Performance of templated mesoporous carbons in supercapacitors

By analogy with other types of carbons, templated mesoporous carbons (TMCs) can be used as supercapacitors. Their contribution arises essentially from the double layer capacity formed on their surface, which corresponds to 0.14 F m⁻² in aqueous electrolytes such as H₂SO₄ and KOH and 0.06 F m⁻² for the aprotic medium (C₂H₅)₄NBF₄ in CH₃CN. In the case of a series of 27 TMCs, it appears that the effective surface area determined by independent techniques can be as high as 1500-1600 m² g⁻¹, and therefore exceeds the value obtained for many activated carbons (typically 900-1300 m² g⁻¹). On the other hand, the relatively low amount of surface oxygen in the present TMCs, as opposed to activated carbons, reduces the contribution of pseudo-capacitance effects and limits the gravimetric capacitance to 200-220 F g⁻¹ for aqueous electrolytes. In the case of non-aqueous electrolyte, it rarely exceeds 100 F g⁻¹.It is also shown that the average mesopore diameter of these TMCs does not improve significantly the ionic mobility compared with typical activated carbons of pore-widths above 1.0-1.3 nm.This study suggests that activated carbons remain the more promising candidates for supercapacitors with high performances.     

Improvement of the structural and chemical properties of a commercial activated carbon for its application in electrochemical capacitors

The present paper shows that the performance of an inexpensive activated carbon used in electrochemical capacitors can be significantly enhanced by a simple treatment with KOH at 850 °C. The changes in the specific surface area, as well as in the surface chemistry, lead to high capacitance values, which provide a noticeable energy density.The KOH-treatment of a commercial activated carbon leads to highly pure carbons with effective surface areas in the range of 1300-1500 m² g⁻¹ and gravimetric capacitances as high as three times that of the raw carbon.For re-activated carbons, one obtains at low current density (50 mA g⁻¹) values of 200 F g⁻¹ in aqueous electrolytes (1M H₂SO₄ and 6M KOH) and around 150 F g⁻¹ in 1M (C₂H₅)₄NBF₄ in acetonitrile. Furthermore, the resulting carbons present an enhanced and stable performance for high charge/discharge load in organic and aqueous media.This work confirms the possibilities offered by immersion calorimetry on its own for the prediction of the specific capacitance of carbons in (C₂H₅)₄NBF₄/acetonitrile. On the other hand, it also shows the limitations of this technique to assess, with a good accuracy, the suitability of a carbon to be used as capacitor electrodes operating in aqueous electrolytes (H₂SO₄ and KOH).     

EDLC performance of carbide-derived carbons in aprotic and acidic electrolytes

This study shows that carbide-derived carbons (CDCs) with average pore size distributions around 0.9-1 nm and effective surface areas of 1300-1400 m² g⁻¹ provide electrochemical double-layer capacitors with high performances in both aqueous (2M H₂SO₄) and aprotic (1M (C₂H₅)₄NBF₄ in acetonitrile) electrolytes.In the acidic electrolytic solution, the gravimetric capacitance at low current density (1 mA cm⁻²) can exceed 200 F g⁻¹, whereas the volumetric capacitance reaches 90 F cm⁻³. In the aprotic electrolyte they reach 150 F g⁻¹ and 60 F cm⁻³.A detailed comparison of the capacitive behaviour of CDCs at high current density (up to 100 mA cm⁻²) with other microporous and mesoporous carbons indicates better rate capabilities for the present materials in both electrolytes. This is due to the high surface area, the accessible porosity and the relatively low oxygen content.It also appears that the surface-related capacitances of the present CDCs in the aprotic electrolyte are in line with other carbons and show no anomalous behaviour.     

High-capacitance carbon electrode prepared by PVDC carbonization for aqueous EDLCs

Porous carbons with high-volumetric capacitance in aqueous electric double layer capacitors (EDLCs) were simply prepared by poly(vinylidene chloride) (PVDC) carbonization at high temperature without activation or any other additional processes. The PVDC-derived carbon is microporous with Brunauer-Emmett-Teller (BET) surface area about 1200 m² g⁻¹. As it possesses not only high-gravimetric capacitance (262 F g⁻¹) but also high-electrode density (0.815 g cm⁻³), the PVDC-derived carbon present an outstanding high-volumetric capacitance of 214 F cm⁻³, twice over of the commercial carbon Maxsorb-3 with a high-surface area of 3200 m² g⁻¹. The PVDC-derived carbon also exhibit good rate performance, indicating that it is a promising electrode material for EDLCs.     

