Lean reduction of NO by C3H6 over Ag/alumina derived from Al2O3, AlOOH and Al(OH)3

The effectiveness of Ag/Al₂O₃ catalyst depends greatly on the alumina source used for preparation. A series of alumina-supported catalysts derived from AlOOH, Al₂O₃, and Al(OH)₃ was studied by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), ultraviolet–visible (UV–vis) spectroscopy, diffuse reflectance infrared Fourier transform (DRIFT) spectroscopy, O₂, NO + O₂-temperature programmed desorption (TPD), H₂-temperature programmed reduction (TPR), thermal gravimetric analysis (TGA) and activity test, with a focus on the correlation between their redox properties and catalytic behavior towards C₃H₆-selective catalytic reduction (SCR) of NO reaction. The best SCR activity along with a moderated C₃H₆ conversion was achieved over Ag/Al₂O₃ (I) employing AlOOH source. The high density of Ag–O–Al species in Ag/Al₂O₃ (I) is deemed to be crucial for NO selective reduction into N₂. By contrast, a high C₃H₆ conversion simultaneously with a moderate N₂ yield was observed over Ag/Al₂O₃ (II) prepared from a γ-Al₂O₃ source. The larger particles of Ag_mO (m > 2) crystallites were believed to facilitate the propene oxidation therefore leading to a scarcity of reductant for SCR of NO. An amorphous Ag/Al₂O₃ (III) was obtained via employing a Al(OH)₃ source and 500 °C calcination exhibiting a poor SCR performance similar to that for Ag-free Al₂O₃ (I). A subsequent calcination of Ag/Al₂O₃ (III) at 800 °C led to the generation of Ag/Al₂O₃ (IV) catalyst yielding a significant enhancement in both N₂ yield and C₃H₆ conversion, which was attributed to the appearance of γ-phase structure and an increase in surface area. Further thermo treatment at 950 °C for the preparation of Ag/Al₂O₃ (V) accelerated the sintering of Ag clusters resulting in a severe unselective combustion, which competes with SCR of NO reaction. In view of the transient studies, the redox properties of the prepared catalysts were investigated showing an oxidation capability of Ag/Al₂O₃ (II and V) > Ag/Al₂O₃ (IV) > Ag/Al₂O₃ (I) > Ag/Al₂O₃ (III) and Al₂O₃ (I). The formation of nitrate species is an important step for the deNO_x process, which can be promoted by increasing O₂ feed concentration as evidenced by NO + O₂-TPD study for Ag/Al₂O₃ (I), achieving a better catalytic performance.     

Selective catalytic reduction of NO by C3H8 over CoOx/Al2O3: An investigation of structure–activity relationships

A series of CoO_x/Al₂O₃ catalysts was prepared, characterized, and applied for the selective catalytic reduction (SCR) of NO by C₃H₈. The results of XRD, UV–vis, IR, Far-IR and ESR characterizations of the catalysts suggest that the predominant oxidation state of cobalt species is +2 for the catalysts with low cobalt loading (≤2 mol%) and for the catalysts with 4 mol% cobalt loading prepared by sol–gel and co-precipitation. Co₃O₄ crystallites or agglomerates are the predominant species in the catalysts with high cobalt loading prepared by incipient wetness impregnation and solid dispersion. An optimized CoO_x/Al₂O₃ catalyst shows high activity in SCR of NO by C₃H₈ (100% conversion of NO at 723 K, GHSV: 10,000 h⁻¹). The activity of the selective catalytic reduction of NO by C₃H₈ increases with the increase of cobalt–alumina interactions in the catalysts. The influences of cobalt loading and catalyst preparation method on the catalytic performance suggest that tiny CoAl₂O₄ crystallites highly dispersed on alumina are responsible for the efficient catalytic reduction of NO, whereas Co₃O₄ crystallites catalyze the combustion of C₃H₈ only.     

A comparative study of Ag/Al2O3 and Cu/Al2O3 catalysts for the selective catalytic reduction of NO by C3H6

The selective catalytic reduction (SCR) of NO by C₃H₆ in excess oxygen was evaluated and compared over Ag/Al₂O₃ and Cu/Al₂O₃ catalysts. Ag/Al₂O₃ showed a high activity for NO reduction. However, Cu/Al₂O₃ showed a high activity for C₃H₆ oxidation. The partial oxidation of C₃H₆ gave surface enolic species and acetate species on the Ag/Al₂O₃, but only an acetate species was clearly observed on the Cu/Al₂O₃. The enolic species is a more active intermediate towards NO + O₂ to yield—NCO species than the acetate species on the Ag/Al₂O₃ catalyst. The Ag and Cu metal loadings and phase changes on Al₂O₃ support can affect the activity and selectivity of Ag/Al₂O₃ and Cu/Al₂O₃ catalysts, but the formation of enolic species is the main reason why the activity of the Ag/Al₂O₃ catalyst for NO reduction is higher than that of the Cu/Al₂O₃ catalyst.     

