Alumina coatings by plasma spraying of monosize sapphire particles

A series of plasma sprayed coatings of controlled microstructure was obtained by spraying three monosize sapphire powders using an axial injection torch in which the plasma gas composition and nozzle diameter were the only processing parameters varied. The effects of changes in these parameters on the coating splat morphology, porosity, angular crack distribution, and hardness are reported. The uniform, dense microstructure and the high hardness of 14 GPa (a level usually only associated with chromia thermal spray coatings) of the best alumina coatings resulted from using tightly controlled processing conditions and monodispersed precursor powders. The microstructural quality of plasma sprayed coatings and, hence, the coating properties can be improved significantly by minimizing variations in processing and raw material parameters. This paper originally appeared in Thermal Spray: Meeting the Challenges of the 21st Century; Proceedings of the 15th International Thermal Spray Conference, C. Coddet, Ed., ASM International, Materials Park, OH, 1998. This proceedings paper has been extensively reviewed according to the editorial policy of the Journal of Thermal Spray Technology.     

Nanostructured photocatalytic titania coatings formed by suspension plasma spraying

This paper describes formation of titanium dioxide coatings designed for photocatalytic applications, obtained by suspension plasma spraying (SPS), an alternative of the atmospheric plasma spraying (APS) technique in which the material feedstock is a suspension of the material to be sprayed. Two different TiO₂ powders were dispersed in distilled water and ethanol and injected in Ar-H₂ or Ar-H₂-He plasma under atmospheric conditions. Scanning electron microscopy (SEM) and x-ray diffraction (XRD) analyses were performed to study the microstructure of the titania coatings. Photocatalytic efficiency of the elaborated samples was evaluated from the conversion ratio of different air pollutants: nitrogen oxides (NOx) and sulfur dioxide (SO₂). The morphology and crystalline structure of the deposits depended mainly on the nature of the solvent (water or alcohol) used in the preparation of the slurries. Dense coatings were obtained starting from aqueous suspensions and porous deposits were elaborated by plasma spraying of a PC105 alcoholic suspension. A significant phase transformation from anatase to rutile occurred when ethanol was used as a solvent. Different photocatalytic performances were observed as a function of the nature of the liquid material feed-stock, the spraying parameters, and the nature of the pollutant. This article was originally published inBuilding on 100 Years of Success, Proceedings of the 2006 International Thermal Spray Conference (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, OH, 2006.     

Suspension plasma spraying of nanostructured WC-12Co coatings

Nanostructured WC-12% Co coatings were deposited by suspension plasma spraying of submicron feedstock powders, using an internal injection plasma torch. The liquid carrier used in this approach allows for controlled injection of much finer particles than in conventional thermal spraying, leading to thin coatings with a fine surface finish. A polyethylene-imine (PEI) dispersant was used to stabilize the colloidal suspension in an ethanol carrier. In-flight particle states were measured for a number of operating conditions of varying plasma gas flow rates, feed rates, and standoff distances and were related to the resulting microstructure, phase composition (EDS, SEM, XRD), and Vickers hardness. High in-flight particle velocities (>800 m/s) were generated, leading to dense coatings. It was observed that the coating quality was generally compromised by the high temperature and reactivity of the small particles. To compensate for this shortcoming, the suspension feed rate was adjusted, thereby varying the thermal load on the plasma. Results showed that a slightly larger agglomerate size, in conjunction with low particle jet temperatures, could somewhat limit the decomposition of WC into brittle W₂C/W₃C and amorphous cobalt containing binder phases. This article was originally published inBuilding on 100 Years of Success, Proceedings of the 2006 International Thermal Spray Conference (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, OH, 2006.     