Highly mesoporous carbonaceous material of activated carbon beads for electric double layer capacitor

The activated carbon beads (ACB) are prepared by a new preparation method, which is proposed by mixing the coal tar pitch and fumed silica powder at a certain weight ratio and activation by KOH at different weight ratios and different temperatures. The BET surface area, pore volume and average pore size are obtained based on the nitrogen adsorption isotherms at 77 K by using ASAP 2010 apparatus. The results show that our samples have much high specific surface area (SSA) of 3537 m² g⁻¹and high pore volume value of 3.05 cm³ g⁻¹. The percentage of mesopore volume increases with the weight ratio of KOH/ACB ranging from 4% to 72%. The electrochemical double layer capacitors (EDLCs) are assembled with resultant carbon electrode and electrolyte of 1 mol L⁻¹ Et₄NBF₄/PC. The specific capacitance of the ACB sample could be as high as 191.7 F g⁻¹ by constant current charge/discharge technique, indicating that the ACB presents good characteristics prepared by the method proposed in this work. The investigation of influence of carbon porosity structure on capacitance indicates that the SSA plays an important role on the capacitance and all the pore sizes of less than 1 nm, from 1 to 2 nm and larger than 2 nm contribute to the capacitance. Mesopore structure is beneficial for the performance at high current density.     

Electrochemical capacitors based on highly porous carbons prepared by KOH activation

Various coal and pitch-derived carbonaceous materials were activated for 5 h at 800 °C using potassium hydroxide and 1:4 component ratio. Porosity development of the resultant activated carbons (ACs) was assessed by N₂ sorption at 77 K and their capability of the charge accumulation in electric double layer was determined using galvanostatic, voltammetric and impedance spectroscopy techniques. ACs produced from different precursors are all microporous in character but differ in terms of the total pore volume (from 1.05 to 1.61 cm³ g⁻¹), BET surface area (from 1900 to 3200 m² g⁻¹) and pore size distribution. Very promising capacitance values, ranging from 200 to 320 F g⁻¹, have been found for these materials operating in acidic 1 mol l⁻¹ H₂SO₄ electrolytic solution. The variations in the electrochemical behavior (charge propagation, self-discharge, frequency response) are considered in relation to the porous texture characteristics, elemental composition but also possible effect of structural ordering due to various precursor materials used. Cycling investigation of all the capacitors has been also performed to compare ability of the charge accumulation for different carbon materials during subsequent cycles.     

Preparation of an electrochemically modified graphite electrode and its electrochemical performance for pseudo-capacitors in a sulfuric acid electrolyte

A graphite electrode was activated using recurrent electrochemical galvanic pulses. After activation, the original smooth surface was changed into an obviously porous, rough surface with microcrystalline flake structures with a larger number of O-containing functional groups. The material had a high capacitance and a satisfactory high-rate performance. The superior volumetric capacitance in active layer was ca. 428 F cm⁻³. Eighty-eight percentage of the capacitance remained after the discharge current increased from 2 mA (1.71 F cm⁻²) to 100 mA (1.50 F cm⁻²) in 2.3 M H₂SO₄.     

Polyfurfuryl alcohol derived activated carbons for high power electrical double layer capacitors

Polyfurfuryl alcohol (PFA) derived activated carbons were prepared by the acid catalysed polymerization of furfuryl alcohol, followed by potassium hydroxide activation. Activated carbons with apparent BET surface areas ranging from 1070 to 2600 m² g⁻¹, and corresponding average micropore sizes between 0.6 and 1.6 nm were obtained. The porosity of these carbons can be carefully controlled during activation and their performance as electrode materials in electric double layer capacitors (EDLCs) in a non-aqueous electrolyte (1 M Et₄NBF₄/ACN) is investigated.Carbon materials with a low average pore size (<∼0.6 nm) exhibited electrolyte accessibility issues and an associated decrease in capacitance at high charging rates. PFA carbons with larger average pore sizes exhibited greatly improved performance, with specific electrode capacitances of 150 F g⁻¹ at an operating voltage window of 0-2.5 V; which corresponds to 32 Wh kg⁻¹ and 38 kW kg⁻¹ on an active material basis. These carbons also displayed an outstanding performance at high current densities delivering up to 100 F g⁻¹ at current densities as high as 250 A g⁻¹. The exceptionally high capacitance and power of this electrode material is attributed to its good electronic conductivity and a highly effective combination of micro- and fine mesoporosity.     

