Preparation,Characterization, and Drug-Release Behaviors of a pH-Sensitive Composite Hydrogel Bead Based on Guar Gum,Attapulgite, and Sodium Alginate

A novel guar gum-g-poly (acrylic acid)/attapulgite/sodium alginate (GG-g-PAA/APT/SA) composite hydrogel bead with excellent pH sensitivity was prepared via a facile ionic gelation approach and characterized by FTIR and SEM techniques. The effect of APT content on the encapsulation efficiency (EE), swelling ratio, and drug release behaviors of the beads was investigated and the in-vitro release kinetics were also evaluated using diclofenac sodium (DS) as the model drug. The results indicate that the burst release effect of DS drug was eliminated due to the incorporation of APT, and the DS cumulative release was clearly decreased with increasing the APT content.     

Superabsorbent composite. XIII. Effects of Al3+‐attapulgite on hydrogel strength and swelling behaviors of poly(acrylic acid)/Al3+‐attapulgite superabsorbent composites

Al³⁺‐attapulgite (Al³⁺‐APT) was prepared by treating attapulgite (APT) with AlCl₃ aqueous solution of various concentrations. The poly(acrylic acid)/Al³⁺‐attapulgite (PAA/Al³⁺‐APT) superabsorbent composite was prepared by reaction of partly neutralized acrylic acid, and Al³⁺‐APT in aqueous solution using N, N′‐methylenebisacrylamide as a crosslinker and ammonium persulfate as an initiator. The surface morphology of the composite was investigated by SEM, and the Al³⁺‐APT composite generated a relatively planar surface comparing the nature APT. The effects of Al³⁺‐APT on hydrogel strength and swelling behaviors, such as equilibrium water absorbency, swelling rate, and reswelling capability, of the superabsorbent composites were also studied. The hydrogel strength and reswelling capability were improved, however, the equilibrium water absorbency and swelling rate decreased with increasing AlCl₃ solution concentration. The equilibrium water absorbency firstly increased, and then decreased with increasing Al³⁺‐APT content. The results indicate that Al³⁺‐APT acts as an assistant crosslinker in the polymeric network, which has great influences on hydrogel strength and swelling behaviors of the PAA/Al³⁺‐APT superabsorbent composites. POLYM. ENG. SCI., 47:619–624, 2007. © 2007 Society of Plastics Engineers.     

Dual‐responsive semi‐interpenetrating network beads based on calcium alginate/poly(N‐isopropylacrylamide)/poly(sodium acrylate) for sustained drug release

To improve the mechanical strength of natural hydrogels and to obtain a sustained drug‐delivery device, temperature‐/pH‐sensitive hydrogel beads composed of calcium alginate (Ca‐alginate) and poly(N‐isopropylacrylamide) (PNIPAAm) were prepared in the presence of poly(sodium acrylate) (PAANa) with ultrahigh molecular weight (M_η ≥ 1.0 × 10⁷) as a strengthening agent. The influence of PAANa content on the properties, including the beads stability, swelling, and drug‐release behaviors, of the hydrogels was evaluated. Scanning electron microscopy and oscillation experiments were used to analyze the structure and mechanical stability of the hydrogel beads, respectively. The results show that stability of the obtained Ca‐alginate/PNIPAAm hydrogel beads strengthened by PAANa the alginate/poly(N‐isopropyl acrylamide) hydrogel bead (SANBs) was significantly improved compared to that of the beads without PAANa (NANBs) at pH 7.4. The swelling behavior and drug‐release capability of the SANBs were markedly dependent on the PAANa content and on the environmental temperature and pH. The bead sample with a higher percentage of PAANa exhibited a lower swelling rate and slower drug release. The drug release profiles from SANBs were further studied in simulated intestinal fluid, and the results demonstrated here suggest that SANBs could serve as a potential candidate for controlled drug delivery in vivo. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Synthesis,characterization and swelling behaviors of hydroxyethyl cellulose‐g‐poly(acrylic acid)/attapulgite superabsorbent composite