The effect of hydrogen on the selective catalytic reduction of NO in excess oxygen over Ag/Al2O3

The selective catalytic reduction (SCR) of nitrogen oxides (NO_x) by propane in the presence of H₂ on sol–gel prepared Ag/Al₂O₃ catalysts (0.5–5 wt.% Ag) was investigated. It was confirmed that hydrocarbon-assisted SCR of NO_x is remarkably enhanced by co-feeding hydrogen to a lean exhaust gas mixture (λ>1), attaining considerable activity within a wide temperature window (470–825 K). The samples had marginal activity at 575 K without co-fed H₂, but achieved up to 60% NO_x conversion in the presence of H₂ at a space velocity of 30,000 h⁻¹. NO₂ as NO_x feed component is not converted to N₂ by C₃H₈ to a substantial extent under lean conditions. This points to an activation route of NO through direct conversion to adsorbed nitrite/nitrate or to a dissociation of NO over Ag⁰, formed through short-term reduction by H₂. The nature of Ag species was characterized by X-ray diffraction, temperature-programmed reduction, pulse thermoanalytical measurements, electron microscopy and FTIR spectroscopy. It could be shown that Ag₂O nano-sized clusters are predominantly present on all samples, whereas formation of silver aluminate could not be confirmed. Nano-sized Ag₂O clusters can reversibly be reduced/reoxidized by H₂. A silver loading higher than 2 wt.% leads to a part of Ag₂O particles, which are thermally decomposed during calcination at 800 K or higher. The catalytic role of this metallic silver is still unclear. Formal kinetic analysis of catalytic data revealed that the activation energy of the overall reaction is significantly lowered in the presence of H₂. The presence of water does not change the activation energy. It is concluded that hydrogen reduces the nano-sized Ag₂O clusters to Ag⁰ on a short-term scale. Zero-valent silver promotes a dissociation pathway of NO_x conversion. The fact that more oxidized ad-species (nitrite/nitrate) are observed in the presence of H₂ is attributed to a dissociative activation of gas-phase oxygen on Ag⁰.     

Enhanced activity of metal oxide-doped Ga2O3–Al2O3 for NO reduction by propene

Effect of additives, In₂O₃, SnO₂, CoO, CuO and Ag, on the catalytic performance of Ga₂O₃–Al₂O₃ prepared by sol–gel method for the selective reduction of NO with propene in the presence of oxygen was studied. As for the reaction in the absence of H₂O, CoO, CuO and Ag showed good additive effect. When H₂O was added to the reaction gas, the activity of CoO-, CuO- and Ag-doped Ga₂O₃–Al₂O₃ was depressed considerably, while an intensifying effect of H₂O was observed for In₂O₃- and SnO₂-doped Ga₂O₃–Al₂O₃. Of several metal oxide additives, In₂O₃-doped Ga₂O₃–Al₂O₃ showed the highest activity for NO reduction by propene in the presence of H₂O. Kinetic studies on NO reduction over In₂O₃–Ga₂O₃–Al₂O₃ revealed that the rate-determining step in the absence of H₂O is the reaction of NO₂ formed on Ga₂O₃–Al₂O₃ with C₃H₆-derived species, whereas that in the presence of H₂O is the formation of C₃H₆-derived species. We presumed the reason for the promotional effect of H₂O as follows: the rate for the formation of C₃H₆-derived species in the presence of H₂O is sufficiently fast compared with that for the reaction of NO₂ with C₃H₆-derived species in the absence of H₂O. Although the retarding effect of SO₂ on the activity was observed for all of the catalysts, SnO₂–Ga₂O₃–Al₂O₃ showed still relatively high activity in the lower temperature region.     

Effect of hydrogen on reaction intermediates in the selective catalytic reduction of NOx by C3H6

Selective catalytic reduction of NO_x by C₃H₆ in the presence of H₂ over Ag/Al₂O₃ was investigated using in situ DRIFTS and GC–MS measurements. The addition of H₂ promoted the partial oxidation of C₃H₆ to enolic species, the formation of –NCO and the reactions of enolic species and –NCO with NO_x on Ag/Al₂O₃ surface at low temperatures. Based on the results, we proposed reaction mechanism to explain the promotional effect of H₂ on the SCR of NO_x by C₃H₆ over Ag/Al₂O₃ catalyst.     

