Synthesis and characterization of novel heat resistance poly(amide‐imide)s from N,N′‐[2,5‐bis(4‐aminobenzylidene) cyclopentanone] bistrimellitimide acid and various aromatic diamines

A new‐type of dicarboxylic acid was synthesized from the reaction of 2,5‐bis(4‐aminobenzylidene)cyclopentanone with trimellitic anhydride in a solution of glacial acetic acid/pyridine (Py) at refluxing temperature. Six novel heat resistance poly(amide‐imide)s (PAIs) with good inherent viscosities were synthesized, from the direct polycondensation reaction of N,N′‐[2,5‐bis(4‐aminobenzylidene)cyclopentanone]bistrimellitimide acid with several aromatic diamines, by two different methods such as direct polycondensation in a medium consisting of N‐methyl‐2‐pyrrolidone (NMP)/triphenyl phosphite (TPP)/calcium chloride (CaCl₂)/pyridine (Py) and direct polycondensation in a p‐toluene sulfonyl chloride (tosyl chloride, TsCl)/pyridine (Py)/N,N‐dimethylformamide (DMF) system. All of the above polymers were fully characterized by ¹H NMR, FTIR, elemental analysis, inherent viscosity, solubility tests, UV‐vis spectroscopy, differential scanning calorimeter (DSC), thermogravimetric analysis (TGA), and derivative of thermaogravimetric (DTG). The resulted poly(amide‐imide)s (PAIs) have showed admirable good inherent viscosities, thermal stability, and solubility. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

New polyamides based on 2,5‐bis[(4‐carboxyanilino) carbonyl] pyridine and aromatic diamines: Synthesis and characterization

Seven new polyamides 6a–g were synthesized through the direct polycondensation reaction of 2,5‐bis[(4‐carboxyanilino) carbonyl] pyridine 4 with seven derivatives of aromatic diamines 5a–g in a medium consisting of N‐methyl‐2‐pyrrolidone, triphenyl phosphite, calcium chloride, and pyridine. The polycondensation reaction produced a series of novel polyamides containing pyridyl moiety in the main chain in high yield with inherent viscosities between 0.32 – 0.72 dL/g. The resulted polymers were fully characterized by means of FTIR spectroscopy, elemental analyses, inherent viscosity, and solubility tests. Thermal properties of these polymers were investigated by using thermal gravimetric analysis and differential thermal gravimetric. All the polymers were soluble at room temperature in polar solvents, such as N,N‐dimethyl acetamide, N,N‐dimethyl formamide, dimethyl sulfoxide, and N‐methyl‐2‐pyrrolidone. 2,5‐Bis[(4‐carboxyanilino) carbonyl] pyridine 4 as a new monomer containing pyridyl moiety was synthesized by using a two‐step reaction. At first 2,5‐pyridine dicarboxylic acid 1 was converted to 2,5‐pyridine dicarbonyl dichloride 2 . Then diacid 4 was prepared by condensation reaction of diacid chloride 2 with p‐aminobenzoic acid 3. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Synthesis of novel optically active poly(ester imide)s by direct polycondensation reaction promoted by tosyl chloride in pyridine in the presence of N,N‐dimethyformamide

4,4′‐Hexafluoroisopropylidene‐2,2‐bis(phthalic acid anhydride) (1) was treated with L ‐methionine (2) in acetic acid and the resulting 4,4′‐(hexafluoroisopropylidene)‐N,N′‐bis(phthaloyl‐L ‐methionine) diacid (4) was obtained in high yields. The direct polycondensation reaction of this diacid with several aromatic diols, such as bisphenol A (5a), phenolphthalein (5b), 1,4‐dihydroxybenzene (5c), 4,4′‐dihydroxydiphenyl sulfide (5 d), 4,6‐dihydroxypyrimidine (5e), 4,4′‐dihydroxydiphenyl sulfone (5f), and 2,4′‐dihydroxyacetophenone (5g), was carried out in a system of tosyl chloride (TsCl), pyridine (Py), and N,N‐dimethylformamide (DMF). The reactions with TsCl were significantly promoted by controlling alcoholysis with diols, in the presence of catalytic amounts of DMF, to give a series of optically active poly(ester imide)s, (PEI)s, with good yield and moderate inherent viscosity ranging from 0.43 to 0.67 dL/g. The polycondensation reactions were significantly affected by the amounts of DMF, molar concentration of monomers, TsCl and Py, aging time, temperature, and reaction time. All of the aforementioned polymers were fully characterized by ¹H NMR, FTIR, elemental analysis, and specific rotation. Some structural characterization and physical properties of these optically active PEIs are reported. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 455–460, 2006     