In this work, a series of novel hydroxyethyl cellulose‐ g‐poly(acrylic acid)/attapulgite (HEC‐g‐PAA/APT) superabsorbent composites were prepared through the graft polymerization of hydroxyethyl cellulose (HEC), partially neutralized acrylic acid (AA), and attapulgite (APT) in aqueous solution, and the composites were characterized by means of Fourier‐transform spectroscopy, scanning electron microscopy, and transmission electronmicroscopy. The effects of polymerization variables including concentrations of the initiator and crosslinker and APT content on water absorbency were studied, and the swelling properties in various pH solutions as well as the swelling kinetics in various saline solutions were also systematically evaluated. Results showed that the introduction of 5 wt% APT into HEC‐g‐PAA polymeric network could improve both water absorbency and water absorption rate of the superabsorbent composites. In addition, the superabsorbent composites retained high water absorbency over a wide pH range of 4–10, and the swelling kinetics of the superabsorbent composites in CaCl₂ and FeCl₃ solutions exhibited a remarkable overshooting phenomenon. POLYM. ENG. SCI., 2010. © 2010 Society of Plastics Engineers     

Calcium‐carboxymethyl chitosan hydrogel beads for protein drug delivery system

In this study, carboxymethyl chitosan (CMC) hydrogel beads were prepared by crosslinking with Ca²⁺. The pH‐sensitive characteristics of the beads were investigated by simulating gastrointestinal pH conditions. As a potential protein drug delivery system, the beads were loaded with a model protein (bovine serum albumin, BSA). To improve the entrapment efficiency of BSA, the beads were further coated with a chitosan/CMC polyelectrolyte complex (PEC) membrane by extruding a CMC/BSA solution into a CaCl₂/chitosan gelation medium. Finally, the release studies of BSA‐loaded beads were conducted. We found that, the maximum swelling ratios of the beads at pH 7.4 (17–21) were much higher than those at pH 1.2 (2–2.5). Higher entrapment efficiency (73.2%) was achieved in the chitosan‐coated calcium‐CMC beads, compared with that (44.4%) in the bare calcium‐CMC beads. The PEC membrane limited the BSA release, while the final disintegration of beads at pH 7.4 still leaded to a full BSA release. Therefore, the chitosan‐coated calcium‐CMC hydrogel beads with higher entrapment efficiency and proper protein release properties were a promising protein drug carrier for the site‐specific release in the intestine. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 3164–3168, 2007     

Synthesis and characterization of poly(N‐vinyl‐2‐pyrrolidone) grafted sodium alginate hydrogel beads for the controlled release of indomethacin

Graft copolymers of sodium alginate (NaAlg) with N‐vinyl‐2‐pyrrolidone were prepared using azobisisobutyronitrile as initiator. The graft copolymers (NaAlg‐g‐PVP) were characterized with Fourier transform infrared spectroscopy, elemental analysis, and differential scanning calorimetry. Polymeric hydrogel beads of NaAlg and NaAlg‐g‐PVP were prepared by crosslinking method using glutaraldehyde (GA) as a crosslinker in the hydrochloric acid catalyst (HCl) and these beads were used to deliver anti‐inflammatory drug, indomethacin (IM). Chemical stability of the IM after encapsulation into beads was confirmed by FTIR. Preparation conditions of the NaAlg‐g‐PVP beads were optimized by considering the percentage entrapment efficiency, particle size, swelling capacity and their release data. In vitro release studies were performed in simulated gastric fluid (pH 1.2) for the initial 2 h, followed by simulated intestinal fluid (pH 7.4) for 4 h. Effects of GA concentration, exposure time to GA, drug/polymer (d/p) ratio, and concentration of HCl on the release of IM were discussed. It was observed that IM release from the beads decreased with increasing GA concentration and exposure time. IM release also decreases with increasing d/p ratio and HCl concentration. The highest IM release was obtained to be 77% for beads crosslinked with 0.027M GA. Swelling experiments were also performed to compute molecular mass between crosslinks of the beads. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Hollow,pH‐sensitive calcium–alginate/poly(acrylic acid) hydrogel beads as drug carriers for vancomycin release

In this study, hollow calcium–alginate/poly(acrylic acid) (PAA) hydrogel beads were prepared by UV polymerization for use as drug carriers. The hollow structure of the beads was fortified by the incorporation of PAA. The beads exhibited different swelling ratios when immersed in media at different pH values; this demonstrated that the prepared hydrogel beads were pH sensitive. A small amount (<9%) of vancomycin that had been incorporated into the beads was released in simulated gastric fluid, whereas a large amount (≤67%) was released in a sustained manner in simulated intestinal fluid. The observed drug‐release profiles demonstrated that the prepared hydrogel beads are ideal candidate carriers for vancomycin delivery into the gastrointestinal tract. Furthermore, the biological response of cells to these hydrogel beads indicated that they exhibited good biological safety and may have additional applications in tissue engineering. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Dual crosslinked carboxymethyl sago pulp/pectin hydrogel beads as potential carrier for colon‐targeted drug delivery