Comparison of the photocatalytic behavior of TiO2 coatings elaborated by different thermal spraying processes

This paper proposes a comparative study on the microstructure and photocatalytic performances of titanium dioxide coatings elaborated by various thermal spraying methods (plasma spraying in atmospheric conditions, suspension plasma spraying, and high-velocity oxyfuel spraying). Agglomerated spray dried anatase TiO₂ powder was used as feedstock material for spraying. Morphology and microstructural characteristics of the coatings were studied mainly by scanning electron microscopy and x-ray diffraction. The photocatalytic behavior of the TiO₂-base surfaces was evaluated from the conversion rate of gaseous nitrogen oxides (NOx). It was found that the crystalline structure depended strongly on the technique of thermal spraying deposition. Moreover, a high amount of anatase was suitable for the photocatalytic degradation of the pollutants. Suspension plasma spraying has allowed retention of the original anatase phase and for very reactive TiO₂ surfaces to be obtained for the removal of nitrogen oxides. This article was originally published inBuilding on 100 Years of Success, Proceedings of the 2006 International Thermal Spray Conference (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, OH, 2006.     

Plasma spray synthesis from precursors: Progress, issues, and considerations

Precursor plasma spray synthesis is an innovative and rapid method for making functional oxide ceramic coatings by starting from solution precursors and directly producing inorganic films. This emerging method utilizes molecularly mixed precursor liquids, which essentially avoids the handling and selection of powders, opening up new avenues for developing compositionally complex functional oxide coatings. Precursor plasma spray also offers excellent opportunities for exploring the nonequilibrium phase evolution during plasma spraying of multicomponent oxides from inorganic precursors. Although there have been efforts in this area since the 1980s and early 1990s with the goal of synthesizing nanoparticles, only recently has the work progressed in the area of functional systems. At the Center for Thermal Spray Research an integrated investigative strategy has been used to explore the benefits and limits of this synthesis strategy. Water- and alcohol-based sol/solution precursors derived from various chemical synthesis methods were used as feedstocks to deposit thin/thick films of spherical and nanostructured coatings of yttrium aluminum garnet (YAG), yttrium iron garnet, lanthanum strontium manganate and Zr-substituted yttrium titanates, and compositions of Y₂O₃-Al₂O₃ and their microstructural space centered around stoichiometric YAG. A detailed discussion of the salient features of the radiofrequency induction plasma spraying approach, the results obtained in the investigations to develop various functional oxide coatings, and process issues and challenges are presented. This article was originally published inBuilding on 100 Years of Success: Proceedings of the 2006 International Thermal Spray Conference (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, OH, 2006.     

Microstructures and characterization of zirconia-yttria coatings formed in laser and hybrid spray process

Hybrid plasma spraying combined with yttrium-aluminum-garnet laser irradiation was studied to obtain optimum zirconia coatings for thermal barrier use. Zirconia coatings of approximately 150 μm thickness were formed on NiCrAlY bond coated steel substrates both by means of conventional plasma spraying and hybrid plasma spraying under a variety of conditions. Post-laser irradiation was also conducted on the plasma as-sprayed coating. The microstructure of each coating was studied and, for some representative coatings, thermal barrier properties were evaluated by hot erosion and hot oxidation tests. With hybrid spraying, performed under optimum conditions, it was found that a microstructure with appropriate partial densification and without connected porosity was formed and that cracks, which are generally produced in the post-laser irradiation treatment, were completely inhibited. In addition, hybrid spraying formed a smooth coating surface. These microstructural changes resulted in improved coating properties with regard to hardness, high temperature erosion resistance, and oxidation resistance. This paper originally appeared in Thermal Spray: Meeting the Challenges of the 21st Century; Proceedings of the 15th International Thermal Spray Conference, C. Coddet, Ed., ASM International, Materials Park, OH, 1998. This proceedings paper has been extensively reviewed according to the editorial policy of the Journal of Thermal Spray Technology.     