The role of textural characteristics and oxygen-containing surface groups in the supercapacitor performances of activated carbons

It is suggested that the specific capacitance C₀ of activated carbons at low current densities (d ∼ 1 mA cm⁻²) consists, to a good first approximation, of two contributions. For the H₂SO₄ electrolyte they correspond to approximately 0.080 F m⁻² from the total accessible surface area and an additional pseudo-capacitance of 63 F mmol⁻¹ from the surface species generating CO in thermally programmed desorption (TPD). The new correlation proposed here is an alternative to Shi's earlier approach which considered contributions from the microporous and the external surface areas. Furthermore, it appears that the variation of the specific capacitance C at high current densities d (up to 100-150 mA cm⁻²) depends essentially on the CO₂-generating surface groups and on 1/L₀, the inverse of the average micropore width.     

Relationship between the nanoporous texture of activated carbons and their capacitance properties in different electrolytes

A series of activated carbons (ACs) with progressively changing nanotextural characteristics was obtained by heat-treatment of a bituminous coal at temperatures ranging from 520 to 1000 °C, and subsequent activation by KOH at 700 °C or 800 °C. As the pre-treatment temperature increases, the total pore volume V_T decreases from 1.28 to 0.30 cm³ g⁻¹, and the BET specific surface area from 3000 to 800 m² g⁻¹. The specific capacitance determined for each series of ACs using symmetric two electrode cells in 6 mol L⁻¹ KOH varies almost linearly with the BET surface area, suggesting that the charge accumulation is controlled primarily by the surface area development. A further analysis of the electrochemical behaviour in different electrolytic media—aqueous and organic—shows that an adequate pore size is more important than a high surface area in order to obtain high values of capacitance. Theoretical values of volumetric capacitance could be evaluated without considering the size of ions, which is always uncertain in solution, and compared with the experimental data as a function of the pore width. The efficiency of pore filling, i.e., of double layer formation, is optimal when the pore size is around 0.7 nm in aqueous media and 0.8 nm in organic electrolyte. A study of the performance of the positive and negative electrodes during the charge/discharge of the capacitor, reveals an additional pseudo-faradaic contribution due to oxygenated functionalities within the working potential window of the negative electrode. This effect is more pronounced for the ACs series obtained at 700 °C, because of their higher oxygen content.     

Graphene nanosheets as electrode material for electric double-layer capacitors

Graphene nanosheets (GNSs) with narrow mesopore distribution around 4 nm were mass-produced from natural graphite via the oxidation and rapid heating processes. The effects of oxidant addition on the morphology, structure and electrochemical performance of GNSs as electrode materials for electric double-layer capacitor (EDLC) were systematically investigated. The electrochemical properties of EDLC were influenced by the specific surface area, pore characteristics, layer stacking and oxygen-containing functional group contents of electrode materials. Deeper oxidation makes graphite possess both higher specific surface area and more graphene edges, which are favorable for the enhancement of capacitive performance of EDLC. The electrodes with freestanding graphene nanosheets prepared by coating method exhibited good rate capability and reversibility at high scan rates (to 250 mV s⁻¹) in electrochemical performances. GNS electrode with specific surface area of 524 m² g⁻¹ maintained a stable specific capacitance of 150 F g⁻¹ under specific current of 0.1 A g⁻¹ for 500 cycles of charge/discharge.     

