Microstructure and properties of porous anorthite/mullite whiskers ceramics with high porosity

Porous anorthite/mullite whiskers ceramics with high porosity (>91%) and high strength (>0.45 MPa) have been successfully prepared by foam gel-casting method. Effects of extra mullite whiskers on properties including thermal conductivity and compressive strength at different temperatures were investigated and discussed in terms of microstructure observed through SEM and TEM. The results showed that the addition of extra mullite whiskers in certain content could effectively reduce thermal conductivity, improve the compressive strength both at room and high temperature at same time. When the mullite whiskers content was 20 mol%, the porosity was as high as 91.6 ± 0.19%, the thermal conductivity was low to 0.034 ± 0.003 W/(m·K), and the compressive strength at 1000°C was high to 0.64 ± 0.11 MPa three times to the pure one. Small pores, small grains, and more phase interface or grain boundary caused by the addition of extra mullite whiskers were the main factors for low thermal conductivity. Meanwhile, small pores, closely bonded small grains, and the stable three-dimension network formed by mullite whiskers helped to improve strength.     

Fibrous porous mullite ceramics modified by mullite whiskers for thermal insulation and sound absorption

In order to meet the demand for thermal insulation and sound absorption, fibrous porous mullite ceramics (FPMC) with high porosity and an interconnected pore structure were prepared, followed by a pore structure modification with in situ grown mullite whiskers on the three-dimensional framework of the FPMC. The resultant hierarchical material exhibited superior sound absorption performance in the low-to-medium frequency to most reported sound-absorbing materials, as well as a sufficient compressive strength of 1.26 MPa with low thermal conductivity of 0.117 W·m^?1·K^?1. Moreover, the effects of solid content and mullite whiskers on the microstructure and physical properties of the material were analyzed. The increase of solid content led to increased compressive strength and thermal conductivity and decreased frequency corresponding to the first sound absorption peak. The thermal conductivity and compressive strength of the material increased as the mullite whiskers grew, while the median pore size decreased.     

High gas permeability and directional channels of mullite porous ceramics prepared by pectin-based freeze-drying method

New gel system for preparing mullite porous ceramics by gel-casting freeze-drying was proposed, using pectin as gel source and alumina and silica as raw materials. Directional channels were formed due to sublimation of water during freeze-drying and decomposition of pectin during high temperature sintering to prepare porous mullite ceramic membranes. Effects of solid content on the properties of mullite ceramics in terms of phase composition, microstructure, apparent porosity, bulk density, pore size distribution, compressive strength, thermal conductivity, pressure drop, and gas permeability were investigated. It was found that prepared porous mullite possessed high apparent porosity (56.04%–75.34%), low bulk density (.77–1.37 g/cm³), uniform pore size distribution, relatively high compressive strength (.61–3.03 MPa), low thermal conductivity (.224–.329 W/(m·K)), high gas permeability coefficient (1.11 × 10⁻¹⁰–4.73 × 10⁻¹¹ m²), and gas permeance (2.18 × 10⁻²–9.32 × 10⁻³ mol⋅m⁻²⋅s⁻¹⋅Pa⁻¹). These properties make prepared lightweight mullite ceramic membranes promising for application in high temperature flue gas filtration. Proposed gel system is expected to provide a new route to prepare porous ceramics with high porosity and directional channels.     

Ultra-low cost porous mullite ceramics with excellent dielectric properties and low thermal conductivity fabricated from kaolin for radome applications

Near-net-shape mullite ceramics with high porosity were prepared from ultra-low cost natural aluminosilicate mineral kaolin as raw material and polystyrene micro-sphere (PS) as pore-forming agent. Microstructure, flexural strength, thermal conductivity and dielectric properties of the ceramics were systematically researched. Results show that the porous mullite ceramics possess fibrous skeleton structure formed by a large quantity of interlocked mullite whiskers, which results in good mechanical properties and low-to-zero sintering shrinkage. Flexural strength of the porous mullite ceramics can be up to 41.01 ± 1.12 MPa, even if the porosity is as high as 62.44%. The dielectric constant and loss tangent of the porous mullite ceramics at room temperature are lower than 2.61 and 5.9 × 10⁻³, respectively. Besides, dielectric constant is very stable with the rising of temperature, and the dielectric loss can be consistently lower than 10⁻² when the temperature is not higher than 800 °C. In addition, thermal conductivity at room temperature is as low as 0.163 W/m/K when the porosity of mullite ceramics is 80.05%. The infiltration of SiO₂ aerogels (SiO₂ AGs) can further decrease the thermal conductivity to 0.075 W/m/K, while has just little effects on the dielectric properties. Excellent mechanical, thermal and dielectric properties show that the porous mullite ceramics have potential applications in radome fields. The porous mullite ceramics prepared from kaolin not only have low cost, but also can achieve near-net-shape.     