The effect of oxygen concentration on the reduction of NO with propylene over CuO/γ-Al2O3

The effect of oxygen concentration on the pulse and steady-state selective catalytic reduction (SCR) of NO with C₃H₆ over CuO/γ-Al₂O₃ has been studied by infrared spectroscopy (IR) coupled with mass spectroscopy studies. IR studies revealed that the pulse SCR occurred via (i) the oxidation of Cu⁰/Cu⁺ to Cu²⁺ by NO and O₂, (ii) the co-adsorption of NO/NO₂/O₂ to produce Cu²⁺(NO₃⁻)₂, and (iii) the reaction of Cu²⁺(NO₃⁻)₂ with C₃H₆ to produce N₂, CO₂, and H₂O. Increasing the O₂/NO ratio from 25.0 to 83.4 promotes the formation of NO₂ from gas phase oxidation of NO, resulting in a reactant mixture of NO/NO₂/O₂. This reactant mixture allows the formation of Cu²⁺(NO₃⁻)₂ and its reaction with the C₃H₆ to occur at a higher rate with a higher selectivity toward N₂ than the low O₂/NO flow. Both the high and low O₂/NO steady-state SCR reactions follow the same pathway, proceeding via adsorbed C₃H₇---NO₂, C₃H₇---ONO, CH₃COO⁻, Cu⁰---CN, and Cu⁺---NCO intermediates toward N₂, CO₂, and H₂O products. High O₂ concentration in the high O₂/NO SCR accelerates both the formation and destruction of adsorbates, resulting in their intensities similar to the low O₂/NO SCR at 523–698 K. High O₂ concentration in the reactant mixture resulted in a higher rate of destruction of the intermediates than low O₂ concentration at temperatures above 723 K.     

Evidence for the formation, isomerization and decomposition of organo-nitrite and -nitro species during the NOx reduction by C3H6 on Ag/Al2O3

The formation of organo-nitrite and -nitro species (R-ONO and R-NO₂) as intermediates during the selective catalytic reduction (SCR) of NO_x by C₃H₆ over Ag/Al₂O₃ was investigated by temperature-programmed desorption (TPD) and in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS). The addition of KBr to Ag/Al₂O₃ catalyses the isomerization of R-NO₂ to R-ONO on KBr-Ag/Al₂O₃, which confirms the presence of R-NO₂ on Ag/Al₂O₃.     

Influence of metal oxides on the catalytic behavior of Au/Al2O3 for the selective reduction of NOx by hydrocarbons

The reduction of NO by propene in the presence of excess oxygen over mechanical mixtures of Au/Al₂O₃ with a bulk oxide has been investigated. The oxides studied were: Co₃O₄, Mn₂O₃, Cr₂O₃, CuO, Fe₂O₃, NiO, CeO₂, SnO₂, ZnO and V₂O₅. Under lean C₃H₆-SCR conditions, these oxides (with the exception of SnO₂) convert selectively NO to NO₂. When mechanically mixed with Au/Al₂O₃, the Mn₂O₃ and Co₃O₄ oxides and, to a much greater extent, CeO₂ act synergistically with this catalyst greatly enhancing its SCR performance. It was found that their synergistic action is not straightforwardly related to their activity for NO oxidation to NO₂. The exhibited catalytic synergy may be due to the operation of either remote control or a bifunctional mechanism. In the later case, the key intermediate must be a short-lived compound and not the NO₂ molecule in gas-phase.     

Influence of BaO on Pd/Al2O3-based catalysts in C2H4 and CO oxidation as well as in NO reduction

In this study, Pd/Al₂O₃ and Pd/BaO/Al₂O₃ metallic monoliths were used to investigate the effect of BaO in C₂H₄ and CO oxidation as well as in NO reduction. A FT-IR gas analyser was used to study the activity of the catalysts. Several activity experiments carried out with dissimilar feedstreams revealed that BaO enhances CO and C₂H₄ oxidation as well as NO reduction reactions in rich conditions. This effect is due to BaO, which causes a decrease in the ethene poisoning of palladium. In lean conditions BaO is present in the form of Ba(OH)₂ which reacts with oxidised NO releasing water. Therefore, NO was stored during the lean reaction.     

