Ultra-fine grained bulk CP-Ti processed by multi-pass ECAP at warm deformation region

In order to refine the grain size of commercially pure titanium (CP-Ti) to a submicrometer scale, equal channel angular pressing (ECAP) was attempted at a temperature range of 200–300 °C. The experiments revealed that, 250 °C was the minimum temperature at which ten passes of ECAP could be performed in a 105° die without the cracking of billets. An ultrafine-grained (UFG) microstructure with a mean grain size of 183 nm was achieved after 10 passes. The processed CP-Ti displayed high tensile strength of 892 MPa and high elongation to failure of 20.5%. The enhancement in mechanical properties is explained in terms of grain refinement and dislocation density increasing. The high ductility of UFG pure Ti with the absence of strain hardening behavior is attributed to its enhanced strain rate sensitivity.     

Microstructure and tensile strength of grade 2 titanium processed by equal-channel angular pressing and by rolling

Commercially pure titanium strengthened by severe plastic deformation constitutes an alternative to the use of complex Ti alloys in many medical or industrial applications. In this research, rods of grade 2 Ti were processed by up to six passes using Equal-channel angular pressing (ECAP) at 573 K followed by cold rolling at room or subzero temperatures. After four passes of ECAP, the grain size was refined down to the submicrometer scale and subsequent rolling led to further refinement. The microstructure was characterized by taking Vickers microhardness measurements and tensile testing was performed both at room temperature and in the temperature range of 573–773 K. The results show that at all temperatures the tensile strength is significantly improved by means of these processing techniques. At room temperature, the ultimate tensile strength of pure Ti after ECAP plus subzero rolling is close to that of the traditional Ti-6Al-4V alloy while maintaining adequate levels of elongation to failure.     

Microstructures and mechanical deformation behaviors of ultrafine-grained commercial pure (grade 3) Ti processed by two-step severe plastic deformation

Ultrafine-grained (UFG) commercial pure (CP, grade 3) Ti was produced using two-step severe plastic deformation, eight passes equal channel angular extrusion (ECAE) and cold rolling (CR) at liquid nitrogen temperature (LNT). Microstructural evolution and mechanical behaviors of UFG CP-Ti have been systematically investigated. After eight passes ECAE, the grain size was refined to sub-micron scale, smaller than 0.5 μm. Subsequent CR at LNT or RT for both UFG and coarse-grained (CG) specimens led to further refinement of structure, dramatically intensifying (0 0 0 2) peak, and the preferred orientation along the (0 0 0 2) crystal plane is formed at the expense of other crystal plane. After eight passes ECAE and CR at LNT, the ultimate tensile strength of UFG CP-Ti (grade 3) is 1218 MPa, and an elongation of 12.6%. Strain hardening behaviors of UFG CP-Ti (grade 3) during tensile deformation at RT have been analyzed.     

Cryogenic equal channel angular pressing of commercially pure titanium: microstructure and properties

Cylindrical samples of CP Titanium (Grade 2) were deformed by one, two and three passes of equal channel angular pressing (ECAP) each at temperatures 77, 300 and 575 K, respectively. The microstructure of samples processed at 77 K shows retardation of recrystallisation, high density of dislocations and deformation twins, diffuse and obscure grain boundaries compare to microstructure of samples processed at room and high temperature, where recrystallised ultrafine equiaxed grains are observed. Mechanical properties for all structural states of Ti were studied by microhardness measurements at 300 K and uniaxial compression at temperatures 300, 170, 77 and 4.2 K. Higher levels of ECAP deformation (more passes of ECAP) lead to higher values of strength and hardness at all studied temperatures. Decrease of ECAP temperature leads to increase of strength characteristics in all cases. Influence of ECAP and compression temperatures on possible changes of deformation mechanism are discussed.     

