超细硬质合金WC-8Co-0.8(Cr_3C_2/TaC)的组织与性能

以超细WC-8Co硬质合金为研究对象,混合添加晶粒长大抑制剂Cr3C2/TaC。结果表明,合金在添加0.8wt%Cr3C2/TaC时的TRS达到3675MPa,而在添加0.5wt%和1.0wt%Cr3C2/TaC时的TRS降到2120MPa;Cr3C2/TaC在很大程度上影响了合金烧结时的致密化,WC-8Co-0.8wt%(Cr3C2/TaC)压坯在1400℃下完全致密化需要的烧结时间为60分钟;而同类普通WC-8Co-0.8wt%(Cr3C2/TaC)的压坯,由于没有超细粉末的高表面能,烧结60分钟后密度只能达到理论密度的98.8%;TaC和Cr3C2对W在γ相中的固溶度具有相反的作用。     

添加VC与Cr_3C_2对超细晶硬质合金烧结过程的影响

系统研究晶粒长大抑制剂VC和Cr3C2对WC-8%Co超细晶硬质合金烧结过程中收缩率、相变温度和晶粒长大的影响。研究表明,WC-8%Co超细晶硬质合金的烧结收缩和致密化过程主要发生在固相烧结阶段,在液相出现前,合金的致密化程度已达到95%。晶粒长大抑制剂VC和Cr3C2的加入,显著降低了超细晶硬质合金烧结过程中液相出现的温度,且不同程度地阻碍了WC-8%Co超细晶硬质合金烧结过程中致密化的进程和速度。与未加入晶粒长大抑制剂的合金相比,其致密化的进程大约延迟80℃。     

VC/Cr_3C_2添加剂对超细硬质合金组织及性能的影响(英文)

研究了VC/Cr3C2添加剂对WC-12Co超细硬质合金的显微组织、硬度和抗弯强度(TRS)的影响.结果表明,舍一定比例VC/Cr3C2添加剂的合金具有更均匀的微观组织和优异的力学性能.当添加剂含量(质量分数)为0.5%VC/0.2%Cr3C2时,1430℃烧结制备的WC-12Co超细硬质合金的抗弯强度达3786 MPa,硬度达91.7 HRA.VC添加剂对WC晶粒的连续长大和非连续长大的抑制作用比Cr3C2添加剂更有效.此外,当烧结温度较高时,VC/Cr3C2添加剂对WC晶粒长大的抑制效果更显著.VC和Cr3C2添加剂抑制WC晶粒长大的作用机理为:VC和Cr3C2添加剂降低了WC相在粘结相中的过饱和度,从而降低烧结温度下粘结相中WC相溶解-析出过程的驱动力,起到阻碍WC晶粒长大的作用.     

VC/Cr_3C_2及配碳量对WC-0.5Co超细硬质合金组织与性能的影响

以超细WC粉末和超细WC-6Co复合粉末为原料,添加VC/Cr3C2作为晶粒长大抑制剂,同时进行配碳,采用高能球磨和气压强化烧结制备晶粒度小于0.5μm的WC-0.5Co超细硬质合金,研究了不同VC/Cr3C2添加量及配碳量对其组织与性能的影响。结果表明:VC/Cr3C2有效抑制了烧结过程中WC晶粒的长大,显著提高了WC-0.5Co超细硬质合金的硬度。当VC/Cr3C2添加量为0.73%(质量分数,下同)时,合金的硬度(HV0.05)最高,达到32 658 MPa;同时一定的配碳量有利于控制合金中的脱碳,提高合金性能,当配碳量为0.2%时,WC-0.5Co-0.73VC/Cr3C2合金的综合力学性能最好,断裂韧性为6.935 MPa·m1/2,维氏硬度(HV0.05)为32 216 MPa。     

超细硬质合金晶粒生长抑制剂VC、Cr_3C_2作用机理的研究

本文以液相复合-连续还原碳化方法制备的掺杂有VC和Cr3C2抑制剂的纳米复合WC-10Co粉末为原料,采用真空烧结+低压处理的工艺制备超细WC-10Co硬质合金,运用原子力显微镜(AFM)和场发射扫描电镜(FESEM)确定VC和Cr3C2抑制剂在硬质合金中的分布,讨论其抑制晶粒生长的机理。一部分VC、Cr3C2抑制剂吸附在WC晶粒表面形成30nm～50nm的沉淀物,降低WC晶粒的表面能;一部分VC、Cr3C2溶解在Co相中,降低WC在液相中的溶解度;其余VC、Cr3C2沉积在WC晶界,从而有效地抑制WC晶粒的长大。     

