丁苯胶乳对固井水泥石性能的影响

针对油田中后期开发面临的固井水泥环受腐蚀、脆性破裂的问题,采用水泥石抗腐蚀性分析、试件抗压和抗折强度实验,对胶乳改善水泥石的抗腐蚀性和韧性进行了研究,分析了胶乳改善水泥石抗腐蚀性和韧性的机理.结果表明,胶乳水泥石比普通水泥石抗腐蚀能力明显提高;随着水泥石中胶乳加量增加,水泥石的脆性系数逐渐减小,抗折强度逐渐增大,韧性增强.m(胶乳)∶ m(水泥)在1∶ 10～1.5∶ 10时,水泥石的致密程度最高,渗透率最小.     

钢渣矿渣复合掺合料对水泥浆体性能的影响

主要研究单掺钢渣以及钢渣与矿渣复合后对水泥浆体各项物理力学性能的影响.结果表明,钢渣掺入水泥中可以改善水泥浆体的流动性.钢渣与矿渣复合的比例约在2:3,总掺量为50%时,水泥硬化浆体各龄期抗压强度均有较大幅度的提高.说明钢渣与矿渣复掺,能起到相互激发、相互活化的作用.     

DEVELOPING A NEW GENERATION OF HIGH PERFORMANCE COMPOSITE CEMENT

This paper proposed a new generation of high performance composite cement which is designed according to the optimization of composition and structure of cement paste and is manufactured by blending the different components with special composite techniques. Each of these components has its different special property, and should be compatible with each other, and match each other,and the properties of them are complementary mutually. At present, such kind of high performance composde cement can be manufactured with high reactivity cement clinker, ground granulated blast—furnace slag, high grade fly ash, silica fume etc..     

MTC固井技术在中原油田的现成应用

泥浆转化为泥浆（Mud-To-Cement,简称MTC）技术是利用钻井液的降失水性和悬浮性,通过加入廉价的高炉水淬矿渣（BFS)和激活剂（BAS）,将钻井液转化为完全可以与油井水泥浆相媲美的固井液。固井作业中,因常规水泥与钻井液难以相容,造成固井水泥污染,严重影响固井质量。设计密度为1．50－1．60g/cm^2泥浆固井液体系,该体系以矿渣为水化材料,再加入激活剂,通过室内和现场应用,结果表明,该技术能提高固井质量,降低固井成本。在中原油田MTC固井技术首先在钻井三公司桥57井等10口井的中完固井中获得了成功现场应用,取得良好的经济效益和社会效益,并推广应用。     

二水石膏沸渣胶结材水化、硬化的研究

通过x射线衍射分析,孔结构分析,并结合宏观试验结果,分析了二水石膏沸渣胶结材水化与凝结硬化,并对外加剂、养护制度对材性的影响及耐水性提高的原因进行了阐述。     

早强剂对掺硅灰的水泥砂浆强度与结构影响的研究

探讨了不同早强剂对掺硅灰的水泥砂浆强度及微观结构的影响.结果表明：掺入不同的早强剂均可提高掺硅灰的水泥砂浆早期强度,且对其1 d抗压强度的增强效果优于3 d.其中掺入适量的硫酸钠可迅速生成大量的钙矾石晶体,提高水泥砂浆的密实度,同时促进了硅灰的火山灰反应,明显提高了掺硅灰的水泥砂浆的早期强度,但早强剂对掺硅灰的水泥砂浆后期强度影响不大.3种早强剂对掺硅灰的水泥砂浆早期强度增强作用从大到小的顺序依次为硫酸钠、氯化钙、三乙醇胺,其中硫酸钠掺量为3%时增强作用最佳.     

碱矿渣水泥复合激发剂的研究

以试验研究结果提出了强碱 硫酸盐 铝酸盐系统可以作为碱矿渣水泥的复合激发剂，其激发效果较单组分激发剂为好。并能够以较简单的方式加以实现，为碱矿渣水泥研制探索出一条新路。     

钛渣与矿渣对水泥修补砂浆性能的影响

研究了在相同水灰比下,单掺或双掺钛渣和矿渣掺合料对水泥修补砂浆流动性、强度的影响,并与水泥修补砂浆进行了比较.结果表明,与纯水泥修补砂浆相比,钛渣、矿渣等量取代水泥能改善修补砂浆的流动性;双掺钛渣和矿渣能显著改善修补砂浆的流动性,提高修补砂浆的中后期强度与耐久性.     

外加剂对水泥浆滤液组成的影响

研究了G级油井水泥及掺入外加剂时水泥浆滤液的离子成份和含量。考察了水泥浆滤液与地层水和泥浆滤液的配伍性。通过对含有外加剂水泥浆滤液组成的分析,提出了一种减少滤液中的有害离子(Ca~(++),Mg~(++),SO_4~-,OH~-等)浓度的新途径。     

煤粉燃烧率的计算及未燃煤粉的行为

采用数学模型对风口回旋区煤粉燃烧率进行了计算，对影响它的因素进行了讨论，并对未燃煤粉的行为作了分析。     

INVESTIGATIONS ON THE INTERFACIAL ZONE BETWEEN AGGREGATE AND PORTLAND SLAG CEMENT PASTE

The composition and structure of the interfacial zone be-tween aggregate and portland slag cement paste as well as the orienta-tion coefficient of portlandite(I_CH) have been studied by means ofXRD and SEM. The results show that the main components in the in-terfacial zone are C-S-H gel, portlandite and AFt as well as unhy-drated clinder particles. Compared with portland cement, there aremore C-S-H gel and less portlandite in the zone and the portlanditecrystallizes badly with lower I_CH in a narrower region. Afer adding5.0% silica fume to the cement, the orientation of portlandite in thezone disappears; afer 90d, the bond strength between # 425 portlandslag cement paste and aggregate approximately attains that between #525 portland ciment paste and aggregate.     