Fabrication and properties of porous anorthite/mullite ceramics with both high porosity and high strength

Porous anorthite/mullite ceramics with both high porosity and high strength have been successfully fabricated by foam-gelcasting and pressureless sintering technology, using α-Al₂O₃, SiO₂, and CaCO₃ as starting materials and MnO₂ as sintering aids. The porous mullite ceramics prepared in this study had 83.3% porosity and 0.3 W/m·K thermal conductivity, exhibited compressive strength value as high as 6.1 MPa. The samples fabricated with mullite content of 30 mol% possessed 79.4% porosity and 5.9 MPa compressive strength showed thermal conductivity as low as 0.19 W/m·K. With the addition of MnO₂, the properties of the prepared materials varied slightly when mullite content changed in a large scale. The results showed that the addition of MnO₂ promoted the reaction, affected sintering and grain growth, and contributed to high strength and low-thermal conductivity.     

Preparation and characterization of porous anorthite ceramics from red mud and fly ash

The porous anorthite ceramics with high porosity, good mechanical strength and low heat conductivity were prepared using red mud and fly ash as raw materials via the pore forming method. The effects of sintering temperature and fly ash on phase evolution, densification, compressive strength, thermal conductivity and microstructure of the ceramic materials were investigated. The results showed that the compressive strength of the porous ceramics had an obvious improvement with the increase in fly ash, and the densification and heat conductivity decreased firstly and then increased. In particular, specimen S2 containing 30 wt% red mud and 40 wt% fly ash sintered at 1150°C had the better performances. It had the water absorption of 18.18%, open porosity of 38.52%, bulk density of 1.29 g/cm³, compressive strength of 42.46 MPa, and heat conductivity of 1.24 W/m·K. X-ray diffraction analysis indicated that mullite, anorthite, α-quartz, and diopside ferrian were the dominant phases in the specimens. Scanning electron microscopy micrographs illustrated that plenty of open pores with strip shape and closed pores with axiolitic shape existed in the specimens. Furthermore, the existence of mullite could prevent crack propagation to enhance the energy of inter-granular fracture. It endowed the porous anorthite ceramics with high porosity, good compressive strength, and low heat conductivity.     

Porous mullite ceramics with enhanced compressive strength from fly ash-based ceramic microspheres: Facile synthesis,structure, and performance

Porous mullite ceramics are widely used in heat insulation owing to their high temperature and corrosion resistant properties. Reducing the thermal conductivity by increasing porosity, while ensuring a high compressive strength, is vital for the synthesis of high-strength and lightweight porous mullite ceramics. In this study, ceramic microspheres are initially prepared from pre-treated high-alumina fly ash by spray drying, and then used to successfully prepare porous mullite ceramics with enhanced compressive strength via a simple direct stacking and sintering approach. The influence of sintering temperature and time on the microstructure and properties of porous mullite ceramics was evaluated, and the corresponding formation mechanism was elucidated. Results show that the porous mullite ceramics, calcined at 1550 °C for 3 h, possess a porosity of 47%, compressive strength of 31.4 MPa, and thermal conductivity of 0.775 W/(m?K) (at 25 °C), similar to mullite ceramics prepared from pure raw materials. The uniform pore size distribution and sintered neck between the microspheres contribute to the high compressive strength of mullite ceramics, while maintaining high porosity.     