纳米晶WC-10Co复合粉末的烧结致密化行为

研究了机械合金化纳米晶WC-10Co复合粉末的真空烧结致密化行为和一般规律.结果表明:烧结温度的提高和烧结时间的延长有利于样品的烧结致密化过程,在1 275～1 300℃致密化速度快,在1 300℃,15 min左右致密化过程已基本完成;VC、Cr3C2等复合晶粒长大抑制剂含量的增加不利于致密化过程;新型晶粒长大抑制剂A可以更有效地阻碍晶粒长大;纳米晶WC-10Co-0.8VC/Cr3C2-0.2A复合粉末压坯在1375℃,30min烧结条件下,所得的密度为14.48 g/cm3,晶粒尺寸约为180 nm.     

烧结温度对WC-14TiC-8Co超细硬质合金组织和性能的影响

采用粉末冶金法制备了WC-14TiC-8Co超细硬质合金,研究了不同的烧结温度对WC-14TiC-8Co超细硬质合金组织和性能的影响。结果表明,随着烧结温度从1300℃升高到1410℃,合金的晶粒逐渐长大,合金的密度、抗弯强度随温度上升呈现出持续升高的走势,而硬度表现出先升后降的走势;当烧结温度为1380℃、保温时间为40min时,WC-14TiC-8Co超细硬质合金获得了最佳综合性能,其密度、抗弯强度和硬度值分别达到11.49g·cm~(-3)、1482MPa和92.8HRA,合金的组织为WC+(Ti,W)C+γ+少量η相,升温过程中的缺碳现象是η相形成的主要原因。     

稀土Y_2O_3对WC-6%Co超细硬质合金组织及性能的影响

本文研究了在复合抑制剂(Cr3C2/VC/TaC)组成及含量不变的基础上,添加不同量Y2O3对WC-6%Co超细硬质合金的组织结构、磁性能及力学性能的影响。通过XRD以及性能测试,研究发现:在WC-6%Co超细硬质合金中添加Y2O3,能起到细化晶粒的效果,当添加0.2%Y2O3时,合金的晶粒最细,致密度最好,WC晶粒分布均匀;Y2O3会影响WC-6%Co超细硬质合金的磁性能,随着Y2O3含量的增加,合金的矫顽磁力增加,磁饱和强度略有降低,Y2O3能有效的改善合金的机械性能,特别是其抗弯强度。结果表明,当抑制剂配方为0.8%(Cr3C2/VC/TaC)+0.2%Y2O3时,制备的WC-6%Co超细硬质合金的机械性能具有最佳值,硬度达到94.1 HRA,抗弯强度1 770 MPa。     

含(W,Ti,Ta)C的超细硬质合金的性能及组织研究

本文在WC-8%Co(文中含量均为质量分数)、复合抑制剂(VC/Cr3C2)的基础上,添加不同配比的Cr3C2及(W,Ti,Ta)C,制备超细硬质合金。采用横向断裂强度检测、洛式硬度检测、SEM分析、TEM检测等方法,研究了Cr3C2和(W,Ti,Ta)C对超细硬质合金力学性能和组织结构的影响。结果表明:随着Cr3C2、(W,Ti,Ta)C的增加,晶粒大小没有显著变化,硬质合金的横向断裂强度减低,硬度提高。通过透射电镜观察,在WC-8%Co-4%(W,Ti,Ta)C-0.5%(VC/Cr3C2)硬质合金中发现了类似于孪晶的结构,并通过能谱证实了Cr3C2和(W,Ti,Ta)C的存在。WC-8%Co-4%(W,Ti,Ta)C硬质合金经1 390℃压力烧结后,硬度为93.8 HRA,抗弯强度为2 250 MPa,相对密度为99.7%。     

