NiFe2O4基金属陶瓷惰性阳极的腐蚀研究进展

综述了近年来国内外铝电解用NiFe2O4基金属陶瓷惰性阳极在阳极组元的溶解与分布、腐蚀率的预测与测定以及氧化物和金属相对阳极腐蚀的影响三个方面所做的研究工作。     

EFFECT OF Cu-Ni CONTENT ON THE CORROSION RESISTANCE OF （Cu-Ni）/（10NiO-90NiFe204） CERMET INERT ANODE FOR ALUMINUM ELECTROLYSIS

（Cu-Ni）/（10NiO-90NiFe204） cermet inert anodes containing metal Cu-Ni0, 5, 10, 15 and 20 wt pct were prepared and their corrosion resistance to Na3AlF6-Al2O3 melts was investigated. The results indicate that the content of metal Cu-Ni has little effect on the steady-state concentration of Ni in the electrolyte and the values could not be used to effectively differentiate their corrosion resistance. The steady-state concentration of Fe decreases from 304×10^-6 to 168×10^-6 and that of Cu increases from 21×10^-6 to 71×10^-6 with the content of metal Cu-Ni increasing from 0 to 20 wt pct. Post-examination shows that metallic phase Cu-Ni is corroded preferentially during electrolysis and many pores are left at the anode surface. Considering the corrosion resistance and electrical conductivity, the cermet containing metal Cu-Ni 5 wt pct should be selected and studied further.