AlGaN/GaN异质结构的欧姆接触

通过改变Ti/Al的结构及退火条件,研究了AlGaN/GaN异质结构上Ti/Al/Ni/Au金属体系所形成的欧姆接触.结果表明,Ti/Al/Ni/Au金属厚度分别为20,120,55和45nm,退火条件为高纯N2气氛中850℃、30s时在AlGaN/GaN异质结构上获得了良好的欧姆接触,其比接触电阻率为3.30×10-6Ω·cm2.SEM分析表明该条件下的欧姆接触具有良好的表面形貌,可以很好地满足高性能AlGaN/GaN高电子迁移率晶体管制造的要求.     

用于紫外探测器的AlGaN/GaN异质结构的Ti/Al/Ni/Au欧姆接触特性

采用Ti/Al/Ni/Au多层金属体系在Al0.27Ga0.73N/GaN异质结构上制备了欧姆接触.分别采用线性传输线方法(LTLM)和圆形传输线方法(CTLM)对其电阻率进行了测试.当Ti(10nm)/Al(100nm)/Ni(40nm)/Au(100nm)金属体系在650℃高纯N2气氛中退火30s时,测量得到的最小比接触电阻率为1.46×10-5Ω·cm2.并制备了Al0.27Ga0.73N/GaN光导型紫外探测器,通过测试发现探测器的暗电流.电压曲线呈线性分布.实验结果表明在Al0.27 Ga0.73N/GaN异质结构上获得了好的欧姆接触,能够满足制备高性能AlGaN/GaN紫外探测器的要求.     

用于紫外探测器的AlGaN/GaN异质结构的Ti/Al/Ni/Au欧姆接触特性

采用Ti/Al/Ni/Au多层金属体系在Al0.27Ga0.73N/GaN异质结构上制备了欧姆接触. 分别采用线性传输线方法(LTLM)和圆形传输线方法(CTLM)对其电阻率进行了测试. 当Ti(10nm)/Al(100nm)/Ni(40nm)/Au(100nm)金属体系在650℃高纯N2气氛中退火30s时,测量得到的最小比接触电阻率为1.46E-5Ω·cm2. 并制备了Al0.27Ga0.73N/GaN光导型紫外探测器,通过测试发现探测器的暗电流-电压曲线呈线性分布. 实验结果表明在Al0.27Ga0.73N/GaN异质结构上获得了好的欧姆接触,能够满足制备高性能AlGaN/GaN紫外探测器的要求.     

Ti/Al/Ti/Au与AlGaN欧姆接触特性

研究了溅射Ti/Al/Ti/Au四层复合金属与AlGaN/GaN的欧姆接触特性,并就环境温度对欧姆接触特性的影响进行了分析研究.试验证实:溅射的Ti/Al/Ti/Au与载流子浓度为2.24×1018cm-3的AlGaN之间在室温下无需退火即可形成欧姆接触.随快速退火温度的升高接触电阻降低.快速退火时间30s已可实现该温度下最佳欧姆接触.当工作温度不高于300℃时接触电阻几乎不受温度的影响.     

AlGaN/GaN MSM紫外探测器特性

在蓝宝石衬底上,用MOCVD(金属有机物气相沉积)法外延生长AlGaN/GaN异质结样品.溅射Ti/Al/Ni/Au和Ni/Au金属膜,在氮气气氛中高温快速退火,分别与样品形成欧姆接触和肖特基接触.随着退火时间的增加,MSM(金属-半导体-金属)结构的I-V特性曲线保持良好的对称性,但C-V曲线逐渐失去其对称性.MSM探测器的紫外响应曲线具有良好的对比度和选择性,出现明显的光电导增益效应.     

AlGaN/GaN MSM紫外探测器特性

在蓝宝石衬底上,用MOCVD(金属有机物气相沉积)法外延生长AlGaN/GaN异质结样品.溅射Ti/Al/Ni/Au和Ni/Au金属膜,在氮气气氛中高温快速退火,分别与样品形成欧姆接触和肖特基接触.随着退火时间的增加,MSM(金属-半导体-金属)结构的I-V特性曲线保持良好的对称性,但C-V曲线逐渐失去其对称性.MSM探测器的紫外响应曲线具有良好的对比度和选择性,出现明显的光电导增益效应.     