Catalytic oxidation of HCN over a 0.5% Pt/Al2O3 catalyst

The adsorption of HCN on, its catalytic oxidation with 6% O₂ over 0.5% Pt/Al₂O₃, and the subsequent oxidation of strongly bound chemisorbed species upon heating were investigated. The observed N-containing products were N₂O, NO and NO₂, and some residual adsorbed N-containing species were oxidized to NO and NO₂ during subsequent temperature programmed oxidation. Because N-atom balance could not be obtained after accounting for the quantities of each of these product species, we propose that N₂ and was formed. Both the HCN conversion and the selectivity towards different N-containing products depend strongly on the reaction temperature and the composition of the reactant gas mixture. In particular, total HCN conversion reaches 95% above 250 °C. Furthermore, the temperature of maximum HCN conversion to N₂O is located between 200 and 250 °C, while raising the reaction temperature increases the proportion of NO_x in the products. The co-feeding of H₂O and C₃H₆ had little, if any effect on the total HCN conversion, but C₃H₆ addition did increase the conversion to NO and decrease the conversion to NO₂, perhaps due to the competing presence of adsorbed fragments of reductive C₃H₆. Evidence is also presented that introduction of NO and NO₂ into the reactant gas mixture resulted in additional reaction pathways between these NO_x species and HCN that provide for lean-NO_x reduction coincident with HCN oxidation.     

Selective catalytic reduction of NO by hydrocarbons on Ga2O3/Al2O3 catalysts

Catalytic properties of supported gallium oxides have been examined for the selective reduction of NO by CH₄ in excess oxygen. The activity was greatly affected by the support; Ga₂O₃/Al₂O₃ (Al₂O₃ supported Ga₂O₃) and Ga₂O₃–Al₂O₃ mixed oxide exhibited high activity and selectivity as comparable to Ga-ZSM-5, while unsupported Ga₂O₃ and the other supported Ga₂O₃ were ineffective. For Ga₂O₃/Al₂O₃, the activity changed with Ga₂O₃ content, and was highest at about 30 wt% Ga₂O₃, which corresponds to a theoretical monolayer coverage. Gallium oxide highly dispersed on Al₂O₃ is considered to be responsible for the high activity and selectivity. The reaction characteristics of Ga₂O₃/Al₂O₃ were studied and compared with Ga-ZSM-5 and Co-ZSM-5. Ga₂O₃/Al₂O₃ exhibited the highest activity and selectivity at high temperature. In addition, Ga₂O₃/Al₂O₃ showed higher tolerance against water than Ga-ZSM-5. C₃H₈ and C₃H₆ were also evaluated as reducing agents, and Ga₂O₃/Al₂O₃ showed higher activity than Ga-ZSM-5 above 723 K achieving almost complete reduction of NO to N₂.     

On the promotional effect of Pd on the propene-assisted decomposition of NO on chlorinated Ce0.68Zr0.32O2

The selective catalytic reduction (SCR) of NO_x assisted by propene is investigated on Pd/Ce_0.68Zr_0.32O₂ catalysts (Pd/CZ), and is compared, under identical experimental conditions, with that found on a Pd/SiO₂ reference catalyst. Physico-chemical characterisation of the studied catalysts along with their catalytic properties indicate that Pd is not fully reduced to metallic Pd for the Pd/CZ catalysts. This study shows that the incorporation of Pd to CZ greatly promotes the reduction of NO in the presence of C₃H₆. These catalysts display very stable deNO_x activity even in the presence of 1.7% water, the addition of which induces a reversible deactivation of about 10%. The much higher N₂ selectivity obtained on Pd/CZ suggests that the lean deNO_x mechanism occurring on these catalysts is different from that occurring on Pd⁰/SiO₂. A detailed mechanism is proposed for which CZ achieves both NO oxidation to NO₂ and NO decomposition to N₂, whereas PdO_x activates C₃H₆ via ad-NO₂ species, intermediately producing R-NO_x compounds that further decompose to NO and C_xH_yO_z. The role of the latter oxygenates is to reduce CZ to provide the catalytic sites responsible for NO decomposition. The proposed C₃H₆-assisted NO decomposition mechanism stresses the key role of NO₂, R-NO_x and C_xH_yO_z as intermediates of the SCR of NO_x by hydrocarbons.     