Microwave‐promoted rapid synthesis of new optically active poly(amide imide)s derived from N,N′‐(pyromellitoyl)‐bis‐L‐isoleucine diacid chloride and aromatic diamines

A pyromellitic dianhydride (benzene‐1,2,4,5‐tetracarboxylic dianhydride) was reacted with L ‐isoleucine in acetic acid, and the resulting imide acid [N,N′‐(pyromellitoyl)‐bis‐L ‐isoleucine] (4) was obtained in a high yield. 4 was converted into N,N′‐(pyromellitoyl)‐bis‐L ‐isoleucine diacid chloride by a reaction with thionyl chloride. The polycondensation reaction of this diacid chloride with several aromatic diamines, including 1,4‐phenylenediamine, 4,4′‐diaminodiphenyl methane, 4,4′‐diaminodiphenylsulfone (4,4′‐sulfonyldianiline), 4,4′‐diaminodiphenylether, 2,4‐diaminotoluene, and 1,3‐phenylenediamine, was developed with two methods. The first method was polymerization under microwave irradiation, and the second method was low‐temperature solution polymerization, with trimethylsilyl chloride used as an activating agent for the diamines. The polymerization reactions proceeded quickly and produced a series of optically active poly(amide imide)s with good yields and moderate inherent viscosities of 0.17–0.25 dL/g. All of the aforementioned polymers were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of these optically active poly(amide imide)s are reported. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 951–959, 2004     

Step‐growth polymerization of 5‐[(9,10‐dihydro‐9,10‐ethanoanthracene‐11,12‐dicarboximido)‐3‐methylbutanoyl‐amino]isophthalic acid with aromatic diols

cis‐9,10‐dihydro‐9,10‐ethanoanthracene‐11,12‐dicarboxylic acid anhydride ( 1 ) was converted to imide acid ( 2 ) by reaction with S‐valine. Compound 2 was converted to the acid chloride ( 3 ) by reaction with thionyl chloride and then treated with 5‐aminoisophthalic acid in dry N,N‐dimethylacetamide to obtain 5‐[(9,10‐dihydro‐9,10‐ethanoanthracene‐11,12‐dicarboximido)‐3‐methylbutanoylamino]isophthalic acid ( 4 ). Direct step‐growth polymerization of this novel chiral diacid monomer 4 with a series of different diols in a system of tosyl chloride, pyridine, and N,N‐dimethylformamide was carried out. The optically active polyesters (PEs) were obtained with good yield and moderate inherent viscosity ranging from 0.23 to 0.48 dL/g. The resulting polymers were characterized with FTIR, ¹H‐NMR, and elemental analysis techniques. The prepared PEs showed good thermal stability up to 320°C as measured by thermogravimetric analysis. Specific rotation experiments demonstrated the induction of optical activity due to successful insertion of S‐valine in the structure of pendant groups. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Synthesis and characterization of new soluble poly(ester‐imide)s containing noncoplanar 2,2′‐dimethyl‐4,4′‐biphenylene unit

A new diimide–diacid chloride (3) containing a noncoplanar 2,2′‐dimethyl‐4,4′‐biphenylene unit was synthesized by treating 2,2′‐dimethyl‐4,4′‐diamino‐biphenylene with trimellitic anhydride followed by refluxing with thionyl chloride. Various new poly(ester‐imide)s were prepared from 3 with different bisphenols by solution polycondensation in nitrobenzene using pyridine as hydrogen chloride quencher at 170°C. Inherent viscosities of the poly(ester‐imide)s were found to range between 0.31 and 0.35 dL g^?1. All of the poly(ester‐imide)s, except the one containing pendent adamantyl group 5e, exhibited excellent solubility in the following solvents: N,N‐dimethylformamide, tetrahydrofuran, tetrachloroethane, dimethyl sulfoxide, N,N‐dimethylacetamide, N‐methyl‐2‐pyrrolidinone, m‐cresol, o‐chlorophenol, and chloroform. The polymers showed glass‐transition temperatures between 166 and 226°C. The 10% weight loss temperatures of the poly(ester‐imide)s, measured by TGA, were found to be in the range between 415 and 456°C in nitrogen. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 2486–2493, 2004     