AlGaN/GaN MSM紫外探测器特性

在蓝宝石衬底上,用金属有机物气相沉积(MOCVD)法外延生长AlGaN/GaN异质结样品.溅射Ti/Al/Ni/Au和Ni/Au金属膜,在氮气气氛中高温快速退火,分别与样品形成欧姆接触和肖特基接触.随着退火时间的增加,金属-半导体金属(MSM)结构的I V特性曲线保持良好的对称性,但C V曲线逐渐失去其对称性.MSM探测器的紫外响应曲线具有良好的对比度和选择性,出现明显的光电导增益效应.     

AlGaN/GaN MSM紫外探测器特性

在蓝宝石衬底上，用MOCVD（金属有机物气相沉积）法外延生长AlGaN/GaN异质结样品. 溅射Ti/Al/Ni/Au和Ni/Au金属膜，在氮气气氛中高温快速退火，分别与样品形成欧姆接触和肖特基接触. 随着退火时间的增加，MSM（金属-半导体-金属）结构的I-V特性曲线保持良好的对称性，但C-V曲线逐渐失去其对称性. MSM探测器的紫外响应曲线具有良好的对比度和选择性，出现明显的光电导增益效应.     

Ti/Al/Ni/Au金属体系在N-polar GaN上的欧姆接触特性

利用金属有机化合物化学气相淀积(MOCVD)在SiC衬底上外延生长了N-polar GaN材料,采用传输线模型(TLM)分析了Ti/Al/Ni/Au金属体系在N-polar GaN上的欧姆接触特性.结果表明,Ti/Al/Ni/Au (20/60/10/50 nm)在N-polar GaN上可形成比接触电阻率为2.2×10-3Ω·cm2的非合金欧姆接触,当退火温度升至200℃,比接触电阻率降为1.44×10-3 Ω·cm2,随着退火温度的进一步上升,Ga原子外逸导致欧姆接触退化为肖特基接触.     

AlGaN/AlN/GaN肖特基二极管的电学性能

利用金属有机化学气相淀积(MOCVD)方法生长的AlGaN/AlN/GaN/蓝宝石材料制备了AlGaN肖特基二极管.器件的肖特基接触和欧姆接触分别为Ti/Pt和Ti/Al/Ti/Au,均采用电子束蒸发的方法沉积.AlGaN表面欧姆接触的比接触电阻率为7.48×10-4Ω/cm2,器件的I-V测试表明该AlGaN肖特基二极管具有较好的整流特性.根据器件的正向,I-V特性计算得到器件的势垒高度和理想因子分别为0.57eV和4.83.将器件在300℃中温退火,器件的电学性能有所改善.     

Vanadium-based ohmic contacts to n-type Al<Subscript>0.6</Subscript>Ga<Subscript>0.4</Subscript>N

Four vanadium-based contacts to n-type Al_0.6Ga_0.4N were compared in this work. Both V/Al/Pd/Au and V/Al/V/Au contacts with optimized layer thicknesses provided lower specific-contact resistances than did the previously reported V/Al/Pt/Au ohmic contact. Specific contact resistances of the V/Al/Pd/Au (15 nm/85 nm/20 nm/95 nm) and V/Al/V/Au (15 nm/85 nm/20 nm/95 nm) contacts were 3×10⁻⁶ Ω·cm² and 4×10⁻⁶ Ω·cm², respectively. On the other hand, an analogous V/Al/Mo/Au contact never became ohmic, even after it was annealed at 900°C for 30 sec. Compared to the V/Al/Pd/Au contact, the V/Al/V/Au contact required a less severe annealing condition (30 sec at 700°C instead of 850°C). The V/Al/V/Au contact also provided a smoother surface, with a root-mean-square (RMS) roughness of 39 nm.     

1.0μm栅长GaAs基MHEMT器件及SPDT开关MMIC

利用MBE外延材料和接触式光学光刻方式,成功制备出1.0μm栅长GaAs基MHEMT器件,分别蒸发Pt/Ti/Pt/Au和Ti/Pt/Au作为栅电极金属.获得了优越的DC和RF性能,Pt/Ti/Pt/Au和Ti/Pt/Au MHEMT器件的gm为502(503)mS/mm,JDss为382(530)mA/mm,VT为0.1(-0.5)V,fT和fmax分别为13.4(14.8),17.0(17.5)GHz.利用单片集成增强/耗尽型GaAs基MHEMT器件制备出九阶环型振荡器,直流电压为1.2V时,振荡频率达到777.6MHz,门延迟时间为71.4ps.利用Ti/Pt/Au MHEMT器件设计并制备出了DC-100Hz单刀双掷(SPDT)关MMIC,其插入损耗、隔离度、输入输出回波损耗分别优于2.93,23.34和20dB.     

