共查询到20条相似文献,搜索用时 31 毫秒
1.
《钢铁》2018,(11)
为了研究炉渣铁水脱硫速率,在实验室条件下进行了温度为1 673~1 773 K时CaO-SiO_2-Al_2O_3-Na_2O-TiO_2渣铁水脱硫的动力学试验。结果表明,随着温度的增加,脱硫速率加快,炉渣熔化效果更好。多数脱硫反应在约50 min后硫质量分数基本不变。通过建立铁水脱硫动力学的数学模型,计算脱硫过程中硫的传质系数和传质阻力。硫的传质系数范围为5.02×10-7~18.69×10-7m/s。温度为1 673~1 723 K时活化能为464.06 kJ/mol,温度为1 723~1 773 K时活化能为176.35 k J/mol。通过矿相解离分析仪(MLA)观察硫在渣铁界面附近的分布情况,结合MLA扫描图片,认为高温时硫在渣中的传质是脱硫过程的限制环节。 相似文献
2.
D. N. Rego G. K. Sigworth W. O. Philbrook 《Metallurgical and Materials Transactions B》1988,19(4):655-661
A gas phase equilibration technique was used to generate Na2O isoactivity data at high-silica compositions in the systems Na2O-CaO-SiO2, Na2O-MgO-SiO2, and Na2O-CaO-SiO2-(10 and 20 wt pct) A12O3 at 1400 °. Loga Na 2 O values referenced to pure liquid Na2O at 1400 ° as standard state ranged from about ?8.0 to ?7.0. Silica activities were calculated in the Na2O-CaO-SiO2 system using the Gibbs-Duhem equation. Richardson’s model for ideal mixing of basic oxides in silica was applied to the Na2O-CaO-SiO2 system. The model shows best fit when cationic mixing is assumed to occur on divalent sites. The alkali retention in slags has been described using a defined “sodium capacity”. The temperature variation of alkali retention was estimated, and the resulting sodium capacity was used to evaluate alkali stability in blast furnace slags. 相似文献
3.
根据熔渣结构的分子离子共存理论,建立了CaO-SiO2-Al2O3-FeO-CaF2-La2O3-Nb2O5-TiO2八元渣系的活度计算模型.利用该活度模型,计算和分析了此渣系中铌、稀土、钛相关组元的活度变化规律.实验结果表明,模型计算结果与实际测量值能较好吻合;在本实验渣系条件下,含铌组元主要为FeO·Nb2O5,含镧组元主要为La2O3和La2O3·Al2O3,含钛组元主要为2FeO·TiO2和FeO·TiO2;随着渣中FeO质量分数的降低,含铌组元由FeO·Nb2O5转变为CaO·Nb2O5,而含钛组元主要由2FeO·TiO2和FeO·TiO2向TiO2转变;当渣中FeO质量分数较低时,ω(CaO)/ω(SiO2)成为影响铌和钛相关组元活度的重要因素,随着ω(CaO)/ω(SiO2)的增大,2CaO·Nb2O5和CaO·TiO2的活度明显增大. 相似文献
4.
Toyo Kohan 公司的研究人员考虑到挤压和注射成形机器零件的磨损和腐蚀等问题,发明了一系列的以复杂的钼铁硼化合物为基体的硬质合金,它由类似于 Mo_2FeB_2的硼化物基的陶瓷粒子组成,含有铬、镍和钼等可以热处理的粘结剂。据称,新型硬质合金的硬度和横向断裂强度分别为80~92HRA 和1000~2600兆帕, 相似文献
5.