Synthesis and characterization of new rigid‐rod and organosoluble poly(amide–imide)s based on 1,4‐bis(trimellitimido)‐2,3,5,6‐tetramethylbenzene

A series of new aromatic poly(amide–imide)s (PAIs) was synthesized by triphenyl phosphite‐activated polycondensation of the diimide–diacid, 1,4‐bis(trimellitimido)‐2,3,5,6‐tetramethylbenzene (I), with various aromatic diamines in a medium consisting of N‐methyl‐2‐pyrrolidone (NMP), pyridine, and calcium chloride. The PAIs had inherent viscosities of 0.82–2.43 dL/g. The diimide–diacid monomer (I) was prepared from 2,3,5,6‐tetramethyl‐p‐phenylenediamine with trimellitic anhydride (TMA). Most of the resulting polymers showed an amorphous nature and were readily soluble in a variety of organic solvents including NMP, N,N‐dimethylacetamide (DMAc), and N,N‐dimethylformamide (DMF). Transparent, flexible, and tough films of these polymers could be cast from DMAc solutions. Their cast films had tensile strengths ranging from 80 to 95 MPa, elongation at break from 10 to 45%, and initial modulus from 2.01 to 2.50 GPa. The 10% weight loss temperatures of these polymers were above 510°C in nitrogen. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 78: 1162–1170, 2000     

Preparation of new poly(amide–imide)s with chiral architectures via direct polyamidation reaction

N‐trimellitylimido‐L ‐methionine ( 3 ) was prepared by reaction of trimellitic anhydride ( 1 ) with ‐L ‐methionine ( 2 ) in acetic acid solution at refluxing temperature. This diacid was reacted with thionyl chloride, and N‐trimellitylimido‐L ‐methionine diacid chloride ( 4 ) was obtained in quantitative yield. The resulting diacid chloride was reacted with p‐aminobenzoic acid in dry acetone and bis(p‐aminobenzoic acid)‐N‐trimellitylimido‐L ‐methionine ( 5 ) was obtained as a novel optically active amide–imide diacid monomer in high yield. The direct polycondensation of amide–imide diacid monomer 5 with several aromatic diamines was carried out with tosyl chloride (TsCl)/pyridine (Py)/dimetheylformamide (DMF) system. The resulting thermally stable poly(amide–imide)s (PAIs) were obtained in good yields and inherent viscosities ranging between 0.24 and 0.46 dL g^?1 and were characterized with FTIR, ¹H NMR, CHN, and TGA techniques. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 1248–1254, 2007     

Synthesis and characterization of novel thermally stable and optically active poly(amide‐imide)s derived from N,N′‐(4,4′‐diphthaloyl)‐bis‐L‐leucine diacid and aromatic diamines

A new diacid containing optically active functional groups, N,N′‐(4,4′‐diphthaloyl)‐bis‐L ‐leucine diacid ( 3 ), was synthesized and used in a preparation of a series of poly(amide‐imide)s (PAIs) by direct polycondensation with various aromatic diamines in N‐methyl‐2‐pyrrolidinone (NMP). All polymers derived from diacid ( 3 ) were highly organosoluble in the solvents like N‐methyl‐2‐pyrrolidinone, N,N‐dimethylacetamide, N,N‐dimethylformamide, dimethyl sulfoxide, tetrahydrofuran, γ‐butyrolactone, cyclohexanone, and chloroform at room temperature or upon heating. Inherent viscosities of the PAIs were found to range between 0.34 and 0.61·dL g^?1. All the PAIs afforded flexible and tough films. The glass‐transition temperatures of these PAIs were recorded between 212 and 237°C by differential scanning calorimetry, and the 10% weight loss temperatures were ranging from 372 to 393°C and 336–372°C under nitrogen and air, respectively. The polyimide films had a tensile strength in the range of 63–88 MPa and a tensile modulus in the range of 1.2–1.7 GPa. Optically active PAIs exhibited specific rotations in the range of ?10.58° to ?38.70°. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