掺矿渣微粉的地面自流平砂浆性能研究

研究了矿渣微粉掺入水泥基自流平地坪砂浆中替代双飞粉后砂浆的各项性能。结果表明,随着矿渣微粉取代双飞粉比例的增加,强度逐渐增强,完全取代时达到最大。同时矿渣微粉的比表面积越大,矿渣的活性发挥越好。而且加入碱性激发剂对矿渣微粉水化活性进行激发,使矿渣微粉的水化活性充分发挥。     

矿渣微粉颗粒群分布及形貌对水泥性能的影响

通过扫描电镜 (SEM)和激光粒度分析仪 (L PS)研究了球磨、气流磨、振动磨所制备矿粉的形貌与粒度分布。结果表明 :气流磨所加工的矿粉粒度大小最均匀 ;球磨机所加工的矿粉颗粒尺寸分布最宽 ;振动磨所加工的矿粉颗粒大多呈圆形 ,表面最光滑。研究同时指出 :在矿粉表面积相近并超过 5 10 m2 / kg时 ,利用矿粉等量取代 5 0 %的硅酸盐水泥 ,其水泥砂浆强度和流动性都与矿粉的颗粒分布有关 ,而矿粉颗粒表面的特性影响并不显著。     

用面元法预报船舶螺旋桨的水动力性能

利用基于速度势煌低介面元法预报船舶螺旋浆的不动力性能,文中采用了计算较为简捷的关于扰动速度势的基本积分微分方程,并采用双曲面形状的面元以消除面元间的缝隙,Newton-Raphson[迭代过程被用来在浆叶随边满足压力Kutta条件,使浆叶上下表面的压力良好的一致性,在计算面元的影响系数时,应用了Morino导出的解析计算公式,加快了数值计算的速度,为避免数值导中的奇异性,用Yanagizawa方法求得物体表面上的速度分布,最后用本文方法预报了普通浆和大侧斜浆并与实验数据及其它计算结果进行了比较分析。     

富氧喷煤的操作线分析

首先提出了一种适宜于分析富氧喷煤工艺的高温区热平衡计算法，然后又将其引入到操作线中，最后结合实例运用操作线分析了富氧喷煤后焦比的变化及其置换比。     

利用铜尾矿烧制水泥熟料的技术研究

利用给定铜尾矿在系统分析的基础上,掺加其它一些原料,在实验室烧制高标号水泥熟料。     

碳化养护对冶金渣-熟石灰砂浆性质的影响

主要研究了碳化养护对冶金渣-熟石灰（SmS-SL）砂浆性质的影响,并通过XRD、真孔隙率和DTA/TG研究了影响机理和SmS-SL砂浆的环保效果.实验结果表明：碳化养护可提升SmS-SL砂浆的强度,改善它的体积稳定性和安定性.随着复合微粉中钢渣比例的提升,碳化养护对SmS-SL砂浆的增强效果逐渐提升,而对体积稳定性的改善效果却逐渐减弱.以钢渣为原料的SmS-SL砂浆的环保效果较为显著,其钢渣利用率达到27.8％,固碳率达到6.4％.     

含矿渣粉复合胶凝材料抗硫酸盐性能研究

采用快速试验方法研究了矿渣粉复合胶凝材料的抗硫酸盐性能,探讨了矿渣粉掺量和细度对复合胶凝材料抗硫酸盐性能的影响。研究结果表明,随着矿渣粉掺量的增加,复合胶凝材料的抗硫酸盐性能均不同程度地得到提高：矿渣粉细度的增加,有利于提高复合胶凝材料的抗硫酸盐性能。     

三轴应力作用下化学侵蚀对砂浆力学性能的影响

开展了不同水化学腐蚀下砂浆试样的常规三轴压缩试验,分析了溶液pH值、浓度及水化学成分对试样的腐蚀程度及微细观结构的影响效应,探讨了砂浆试样的水化学腐蚀机理,并进一步对比分析了不同水化学作用对砂浆物理力学参数的影响规律。基于化学腐蚀后试样产生的次生孔隙率,建立了新的损伤参量来定量描述试样物理力学性质随水化学损伤的演化过程。     

APPLICATION OF SLAG HIGH PERFORMANCE CONCRETE (SHPC) IN A CAR PARKING BUILDING

Using ground granulated blast furnace slag as the active stuff of high performance concrete (HPC) , the C60 SHPC was prepared. The behaviour of the C60 SHPC and its application in the Car Parking Building of Beijing Capital International Airport were described. Also, the manufacturing techniques of reducing cement consumption, lowering hydratimi heat ,minimizing shrinkage cracks and improving durability of the C60 SH-PC were discussed.