Mean field modelling of NOx storage on Pt/BaO/Al2O3

A mean field model, for storage and desorption of NO_x in a Pt/BaO/Al₂O₃ catalyst is developed using data from flow reactor experiments. This relatively complex system is divided into five smaller sub-systems and the model is divided into the following steps: (i) NO oxidation on Pt/Al₂O₃; (ii) NO oxidation on Pt/BaO/Al₂O₃; (iii) NO_x storage on BaO/Al₂O₃; (iv) NO_x storage on Pt/BaO/Al₂O₃ with thermal regeneration and (v) NO_x storage on Pt/BaO/Al₂O₃ with regeneration using C₃H₆. In this paper, we focus on the last sub-system. The kinetic model for NO_x storage on Pt/BaO/Al₂O₃ was constructed with kinetic parameters obtained from the NO oxidation model together with a NO_x storage model on BaO/Al₂O₃. This model was not sufficient to describe the NO_x storage experiments for the Pt/BaO/Al₂O₃, because the NO_x desorption in TPD experiments was larger for Pt/BaO/Al₂O₃, compared to BaO/Al₂O₃. The model was therefore modified by adding a reversible spill-over step. Further, the model was validated with additional experiments, which showed that NO significantly promoted desorption of NO_x from Pt/BaO/Al₂O₃. To this NO_x storage model, additional steps were added to describe the reduction by hydrocarbon in experiments with NO₂ and C₃H₆. The main reactions for continuous reduction of NO_x occurs on Pt by reactions between hydrocarbon species and NO in the model. The model is also able to describe the reduction phase, the storage and NO breakthrough peaks, observed in experiments.     

Surface properties and reactivity of Cu/γ-Al2O3 catalysts for NO reduction by C3H6: Influences of calcination temperatures and additives

The influences of calcination temperatures and additives for 10 wt.% Cu/γ-Al₂O₃ catalysts on the surface properties and reactivity for NO reduction by C₃H₆ in the presence of excess oxygen were investigated. The results of XRD and XPS show that the 10 wt.% Cu/γ-Al₂O₃ catalysts calcined below 973 K possess highly dispersed surface and bulk CuO phases. The 10 wt.% Cu/γ-Al₂O₃ and 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalysts calcined at 1073 K possess a CuAl₂O₄ phase with a spinel-type structure. In addition, the 10 wt.% La–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K possesses a bulk CuO phase. The result of NO reduction by C₃H₆ shows that the CuAl₂O₄ is a more active phase than the highly dispersed and bulk CuO phase. However, the 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K possesses significantly lower reactivity for NO reduction than the 10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K, although these catalysts possess the same CuAl₂O₄ phase. The low reactivity for NO reduction for 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K is attributed to the formation of less active CuAl₂O₄ phase with high aggregation and preferential promotion of C₃H₆ combustion to CO_x by MnO₂. The engine dynamometer test for NO reduction shows that the C₃H₆ is a more effective reducing agent for NO reduction than the C₂H₅OH. The maximum reactivity for NO reduction by C₃H₆ is reached when the NO/C₃H₆ ratio is one.     

The catalytic activity of FeOx/ZrO2 for the abatement of NO with propene in the presence of O2

FeO_x/ZrO₂ samples, prepared by impregnation with Fe(NO₃)₃, were characterised by means of DRS, XRD, FTIR, redox cycles and volumetric CO adsorption. Volumetric CO adsorption, combined with FTIR, showed that 45% of iron in the sample containing 2.8 Fe atoms nm⁻² was capable of forming iron carbonyls. DRS evidenced Fe₂O₃ on samples with Fe-content≥2.8 atoms nm⁻². The selective catalytic reduction of NO with C₃H₆ in the presence of O₂ was studied with a reactant mixture containing NO=4000 ppm, C₃H₆=4000 ppm, O₂=2%. The dependence on iron-content suggests that only isolated iron, prevailing in dilute FeO_x/ZrO₂, is active for NO reduction, whereas iron on the surface of small oxide particles, prevailing in concentrated FeO_x/ZrO₂, is active for C₃H₆ combustion.     

Total oxidation of propene and propane over gold–copper oxide on alumina catalysts: Comparison with Pt/Al2O3

Oxidation of propene and propane to CO₂ and H₂O has been studied over Au/Al₂O₃ and two different Au/CuO/Al₂O₃ (4 wt.% Au and 7.4 wt.% Au) catalysts and compared with the catalytic behaviour of Au/Co₃O₄/Al₂O₃ (4.1 wt.% Au) and Pt/Al₂O₃ (4.8 wt.% Pt) catalysts. The various characterization techniques employed (XRD, HRTEM, TPR and DR-UV–vis) revealed the presence of metallic gold, along with a highly dispersed CuO (6 wt.% CuO), or more crystalline CuO phase (12 wt.% CuO).