The nanocomposites of zinc oxide/L‐amino acid‐based chiral poly(ester‐imide) via an ultrasonic route: Synthesis,characterization, and thermal properties

In this investigation, a chiral poly) ester‐imide) (PEI) via direct polyesterification of N,N′‐(pyromellitoyl)‐bis‐(L ‐tyrosine dimethyl ester) and N‐trimellitylimido‐L ‐methionine was prepared using the tosyl chloride/pyridine/N,N′‐dimethylformamide system as a condensing agent. This approach allows the insertion of two natural amino acids into the polymer backbone and the creation of a bioactive polymer. From the chemical point of view, the ester groups impart to the polymer's main and side chain increased sensibility to hydrolysis that can cause chain breaking. Therefore, this polymer is expected to be biodegradable and could be classified as an eco‐friendly polymer. The polymer also had a useful level of thermal stability associated with excellent solubility. PEI/zinc oxide bionanocomposites were subsequently prepared by an ultrasonic method as a simple and inexpensive route, using ZnO nanoparticles (ZnO‐NPs) modified by 3‐aminopropyltriethoxylsilane (KH550) as a coupling agent. The structure and properties of the obtained BNC polymers were confirmed by Fourier transform infrared spectroscopy, X‐ray diffraction, field emission scanning electron microscopy (FE‐SEM), transmission electron microscopy (TEM), and thermogravimetric analysis (TGA). The direct proofs for the formation of the true BNC polymers were provided by TEM. Also, the morphology study of the synthesized polymer‐based BNCs showed well‐dispersed ZnO‐NPs in the polymer matrix by FE‐SEM analysis. TGA studies indicated that an increase of the NP content led to an enhancement of the thermal stability of the new BNC polymers. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Chromophoric poly(urea‐urethane)s with pendent 3‐hydroxynaphthalene group: Synthesis and characterization

The reaction of 4‐(3‐hydroxynaphthalene)‐1,2,4‐triazolidine‐3,5‐dione ( 3HNTD ) with n‐propylisocyanate was performed at different molar ratios. The resulting monosubstituted urea and disubstituted urea‐urethane derivatives were obtained in high yields and were used as model compounds for polymerization reactions. 3HNTD as a monomer was used in the preparation of heterocyclic poly(urea‐urethane)s to produce photoactive polymers, by polycondensation with different diisocyanates in N,N‐dimethylacetamide (DMAc) solution. Chromophoric heterocyclic polymers containing naphthalene group, obtained in quantitative yields, possessed inherent viscosities in the range of 0.14–0.38 dL/g. The resulting poly(urea‐urethane)s is insoluble in most organic solvents, but easily soluble in polar solvents such as dimethyl sulfoxide (DMSO), DMAc, and N‐methylpyrrolidone (NMP). The polymers were characterized by IR, ¹H‐NMR, elemental analysis, and TGA. Fluorimetric and UV–vis studies of the monomer as well as polymers were performed. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Phosphorus‐containing poly(ester‐imide)–polydimethylsiloxane copolymers

New phosphorus‐containing poly(ester‐imide)‐polydimethylsiloxane copolymers were prepared by solution polycondensation of 1,4‐[2‐(6‐oxido‐6H‐dibenz < c,e > < 1, 2 > oxaphosphorin‐6‐yl)]naphthalene‐bis(trimellitate) dianhydride with a mixture of an aromatic diamine (1,3‐bis(4‐aminophenoxy)benzene) and α,ω‐bis(3‐aminopropyl)oligodimethylsiloxane of controlled molecular weight, in various ratios. Poly(amic acid) intermediates were converted quantitatively to the corresponding polyimide structures using a solution imidization procedure. The polymers are easily soluble in polar organic solvents, such as N‐methyl‐2‐pyrrolidone and N,N‐dimethylformamide, as well as in less polar solvents such as tetrahydrofuran. They show good thermal stability, the decomposition temperature being above 370 °C. The glass transition temperatures are in the range 165–216 °C. Solutions of the polymers in N‐methyl‐2‐pyrrolidone exhibit photoluminescence in the blue region. Copyright © 2010 Society of Chemical Industry     

