低温钢16MnDR的埋弧焊

对选用四种埋弧焊焊丝、焊剂组配（Ｈ１０Ｍｎ２／ＨＪ４３１、Ｈ０８ＭｎＡ／ＨＪ４３１、Ｈ０８ＭｎＭｏＡ／ＨＪ３５０、Ｈ０８ＭｎＭｏＡ／ＨＪ２５０）焊接的１６ＭｎＤＲ接头在－３０℃下的低温韧性进行了对比试验，试验表明Ｈ０８ＭｎＭｏＡ／ＨＪ２５０焊接接头低温韧性最好，在－３０℃下冲击吸收功可达４６．５Ｊ。对接头熔敷金属进行了化学成分测试，分析了Ｈ０８ＭｎＭｏＡ／ＨＪ２５０焊接接头具有最高韧性的原因。用此     

IMPROVED LEACHING METHOD AND KINETICS OF MANGANESE CARBONATE ORE AT ROOM TEMPERATURE

ＩＭＰＲＯＶＥＤＬＥＡＣＨＩＮＧＭＥＴＨＯＤＡＮＤＫＩＮＥＴＩＣＳＯＦＭＡＮＧＡＮＥＳＥＣＡＲＢＯＮＡＴＥＯＲＥＡＴＲＯＯＭＴＥＭＰＥＲＡＴＵＲＥＹｕａｎＭｉｎｇｌｉａｎｇ；ＭｅｉＸｉａｎｇｏｎｇ；ＣｈｅｎＪｉｎ；ＺｈｕａｎｇＪｉａｎｍｉｎｇ（Ｄｅｐ...     

COMPUTERIZED PREDICTION SYSTEM FOR THERMOPHYSICAL PROPERTIES

ＣＯＭＰＵＴＥＲＩＺＥＤＰＲＥＤＩＣＴＩＯＮＳＹＳＴＥＭＦＯＲＴＨＥＲＭＯＰＨＹＳＩＣＡＬＰＲＯＰＥＲＴＩＥＳ①ＺｈａｎｇＪｉａｙｕｎ，ＭａＹｏｎｇｊｉａｎ，ＺｈｏｕＴｕｐｉｎｇ，ＬｅｉＪｕｎｂｏ，ＦａｎｇＸｕｅｌｉａｎｇＤｅｐａｒｔｍｅｎｔｏｆＰ...     

TEMPERING RESPONSE OF A DEFORMED LOW CARBON DUAL PHASE STRUCTURE

ＴＥＭＰＥＲＩＮＧＲＥＳＰＯＮＳＥＯＦＡＤＥＦＯＲＭＥＤＬＯＷＣＡＲＢＯＮＤＵＡＬＰＨＡＳＥＳＴＲＵＣＴＵＲＥ￥ＪＩＮＭａｎ;ＪＩＡＮＧＺｈｏｎｇｈａｏ;ＮＡＮＳｈｅｎｇｈｕｉ;ＨＵＪｉａｎｄｏｎｇ;ＬＩＡＮｊｉａｎｓｈｅ（ＪｉｌｉｎＵｎｉｖｅｒｓｉ...     

THERMAL DECOMPOSITION OF ZINC CARBONATE HYDROXIDE HYDRATE POWDERS OF DIFFERENT PARTICLE SIZE AND SAMPLE MASS

ＴＨＥＲＭＡＬＤＥＣＯＭＰＯＳＩＴＩＯＮＯＦＺＩＮＣＣＡＲＢＯＮＡＴＥＨＹＤＲＯＸＩＤＥＨＹＤＲＡＴＥＰＯＷＤＥＲＳＯＦＤＩＦＦＥＲＥＮＴＰＡＲＴＩＣＬＥＳＩＺＥＡＮＤＳＡＭＰＬＥＭＡＳＳ①ＣｈｅｎＪｉａｎｘｕｎ,ＺｈａｏＲｕｉｒｏｎｇａｎｄＪｉａｎ...     

OSTWALD COARSENING UNDER CHANGING VOLUME FRACTION CONDITION

ＯＳＴＷＡＬＤＣＯＡＲＳＥＮＩＮＧＵＮＤＥＲＣＨＡＮＧＩＮＧＶＯＬＵＭＥＦＲＡＣＴＩＯＮＣＯＮＤＩＴＩＯＮＺｈａｏ；ＪｉｕｚｈｏｕＧｕｏ，ＪｉｎｇｊｉｅＪｉａ；ＪｕｎＬｉ；Ｑｉｎｇｃｈｕｎ（ＣｏｌｌｅｇｅｏｆＭａｔｅｒｉａｌｓＳｃｉｅｎｃｅａｎｄＥｎ...     