Ultrafine-grained Ti–Nb–Ta–Zr alloy produced by ECAP at room temperature

To ascertain the influence of severe plastic deformation (SPD) on a Ti–Nb–Ta–Zr (TNTZ) alloy, we studied the room temperature mechanical behavior and microstructural evolution of an ultrafine-grained (UFG) Ti–36Nb–2Ta–3Zr (wt%) alloy prepared via equal-channel angular pressing (ECAP) of the as-hot-extruded alloy. The tensile behavior, phase composition, grain size, preferred orientation, and dislocation density of the UFG alloy, processed under different conditions, were analyzed and discussed. Compared to the as-hot-extruded alloy, the ECAP-processed TNTZ alloy (3 passes) exhibited approximately 40 and 88 % increase in average ultimate strength and yield strength, respectively. Moreover, as the number of ECAP passes increased from 3 to 6, the TNTZ alloy exhibited not only the expected increase in ultimate and yield strength values, but also a slight increase in elongation. Our results suggest that the deformation mechanisms that govern the behavior of the as-hot-extruded coarse grained (CG) TNTZ alloy during ECAP involve a combination of stress-induced martensitic transformation and dislocation activity. In the case of the ECAP-processed UFG TNTZ alloy, the deformation mechanism is proposed to involve two components: first, dislocation activity induced by the strain field imposed during ECAP; and second, the formation of α″ martensite phase during the early stages of ECAP which eventually transforms into β phase during continued deformation. We propose that the deformation mechanism governing the room temperature behavior of the TNTZ alloy strongly depends on the grain size of the β phase.     

Equal channel angular pressing of a TWIP steel: microstructure and mechanical response

A Fe–20.1Mn–1.23Si–1.72Al–0.5C TWIP steel with ultrafine grain structure was successfully processed through equal channel angular pressing (ECAP) at warm temperature up to four passes following the B _C route. The microstructure evolution was characterized by electron backscattered diffraction to obtain the grain maps, which revealed an obvious reduction in grain size, as well as a decrease in the twin fraction, with increasing number of ECAP passes. The texture evolution during ECAP was analyzed by orientation distribution function. The results show that the annealed material presents brass (B) as dominant component. After ECAP, the one pass sample presents A ₁* and A ₂* as the strongest components, while the two passes and four passes samples change gradually toward \( B/\bar{B} \) components. TEM analysis shows that all samples present twins. The twin thickness is reduced with increasing the number of ECAP passes. Nano-twins, as a result of secondary twinning, are also observed in the one and two passes samples. In the four passes sample, the microstructure is extensively refined by the joint action of ultrafine subgrains, grains and twins. The mechanical behavior was studied by tensile samples, and it was found that the yield strength and the ultimate tensile strength are significantly enhanced at increasing number of ECAP passes. Although the ductility and strain hardening capability are reduced with ECAP process, the present TWIP steel shows significant uniform deformation periods with positive work hardening rates.     

Effects of processing conditions on microstructure and mechanical properties of equal-channel-angular-pressed titanium

This review presents an investigation on effects of the processing conditions on the microstructural evolution and mechanical properties of commercial pure titanium processed by Equal Channel Angular Pressing (ECAP). An overview of ECAP processing is presented. A discussion on the microstructure evolution of ECAPed titanium emphasising effects of the ECAP-route type, processing temperature, number of ECAP passes, and mechanical/thermal treatments is presented. Moreover, the variations of the mechanical properties (yield strength, tensile strength, and ductility) of titanium as functions of the grain size are reported for the different conditions of ECAP processing. In addition, the best estimates of the Hall–Petch parameters for titanium processed by ECAP, ECAP followed by mechanical and/or thermal annealing are reported.     

室温ECAP和冷轧复合变形工业纯钛的组织和性能

采用ECAP技术和常规冷轧复合变形工艺制备了高强度工业纯钛,研究了复合变形后试样的力学性能与显微组织的关系.结果表明,工业纯钛经室温单道次ECAP和冷轧复合变形后,晶粒被严重拉长,形成了明显的纤维状组织,试样的抗拉强度高达805MPa;随着冷轧变形量的增大,变形组织的细化程度和均匀性提高,使试样的强度和塑性进一步提高.位错滑移和孪生是工业纯钛室温ECAP和冷轧复合变形的主要变形机制.     