Synthesis of soluble and thermally stable polyimides from 3,5‐diamino‐N‐(4‐(8‐quinolinoxy) phenyl) aniline and various dianhydrides

Three novel polyimides (PIs) having pendent 4‐(quinolin‐8‐yloxy) aniline group were prepared by polycondensation of a new diamine with commercially available tetracarboxylic dianhydrides, such as pyromellitic dianhydride, 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride, and bicyclo[2.2.2]‐oct‐7‐ene‐2,3,5,6‐tetracarboxylic dianhydride. These PIs were characterized by FTIR, ¹H NMR, and elemental analysis; they had high yields with inherent viscosities in the range of 0.4–0.5 dl g⁻¹, and exhibited excellent solubility in many organic solvents such as N,N‐dimethyl acetamide, N,N′‐dimethyl formamide, N‐methyl pyrrolidone (NMP), dimethyl sulfoxide, and pyridine. These PIs exhibited glass transition temperatures (T_g) between 250 and 325° C. Their initial decomposition temperatures (T_i) ranged between 270 and 450°C, and 10% weight loss temperature (T₁₀) up to 500°C with 68% char yield at 600°C under nitrogen atmosphere. Transparent and hard polymer films were obtained via casting from their NMP solutions. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Synthesis and characterization of poly(ester‐ether‐imide)s derived from 5‐(4‐trimellitimidophenoxy)‐1‐trimellitimido naphthalene

A series of novel aromatic poly(ester‐ether‐imide)s with inherent viscosity values of 0.44–0.74 dL g^?1 were prepared by the diphenylchlorophosphate‐activated direct polycondensation of an imide ring‐containing diacid namely 5‐(4‐trimellitimidophenoxy)‐1‐trimellitimido naphthalene ( 1 ) with various aromatic dihydroxy compounds in the presence of pyridine and lithium chloride. Owing to comparison of the characterization data, an ester‐containing model compound ( 2 ) was also synthesized by the reaction of 1 with phenol. The model compound 2 and the resulted polymers were fully characterized by FT‐IR and NMR spectroscopy. The ultraviolet λ_max values of the poly(ester‐ether‐imide)s were also determined. The resulting polymers exhibited an excellent organosolubility in a variety of high polar solvents such as N,N‐dimethylacetamide, N,N‐dimethylformamide, dimethyl sulfoxide, and N‐methyl‐2‐pyrrolidone. They were soluble even in common less polar organic solvents such as pyridine, m‐cresol, and tetrahydrofuran on heating. Crystallinity of the polymers was estimated by means of wide‐angle X‐ray diffraction. The resulted polymers exhibited nearly an amorphous nature. From differential scanning calorimetry thermograms, the polymers showed glass‐transition temperatures between 221 and 245°C. Thermal behaviors of the obtained polymers were characterized by thermogravimetric analysis, and the 10% weight loss temperatures of the poly(ester‐ether‐imide)s were found to be over 410°C in nitrogen. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Synthesis and characterization of aromatic/cycloaliphatic poly(amide‐ imide‐imide)s from bis(4‐amino‐ 3,5‐dimethylphenyl) cycloalkane derivatives

A series of novel aromatic diamines containing cycloaliphatic moieties was synthesized by the reaction of cycloalkanones like cyclohexanone and cycloheptanone with 2,6‐dimethylaniline. The tetrimide diacid was synthesized using the prepared diamine with 3,3′,4,4′‐benzophenonetetracarboxylic acid dianhydride/pyromellitic dianhydride and p‐aminobenzoic acid. The polymers were prepared by treating the tetrimide diacid with different aromatic diamines. The structures of the monomers and polymers were identified using elemental analysis and Fourier transform infrared, ¹H NMR and ¹³C NMR spectroscopy. The polymers show excellent solubility. The polymers are amorphous and have high optical transparency. They also show good thermal stability and their T_g value is found to be in the range 268–305 °C. Copyright © 2007 Society of Chemical Industry     