Fabrication and characterization of anorthite–mullite–corundum porous ceramics from construction waste

In this work, anorthite–mullite–corundum porous ceramics were prepared from construction waste and Al₂O₃ powders by adding AlF₃ and MoO₃ as mineralizer and crystallization catalyst, respectively. The effects of the sintering temperature and time on open porosity, mechanical properties, pore size distribution, microstructure, and phase composition were characterized in detail. The results showed that the formation of the mullite whiskers and the properties of the anorthite–mullite–corundum porous ceramics depended more on the sintering temperature than the holding time. By co-adding 12 wt% AlF₃ and 4 wt% MoO₃, mullite whiskers were successfully obtained at sintering temperatures upon 1350 °C for 1 h. Furthermore, the resultant specimens exhibited excellent properties, including open porosity of 66.1±0.7%, biaxial flexural strength of 23.8±0.9 MPa, and average pore size of 1.32 µm (the corresponding cumulative volume percent was 37.29%).     

In-situ growth of mullite whiskers and their effect on the microstructure and properties of porous mullite ceramics with an open/closed pore structure

Porous mullite ceramics with an open/closed pore structure were prepared by protein foaming method combined with fly ash hollow spheres. Both the open porosity and total porosity of samples were enhanced by increasing the hollow sphere content. Mullite whiskers with a diameter of 0.2–4 μm were grown in-situ in the porous mullite ceramics with an AlF₃ catalyst, conforming to a vapor-solid growth mechanism. The pore structure of the porous mullite ceramics was significantly affected by the mullite whiskers which increased the open porosity and total porosity. Moreover, the median pore size was reduced from 65.05 μm to 36.92 μm after the introduction of mullite whiskers. The flexural strength and the thermal conductivity of the samples decreased with increasing total porosity. The porosity dependence of the thermal conductivity was well described by the universal model, providing a reference for the prediction of thermal conductivity of porous ceramics with open/closed pores.     

Preparation and properties of mullite-bonded porous fibrous mullite ceramics by an epoxy resin gel-casting process

Porous fibrous mullite ceramics with a narrow range of pore size distribution have been successfully prepared utilizing a near net-shape epoxy resin gel-casting process by using mullite fibers, Al₂O₃ and SiC as raw materials. The effects of sintering temperatures, different amounts of fibers and Y₂O₃ additive on the phase compositions, linear shrinkage, apparent porosity, bulk density, microstructure, compressive strength and thermal conductivity were investigated. The results indicated that mullite-bonded among fibers were formed in the porous fibrous mullite ceramics with a bird nest pore structure. After determining the sintering temperatures and the amount of fibers, the tailored porous fibrous mullite ceramics had a low linear shrinkage (1.36–3.08%), a high apparent porosity (61.1–71.7%), a relatively high compressive strength (4.4–7.6 MPa), a low thermal conductivity (0.378–0.467 W/m K) and a narrow range of pore size distribution (around 5 µm). The excellent properties will enable the porous ceramics as a promising candidate for the applications of hot gas filters, thermal insulation materials at high temperatures.     

High-strength thermal insulating porous mullite fiber-based ceramics

How to improve the strength of fibrous porous ceramics dramatically under the premise of no sacrificing its low density and thermal conductivity has remained a challenge in the high-temperature thermal insulation field. In this paper, a new kind of high-strength mullite fiber-based ceramics composed of interlocked porous mullite fibers was prepared by nanoemulsion electrospinning and dry pressing method. Results show that as to the porous ceramics with the same density (～ 0.8 g/cm³), the three-dimensional skeleton structure composed of porous mullite fibers was much denser than that composed of solid mullite fibers. Therefore, porous mullite fiber-based ceramics exhibited a higher compressive strength (5.53 MPa) than that of solid mullite fiber-based ceramics (3.21 MPa). In addition, porous mullite fiber-based ceramics exhibited a superior high-temperature heat insulation property because the porous structure in fibers could reduce the radiant heat conduction. This work provides new insight into the development of high-temperature thermal insulators.     

Effect of mullite phase formed in situ on pore structure and properties of high-purity mullite fibrous ceramics

Porous mullite ceramics are potential advanced thermal insulating materials. Pore structure and purity are the main factors that affect properties of these ceramics. In this study, high performance porous mullite ceramics were prepared via aqueous gel-casting using mullite fibers and kaolin as the raw materials and ρ-Al₂O₃ as the gelling agent. Effects of addition of mullite fibers on the pore structure and properties were examined. The results indicated that mullite phase in situ formed by kaolin, and ρ-Al₂O₃ ensured the purity of mullite samples and mullite fibers bonded together to form a nest-like structure, greatly improving the properties of ceramic samples. In particular, the apparent porosity of mullite samples reached 73.6%. In the presence of 75% of mullite fibers, the thermal conductivity was only 0.289 W/m K at room temperature. Moreover, the mullite samples possessed relatively high cold compressive strength in the range of 4.9–9.6 MPa. Therefore, porous mullite ceramics prepared via aqueous gel-casting could be used for wide applications in thermal insulation materials, attributing to the excellent properties such as high cold compressive strength and low thermal conductivity.     