为揭示Nb2O5-Al2O3-MgO-Na2O-CaO-SiO2多元含铌炉渣体系中的铌矿物的定向结晶规律,采用高温相平衡—冷淬—SEM-EDS/XRD/EMPA试验方法,考察了温度、钙硅比(CaO/SiO2)、Nb2O5含量等因素对炉渣相平衡关系的影响,并构建了含铌矿物结晶析出的优势相图。结果表明:铌的结晶矿物主要有三种,分别为Ca2Nb2O7、Ca(14-x)Nb(2+x)Si8O(35+1.5x)和3CaO?MgO?Nb2O5;铌先富集于液相,相较于脉石组分,含铌固相为后析出相;CaO/SiO2增加会使含铌固相优势区间发生从Ca2Nb2O7相到Ca(14-x)Nb(2+x)Si8O(35+1.5x)相、再到3CaO?MgO?Nb2O5相的转变。Ca2Nb2O7相的优势析晶区间为:温度1 050~1 200 ℃,C/S=0.8~1.2。Nb2O5在Ca(14-x)Nb(2+x)Si8O(35+1.5x)相中的嵌布质量浓度在18.5%~19.5%。 相似文献
6.
7.
8.
分析了加入不同质量分数的CaO-SiO_2对CaCl_2-CaF_2空白熔盐的电导率、密度以及初晶温度的影响。结果表明,每添加2%的CaO-SiO_2,熔盐体系的初晶温度平均升高17.5℃、密度相应增加0.015 1g/cm~3、电导率增大0.224 13S/cm,侧面论证了CaO-SiO_2在基础体系中以硅酸盐分子形式存在。 相似文献
9.
含铝钢连铸时,钢水中的铝与保护渣中SiO2反应导致保护渣中Al2O3含量增加而SiO2含量减少,导致保护渣的热物理性能发生变化,从而影响了铸坯的质量。在以前的研究基础上使用X射线衍射仪(XRD)和差热分析仪(DTA)以及扫描电镜(SEM)研究了高铝保护渣固态渣膜的结晶行为与晶体显微结构的变化规律。结果表明,高铝保护渣中CaF2的析出主要是因为SiO2含量的减少和Al2O3含量的增加导致大量的Ca2+的功能由电荷补偿变为网络修饰体,温度降低时CaF2首先析出;随着保护渣中Al2O3含量的增加,在同一加热速率下析晶温度升高;当保护渣中Al2O3含量较少时,析出晶体为枪晶石(Ca4Si2O7F2)和少量的CaF2,当Al2O3含量大于5%(质量分数,下同)时,霞石(NaAlSiO4)进一步析出,且随着Al2O3含量的增加,析出晶体的尺寸减小。 相似文献
10.
CaO-SiO2-Na2O-CaF2-Al2O3-MgO渣系的粘性活化能 总被引:1,自引:1,他引:0
采用CaO-Si02-Na20-CaF2-Al2O3-MgO渣系,通过测定粘度和粘性活化能,建立二次回归正交设计模型,借此研究了粘性特征与碱度、Na20含量、CaF2含量、Al2O3含量及MgO含量之间的关系,为设计开发连铸保护渣提供了理论依据。研究结果表明,粘性活化能随着渣中碱度、Na2C03含量和CaF2含量的增加而减小;Al2O3和MgO对粘性活化能的影响与碱度密切相关。连铸保护渣的粘度和粘性活化能具有相似的变化规律。 相似文献
11.
Takashi Watanabe Hiroyuki Fukuyama Kazuhiro Nagata Masahiro Susa 《Metallurgical and Materials Transactions B》2000,31(6):1273-1281
Equilibrium phase diagram for the system cuspidine (3CaO · 2SiO2 · CaF2)-CaF2 has been studied by the quenching method and differential thermal analysis (DTA). Hermetically closed platinum capsules were
used in both methods to prevent fluorine loss in the form of HF and SiF4 by reaction of the CaF2 with water vapor or SiO2. Cuspidine congruently melts at 1680±2 K. The cuspidine-CaF2 system presents a simple eutectic type of phase diagram. The eutectic composition and temperature are 46 mass pct 3CaO ·
2SiO2−54 mass pct CaF2 and 1515±3 K, respectively. 相似文献
12.
13.