Au/BIT/PZT/BIT/p-Si(100)存储器

利用准分子激光原位淀积方法制备了BIT／PZT／BIT，PZT／BIT和BIT层状铁电薄膜，获得了电流密度－电压（I－V）回线和极化强度P－V电滞回线。在这三种结构中，Au/BIT/PZT/BIT/p-Si(100）结构的界面电位降、内建电压及频率效应是最小的。在电压转变电VT、饱和极化强度Ps及矫顽场Vc之间有三种关系，他们与I－V回线及P－V回线的关系相匹配，这种匹配关系使得以I－V回线操作的存储器将能够非挥发和非破坏读出及具有保持力。     

多媒体通信中基于ABR业务的融入凭证方式的速率控制机制

提出了一种融入基于凭证方式的基于速率的流量控制模型，该模型继承了基于凭证方法的记数机制，通过设定高低缓存门限和调节速率升降因数来控制源端速率。仿真结果表明，这种控制机制不仅能够保证缓存的充分利用，而且能够提高其在减少信元丢失、降低传输时延等方面的性能。     

WLAN工程设计

本文就WLAN工程设计提出了带有普遍意义的概念,包含室内覆盖、室外覆盖、室外(视距内)无线桥接。并就无线侧的规划、优化进行了浅析。     

难熔金属与n-GaAs的欧姆接触特性

用磁控溅射系统和快速合金化法制备了Mo/W/Ti/Au多层金属和n-GaAs材料的欧姆接触,在溅射金属层之前分别用HCl溶液和(NH4)2S溶液对n-GaAs材料的表面进行处理．用传输线法对比接触电阻进行了测试,并利用俄歇电子能谱（AES）、X射线衍射图谱（XRD）对接触的微观结构进行了分析．结果表明,用(NH4)2S溶液对n-GaAs材料表面进行处理后,比接触电阻最小;在700℃快速合金化后获得最低的比接触电阻,约为4.5×10－6Ω·cm2．这是由于(NH4)2S溶液钝化处理后降低了GaAs的表面态密度,消除了费米能级钉扎效应,从而改善了难熔金属与GaAs的接触特性．     

TiO2/n-Si/p-Si及n-PS/p-PS/Si的光伏特性

在抛光的p型单晶硅上通过扩散工艺制备pn结,采用此种硅片利用阳极腐蚀法制备多孔硅(PS).用磁控溅射镀膜机在有pn结的单晶硅表面镀上一层TiO2纳米结构薄膜,并用表面光电压谱(SPS)研究了n-PS/p-PS/Si和TiO2/n-Si/p-Si的表面光伏特性.结果表明TiO2/n-Si/p-Si和n-PS/p-PS/Si的光伏效应比n-Si/p-Si在不同程度上有所提高.在300～600 ℃热处理温度范围内TiO2/n-Si/p-Si的光伏效应随温度的升高而增强,600～800 ℃范围内随温度的升高而降低.     

一种适用于科研单位的混合组网方式

本文基于网络逻辑隔离概念,利用业务随行、VxLAN和SDN等网络新技术进行网络架构规划,在减少基础建设投资的前提下,通过精准逻辑隔离的方式对科研单位的办公网、科研网和数据中心网络进行整体架构设计.该方式在不能单独组网(传统物理隔离)的条件下实现了网络终端、服务器、试验装置的访问可控和权限可控,可保障科研单位的整体网络运...     

1.0μm栅长GaAs基MHEMT器件及SPDT开关MMIC

利用MBE外延材料和接触式光学光刻方式,成功制备出1.0μm栅长GaAs基MHEMT器件,分别蒸发Pt/Ti/Pt/Au和Ti/Pt/Au作为栅电极金属.获得了优越的DC和RF性能,Pt/Ti/Pt/Au和Ti/Pt/Au MHEMT器件的gm为502(503)mS/mm,JDss为382(530)mA/mm,VT为0.1(-0.5)V,fT和fmax分别为13.4(14.8),17.0(17.5)GHz.利用单片集成增强/耗尽型GaAs基MHEMT器件制备出九阶环型振荡器,直流电压为1.2V时,振荡频率达到777.6MHz,门延迟时间为71.4ps.利用Ti/Pt/Au MHEMT器件设计并制备出了DC-100Hz单刀双掷(SPDT)关MMIC,其插入损耗、隔离度、输入输出回波损耗分别优于2.93,23.34和20dB.     

面向全业务运营的城域传送网的建设

本文首先展望了全业务的发展,然后主要阐述为了满足全业务接入需求,城域传送网的建设方案。