A higher CuO loading does not significantly influence the catalytic performance of the catalyst in propene oxidation, the gold loading appears to be more important. Moreover, it was found that 7.4Au/CuO/Al₂O₃ is almost as active as Pt/Al₂O₃, whereas Au/Co₃O₄/Al₂O₃ performs less than any of the CuO-containing gold-based catalysts.

The light-off temperature for C₃H₈ oxidation is significantly higher than for C₃H₆. For this reaction the particle size effect appears to prevail over the effect of gold loading. The most active catalysts are 4Au/CuO/Al₂O₃ (gold particles less than 3 nm) and 4Au/Co₃O₄/Al₂O₃ (gold particles less than 5 nm).     

The reduction phase in NOx storage catalysis: Effect of type of precious metal and reducing agent

The effect of different reducing agents (H₂, CO, C₃H₆ and C₃H₈) on the reduction of stored NO_x over PM/BaO/Al₂O₃ catalysts (PM = Pt, Pd or Rh) at 350, 250 and 150 °C was studied by the use of both NO₂-TPD and transient reactor experiments. With the aim of comparing the different reducing agents and precious metals, constant molar reduction capacity was used during the reduction period for samples with the same molar amount of precious metal. The results reveal that H₂ and CO have a relatively high NO_x reduction efficiency compared to C₃H₆ and especially C₃H₈ that does not show any NO_x reduction ability except at 350 °C over Pd/BaO/Al₂O₃. The type of precious metals affects the NO_x storage-reduction properties, where the Pd/BaO/Al₂O₃ catalyst shows both a high storage and a high reduction ability. The Rh/BaO/Al₂O₃ catalyst shows a high reduction ability but a relatively low NO_x storage capacity.     

Influence of the pre-treatment on the structure and reactivity of Ir/γ-Al2O3 catalysts in the selective reduction of nitric oxide by propene

The selective catalytic reduction (SCR) of nitric oxide by propene over Ir/Al₂O₃ under lean-burn conditions (1000 vpm NO, 2000 vpm C₃H₆, 500 vpm CO, 10 vol.% O₂) was studied. The activity was shown to be strongly enhanced after exposure of the catalyst at 600°C under the reaction mixture, irrespective of the oxidising or reducing pre-treatment. Simultaneously, the Ir dispersion decreased from 78 to 10%. The influence of each component of the reaction mixture on the activation process was examined. The presence of both CO and O₂ was found to be necessary to activate Ir/Al₂O₃ while NO would not be. In situ FT-IR results revealed that initially fully oxidised Ir particles partially reduced in the feed to form Ir⁰ reduced surface sites (νCO at 2060 cm⁻¹) which adsorbed CO up to 350–400°C. The activation under reactants was related to the formation of these sites. The presence of reduced (or partially reduced) Ir sites, possibly siting at the surface of IrO₂ particles and stabilised by CO adsorption, was proposed to be responsible for the SCR activity.     

A comparison study on non-thermal plasma-assisted catalytic reduction of NO by C3H6 at low temperatures between Ag/USY and Ag/Al2O3 catalysts

A comparison study was carried out on non-thermal plasma (NTP)-assisted selective catalytic reduction (SCR) of NO_x by propene over Ag/USY and Ag/Al₂O₃ catalysts. Ag/USY was almost inactive in thermal SCR while it showed obvious activities in NTP-assisted SCR at 100 °C–200 °C. Although the NO_x conversion over Ag/Al₂O₃ was also enhanced at 300 °C–400 °C by the assistance of NTP, it was ineffective below 250 °C. The intermediates over Ag/USY and Ag/Al₂O₃ were investigated using in situ DRIFTS method. It was found that key intermediates in HC-SCR, such as NCO, CN, oxygenates and some N-containing organic species were enriched after the assistance of NTP. The differences in the behaviors of above intermediates were not found between these two kinds of catalysts. However, some evidences suggested that different properties of the absorbed NO_x species resulted in the distinction of SCR reactions over Ag/USY and Ag/Al₂O₃. TPD profiles of Ag/Al₂O₃ showed that nitrates formed over the catalyst were quite stable at low temperatures, which might occupy the active sites and were unfavorable to SCR reactions. The nitrates over Ag/USY were unstable, among which the unidentate nitrate species is probably contributed to the SCR reactions at low temperatures.