Effect of Powder Injection Location on Ceramic Coatings Properties When Using Plasma Spray

The effect of powder injecting location of the plasma spraying on spraying properties was studied. Three different powder-injecting methods were applied in the experiment. In the first method, the particles were axially injected into the plasma flow from the cathode tip. In the second method, the particles were radially injected into the plasma flow just downstream of the anode arc root inside the anode nozzle. In the third method, the particles were radially injected into the plasma jet at the nozzle exit. The alumina particles with a mean diameter of 20 μm were used to deposit coatings. Spraying properties, such as the deposition efficiency, the melting rate of the powder particles, and the coating quality were investigated. The results show that the spraying with axial particle injecting can heat and melt the powder particles more effectively, produce coatings with better quality, and have higher deposition efficiency. This article is an invited paper selected from presentations at the 2007 International Thermal Spray Conference and has been expanded from the original presentation. It is simultaneously published in Global Coating Solutions, Proceedings of the 2007 International Thermal Spray Conference, Beijing, China, May 14-16, 2007, Basil R. Marple, Margaret M. Hyland, Yuk-Chiu Lau, Chang-Jiu Li, Rogerio S. Lima, and Ghislain Montavon, Ed., ASM International, Materials Park, OH, 2007.     

Liquid Precursor Plasma Spraying: Modeling the Interactions Between the Transient Plasma Jet and the Droplets

Plasma spraying using liquid feedstock makes it possible to produce thin coatings (<100 μm) with more refined microstructures than in conventional plasma spraying. However, the low density of the feedstock droplets makes them very sensitive to the instantaneous characteristics of the fluctuating plasma jet at the location where they are injected. In this study, the interactions between the fluctuating plasma jet and droplets are explored by using numerical simulations. The computations are based on a three-dimensional and time-dependent model of the plasma jet that couples the dynamic behaviour of the arc inside the torch and the plasma jet issuing from the plasma torch. The turbulence that develops in the jet flow issuing in air is modeled by a large Eddy simulation model that computes the largest structures of the flow which carry most of the energy and momentum. This article is an invited paper selected from presentations at the 2007 International Thermal Spray Conference and has been expanded from the original presentation. It is simultaneously published in Global Coating Solutions, Proceedings of the 2007 International Thermal Spray Conference, Beijing, China, May 14-16, 2007, Basil R. Marple, Margaret M. Hyland, Yuk-Chiu Lau, Chang-Jiu Li, Rogerio S. Lima, and Ghislain Montavon, Ed., ASM International, Materials Park, OH, 2007.     

Plasma sprayed cast iron coatings containing solid lubricant graphite and h-BN structure

Water-atomized cast iron powder of Fe-2.17 at.%C-9.93at.%Si-3.75at.%Al were deposited onto an aluminum alloy substrate by atmospheric direct current plasma spraying to improve its tribological properties. Preannealing of the cast iron powder allows the precipitation of considerable amounts of graphite structure in the powder. However, significant reduction in graphitized carbon in cast iron coatings is inevitable after plasma spraying in air atmosphere due to the in-flight burning and dissolution into molten iron droplets. Hexagonal boron nitride (h-BN) powders, which have excellent lubricating properties like graphite, were incorporated into the cast iron powder as a solid lubricant by the sintering process (1300°C) to obtain protective coatings with a low friction coefficient. The performance of each coating was evaluated using a ring-on-disk-type wear tester under a paraffin-based oil condition in an air atmosphere. A conventional cast iron liner, which had a flaky graphite embedded in the pearlitic matrix, was also tested under similar conditions for comparison. Sections of worn surfaces and debris were characterized, and the wear behavior of plasma-sprayed coatings was discussed. The original version of this paper was published in the CD ROM Thermal Spray Connects: Explore Its Surfacing Potential, International Thermal Spray Conference, sponsored by DVS, ASM International, and HW International Institute of Welding, Basel, Switzerland, May 2–4, 2005, DVS-Verlag GmbH, Düsseldorf, Germany.     