Effect of commercial purity levels on the mechanical properties of ultrafine-grained titanium

Two grades of commercial purity (CP) titanium (grades 2 and 4) were processed using equal-channel angular extrusion (ECAE) at 300 °C and 450 °C, respectively. The processing temperatures were the minimum temperatures at which eight pass ECAE could be performed without any shear-localization. The coarse-grained (CG) microstructures of as-received grade-2 and grade-4 CP-Ti, with average grain sizes of 110 μm and 70 μm, respectively, were refined down to sub-micron levels with a mean grain size of about 300 nm for both grades after 8 ECAE passes. The ultrafine-grained (UFG) microstructures led to substantial enhancement in strength for both grades. The grade-2 sample showed a more than two fold increase in yield strength (σ_y), from 307 MPa for the as-received one to about 620 MPa for the processed samples. The grade-4 CP-Ti exhibited a relatively smaller increase in strength due to the higher processing temperature, and it showed about 50% increase in σ_y after eight pass ECAE, from 531 to 758 MPa. These strength levels were obtained with high ductility levels of 21% and 25% for UFG grade-2 and grade-4 Ti, respectively. These improvements in mechanical properties are attributed to the substantially refined grain size and increased dislocation density. Grade-4 Ti is stronger than grade-2 because of the higher oxygen content. The higher ductility and significantly higher strain hardening capability of UFG grade-4 Ti, in spite of the similar grain size and microstructure with UFG grade-2 Ti, is also due to the higher impurity content, probably resulting in a higher dislocation storage capability during room temperature deformation, and thus, higher strain hardening capacity. Such properties make UFG grade-4 Ti comparable to the commercial Ti-6Al-4V alloy for biomedical applications without negative effects of the alloying elements on biocompatibility.     

应用于医学的ECAP处理Ti及Ti合金的研究现状

综述了目前国际上应用于医用生物材料的等通道挤压(Equal-channel angular pressure,ECAP)处理工业纯钛和钛合金的研究进展,介绍了等通道挤压技术的最新进展,ECAP处理工业纯钛的微观组织演变,ECAP处理后Ti的强度、抗疲劳性、耐腐蚀性和生物活性的改善以及ECAP处理Ti-6Al-4V的超塑性和超塑变形后的微观组织,最后展望了未来的研究方向。     

Thermophysical Properties of Aluminum 1060 Fabricated by Equal Channel Angular Pressing

Equal channel angular pressing (ECAP) has the advantage of enabling an ultrafine grain size. Aluminum 1060 is used as a power plant material because of its favorable electrical properties. However, the weak strength of aluminum limits its application. In this study, the thermal conductivity and electrical conductivity of Al 1060 made by ECAP was investigated. ECAP was conducted through the die having a channel angle of 90° and a corner angle of 20° at a temperature of 473 K with a strain rate of 2 mm · s⁻¹. The specimen was then processed with 1 to 8 passes by the route Bc method with 90° rotation. In the case of eight passes, the grain size was reduced to as small as 300 nm. As a result of the ECAP, the tensile strength was raised from 75 MPa to 134 MPa, while the electrical conductivity did not show a significant difference after eight passes. The thermal conductivity gradually decreased with ECAP passes, because of the decreased grain size by ECAP.     

Microstructure and mechanical properties of ultrafine grain ZK60 alloy processed by equal channel angular pressing

The microstructure evolution and tensile properties of ZK60 magnesium alloy after equal channel angular pressing (ECAP) have been investigated. The results show that the two-step ECAP process is more effective in grain refinement than the single-step ECAP process due to the lower deformation temperature, a mean grain size of ~0.8 μm was obtained after two-step ECAP process at 513 K for four passes and 453 K for four passes. The EBSD examination reveals that ZK60 alloy after two-step ECAP process exhibits a more homogeneous grain size and misorientation distribution than single-step ECAP process. Both alloys after ECAP process present similar strong {0002} texture. The tensile strength of two-step ECAP alloy has also been improved compared with the single-step ECAP alloy. The strengthening effect was mainly ascribed to grain refinement.     