晶粒长大抑制剂对超细WC-9%Co硬质合金性能的影响

在复合抑制剂(VC/Cr3C2)的基础上,添加了不同配比的TaC,研究了TaC对超细WC-9%Co硬质合金组织结构和力学性能的影响。结果表明:添加不同配比的TaC制备的WC-9%Co硬质合金的硬度随着TaC质量分数的增加先增大后减小;TaC的加入降低了W在Co相中的固溶度,从而抑制了晶粒长大。在本实验范围内,在复合抑制剂(VC/Cr3C2)质量分数为0.6%的基础上添加质量分数0.3%的TaC,经1 390℃真空烧结后,制备的超细WC-9%Co硬质合金硬度为93.5 HRA,TRS为2 370 MPa,致密度为99.5%,磁饱和强度为13.29 G.cm3/g,矫顽磁力为31.86 kA/m,此时具有较佳的综合力学性能。     

Effect of VC and NbC additions on microstructure and properties of ultrafine WC-10Co cemented carbides

The nanocomposite WC-Co powders were prepared through planetary ball milling method. Effects of grain growth inhibitor addition and the vacuum sintering parameters on the microstructure and properties of ultrafine WC-10Co cemented carbides were investigated using X-ray diffractometer, scanning electron microscope and mechanical property tester. The results show that VC and NbC additions can refine the WC grains, decrease the volume fraction of Co₃W₃C phase in ultrafine WC-10Co cemented carbides, and increase the hardness and fracture toughness of the base alloys. After sintering for 60 min at 1400 °C, the average grain size and hardness of ultrafine-grained WC-10Co-1VC cemented carbide are 470 nm and HRA 91.5, respectively. The fracture toughness of cemented carbide WC-10Co-1NbC alloy is over 7 MN·m^?3/2.     

Sintering characteristics and microstructure of WC-Co-VC/Cr<Subscript>3</Subscript>C<Subscript>2</Subscript> ultrafine cemented carbides

The sintering characteristics, microstructure, and mechanical properties of ultrafine WC-12%Co-0.2%VC/0.5%Cr₃C₂ cemented carbides were investigated. Dilatometric and differential thermal analyses (DTA) indicate that the compacts start to shrink at 600°C, the shrinkage rate peak is at 1190°C, and the liquid formation temperature is lower than the W-C-Co eutectic temperature (1330°C). Microstructure analysis results show that the cemented carbides with fine and homogeneous microstructure were obtained when sintered at 1430°C. Continuous and discontinuous grain growth was suppressed due to the synergistic action of VC/Cr₃C₂. The transverse rupture strength (TRS) of the samples reaches 4286 MPa, with the hardness HRA 92.1. The fine and homogeneous microstructure, alloy strengthening, and different phase constitutions of binder in the cemented carbides result in high hardness and TRS. Continuous and discontinuous grain growth was observed in the cemented carbide sintered at 1450°C, which results in significant decreases of hardness and TRS. It indicates that VC/Cr₃C₂ additions in the cemented carbides can only suppress the grain growth at a certain temperature.     

Consolidation and properties of ultrafine binderless cemented carbide by spark plasma sintering

Owing to the absence of metal binder, binderless cemented carbides have higher wear, corrosion, and oxidation resistance. WC-0.3VC-0.5Cr3C2 powders with an average particle size of 200nm and a little amount of active element were consolidated by spark plasma sintering. The sintered microstructure revealed that the average WC grain size was 0.24μm, which was almost consistent with the initial fine powder. The results of XRD showed that W2C phase was formed. Nearly complete densification of ultrafine binderless cemented carbide was achieved by sintering at 1400℃ for 120s under 50MPa. The resulting hardness and the fracture toughness were 28.18 GPa and 6.05MPa·m1/2, respectively.     

工艺条件对WC-12%Co超细硬质合金性能的影响

采用不同粒度的WC粉,加入VC、Cr3C2做抑制剂,制备WC-12%Co超细硬质合金。采用D60-25型钴磁仪测量合金磁饱和,利用排水法测定合金密度,采用三点弯曲法在CMT4504拉伸机上检测合金的抗弯强度,试样抛光后在JEOL-6701F扫描电镜下观察合金的显微组织。研究了不同的WC粉末粒度、球磨时间、烧结工艺对WC-12%Co的超细硬质合金性能的影响。结果表明:过压烧结可明显提高合金抗弯强度、硬度和密度;随着球磨时间的增加,合金硬度不断上升,抗弯强度先增后减;采用0.55μm粒度WC粉制备的合金的硬度明显高于0.70μm粒度WC粉制备的合金。在本次实验中,选用0.55μm的WC粉末原料,混合料球磨85 h,通过过压烧结,可制备出性能优良的WC-12%Co超细硬质合金,硬度HV≥1 800,抗弯强度≥3 400 N/mm2。