A STUDY OF CARBIDE GROWTH IN MAR-M247 LC ALLOY BY DIRECTIONAL SOLIDIFICATION METHOD

ＡＳＴＵＤＹＯＦＣＡＲＢＩＤＥＧＲＯＷＴＨＩＮＭＡＲ－Ｍ２４７ＬＣＡＬＬＯＹＢＹＤＩＲＥＣＴＩＯＮＡＬＳＯＬＩＤＩＦＩＣＡＴＩＯＮＭＥＴＨＯＤＪ．ＨＬｅｅ;Ｊ．Ｃｈｅｎ;Ｓ．Ｊ．Ｃｈｏｅ;Ｙ．Ｔ．ＬｅｅａｎｄＨ．Ｍ．Ｋｉｍ（ＨｉｇｈＴｅｍｐｅｒａｔｕ...     

THERMODYNAMIC ANALYSIS OF Mo-La_2O_3 THERMIONIC CATHODE WIRE

ＴＨＥＲＭＯＤＹＮＡＭＩＣＡＮＡＬＹＳＩＳＯＦＭｏ－Ｌａ_２Ｏ_３ＴＨＥＲＭＩＯＮＩＣＣＡＴＨＯＤＥＷＩＲＥ￥ＺｈｏｕＭｅｉｌｉｎｇ；ＷａｎｇＪｉｎｓｈｕ；ＺｈａｎｇＪｉｕｘｉｎｇ；ＮｉｅＺｕｏｒｅｎ；ＬｉＥｒ；ＺｕｏＴｉｅｙｏｎｇ（Ｄｅｐａｒｔｍｅｎ...     

SiOx纳米抗菌剂制备及在羊毛纤维中的应用研究

利用纳米SiOx的多孔结构,采用离子交换法制备纳米SiOx抗菌剂,使用硅烷偶联剂对纳米抗菌剂进行表面改性,降低其表面自由能,并初步探讨了该抗菌剂在羊毛纤维中的应用。经测试表明,纳米抗菌剂的抗菌率可达96％以上;表面改性可增强纳米抗菌剂与高聚物的相容性,用该抗菌剂制备的抗菌羊毛纤维,在具备抗菌功能的同时,又具有良好的力学性能。     

新型硅烷复合物在铝材表面处理中的应用

目的研制一种新型硅烷复合物,以替代传统的铬酸盐钝化液对铝材进行表面处理。方法将KH-560和A-151两种偶联剂进行复合,并添加合成的水性聚酯水解促进剂和带有活性基团的交联剂R,考察偶联剂配比、水解促进剂和交联剂R的用量对处理液稳定性及硅烷膜耐腐蚀性的影响。结果当KH-560与A-151的质量比为4∶1,水解促进剂的质量分数为0.4%~0.6%时,处理液的储存时间超过90天,硅烷膜也具有良好的耐腐蚀性能。对于储存后性能下降的处理液,添加4%(占处理液质量的百分比)的交联剂R后,即能在硅羟基之间形成明显的交联作用,有效增强硅烷膜的防护性能。结论该硅烷复合物的综合性能达到了工业化应用要求,可解决铬酸盐钝化液对环境的污染问题,具有良好的社会效益。     

Antibacterial activity of nano-SiO2 antibacterial agent grafted on wool surface

A composite antibacterial agent of Ag-loaded nano-SiO₂ was prepared by adsorption methodology and grafted on wool surface. The antibacterial performance of the antibacterial wool fibers was tested for different concentration of composite antibacterial agent, contact time with germs and washing time. The content of the composite antibacterial agent grafted on wool fibers was easily controlled by varying the antibacterial agent concentration in the grafting process. The results showed that antibacterial activity increased with the increasing concentration of the composite antibacterial agent. The antibacterial wool fibers grafted 4.3% of composite antibacterial agent was highly effective in killing test bacteria and had excellent water-resisting property.     