Low sintering shrinkage porous mullite ceramics with high strength and low thermal conductivity via foam-gelcasting

Excessive sintering shrinkage leads to severe deformation and cracking, affecting the microstructure and properties of porous ceramics. Therefore, reducing sintering shrinkage and achieving near-net-size forming is one of the effective ways to prepare high-performance porous ceramics. Herein, low-shrinkage porous mullite ceramics were prepared by foam-gelcasting using kyanite as raw material and aluminum fluoride (AlF₃) as additive, through volume expansion from phase transition and gas generated from the reaction. The effects of AlF₃ content on the shrinkage, porosity, compressive strength, and thermal conductivity of mullite-based porous ceramics were investigated. The results showed that with the increase of content, the sintering shrinkage decreased, the porosity increased, and mullite whiskers were produced. Porous mullite ceramics with 30 wt% AlF₃ content exhibited a whisker structure with the lowest shrinkage of 3.5%, porosity of 85.2%, compressive strength of 3.06 ± 0.51 MPa, and thermal conductivity of 0.23 W/(m·K) at room temperature. The temperature difference between the front and back sides of the sample reached 710°C under high temperature fire resistance test. The low sintering shrinkage preparation process effectively reduces the subsequent processing cost, which is significant for the preparation of high-performance porous ceramics.     

Carbothermal reduction synthesis of high porosity and low thermal conductivity ZrC-SiC ceramics via an one-step sintering technique

In this work, porous ZrC-SiC ceramics with high porosity and low thermal conductivity were successfully prepared using zircon (ZrSiO₄) and carbon black as material precursors via a facile one-step sintering approach combining in-situ carbothermal reduction reaction (at 1600 °C for 2 h) and partial hot-pressing sintering technique (at 1900 °C for 1 h). Carbon black not only served as a reducing agent, but also performed as a pore-foaming agent for synthesizing porous ZrC-SiC ceramics. The prepared porous ZrC-SiC ceramics with homogeneous microstructure (with grain size in the 50–1000 nm range and pore size in the 0.2–4 µm range) possessed high porosity of 61.37–70.78%, relatively high compressive strength of 1.31–7.48 MPa, and low room temperature thermal conductivity of 1.48–4.90 W·m^?1K^?1. The fabricated porous ZrC-SiC ceramics with higher strength and lower thermal conductivity can be used as a promising light-weight thermal insulation material.     

Preparation and characteristics of porous anorthite ceramics with high porosity and high-temperature strength

High-temperature properties including compressive strength, thermal shock behavior, and thermal conductivity of porous anorthite ceramics with high specific strength were tested and analyzed. The results showed that the prepared materials merit high-temperature compressive strength, thermal stability, and conductivity. With the appropriate fabrication parameters, even though containing 0.33 g/cm³ bulk density and 88.2% porosity, its compressive strength could reach 2.03 MPa at 1000°C, 147% of that at room temperature; the residual strength ratio kept as 114.7% after a thermal shock at 1200°C. The X-ray diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscope (TEM) showed that anorthite grains refinement and intergranular voids filling by liquid phase were main factors for the high strength. From room temperature to 1200°C, its thermal conductivity only varied from 0.085 to 0.258 W·(m·K)⁻¹. High porosity, a large number of nanoregions in anorthite grains and amorphous phase in grain boundary were main reasons for low thermal conductivity.     