On the Role of Spraying Process on Microstructural, Mechanical, and Thermal Response of Alumina Coatings

Thermal spraying is a widely used technology for industrial applications to provide coatings that improve the surface characteristics. According to the specificities of processes (APS, VPS, flame, electric arc), any kind of material can be sprayed. Among materials, ceramic coatings present several interesting aspects such as wear resistance, corrosion protection as well as thermal or electrical insulation; particularly alumina coatings which appear as the most commonly used. From all spraying processes, atmospheric plasma spraying (APS) is a rather well-established process but some others can also be used with a lower economical impact such as the flame technology. The aim of this study was to analyze the alumina coating properties according to the technology employed such as APS or wire flame spraying using the Rokide™ and the Master Jet^? guns. After micrographic analyses by SEM, physical and mechanical properties were measured considering the thermal conductivity and the hardness. This article is an invited paper selected from presentations at the 2007 International Thermal Spray Conference and has been expanded from the original presentation. It is simultaneously published in Global Coating Solutions, Proceedings of the 2007 International Thermal Spray Conference, Beijing, China, May 14-16, 2007, Basil R. Marple, Margaret M. Hyland, Yuk-Chiu Lau, Chang-Jiu Li, Rogerio S. Lima, and Ghislain Montavon, Ed., ASM International, Materials Park, OH, 2007.     

High-velocity oxyfuel reactive spraying of mechanically alloyed Ni-Ti-C powders

Recently, there has been considerable interest in producing cermet coatings with nanoscale carbide grains in the size range 50 to 500 nm. In this article, the production of nanoscale TiC grains in a Ni-based alloy matrix by reactive high-velocity oxyfuel (HVOF) spraying of metastable Ni-Ti-C powder is reported. Mechanical alloying of a Ni(Cr) prealloyed powder and Ti and C elemental powders was performed in a planar-type ball mill, and materials were characterized in detail using x-ray diffraction (XRD) and scanning electron micros-copy (SEM). Phase changes were correlated with milling time and other processing conditions. Results show that, by the selection of appropriate conditions, a metastable Ni-Ti-C powder could be obtained with the nominal composition 50wt.%Ni-40wt.%Ti-10wt.%C. Following sieving and classification, powder was produced with a particle size range of −38 to 8 μm, which is suitable for HVOF spraying. Coatings, approximately 250 μm thick, were deposited by HVOF spraying onto mild steel substrates, and the microstructures formed were investigated. XRD showed that a self-propagating high-temperature synthesis (SHS) reaction had occurred in the powder particles during spraying and that the principal phases present in the coating were TiC and a Ni-rich solid solution; small quantities of NiTi, TiO₂, and NiTiO₃ were also present. SEM revealed that the coatings had a characteristic, splatlike morphology and that TiC formed as a nanoscale dispersion, with a size range of ∼50 to 200 nm, within solidified splats. The microstructures of these reactively sprayed Ni-TiC coatings are briefly compared with those observed in HVOF-sprayed coatings deposited using prereacted SHS powder. The original version of this paper was published as part of the ASM Proceedings, Thermal Spray 2003: Advancing the Science and Applying the Technology, International Thermal Spray Conference (Orlando, FL), May 5–8, 2003, Basil R. Marple and Christian Moreau, Ed., ASM International, 2003.     

Manufacturing Process of Nanostructured Alumina Coatings by Suspension Plasma Spraying

This paper describes the formation process of nanostructured alumina coatings and the injection system obtained by suspension plasma spraying (SPS), an alternative to the atmospheric plasma spraying technique in which the material feedstock is a suspension of the nanopowder to be sprayed. The nanoscale alumina powders (d ≈ 20 nm) were dispersed in distilled water or ethanol and injected by a peristaltic pump into plasma under atmospheric conditions. Optical microscopy (OM), scanning electron microscopy (SEM), and x-ray diffraction (XRD) analyses were performed to study the microstructure of the nanostructured alumina coatings. The results showed that the nanoscale alumina powders in suspension were very easily adsorbed at the inner surface of injection, which caused the needle to jam. The rotation of the pump had a great effect on the suspension injection in the plasma. The very small resistance of the thin plasma boundary layer near the substrate can drastically decrease the impacting velocity of nanosize droplets. The concentration of suspension also has a significant influence on the distribution of the size of the droplet, the enthalpy needed for spraying suspension, and the roughness of the coating surface. The phase structures of alumina suspension coatings strongly depend on the plasma spraying distance. A significant nanostructured fine alumina coating was obtained in some areas when ethanol was used as a solvent. The microstructures of the coating were observed as a function of the solvent and the spraying parameters.     