镀液成分对微弧氧化膜表面化学镀镀层的影响

为提高镀层质量,通过对镀层表面形貌观察、镀液稳定性测试等方法,研究缓冲剂、络合剂对镀液稳定性以及镀层质量的影响,结果表明：加入单一缓冲剂的镀液,反应25 min后镀液开始分解;加入复合络合剂和复合缓冲剂的镀液静置96 h没有分解,得到的镀镍层完全覆盖微弧氧化膜,镀层化学活性高且耐酸性好。     

固定剂对钎焊金刚石工具质量的影响

为研究固定剂对钎焊金刚石工具质量的影响,我们使用SZ、NH和GY三种固定剂,分别制作试块和产品,观测其外观形貌并进行实际切割钻进验证。结果显示:GY固定剂加热后的碳化物残留最少、外观质量最好,其次为NH固定剂,SZ固定剂的表现最差;以三种固定剂制作的锯片和钻头中,使用GY固定剂的寿命最长、速度最快,其次为使用NH固定剂的制品,最次为使用SZ固定剂的制品。      

不同固化剂对环氧树脂的性能影响

固化剂对环氧树脂固化产物的最终性能具有重要的作用,本研究以市场上常见的不同结构固化剂为对象,包括593、IPDA、D400和651,通过考察固化剂种类和用量对涂层干燥时间、硬度、附着力和抗冲击性能的影响,得到固化剂结构与固化树脂的性能关系,为高性能固化剂的结构设计提供基础理论依据。     

某新型清洗剂在弹药弹筒表面漆膜清洗上的应用

目的用某新型清洗剂代替酒精、汽油应用于弹药弹筒表面漆膜清洗。方法选取先进、可靠、安全环保的某新型清清洗剂,应用于弹药弹筒表面漆膜中间过程中漆膜上的油污、汗渍、红丹、记号笔、药粉等污物的清洗。通过对弹药弹筒表面漆膜的特点、漆膜上各类污渍的组成以及对漆膜中间清洗工艺过程进行分析,同时针对上述特点,拟定清洗剂选用原则,结合清洗剂的组成、特点、除污机理,通过对清洗剂进行应用试验,从清洗剂安全性能、清洗后漆膜附着力性能、清洗后漆膜耐盐雾性能、清洗剂的清洗效果、清洗剂的挥发速度、清洗剂气味等几个方面进行试验。结果某新型清洗剂具备清洗效果好、挥发速度快、清洗效率高等优点,清洗后对弹药弹筒表面漆膜无影响,满足弹劳逸结合漆膜清洗质量要求。结论某新型清洗剂可以代替酒精和汽油在弹药弹筒表面漆膜清洗上进行应用,具有环保、无毒等特点,在弹药弹筒表面漆膜清洗应用领域具有推广意义。     

铸造用呋喃树脂新型增强剂的研究与应用

介绍了新型硅烷偶联剂对铸造用呋喃树脂的增强效果,研究了生产工艺、外界环境对增强剂的影响,探索了新型硅烷偶联剂的有效期等性能,并对其增强原理进行了初步讨论.     

代理技术在车间制造混合控制系统中的应用研究

分析了车间控制结构的演变和代理技术在制造控制中的应用,提出了一个通用的制造代理模型。基一过个模型进一步讨论了车间制造混合控制的结构,并着重研究了单元代理的报一间代理的任务分源过程及系统对设备故障的处理过程。研究指出基于代一间制造混合控制系统,既具有递阶控制的高效率,又具有分布式控制的高可靠必与自适应性。     

CeO2纳米粒子抛光液分散稳定性及其化学机械抛光特性研究

目的制备性能优良的CeO_2纳米粒子抛光液。方法通过使用不同种类及不同浓度的分散剂制备了一种良好的CeO_2纳米粒子抛光液,采用激光粒度仪,紫外可见分光光度仪等对其进行了表征,进而研究了其在石英玻璃片化学机械抛光中的特性。结果不同分散剂的分散作用不同,且分散剂的浓度直接影响分散效果。离子型分散剂主要通过静电稳定作用实现抛光液的分散稳定,而非离子型分散剂则通过空间位阻作用实现抛光液的分散稳定。阴离子型分散剂与非离子型分散剂的分散稳定效果明显强于阳离子型分散剂,而阴离子型分散剂与非离子型分散剂混合复配后的分散稳定效果又强于单一分散剂的效果。结论混合复配型分散剂配制的CeO_2纳米粒子抛光液静置72 h后仍分散均一稳定,基本可以满足抛光液分散稳定性能的要求。配制的CeO_2纳米粒子抛光液在石英玻璃化学机械抛光中主要通过纳米粒子的吸附作用实现材料的去除,抛光后的石英玻璃表面无划痕,表面粗糙度可以达到10 nm左右,有效提高了石英玻璃的抛光质量。