Effects of SiC whisker addition on mechanical,thermal, and permeability properties of porous silica-bonded SiC ceramics

The effects of SiC whisker addition into nano-SiC powder-carbon black template mixture on flexural strength, thermal conductivity, and specific flow rate of porous silica-bonded SiC ceramics were investigated. The flexural strength of 1200°C-sintered porous silica-bonded SiC ceramics increased from 9.5 MPa to 12.8 MPa with the addition of 33 wt% SiC whisker because the SiC whiskers acted as a reinforcement in porous silica-bonded SiC ceramics. The thermal conductivity of 1200°C-sintered porous silica-bonded SiC ceramics monotonically increased from 0.360 Wm^–1K^–1 to 1.415 Wm^–1K^–1 as the SiC whisker content increased from 0 to 100 wt% because of the easy heat conduction path provided by SiC whiskers with a high aspect ratio. The specific flow rate of 1200°C-sintered porous SiC ceramics increased by two orders of magnitude as the SiC whisker content increased from 0 to 100 wt%. These results were primarily attributed to an increase in pore size from 125 nm to 565 nm and secondarily an increase in porosity from 49.9% to 63.6%. In summary, the addition of 33 wt% SiC whisker increased the flexural strength, thermal conductivity, and specific flow rate of porous silica-bonded SiC ceramics by 35%, 133%, and 266%, respectively.     

Preparation of Porous Mullite Ceramics Using Fly Ash Cenosphere as a Pore‐Forming Agent by Gelcasting Process

Porous mullite ceramics were fabricated from an industrial grade mullite powder by gelcasting process using fly ash cenospheres (FAC) as a pore‐forming agent. The influence of content of FAC and sintering temperature on the density and strength was evaluated. The microstructure showed that FAC can act as a sintering aid and a pore‐forming agent. When the sintering temperature at 1200°C, porous mullite ceramics with a relatively high porosity (48.1–72.2%), low density (0.84–1.64 g/cm³), low thermal conductivity (0.16–0.22 W/m · K), and high compressive strength (6.21–14.70 MPa) have been obtained.     

Near-net-size preparation of porous mullite matrix ceramics with in situ formed 3D mullite whisker network

Porous mullite matrix ceramics have excellent thermal and mechanical properties suitable for applications such as in thermal insulation. However, their applications are limited by processing defects from nonuniform sintering shrinkage and the trade-off between high porosity (preferred for low thermal conductivity) and high mechanical strength. Herein, we seek to minimize the sintering shrinkage by near-net-size preparation and improve the strength by in situ formed whisker network structure. Gelcasting forming technology and pressureless sintering were used to prepare porous mullite matrix ceramics using kyanite and α-Al₂O₃ powders as the starting materials and using MoO₃ to promote the growth of mullite whiskers. The results showed that the sintering shrinkage could be compensated by the volume expansion from solid-state reaction during reaction sintering. The in situ formed three-dimensional (3D) whisker network further reduced sintering shrinkage and effectively improved the strength of the ceramics. An ultralow sintering shrinkage of .78% was achieved. The near-net-shape porous mullite matrix ceramics strengthened by 3D whisker network had a high porosity of 63.9%, a high compressive strength of 83.8 MPa and a high flexural strength of 53.5 MPa.     

Effects of V2O5 addition on the synthesis of columnar self-reinforced mullite porous ceramics

Spearhead columnar mullite was synthesized by in-situ reaction with V₂O₅ as additive. When the content of V₂O₅ was 7 wt%, the length of the spearhead columnar mullite was the longest with an aspect ratio of about 3.5. Furthermore, columnar self-reinforced mullite porous ceramics were prepared by a foam-gelcasting method, and the effects of V₂O₅ content on the rheological and gelling properties of mullite slurries as well as the microstructure, physical property and thermal insulation property of the prepared mullite porous ceramics were studied. The results showed that the flexural strength and compressive strength of the porous ceramics with 63% porosity prepared by using 2 wt% V₂O₅ additive were respectively as high as 13.9 and 41.3 MPa, and the thermal conductivity was about 1.04 W m^?1 K^?1.     

Microstructure and properties of lightweight fibrous porous mullite ceramics prepared by vacuum squeeze moulding technique

A novel fibrous porous mullite network with a quasi-layered microstructure was produced by a simple vacuum squeeze moulding technique. The effects of organic binder content, inorganic binder and adsorbent on the microstructure and the room-temperature thermal and mechanical properties of fibrous porous mullite ceramics were systematically investigated. An anisotropy microstructure without agglomeration and layering was achieved. The fibrous porous mullite ceramics reported in this study exhibited low density (0.40 g/cm³), low thermal conductivity (~0.095 W/(m K)), and high compressive strength (~2.1 MPa in the x/y direction). This study reports an optimal processing method for the production of fibrous porous ceramics, which have the potential for use as high-temperature thermal insulation material.