3D Modeling of Transport Phenomena and the Injection of the Solution Droplets in the Solution Precursor Plasma Spraying

Solution precursor plasma spraying has been used to produce finely structured ceramic coatings with nano- and sub-micrometric features. This process involves the injection of a solution spray of ceramic salts into a DC plasma jet under atmospheric condition. During the process, the solvent vaporizes as the droplet travel downstream. Solid particles are finally formed due to the precipitation of the solute, and the particle are heated up and accelerated to the substrate to generate the coating. This article describes a 3D model to simulate the transport phenomena and the trajectory and heating of the solution spray in the process. The jet-spray two-way interactions are considered. A simplified model is employed to simulate the evolution process and the formation of the solid particle from the solution droplet in the plasma jet. The temperature and velocity fields of the jet are obtained and validated. The particle size, velocity, temperature, and position distribution on the substrate are predicted. This article is an invited paper selected from presentations at the 2007 International Thermal Spray Conference and has been expanded from the original presentation. It is simultaneously published in Global Coating Solutions, Proceedings of the 2007 International Thermal Spray Conference, Beijing, China, May 14-16, 2007, Basil R. Marple, Margaret M. Hyland, Yuk-Chiu Lau, Chang-Jiu Li, Rogerio S. Lima, and Ghislain Montavon, Ed., ASM International, Materials Park, OH, 2007.     

Numerical Simulation of Droplet Breakup and Collision in the Solution Precursor Plasma Spraying

Finely structured ceramic coatings can be obtained by solution precursor plasma spraying. The final structure of the coating highly depends on the droplet size and velocity distribution at the injection, the evolution of the spray in the jet, and droplet breakup and collision within the spray. This article describes a 3D model to simulate the transport phenomena and the trajectory and heating of the solution spray in the process. O’Rourke’s droplet collision model is used to take into account the influence of droplet collision. The influence of droplet breakup is also considered by implementing TAB droplet breakup models into the plasma jet model. The effects of droplet collisions and breakup on the droplet size, velocity, and temperature distribution of the solution spray are investigated. The results indicate that droplet breakup and collision play an important role in determining the final particle size and velocity distributions on the substrate. This article is an invited paper selected from presentations at the 2007 International Thermal Spray Conference and has been expanded from the original presentation. It is simultaneously published in Global Coating Solutions, Proceedings of the 2007 International Thermal Spray Conference, Beijing, China, May 14-16, 2007, Basil R. Marple, Margaret M. Hyland, Yuk-Chiu Lau, Chang-Jiu Li, Rogerio S. Lima, and Ghislain Montavon, Ed., ASM International, Materials Park, OH, 2007.     

Tribological and Corrosion Behavior of Vacuum Plasma Sprayed Ti-Zr-Ni Quasicrystalline Coatings