Carboxymethyl sago pulp (CMSP)/pectin hydrogel beads were synthesized by calcium crosslinking and further crosslinked by electron beam irradiation to form drug carrier for colon‐targeted drug. Sphere‐shaped CMSP/pectin 15%/5% hydrogel beads is able to stay intact for 24 h in swelling medium at pH 7.4. It shows pH‐sensitive behavior as the swelling degree increases as pH increases. Fourier transform infrared spectroscopy analysis confirmed the absence of chemical interaction between hydrogel beads and diclofenac sodium. Differential scanning calorimetric and X‐ray diffraction studies indicate the amorphous nature of entrapped diclofenac sodium. The drug encapsulation efficiency is up to about 50%. Less than 9% of drug has been released at pH 1.2 and the hydrogel beads sustain the drug release at pH 7.4 over 30 h. This shows the potential of CMSP/pectin hydrogel beads as carrier for colon‐targeted drug. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 43416.     

Ethanol‐assisted dispersion of attapulgite and its effect on improving properties of alginate‐based superabsorbent nanocomposite

The dispersion of attapulgite (APT) as nanorod‐like single crystals is crucial to fully develop its functionality of one‐dimensional nanometer material as a filler of composite materials. In this study, APT was dispersed by the assistance of ethanol during the high‐pressure homogenization process to form individual nanorod‐like crystals. The dispersed APT was used to prepare new sodium alginate‐g‐poly(sodium acrylate‐co‐styrene)/attapulgite (NaAlg‐g‐P(NaA‐co‐St)/APT) superabsorbent nanocomposites. The effect of ethanol/water ratio on the dispersion of crystal bundles of APT was investigated by field emission scanning electron microscopy, and the results indicate that APT crystal bundles were effectively disaggregated in ν(CH₃CH₂OH) : ν(H₂O) ? 5 : 5 solution after homogenized at 50 MPa. The better dispersion of APT in NaAlg‐g‐P(NaA‐co‐St) matrix has clearly improved the gel strength (from 1300 Pa to 1410 Pa, ω = 100 rad/s), swelling capacity (442–521 g/g), swelling rate (3.3303–4.5736 g/g/s), and reswelling ability of the superabsorbent nanocomposite. Moreover, the nanocomposites showed fast swelling–deswelling responsive behavior in different saline solutions. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Poly(acrylic acid‐co‐acrylamide‐co‐2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid)‐grafted nanocellulose/poly(vinyl alcohol) composite for the in vitro gastrointestinal release of amoxicillin

Superabsorbent polymer composites (SAPCs) are very promising and versatile materials for biomedical applications. This study concentrates on the development of novel cellulose‐based SAPC, Poly(acrylic acid‐co‐acrylamide‐co?2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid)‐grafted nanocellulose/poly(vinyl alcohol) composite, P(AA‐co‐AAm‐co‐AMPS)‐g‐NC/PVA, as a potential drug delivery vehicle. Amoxicillin was selected as a model drug, which is used for the treatment of Helicobacter pylori induced peptic and duodenal ulcers. P(AA‐co‐AAm‐co‐AMPS)‐g‐NC/PVA was synthesized by graft copolymerization reaction, and FTIR, XRD, SEM, and DLS analyses were performed for its characterization. Equilibrium swelling studies were conducted to evaluate the stimuli‐response behavior of the SAPC and found that equilibrium swelling was dependent on pH, contact time, temperature, ionic strength, concentration of crosslinker and PVA. Maximum drug encapsulation efficiency was found out by using different concentrations of amoxicillin. Drug release studies were carried out at simulated gastric and intestinal fluids and the release % was observed as maximum in intestinal fluids within 4 h. The drug release kinetics was investigated using Peppas' potential equation and follows non‐Fickian mechanism at pH 7.4. Thus, the drug release experiments indicate that P(AA‐co‐AAm‐co‐AMPS)‐g‐NC/PVA would be a fascinating vehicle for the in vitro administration of amoxicillin into the gastrointestinal tract. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40699.     