Nitrogen-containing microporous carbons prepared from anionic surfactant-melamine/formaldehyde composites

Nitrogen-containing microporous carbons have been synthesized by the carbonization of anionic surfactant-melamine/formaldehyde (MF) composites, which were themselves formed by an electrostatic organic-organic interaction. The carbons prepared from sodium dioctyl sulfosuccinate-MF and sodium dodecyl sulfate-MF mixtures have high surface area of 464 and 539 m² g⁻¹, respectively. The N/C molar ratios of the carbons are 0.11. The resultant carbons showed capacitances higher than 200 F g⁻¹ in an acidic solution of 1 M H₂SO₄ at a scan rate of 1 mV s⁻¹.     

Electrode properties of a double layer capacitor of nano-structured graphite produced by ball milling under a hydrogen atmosphere

Nano-structural graphite prepared by ball milling under H₂ or Ar atmosphere was studied as an electrode for electric double layer capacitors (EDLCs) by means of a conventional 2-electrode galvanostatic method. Especially, the product prepared under H₂ atmosphere using zirconia balls revealed 500 m² g⁻¹ surface area and showed 12 F g⁻¹ specific capacitance, which was comparable to that of an activated carbon with large specific surface area of 3000 m² g⁻¹ examined as a reference. A proper condition of the milling time is rather a shorter time than ∼8 h, where the graphitic feature is remained in the ball milled product. On the other hand, for the sample prepared by using steel balls, the specific capacitance per surface area was several hundreds times smaller than the others, indicating that the small amount of Fe contamination during milling played a negative role for the EDLC properties.     

Effect of activation time on the properties of activated carbons prepared by microwave-assisted activation for electric double layer capacitors

Activated carbons (ACs) were prepared by microwave-assisted heat treatment of petroleum coke with KOH as activation agent, and characterized by infrared spectroscopy and nitrogen adsorption technique with the aim of studying the effect of activation time on the properties of ACs for electrodes in electric double layer capacitors (EDLCs). The electrochemical properties of AC electrodes in EDLCs were studied by cyclic voltammetry, constant current charge-discharge and electrochemical impedance spectroscopy. The results show that the specific surface area (S_BET) and total pore volume of ACs goes through a maximum as the activation time increases. At 35 min of the activation time, the as-made AC (denoted as AC-35) has a S_BET of 2312 m²/g. With AC-35 as the electrode, its specific capacitance in EDLC at a current density of 50 mA/g can reach 342.8 F/g, and remains at 245.6 F/g even after 800 cycles while the energy density of the capacitor remains at 8.0 Wh/kg. The results have demonstrated that the microwave-assisted heat treatment is an efficient approach to the preparation of ACs with high performance for EDLCs.     

High capacitance properties of polyaniline by electrochemical deposition on a porous carbon substrate

Electrochemical deposition of polyaniline (PANI) is carried out on a porous carbon substrate for supercapacitor studies. The effect of substrate is studied by comparing the results obtained using platinum, stainless steel and porous carbon substrates. PANI deposited at 100 mV s⁻¹ sweep rate by potentiodynamic technique on porous carbon substrate is found to possess superior capacitance properties. Experimental variables, namely, concentrations of aniline monomer and H₂SO₄ supporting electrolyte are varied and arrived at the optimum concentrations to obtain a maximum capacitance of PANI. Low concentrations of both aniline and H₂SO₄, which produce PANI at low rates, are desirable. The PANI deposits prepared under these conditions possess network morphology of nanofibrils. Capacitance values as high as 1600 F g⁻¹ are obtained and PANI coated carbon electrodes facilitate charge-discharge current densities as high as 45 mA cm⁻² (19.8 A g⁻¹). Electrodes are found to be fairly stable over a long cycle-life, although there is some capacitance loss during the initial stages of cycling.     

Preparation of functionalized graphene sheets by a low-temperature thermal exfoliation approach and their electrochemical supercapacitive behaviors

Two kinds of functionalized graphene sheets were produced by thermal exfoliation of graphite oxide. The first kind of functionalized graphene sheets was obtained by thermal exfoliation of graphite oxide at low temperature in air. The second kind was prepared by carbonization of the first kind of functionalized graphene sheets at higher temperature in N₂. Scanning electron microscopy images show that both two kinds of samples possess nanoporous structures. The results of N₂ adsorption-desorption analysis indicate that both of two kinds of samples have high BET surface areas. Moreover, the second kind of functionalized graphene sheets has a relatively higher BET surface area. The results of electrochemical tests is as follows: the specific capacitance values of the first kind of functionalized graphene sheets in aqueous KOH electrolyte are about 230 F g⁻¹; the specific capacitance values of the second kind of functionalized graphene sheets with higher BET surface areas are only about 100 F g⁻¹; however, compared with the first kind of functionalized graphene sheets, the second kind has a higher capacitance retention at large current density because of its good conductive behaviors; furthermore, in non-aqueous EC/DEC electrolyte, the specific capacitance values of the first kind sample and the second kind sample are about 73 F g⁻¹ and 36 F g⁻¹, respectively.     