This investigation deals with a study of the friction, wear, and corrosion behavior of vacuum plasma sprayed quasicrystalline (QC) Ti_41.5Zr_41.5Ni₁₇ coatings. During pin on disc experiments, a change in the mode of wear has been found to occur with corresponding changes in normal load and sliding velocity. The low thermal conductivity of quasicrystals and its brittleness play a vital role in determining the friction and wear behavior of such materials. When these coatings are subjected to rubbing for a longer period of time, wear occurs by subsurface crack propagation, and subsequent delamination within the coated layer. By comparing the QC to its polycrystalline counterpart during potentiodynamic measurements according to ASTM G 31, higher currents were found over the whole range of potentials for QC when immersed in 1 M HCl solution. This article is an invited paper selected from presentations at the 2007 International Thermal Spray Conference and has been expanded from the original presentation. It is simultaneously published in Global Coating Solutions, Proceedings of the 2007 International Thermal Spray Conference, Beijing, China, May 14-16, 2007, Basil R. Marple, Margaret M. Hyland, Yuk-Chiu Lau, Chang-Jiu Li, Rogerio S. Lima, and Ghislain Montavon, Ed., ASM International, Materials Park, OH, 2007.     

Corrosion Behavior of Arc Sprayed Nickel-Base Coatings

In this study, nickel-base cored wires were prepared by using NiCr strip to wrap metal powders of nickel (Ni), chromium (Cr), molybdenum (Mo), and chromium boron (CrB). Nickel-base coatings were prepared by electric arc spraying. Microstructures of Ni-Cr-Mo and Ni-Cr-B coatings were investigated using scanning electron microscopy (SEM), energy-dispersive analysis (EDAX), and x-ray diffraction (XRD) analysis. The coatings have a compact surface and presented a bonding strength higher than 40 MPa. Potentiodynamic polarization measurements and salt-spray test were carried out to determine the corrosion behavior of the coatings. The results showed that Ni-base coatings containing Mo (5%) or B (2-4%) had better antichlorine ion corrosion performance than that of Ni-base coatings without Mo element, and PS45 (Ni-Cr-Ti) coating. The antichlorine ion corrosion coatings could be used for resolving the corrosion protection problem of the equipment and piping contacting sour, alkali, salt liquid in petrochemical engineering applications. This article is an invited paper selected from presentations at the 2007 International Thermal Spray Conference and has been expanded from the original presentation. It is simultaneously published in Global Coating Solutions, Proceedings of the 2007 International Thermal Spray Conference, Beijing, China, May 14-16, 2007, Basil R. Marple, Margaret M. Hyland, Yuk-Chiu Lau, Chang-Jiu Li, Rogerio S. Lima, and Ghislain Montavon, Ed., ASM International, Materials Park, OH, 2007.     

Characterization of YSZ solid oxide fuel cells electrolyte deposited by atmospheric plasma spraying and low pressure plasma spraying

Yttria doped zirconia has been widely used as electrolyte materials for solid oxide fuel cells (SOFC). Plasma spraying is a cost-effective process to deposit YSZ electrolyte. In this study, the 8 mol% Y₂O₃ stabilized ZrO₂ (YSZ) layer was deposited by low pressure plasma spraying (LPPS) and atmospheric plasma spraying (APS) with fused-crushed and agglomerated powders to examine the effect of spray method and particle size on the electrical conductivity and gas permeability of YSZ coating. The microstructure of YSZ coating was characterized by scanning electron microscopy and x-ray diffraction analysis. The results showed that the gas permeability was significantly influenced by powder structure. The gas permeability of YSZ coating deposited by fused-crushed powder is one order lower in magnitude than that by agglomerated powder. Moreover, the gas permeability of YSZ deposited by LPPS is lower than that of APS YSZ. The electrical conductivity of the deposits through thickness direction was measured by potentiostat/galvanostat based on three-electrode assembly approach. The electrical conductivity of YSZ coating deposited by low pressure plasma spraying with fused-crushed powder of small particle size was 0.043 S cm⁻¹ at 100 °C, which is about 20% higher than that of atmospheric plasma spraying YSZ with the same powder. This article was originally published inBuilding on 100 Years of Success, Proceedings of the 2006 International Thermal Spray Conference (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, OH, 2006.     