Synthesis and properties of poly(sodium acrylate‐co‐2‐acryloylamino‐2‐methyl‐1‐propanesulfonic acid)/attapulgite as a salt‐resistant superabsorbent composite

A novel salt‐resistant superabsorbent composite was prepared by copolymerization of partially neutralized acrylic acid, 2‐acryloylamino‐2‐methyl‐1‐propanesulfonic acid (AMPS) and attapulgite (APT). To enhance the swelling rate (SR) of the copolymer, sodium bicarbonate was used as a foaming agent in the course of copolymerization. Furthermore, for improving the properties of swollen hydrogel, such as strength, resilience and dispersion, the copolymer was surface‐crosslinked with glycerine and sodium silicate, and then the surface‐crosslinked copolymer was blended with aluminum sulfate and sodium carbonate in post treatment process. The influences of some reaction conditions, such as amount of AMPS, APT, and initiator, and neutralization degree of acrylic acid on water absorbency in 0.9 wt% NaCl aqueous solution both under atmospheric pressure (WA) and load (WA_P, P ≈ 2 × 10³ Pa) were investigated. In addition, the effect of them on SR was also studied. The WA and WA_P of the superabsorbent composite prepared under optimal conditions in 0.9 wt% NaCl aqueous solution were 52 g·g^?1 and 8 g·g^?1, respectively. Besides, the SR was fast, and it could reach 0.393 mL·(g·s)^?1. Moreover, the swollen hydrogel possessed excellent salt resistance, hydrogel resilience and dispersion. POLYM. ENG. SCI., 2009. © 2008 Society of Plastics Engineers     

Preparation and in vitro evaluation of new pH‐sensitive hydrogel beads for oral delivery of protein drugs

New biodegradable pH‐responsive hydrogel beads based on chemically modified chitosan and sodium alginate were prepared and characterized for the controlled release study of protein drugs in the small intestine. The ionotropic gelation reaction was carried out under mild aqueous conditions, which should be appropriate for the retention of the biological activity of an uploaded protein drug. The equilibrium swelling studies were carried out for the hydrogel beads at 37°C in simulated gastric (SGF) and simulated intestinal (SIF) fluids. Bovine serum albumin (BSA), a model for protein drugs was entrapped in the hydrogels and the in vitro drug release profiles were established at 37°C in SGF and SIF. The preliminary investigation of the hydrogel beads prepared in this study showed high entrapment efficiency (up to 97%) and promising release profiles of BSA. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Preparation and swelling properties of semi‐IPN hydrogels based on chitosan‐g‐poly(acrylic acid) and phosphorylated polyvinyl alcohol

The phosphorylated poly(vinyl alcohol) (P‐PVA) samples with various substitution degrees were prepared through the esterification reaction of PVA and phosphoric acid. By using chitosan (CTS), acrylic acid (AA) and P‐PVA as raw materials, ammonium persulphate (APS) as an initiator and N,N‐methylenebisacrylamide as a crosslinker, the CTS‐g‐PAA/P‐PVA semi‐interpenetrated polymer network (IPN) ssuperabsorbent hydrogel was prepared in aqueous solution by the graft copolymerization of CTS and AA and followed by an interpenetrating and crosslinking of P‐PVA chains. The hydrogel was characterized by Fourier transform infrared (FTIR), scanning electron microscopy (SEM), and differential scanning calorimetry (DSC) techniques, and the influence of reaction variables, such as the substitution degree and content of P‐PVA on water absorbency were also investigated. FTIR and DSC results confirmed that PAA had been grafted onto CTS backbone and revealed the existence of phase separation and the formation of semi‐IPN network structure. SEM observations indicate that the incorporation of P‐PVA induced highly porous structure, and P‐PVA was uniformly dispersed in the polymeric network. Swelling results showed that CTS‐g‐PAA/P‐PVA semi‐IPN superabsorbent hydrogel exhibited improved swelling capability (421 g·g^?1 in distilled water and 55 g·g^?1 in 0.9 wt % NaCl solution) and swelling rate compared with CTS‐g‐PAA/PVA hydrogel (301 g·g^?1 in distilled water and 47 g·g^?1 in 0.9 wt % NaCl solution) due to the phosphorylation of PVA. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Preparation and application in drug controlled delivery of pH‐sensitive P(CE‐co‐DMAEMA‐co‐MEG) hydrogel

A pH‐sensitive hydrogel [P(CE‐co‐DMAEMA‐co‐MEG)] was synthesized by the free‐radical crosslinking polymerization of N,N‐dimethylaminoethyl methacrylate (DMAEMA), poly(ethylene glycol) methyl ether methacrylate(MPEG‐Mac) and methoxyl poly(ethylene glycol)‐poly(caprolactone)‐methacryloyl methchloride (PCE‐Mac). The effects of pH and monomer content on swelling property, swelling and deswelling kinetics of the hydrogels were examined and hydrogel microstructures were investigated by SEM. Sodium salicylate was chosen as a model drug and the controlled‐release properties of hydrogels were pilot studied. The results indicated that the swelling ratios of the gels in stimulated gastric fluids (SGF, pH = 1.4) were higher than those in stimulated intestinal fluids (SIF, pH = 7.4), and followed a non‐Fickian and a Fickian diffusion mechanism, respectively. In vitro release studies showed that its release rate depends on different swelling of the network as a function of the environmental pH and DMAEMA content. SEM micrographs showed homogenous pore structure of the hydrogel with open pores at pH 1.4. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40737.     