Activated carbon fiber cloths as electrodes for high performance electric double layer capacitors

Activated carbon fiber cloth (ACFC) electrodes with high double layer capacitance and good rate capability were prepared from polyacrylonitrile (PAN) fabrics by optimizing the carbonization temperature prior to CO₂ activation. The carbonization temperature has a marked effect on both the pore structure and the electrochemical performances of the ACFCs. Moderate carbonization at 600 °C results in higher specific surface area and larger pore size, and hence higher capacitance and better rate capability. The specific capacitance of the ACFCs in 6 mol L⁻¹ KOH aqueous solution can be as high as 208 F g⁻¹. It remains 129 F g⁻¹ as the current density increases to 10 000 mA g⁻¹.     

Optimisation of supercapacitors using carbons with controlled nanotexture and nitrogen content

In order to optimize the performance of supercapacitors, the capacitance of the carbon materials used as electrodes was strictly related to their pores size and also to their redox properties. Well-sized carbons have been elaborated through a template technique using mesoporous silica. For a series of template carbons, a perfect linear dependence has been found for the capacitance values versus the micropore volume determined by CO₂ adsorption. The redox properties of carbons were enhanced by substituting nitrogen for carbon up to ca. 7 wt.%. For carbons with similar nanotextural characteristics, the electrochemical measurements showed a proportional increase of the specific capacitance with the nitrogen content in acidic electrolyte. For an activated carbon from polyacrylonitrile with a specific surface area of only 800 m² g⁻¹, but with a nitrogen content of 7 wt.%, the capacitance reaches 160 F g⁻¹, with very little fading during cycling.     

Nanosized α-LiFeO2 as electrochemical supercapacitor electrode in neutral sulfate electrolytes

In this work we have explored the electrochemical properties of two lithiated iron oxide powders for supercapacitor purposes. These samples mainly consisted of α-LiFeO₂ in nanosized or micrometric form. Electrolyte was an aqueous 0.5 M Li₂SO₄ solution and voltage range studied was between 0 and −0.7 V vs. a Ag/AgCl reference electrode. As expected, electrochemical performance was dependent on the particle size. When electrolyte was deaerated a stable capacitance of ≈50 F g⁻¹ is provided by the nanosized sample for several hundred cycles. Other sulfate based salts (Na₂SO₄, K₂SO₄, Cs₂SO₄) were investigated as electrolytes but only Li₂SO₄ leads to a stable capacitance upon cycling, probably due to lithium intercalation. An hybrid cell consisting of this sample and MnO₂ as negative and positive electrodes, respectively, delivered 0.3 F cm⁻² (10 F g⁻¹). Although these values are lower than reported for other aqueous hybrid cell, α-LiFeO₂/MnO₂ asymmetric capacitor is interesting from both, an economic and an environmental point of view.     

Effect of mesoporosity on specific capacitance of carbons

The study compares the structural and electrochemical properties of 12 porous carbons based on phenolic resins, using both aqueous (H₂SO₄) and aprotic ((C₂H₅)₄NBF₄ in acetonitrile) electrolytes. It appears that they fit into the general pattern observed for other carbons. The present carbons have micropore volumes varying between 0.29 and 0.66 cm³ g⁻¹ and average pore widths L_o between 0.62 and 1.23 nm. Five samples are exclusively microporous, whereas seven also display a relatively important mesoporosity. This allows a direct comparison between pairs of carbons with similar micropore systems, with and without mesopores, in order to assess the role of mesoporosity in the electrochemical properties. It appears that mesopores have only a limited influence on the decrease in capacitance at high current density as opposed to earlier assumptions.