135°ECAP+旋锻变形工业纯钛的热稳定性研究

对经过135°ECAP+旋锻变形后的工业纯钛100,150,200,250,300,350,400,450℃和500℃下保温1h退火。采用透射电子显微镜(TEM)、扫描电子显微镜(SEM)、拉伸试验机及显微硬度仪等技术研究ECAP+旋锻变形工业纯钛退火后的组织与性能变化。结果表明:在400℃以下退火时,显微组织中位错密度降低,晶界逐渐清晰,变形组织未发生明显变化,材料的抗拉强度和显微硬度略有降低,伸长率增加不明显;在400℃以上退火时,随着退火温度的升高,发生再结晶,晶粒尺寸明显增大,平均晶粒尺寸约为5μm,材料的抗拉强度和显微硬度均出现明显降低,伸长率增加。拉伸断口表明,ECAP+旋锻变形退火后工业纯钛的拉伸断裂均为韧性断裂。随着退火温度的升高,韧窝尺寸变大,韧窝深度变深。     

Mechanical behaviour and texture of annealed AZ31 Mg alloy deformed by ECAP

Abstract

AZ31 Mg alloy samples were processed by equal channel angular pressing (ECAP) at 220°C for four passes. An average grain size of ～1·9 μm with reasonable homogeneity was obtained. The ECAP process imparted large plastic shear strains and strong deformation textures to the material. Subsequent annealing of the equal channel angular pressed samples produced interesting mechanical behaviours. While yield strength increased and ductility decreased immediately after undergoing ECAP, annealing at temperatures <250°C restored ductility significantly at a small decrease in of yield strength. Annealing at temperatures >250°C reduced yield strength without additional improvement in ductility. It is believed that the combination of stress relief via dislocation elimination, refined microstructure and the retention of a strong ECAP texture at low annealing temperatures enhance ductility. High temperature annealing breaks down the ECAP texture resulting in no further improvement in ductility. The results show that the mechanical properties of the alloy can be positively influenced by annealing after ECAP to achieve a combination of strength and ductility.     

ECAP变形对20MnSi钢组织与性能的影响

采用C方式等径弯曲通道变形(Equal Channel Angular Pressing,简称ECAP)对20MnSi钢进行了4道次室温变形,研究了变形道次对显微组织和力学性能的影响.结果表明,铁素体组织随变形道次的增加逐渐演变为等轴状大角度晶界的亚微晶组织;试验用钢的硬度和强度随变形道次的增加而增加,4道次后强度有所降低;在本试验条件下,珠光体组织中的片状渗碳体表现出很强的塑性变形能力.     

ECAP变形对Mg2Si增强耐热镁合金组织及性能的影响

为了提高镁合金的耐热性能,在Mg-Zn合金中加入Si,形成Mg-Zn-Si镁合金.采用ECAP工艺在变形温度为573 K和挤压路径为Bc条件下对Mg-Zn-Si镁合金进行不同道次的变形.运用金相显微镜(OM)、X射线衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)等手段对变形后的Mg-Zn-Si镁合金进行了组织表征,对变形后的合金进行了室温拉伸和高温蠕变等力学性能测试.结果表明:随着挤压道次增加,α-Mg基体、Mg Zn相及Mg2Si相均得到细化且分布趋于均匀.1道次挤压后部分基体α-Mg细化,4道次挤压后α-Mg的尺寸减小为5~10μm,且晶粒大小趋于均匀;2道次挤压后Mg2Si相枝晶在原位置破碎为颗粒状,6、8道次挤压后Mg_2Si相呈弥散分布.4道次挤压后合金的屈服强度和抗拉强度均提高120%,伸长率提高353%;8道次挤压后合金的抗拉强度和伸长率与4道次相比变化不大,但屈服强度进一步提高了19%.随着挤压道次增加,高温抗蠕变性能提高,8道次后高温稳态蠕变速率降低5倍.Mg2Si相细化机理为受剪切而机械碎断.     

