在加热到大约２７５Ｋ时,观察到奥氏体（２００）衍射强度出现异常降低,而马氏体（１０１）衍射强度正常。这种异常     

γ-Fe-X(Ni,Mn)系的价电子结构和马氏体相变

本文根据“固体与分子的经验电子理论”对γ-Fe-Ni和γFe-Mn固溶体在马氏体相交温度下的价电子结构及磁矩结构进行了分析。结果表明;γ-Fe-X(Ni,Mn)中共价电子数在总价电子中所占的比例η与马氏体相变驱动力ΔGα-M之间存在很好的对应关系。从而揭示了马氏体相变驱动力决定下晶体原子间结合强弱的物理本质。     

固溶处理温度对Fe-14Mn-0.22C减振合金阻尼性能的影响

研究了Fe-Mn基减振合金的减振机制，并深入分析了固溶处理温度对Fe-14Mn-0．22C减振合金阻尼性能的影响，研究结果表明，该合金在固溶处理时，发生了γ-ε转变，固溶处理温度越高，γ-ε转变生成的马氏体越多，合金的阻尼性能随固溶处理温度的升高而升高，在1000℃时，合金的阻尼性能达到最大值，随温度的进一步升高，阻尼性能反而恶化了，主要因为在1200℃时马氏体粗化严重。     

Ti-Mo合金氢化物原位脱氢的相变研究

目的 研究Ti-Mo合金氢化物在原位退火中相变行为,分析Ti-Mo合金氢化物原位退火中的结构变化.方法 利用X射线原位衍射对不同成分的Ti-Mo合金的氢化物在退火过程中的相变用Rietveld法进行了分析.对晶格参数、微观应变在退火过程中的变化用Rietveld法程序进行了计算.对部分样品进行了透射电镜分析.结果 Ti-Mo合金饱和充氢后形成面心立方6相氢化物,在升温过程中转变为体心立方β相固溶体.随着温度升高,δ相与β相的晶粒尺寸和微观应变基本上都经历逐渐增大然后又变小的过程.在相转化的同时,δ相与β相的晶格参数基本随温度的升高而减小.衍射峰形和峰位存在各向异性展宽和位移.结论 用X射线原位衍射结合Rietveld法得到了Ti-Mo合金氢化物的相变信息.δ相氢化物存在广泛的位错和层错(孪晶).一些样品在退火中同时出现两个不同晶格参数的β相.     

退火处理对La-Mg-Ni-Co合金电化学性能的影响

为了改善La-Mg-Ni-Co系贮氢电极合金的综合电化学性能，研究了退火处理对La0.7Mg0.3(Ni0.85Co0.15)3.4相结构和电化学性能的影响.在1 073 ～1 223 K下退火9 h制得样品，并进行了XRD分析以及恒电流充放电、线性极化和恒电位阶跃3种电化学测试.结果表明，铸态和退火态合金均由具有PuNi3结构的主相及少量杂相组成.退火态合金相的成分和结构均匀性得到明显改善，并具有较低的吸氢体积膨胀率.退火处理使合金的最大放电容量有所提高，循环稳定性得到明显改善.退火态合金放电容量的提高与合金中主相丰度的增大密切相关.合金循环稳定性的改善主要归结于退火态合金具有较低的吸氢体积膨胀率和较好的合金成分均匀性.     

Effect of Sm-doping on the morphology and magnetic properties of radio frequency magnetron sputtered Ni-Mn-Ga films

Ni55.5Mn21Ga23.5 and Ni54Mn22Ga23Sm1 films were prepared by radio frequency (RF) magnetron sputtering. The effect of Sm do-pant on the morphologic and magnetic properties of Ni55.5Mn21Ga23.5 films was investigated. Sm doping can refine the particle size of the films from 100 to 60 nm, and further grain growth is not occurs even after annealing at 1073 K for 3.6 ks. Compared to Ni55.5Mn21Ga23.5 films, Sm-doped Ni54Mn22Ga23Sm1 films are easier to be magnetized and have a lower martensitic transformation temperature. In addition, the Curie temperature can also be adjusted, decreasing from 350 to 325 K after Sm doping. Martensitic transformation is not observed in the Sm-free films, which is close to the Curie temperature in the Sm-doped films, giving rise to the overlap of the structural and magnetic transi-tion temperatures.     