Idil Arslan Isil Akmehmet Balcioglu Tuula Tuhkanen Detlef Bahnemann 《Canadian Metallurgical Quarterly》2000,126(10):903-911
This study investigated the advanced oxidation of commonly used reactive dyestuffs in exhausted dye-bath effluents in homogeneous (H2O2∕UV-C and photo-Fenton) and heterogeneous (TiO2∕UV-A) media. Photocatalytic treatment efficiencies of two different TiO2 powders (PC 500 and Mikroanatas) and the platinized Degussa P25 were compared with that of the more well-known Degussa P25 in varying pH media. Treatment performance was strongly affected by the initial H2O2 concentration for H2O2∕UV-C and photo-Fenton oxidation systems, whereas for the TiO2∕UV-A process only PC 500 TiO2 powder, an anatase crystal phase of the semiconductor, exhibited a significantly pH-dependent reaction efficiency. The decolorization rate followed the order of Fenton∕UV-C > Pt-P25∕UV-A > Mikroanatas∕UV-A > P25∕UV-A > PC 500∕UV-A > H2O2∕UV-C, whereas the decreasing order for total organic carbon reduction was Fenton∕UV-C > H2O2∕UV-C > Mikroanatas∕UV-A > Pt-P25∕UV-A > P25∕UV-A > PC 500∕UV-A for the studied reaction conditions. Removal of optical density at 254-nm wavelength ranged between 75 and 96%. 相似文献
14.
Thewettability phenomenonbetweenmoltensteelandmetallurgicalslagisoneofthemostimpor tantsubjectsinsteelmakingprocess.Theformationofsteel slagemulsions ,andtheformationandelimina tionofnon metallicinclusionsinsteelaretypicalex amples.Theinterfacialtensionan… 相似文献
15.
RE2O3-CaO-SiO2-CaF2-MgO-Al2O3系炉渣的凝固组织 总被引:2,自引:1,他引:1
为了综合利用富稀土高炉渣,利用扫描电镜观察并配合能谱分析和X射线衍射分析研究了RE2O3-CaO-SiO2-CaF2-MgO-Al2O3系炉渣于1 400 ℃熔化并保温30 min,再以1 ℃/min的冷却速度凝固后的组织.结果表明在凝固过程中,绝大部分稀土富集于铈钙硅石(RE2O3·CaO·SiO2)相中;熔渣的凝固组织主要由铈钙硅石、枪晶石(CaF2· 3CaO·2SiO2)、萤石(CaF2)和硫化钙(CaS)这4种相组成. 相似文献
16.
17.
18.
本文观测了2Cr12Ni2Mo2WV钢的回火转变,结果表明:回火温度从室温至400℃,马氏体分解,析出M_3C;从400~500℃,M_3C回溶到基体中,M_7C_3直接从基体中沉淀析出,产生二次硬化;从500~600℃,M_7C_3转变成M_(23)C_6,钢中碳化物含量显著增加,钢的强度急剧下降;回火温度超过600℃,M_(23)C_6继续析出并长大;该钢的残余奥氏体和它的过冷奥氏体相似,在A_(c 1)~M_s温度范围内十分稳定,回火过程中不发生残余奥氏体转变。 相似文献
19.
B2O3在CaO-BaO-SiO2-Al2O3-CaF2精炼渣中的作用 总被引:1,自引:0,他引:1
选择w(CaO)=46%,w(BaO)=10%,w(SiO2)=11.2%,w(Al2O3)=11.6%的渣作基础渣系,将B2q作助熔剂替代CaF2,发现B2q和CaF2的助熔效果相当,B2q可用作环保型助熔剂。将CaO-SiO2-BaO-Al2O3-CaF2作基础渣系,B2O3作酸性氧化物,在碱度(m(CaO+BaO)/m(SiO2+B2O3))为2.5和2.8时,研究B2O3替代SiO2后精炼渣的熔化性能。结果表明,B2O3替代25%的SiO2后就可大幅度降低粘度,并且发现富硼精炼渣的高温熔化性能稳定,粘度值稳定在0.3~0.5Pa·s。在碱度为2.8wt进行脱硫工艺实验,当w(SiO2)=20.6%时渣剂脱硫率为80%,当w(SiO2)=10.3%,w(B2O3)=10.3%时渣剂脱硫率为91.3%,主要原因是熔化性能良好的熔渣有助于提高传质速率。 相似文献