超细晶铜力学和阻尼性能及微观结构研究

在众多阻尼材料中,金属阻尼材料既能满足高阻尼减振降噪性能,又具有较高的强度,是理想的阻尼材料.为了提高商业纯铜的力学性能,分析晶粒细化程度对纯铜力学性能和阻尼性能的影响,在室温下对商业纯铜棒进行12道次BC路径等通道转角挤压(ECAP)实验.对挤压后样品进行单轴微拉伸试验和高循环拉伸疲劳试验研究其力学性能;通过动态力学...     

Grain refinement in as cast Al–Mg–Mn alloy during high temperature equal channel angular pressing

Abstract

An as cast Al–Mg–Mn alloy with coarse equiaxed grain structure was processed by equal channel angular pressing (ECAP) at 350°C up to eight passes. Systematic studies were made on the microstructural evolution during ECAP by optical microscopy, electron backscattered diffraction and TEM. Equal channel angular pressing led to a considerable grain refinement, resulting in an average cell size of about 1 μm and a fraction of high angle boundaries of 75% after eight pressing passes. Deformation bands were not developed during the ECAP process, and a reasonably equiaxed substructure was obtained even after one pass. The main mechanism of grain refinement was attributed to the continuous dynamic recrystallisation based on the motion of deformation induced dislocations. Discontinuous recrystallisation at grain boundaries and triple junctions also contributed to the refinement, which played an important role especially at high strain of eight passes.     

Impact Toughness of Ultrafine‐Grained Commercially Pure Titanium for Medical Application

This study aims at achieving the best combination of strength, ductility, and impact toughness in ultrafine‐grained (UFG) Ti Grade 4 produced by equal‐channel angular pressing via Conform scheme (ECAP‐C) with subsequent cold drawing. UFG structures with various parameters (e.g., size and shape of grains, dislocation density, conditions of boundaries) are formed by varying the treatment procedures (deformation temperature and speed at drawing, annealing temperature). The tensile and impact toughness tests were performed on samples with a V‐shaped notch and different structures of commercially pure Ti Grade 4 in the coarse‐grained and UFG states. The results demonstrated that grain refinement, higher dislocation density, and their elongated shape were obtained as a result of drawing at 200 °С, which led to a decrease in both the uniform elongation at tension and the impact toughness of Ti Grade 4. Short‐term annealing at 400–450 °C could improve the impact toughness of UFG Ti with a non‐significant decrease in strength. This short‐term annealing contributes to the dislocation density decrease without considerable grain growth as a result of the recovery and redistribution of dislocations. The dependence of impact toughness on the strain hardening ability of UFG Ti was discussed.

     

Effect of equal channel angular pressing on fracture toughness of Al-7075

In this paper, influence of equal channel angular pressing (ECAP) on the fracture behavior of Al-7075 alloy is experimentally investigated. The specimens are successfully processed by ECAP methodology up to four passes using different routes. Transmission electron microscope (TEM) images showed that after four passes of ECAP, the average grain size is refined from 40 μm to less than about 500 nm. The percentage increase in yield strength, ultimate strength and microhardness of the specimens after four ECAP passes was 230, 90 and 110 respectively. Standard tests on the disk-shaped compact DC(T) specimens showed that fracture toughness is decreased up to 8% at the first ECAP pass while after four passes, this parameter roused to 17% higher than that of annealed condition. Furthermore, scanning electron microscope (SEM) micrographs demonstrated that ductile fracture mechanism with large dimples occurred in the annealed samples, changed to limited ductile fracture with fine dimples after ECAP process. This research provides new insights into the effect of ECAP and grain refinement on the fracture behavior of materials.