Influence of Tb substitution on low-field magnetocaloric effect in Gd5Si1.72Ge2.28 alloy

The lattice parameters, magnetic phase transition, Curie temperature and magnetocaloric properties for (Gd1-xTbx)5Si1.72-Ge2.28 alloys with x = 0, 0.15, 0.20 and 0.25 were investigated by X-ray powder diffractometry and magnetization measurements. The results show that suitable partial substitution of Tb in Gd5Si1.72Ge2.28 compound remains the first-order magnetic-crystallographic transition and enhances the magnetic entropy change, although Tb substitution decreases the Curie temperature (Tc) of the compounds. The magnetic entropy change of (Gd1-xTbx)5Si1.72Ge2.28 alloys retains a large value in the low magnetic field of 1.0 T.The maximum magnetic entropy change for (Gd0.80Tb0.20)5Si1.72Ge2.28 alloy in the magnetic field from 0 to 1.0 T reaches 8.7 J/(kg·K),which is nearly 4 times as large as that of (Gd0.3Dy0.7)5Si4 compound (|△Smax| = 2.24 J/(kg·K), TC = 198 K).     

Tm2CrFe16-xSix化合物的结构和居里温度

通过X射线衍射和磁测量手段研究Tm2CrFe16-xSix（X=0,0．5,1．0,1．5,2．0,2．5,3．0）化合物的结构和居里温度．结果表明,Tm2CrFe16-xSix化合物具有Th2Ni17型结构,随着Si替代量X的增加,Tm2CrFe16-xSix化合物的单胞体积、晶胞参数都减小．在Tm2CrFe16-xSix化合物中存在着各向异性的磁弹耦合效应．随着x的增加,Tm2CrFe16-xSix化合物的居里温度升高,在x=1．5时达到最大值,约为450K,比Tm2Fe17化合物的居里温度高出约140K,当x继续增加时,Tm2CrFe16-xSix化合物的居里温度下降．     

工作频率对测量磁性材料居里温度的影响

采用RL交流电桥来测量磁性材料的居里温度,通过分析升温和降温两种过程曲线,研究低频和高频工作状态对测量磁性材料居里温度的影响。结果表明：工作频率的高低对测量磁性材料居里温度的影响不大,但在高频条件下测得的居里温度更精确,这符合铁氧体磁性材料具有适于更高频率下工作的特性。     

Influence of stresses on martensitic transformation in ferromagnetic shape memory Ni_(50)Mn_(19)Fe_6Ga_(25) ribbons

~~Influence of stresses on martensitic transformation in ferromagnetic shape memory Ni_(50)Mn_(19)Fe_6Ga_(25) ribbons1. Ullakko, K., Huang, J. K., O'Handley, R. C. et al., Large magnetic-field-induced strains in Ni2MnGa single crystals, Appl. Phys. Lett., 1996, 69(13): 1966-1968. 2. James, R. D., Wuttig, M., Magnetostriciton of martensite, Philos. Mag., 1998, A 77: 1273-1275. 3. Wu, G. H., Yu, C. H., Meng, L. Q. et al., Giant magnetic-field-induced strains in H…     

稀释合金中铁离子交换电子和能量作用的证明

利用稀释的金铁和铜铁合金中相邻4个铁离子构成的正方形4L回路上的铁离子间存在交换电子(EE)和能量的作用过程计算了合金的热电势、铁离子磁矩和居里温度、电阻极大值温度和极小值温度、传导电子的比热增加和熵值减少、负磁阻效应等,与测量值相符.这些结果证明铁离子或4s传导电子产生了新的正方形原子轨道4L,2个4sEE在4L轨道上产生的磁矩2PmOK构成铁离子的磁矩,居里温度Tc与4sEE的量子化能量成比例,基金属传导电子(HMCE)产生了反向旋转或反向自旋能量UOK,UOK使合金产生大的热电势等反常物理量.     

Influences of composition and annealing on the martensitic transformation in Ni-Fe-Ga alloys

A series of Ni-Fe-Ga alloys near the prototype Heusler composition (X₂YZ) were prepared through arc-melting suction-casting method. The dependences of the transformation behavior on the alloy composition and annealing treatment were studied in detail by an optical microscope, X-ray diffraction, and differential scanning calorimeters methods. The experimental results show that the martensitic transformation temperatures increase almost linearly with increasing Ni content in all the NiFeGa alloys. Annealing the Ni_55.5Fe₁₈Ga_26.5 alloy at 100?C500 °C for 3 h and at 300 °C for 1?C10 h shifts the martensitic transformation start temperature by almost 20 °C to high temperature. The variations in the martensitic transformation temperatures in these alloys are discussed in terms of structural differences resulting from alloy composition and annealing treatment.     

热处理工艺对Fe-23Ni-0.55C马氏体表面浮凸形貌的影响

利用金相显微镜、扫描电镜观察了不同热处理工艺对Ｆｅ－２３Ｎｉ－０．５５Ｃ马氏体表面浮凸形貌的影响．结果表明：深冷温度越低,马氏体表面浮凸越显著,边界越平整,预马氏体转变效应越少;随奥氏体化温度降低,马氏体表面浮凸由较宽的平行排列、边界不平整的长片状转变为无方向性、边界平整的蝶状;由于浮凸协作形变效应,马氏体的显微组织较浮凸窄得多．