Fabrication of citric acid crosslinked β‐cyclodextrin/hydroxyethylcellulose hydrogel films for controlled delivery of poorly soluble drugs

β‐cyclodextrin grafted hydroxyethylcellulose (βCD‐g‐HEC) hydrogel films were prepared for the controlled release of poorly soluble model drug (ketoconazole) using citric acid as crosslinking agent. The active βCD and carboxyl content of the hydrogel films were determined by phenolphthalein assay and acid–base titration. The films were characterized by solid state ¹³C NMR, ATR–FTIR, thermogravimetric analysis, and differential scanning calorimetric, and analyzed for tensile strength, swelling ratio, drug loading, release, hemocompatibility, in vitro cytotoxicity, and implantation test. An increase in the concentration of βCD in feed increased the active βCD content of the hydrogel films but reduced their extent of interpolymer crosslinking. The βCD‐g‐HEC hydrogel films with high active βCD content showed maximum drug loading whereas those with high crosslinking density were capable of controlling the drug release for long duration. Hemolysis assay and in vitro cytotoxicity study revealed the biocompatible nature of the hydrogel films whereas implantation test indicated their minimal inflammatory effect. From the overall results, βCD‐g‐HEC hydrogel films were found to be better alternative to the previously reported βCD‐HPMC and βCD‐CMC hydrogel films for enhanced loading and long‐term release, respectively, of the poorly soluble drugs. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46452.     

Study on superabsorbent composite. VIII. Effects of acid‐ and heat‐activated attapulgite on water absorbency of polyacrylamide/attapulgite

A novel superabsorbent composite, polyacrylamide/attapulgite, from acrylamide (AM) and attapulgite (APT), was prepared by free‐radical polymerization, using N,N′‐methylenebisacrylamide (MBA) as a crosslinker and ammonium persulfate (APS) as an initiator. The effects of hydrochloric acid (HCl) concentration, acidification time, and acidification temperature while acidifying APT and temperature and APT heat‐activation on water absorbency of the superabsorbent composite in distilled water and in 0.9 wt % NaCl solution were studied. The water absorbency first decreases with increasing the HCl concentration while acidifying APT, and then increases with further increasing the HCl concentration. Prolongation of acidification time is of benefit to the increase of water absorbency. At a given HCl concentration, water absorbency for the composite increases with increasing acidification temperature. An important increase in water absorbency was observed after incorporating heat‐activated APT into the polymeric network, reaching a maximum of 1964 g g^?1 with the APT heat‐activated at 400°C. Acid‐ and heat‐activation can influence chemical composition, crystalline structure, cation exchange capacity (CEC), and specific surface area of APT according XRF, XRD, FTIR analysis, and physicochemical properties test, and then on water absorbency of corresponding PAM/APT superabsorbent composite. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 2419–2424, 2007     

Thermo‐ and pH‐responsive microgels for controlled release of insulin

Microgel particles were prepared, made of hydroxypropylcellulose‐graft‐(acrylic acid) (HPC‐g‐AA) and acrylic acid(AA). The particles undergo reversible volume phase transitions in response to both pH and temperature changes while keeping the inherent properties of PAA and HPC‐g‐AA. Dynamic light scattering measurements reveal that the average hydrodynamic radius and hydrodynamic radius distributions of the microgel particles depend on temperature and pH. The microgels exhibit excellent pH sensitivity and a higher swelling ratio at higher pH in aqueous solution. In vitro release study shows that the amount of insulin released from the microgels is less at pH = 1.2 than at pH = 6.8. The results indicate that the resultant microgels seem to be of great potential for intelligent oral drug delivery. Copyright © 2012 Society of Chemical Industry     

Gum Acacia‐cl‐poly(acrylamide)@carbon nitride Nanocomposite Hydrogel for Adsorption of Ciprofloxacin and its Sustained Release in Artificial Ocular Solution