Effect of steam treatment during plasma spraying on the microstructure of hydroxyapatite splats and coatings

The major problems with plasma sprayed hydroxyapatite (HA) coatings for hard tissue replacement are severe HA decomposition and insufficient mechanical properties of the coatings. Loss of crystalline HA after the high-temperature spraying is due mainly to the loss of OH⁻ in terms of water. The current study used steam to treat HA droplets and coatings during both in-flight and flattening stages during plasma spraying. The microstructure of the HA coatings and splats was characterized using scanning electron microscope, Raman spectroscopy, Fourier transform IR spectroscopy, and x-ray diffraction. Results showed that a significant increase in crystallinity of the HA coating was achieved through the steam treatment (e.g., from 58 to 79%). In addition, the effects were dependent on particle sizes of the HA feedstock, more increase in crystallinity of the coatings made from smaller powders was revealed. The Raman spectroscopy analyses on the individual splats and coatings indicate that the mechanism involves entrapping of water molecules by the individual HA droplets upon their impingement. It further suggests that the HA decomposition has already taken place before the impingement of the droplets on precoating or substrate. The improvement in crystallinity and phases, for example, from tricalcium phosphate and amorphous calcium phosphate to HA, was achieved by reversing the HA decomposition through providing extra OH⁻. Furthermore, the steam treatment during the spraying also accounts for remarkably increased adhesion strength from 9.09 to 23.13 MPa. The in vitro testing through immersing the HA coatings in simulated body fluid gives further evidence that the economic and simple steam treatment is promising in improving HA coating structure. This article was originally published inBuilding on 100 Years of Success, Proceedings of the 2006 International Thermal Spray Conference (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, OH, 2006.     

Wear characteristics of plasma-sprayed nanostructured yttria partially stabilized zirconia coatings

Reconstituted nanostructured and conventional yttria partially stabilized zirconia coatings were deposited by atmospheric plasma spray. The tribologic properties of the coatings against 100C6 steel were evaluated with a ball-on-disc configuration under dry friction conditions at room temperature. Microstructure and the phase composition of the powders and the coatings were examined using a scanning electron microscope, optical microscope, and x-ray diffraction. Microhardness and the Young’s modulus of coatings were measured by indentation testing. Results showed that the wear resistance of the coatings produced using the nanostructured powder is improved compared with the coating produced using the conventional powder. The wear rates of nanostructured zirconia coatings are about four-fifths of those of conventional counterparts under a load of 5 N. The wear mechanism is also discussed. The original version of this paper was published as part of the DVS Proceedings: “Thermal Spray Solutions: Advances in Technology and Application,” International Thermal Spray Conference, Osaka, Japan, 10–12 May 2004, CD-Rom, DVS-Verlag GmbH, Düsseldorf, Germany.     

Microstructure and properties of tungsten carbide coatings sprayed with various high-velocity oxygen fuel spray systems

This article reports on a series of experiments with various high-velocity oxygen fuel spray systems (Jet Kote, Top Gun, Diamond Jet (DJ) Standard, DJ 2600 and 2700, JP-5000, Top Gun-K) using different WC-Co and WC-Co-Cr powders. The microstructure and phase composition of powders and coatings were analyzed by optical and scanning electron microscopy and x-ray diffraction. Carbon and oxygen content of the coatings were determined to study the decarburization and oxidation of the material during the spray process. Coatings were also characterized by their hardness, bond strength, abrasive wear, and corrosion resistance. The results demonstrate that the powders exhibit various degrees of phase transformation during the spray process depending on type of powder, spray system, and spray parameters. Within a relatively wide range, the extent of phase transformation has only little effect on coating properties. Therefore, coatings of high hardness and wear resistance can be produced with all HVOF spray systems when the proper spray powder and process parameters are chosen. This paper originally appeared in Thermal Spray: Meeting the Challenges of the 21st Century; Proceedings of the 15th International Thermal Spray Conference, C. Coddet, Ed., ASM International, Materials Park, OH, 1998. This proceedings paper has been extensively reviewed according to the editorial policy of the Journal of Thermal Spray Technology.