Microwave‐assisted and classical heating polycondensation reaction of bis(p‐amido benzoic acid)‐N‐trimellitylimido‐L‐leucine with diisocyanates as a new method for preparation of optically active poly(amide imide)s

A new class of optically active poly(amide imide)s were synthesized via direct polycondensation reaction of diisocyanates with a chiral diacid monomer. The step‐growth polymerization reactions of monomer bis(p‐amido benzoic acid)‐N‐trimellitylimido‐L‐leucine (BPABTL) (5) as a diacid monomer with 4,4′‐methylene bis(4‐phenylisocyanate) (MDI) (6) was performed under microwave irradiation, solution polymerization under gradual heating and reflux condition in the presence of pyridine (Py), dibuthyltin dilurate (DBTDL), and triethylamine (TEA) as a catalyst and without a catalyst, respectively. The optimized polymerization conditions according to solvent and catalyst for each method were performed with tolylene‐2,4‐diisocyanate (TDI) (7), hexamethylene diisocyanate (HDI) (8), and isophorone diisocyanate (IPDI) (9) to produce optically active poly(amide imide)s by the diisocyanate route. The resulting polymers have inherent viscosities in the range of 0.09–1.10 dL/g. These polymers are optically active, thermally stable, and soluble in amide type solvents. All of the above polymers were fully characterized by IR spectroscopy, ¹H NMR spectroscopy, elemental analyses, specific rotation, and thermal analyses methods. Some structural characterization and physical properties of this new optically active poly(amide imide)s are reported. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 1647–1659, 2004     

Facile synthesis of novel optically active poly(amide‐imide)s containing N,N′‐(pyromellitoyl)‐bis‐l‐phenylalanine diacid chloride and 5,5‐disubstituted hydantoin derivatives under microwave irradiation

Pyromellitic dianhydride (1,2,4,5‐benzenetetracarboxylic acid 1,2,4,5‐dianhydide) (1) was reacted with L‐phenylalanine (2) in a mixture of acetic acid and pyridine (3 : 2) at room temperature, then was refluxed at 90–100°C and N,N′‐(Pyromellitoyl)‐bis‐L ‐phenylalanine diacid (3) was obtained in quantitative yield. The imide‐acid (3) was converted to N,N′‐(Pyromellitoyl)‐bis‐L ‐phenylalanine diacid chloride (4) by reaction with thionyl chloride. Rapid and highly efficient synthesis of poly(amide‐imide)s (6a–f) was achieved under microwave irradiation by using a domestic microwave oven from the polycondensation reactions of N,N′‐(Pyromellitoyl)‐bis‐L ‐phenylalanine diacid chloride (4) with six different derivatives of 5,5‐disubstituted hydantoin compounds (5a–f) in the presence of a small amount of a polar organic medium that acts as a primary microwave absorber. Suitable organic media was o‐cresol. The polycondensation proceeded rapidly, compared with the conventional melt polycondensation and solution polycondensation, and was almost completed within 10 min, giving a series of poly(amide‐imide)s with inherent viscosities about 0.28–0.44 dL/g. The resulting poly(amide‐imide)s were obtained in high yield and are optically active and thermally stable. All of the above compounds were fully characterized by means of FTIR spectroscopy, elemental analyses, inherent viscosity (η_inh), solubility test and specific rotation. Thermal properties of the poly(amide‐imide)s were investigated using thermal gravimetric analysis (TGA). © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 516–524, 2004     

Microwave‐assisted synthesis of new optically active poly(ester‐imide)s containing N,N′‐(pyromellitoyl)‐bis‐L‐phenylalanine moieties