In the present work, a nanocomposite hydrogel is designed consisting of gum acacia, poly(acrylamide) and carbon nitride by facile microwave approach. This nanocomposite hydrogel is sensitive to environmental stimuli which is essential for its application in environmental remediation and as a drug delivery system. The effects of carbon nitride percentage and microwave Watt variation on swelling capacity of gum acacia‐cl‐poly(acrylamide)@carbon nitride (Ga‐cl‐PAM@C₃N₄) nanocomposite hydrogel are analyzed. The structural characterizations are considered by numerous techniques such as FTIR (Fourier transform infra‐red spectroscopy), X‐ray diffraction, transmission electron microscopy, scanning electron microscopy, and elemental mapping. Batch experiment is performed for remediation of ciprofloxacin (CIP) drug from water. Various parameters such as effect of ciprofloxacin doses, Ga‐cl‐PAM@C₃N₄ nanocomposite hydrogel dosage, pH, time and temperature for adsorption of CIP on gum acacia‐cl‐poly(acrylamide)@carbon nitride nanocomposite hydrogel is examined. Maximum adsorption capacity of Ga‐cl‐PAM@C₃N₄ nanocomposite hydrogel observed is 169.49 mg g^?1 at pH 6.4. The drug loading and drug release capacity of Ga‐cl‐PAM@C₃N₄ nanocomposite hydrogel is investigated for ciprofloxacin. Drug release is monitored in artificial ocular solution (pH 8), saline (pH 5.5), acetate buffer (pH 2.2), and distilled water. Maximum drug release is observed in artificial ocular solution.     

Colon‐specific oral delivery of vitamin B2 from poly(acrylamide‐co‐maleic acid) hydrogels: An in vitro study

Hydrogels, composed of poly(acrylamide‐co‐maleic acid) were synthesized and the release of vitamin B₂ from these gels was studied as a function of the pH of the external media, the initial amount of the drug loaded, and the crosslinking ratio in the polymer matrix. The gels containing 3.8 mg of the drug per gram gel exhibit almost zero‐order release behavior in the external media of pH 7.4 over the time interval of more than their half‐life period (t_1/2). The amount of the drug loaded into the hydrogel also affected the dynamic release of the encapsulated drug. As expected, the gels showed a complete swelling‐dependent mechanism, which was further supported by the similar morphology of the swelling and release profiles of the drug‐loaded sample. The hydrophilic nature of the drug riboflavin does not contribute toward the zero‐order release dynamics of the hydrogel system. On the other hand, the swelling osmotic pressure developed between the gels and the external phase, due to loading of the drug by equilibration of the gels in the alkaline drug solution, plays an effective role in governing the swelling and release profiles. Finally, the minimum release of the drug in the swelling media of pH 2.0 and the maximum release with zero‐order kinetics in the medium of pH 7.4 suggest that the proposed drug‐delivery devices have a significant potential to be used as an oral drug‐delivery system for colon‐specific delivery along the gastrointestinal (GI) tract. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 1133–1145, 2002; DOI 10.1002/app.10402     

Magnetic and electric responsive hydrogel–magnetic nanocomposites for drug‐delivery application

Magnetic and electrically responsive hydrogel networks were developed for drug‐delivery applications. The hydrogel matrices were synthesized by the polymerization of acrylamide monomer in the presence of carboxymethylcellulose (CMC) or methylcellulose (MC) with N,N‐methylenebisacrylamide, a crosslinker with the redox initiating system ammonium persulfate/tetramethylethylenediamine. The magnetic nanoparticles were generated throughout these hydrogel matrices by an in situ method by the incorporation of iron ions and their subsequent reduction with ammonia. A series of hydrogel–magnetic nanocomposites (HGMNCs) were developed with various CMC and MC compositions. The synthesized HGMNCs were characterized with spectral (Fourier transform infrared and ultraviolet–visible spectroscopy), X‐ray diffraction, thermal, and microscopy methods. These HGMNCs contained iron oxide (Fe₃O₄) nanoparticles with an average particle size of about 22 nm, as observed by transmission electron microscopy. The dielectrical properties of the pure hydrogel (HG); the hydrogel loaded with iron ions, or the hydrogel iron‐ion composite (HGIC); and the HGMNCs were measured. These results suggest that HGMNCs exhibited higher dielectric constants compared to HG and HGICs. The curcumin loading and release characteristics were also measured for HG, HGIC, and HGMNC systems. These data revealed that there was a sustained release of curcumin from HGMNCs because of the presence of magnetic nanoparticles in the hydrogel networks. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011