Pyromellitic dianhydride (benzene‐1,2,4,5‐tetracarboxylic dianhydride) (1) was reacted with L‐phenylalanine (2) in a mixture of acetic acid and pyridine (3 : 2) and the resulting imide‐acid [N,N′‐(pyromellitoyl)‐bis‐L‐phenylalanine diacid] (4) was obtained in quantitative yield. The compound (4) was converted to the N,N′‐(pyromellitoyl)‐bis‐L‐phenylalanine diacid chloride (5) by reaction with thionyl chloride. A new facile and rapid polycondensation reaction of this diacid chloride (5) with several aromatic diols such as phenol phthalein (6a), bisphenol‐A (6b), 4,4′‐hydroquinone (6c), 1,8‐dihydroxyanthraquinone (6d), 4,4‐dihydroxy biphenyl (6e), and 2,4‐dihydroxyacetophenone (6f) was developed by using a domestic microwave oven in the presence of a small amount of a polar organic medium such as o‐cresol. The polymerization reactions proceeded rapidly and are completed within 20 min, producing a series of optically active poly(ester‐imide)s with good yield and moderate inherent viscosity of 0.10–0.26 dL/g. All of the above polymers were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of these optically active poly(ester‐imide)s are reported. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 2211–2216, 2002     

Synthesis and properties of new aromatic poly(ester‐imide)s derived from 4‐p‐biphenyl‐2,6‐bis(4‐trimellitimidophenyl) pyridine and various dihydroxy compounds

A novel class of wholly aromatic poly(ester‐imide)s, having a biphenylene pendant group, with inherent viscosities of 0.32–0.49 dL g^?1 was prepared by the diphenylchlorophosphate‐activated direct polyesterification of the preformed imide‐ring‐containing diacid, 4‐p‐biphenyl‐2,6‐bis(4‐trimellitimidophenyl)pyridine (1) with various aromatic dihydroxy compounds in the presence of pyridine and lithium chloride. A reference diacid, 2,6‐bis(trimellitimido)pyridine (2) without a biphenylene pendant group and two phenylene rings in the backbone, was also synthesized for comparison purposes. At first, with due attention to structural similarity and to compare the characterization data, a model compound (3) was synthesized by the reaction of compound 1 with two mole equivalents of phenol. Moreover, the optimum condition of polymerization reactions was obtained via a study of the model compound synthesis. All of the resulting polymers were characterized by Fourier transform infrared and ¹H NMR spectroscopy and elemental analysis. The ultraviolet λ_max values of the poly(ester‐imide)s were also determined. All of the resulting polymers exhibited excellent solubility in common organic solvents, such as pyridine, chloroform, tetrahydrofuran, and m‐cresol, as well as in polar organic solvents, such as N‐methyl‐2‐pyrrolidone, N,N‐dimethylacetamide, N,N‐dimethylformamide, and dimethyl sulfoxide. The crystalline nature of the polymers obtained was evaluated by means of wide‐angle X‐ray diffraction. The resulting poly(ester‐imide)s showed nearly an amorphous nature, except poly(ester‐imide) derived from 4,4′‐dihydroxy biphenyl. The glass transition temperatures (T_g) of the polymers determined by differential scanning calorimetry thermograms were in the range 298–342 °C. The 10% weight loss temperatures (T_10%) from thermogravimetric analysis curves were found to be in the range 433–471 °C in nitrogen. Films of the polymers were also prepared by casting the solutions. Copyright © 2006 Society of Chemical Industry     

Preparation and properties of organo‐soluble polyimides based on 4,4′‐diamino‐3,3‐dimethyldiphenylmethane and conventional dianhydrides

4,4′‐Diamino‐3,3′‐dimethyldiphenylmethane was used to prepare polyimides in an attempt to achieve good organo‐solubility and light color. Polyimides based on this diamine and three conventional aromatic dianhydrides were prepared by solution polycondensation followed by chemical imidization. They possess good solubility in aprotonic polar organic solvents such as N‐methyl 2‐pyrrolidone, N,N‐dimethyl acetamide, and m‐cresol. Polyimide from 4,4′‐diamino‐3,3′‐dimethyldiphenylmethane and diphenylether‐3,3′,4,4′‐tetracarboxylic acid dianhydride is even soluble in common solvents such as tetrahydrofuran and chloroform. Polyimides exhibit high transmittance at wavelengths above 400 nm. The glass transition temperature of polyimide from 4,4′‐diamino‐3,3′‐dimethyldiphenylmethane and pyromellitic dianhydride is 370°C, while that from 4,4′‐diamino‐3,3′‐dimethyldiphenylmethane and diphenylether‐3,3′,4,4′‐tetracarboxylic acid dianhydride is about 260°C. The initial thermal decomposition temperatures of these polyimides are 520–540°C. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 72: 1299–1304, 1999