Effects of K0.5Bi0.5TiO3 addition on dielectric properties of BaTiO3 ceramics

(1?x)BaTiO₃–xK_0.5Bi_0.5TiO₃ (abbreviated as BT–KBT, 0.10≦x≦0.15) dielectric ceramics were prepared by a conventional oxide mixing method. The effects of KBT content on the densification, microstructure and dielectric properties of BT ceramics were investigated. The density characterization results show that the addition of KBT significantly lowered the sintering temperature of BT ceramics to about 1280 °C. The XRD results showed that the phase compositions of all samples were pure tetragonal phases. The dielectric constant and dielectric loss firstly increased and then decreased with the increase of KBT. In addition, dielectric constant and dielectric loss versus frequency were characterized in the frequency range from 100 Hz to 2 MHz. It is found that the dielectric constant and the dielectric loss changed with the increase of KBT contents regularly.     

Compositional range and electrical properties of the morphotropic phase boundary in the Na0.5Bi0.5TiO3–K0.5Bi0.5TiO3 system

We have investigated the Na_0.5Bi_0.5TiO₃–K_0.5Bi_0.5TiO₃ (NBT–KBT) system, with its complex perovskite structure, as a promising material for piezoelectric applications. The NBT–KBT samples were synthesized using a solid-state reaction method and characterized with XRD and SEM. Room-temperature XRD showed a gradual change in the crystal structure from tetragonal in the KBT to rhombohedral in the NBT, with the presence of an intermediate morphotropic region in the samples with a compositional fraction x between 0.17 and 0.25. The fitted perovskite lattice parameters confirmed an increase in the size of the crystal lattice from NBT towards KBT, which coincides with an increase in the ionic radii. Electrical measurements on the samples showed that the maximum values of the dielectric constant, the remanent polarization and the piezoelectric coefficient are reached at the morphotropic phase boundary (MPB) (? = 1140 at 1 MHz; P_r = 40 μC/cm²; d₃₃ = 134 pC/N).     

Dielectric,ferroelectric and field-induced strain behavior of K0.5Na0.5NbO3-modified Bi0.5(Na0.78K0.22)0.5TiO3 lead-free ceramics

Lead-free piezoelectric (1 ? x)Bi_0.5(Na_0.78K_0.22)_0.5TiO₃–xK_0.5Na_0.5NbO₃ (BNKT–xKNN, x = 0–0.10) ceramics were synthesized using a conventional, solid-state reaction method. The effect of KNN addition on BNKT ceramics was investigated through X-ray diffraction (XRD), dielectric, ferroelectric and electric field-induced strain characterizations. XRD revealed a pure perovskite phase with tetragonal symmetry in the studied composition range. As the KNN content increased, the depolarization temperature (T_d) as well as maximum dielectric constant (?_m) decreased. The addition of KNN destabilized the ferroelectric order of BNKT ceramics exhibiting a pinched-type hysteresis loop with low remnant polarization (11 μC/cm²) and small piezoelectric constant (27 pC/N) at 3 mol% KNN. As a result, at x = 0.03 a significant enhancement of 0.22% was observed in the electric field-induced strain, which corresponds to a normalized strain (S_max/E_max) of ～434 pm/V. This enhancement is attributed to the coexistence of ferroelectric and non-polar phases at room temperature.     

Dielectric and ferroelectric properties of (1 − x)BaTiO3–xBi0.5Na0.5TiO3 ceramics

Lead-free (1 − x)BaTiO₃–xBi_0.5Na_0.5TiO₃ (x = 0.01, 0.02, 0.05, 0.1, 0.2, 0.3) ferroelectric ceramics were fabricated by the conventional ceramic technique. Sintering was made at 1200 °C for 2–4 h in air atmosphere. The crystal structure was investigated by X-ray diffraction. The dielectric and ferroelectric properties were also studied. Room temperature permittivity was found to decrease as Bi_0.5Na_0.5TiO₃ (BNT) content increases. Only the sample with 0.3 mol BNT was found to have relaxor behaviour. The T_c shifted slightly only for BNT addition lower than 0.1 mol. The highest T_c (about 150 °C) was obtained for 0.2 mol BNT addition. The remanent polarization, P_r, decreases whereas the coercive field, E_c, increases monotonously as the BNT content increases.     

Effect of Li2O–V2O5 on the low temperature sintering and microwave dielectric properties of Li1.0Nb0.6Ti0.5O3 ceramics

Li₂O–Nb₂O₅–TiO₂ based ceramic systems have been the candidate materials for LTCC application, due to their high dielectric constant and Q × f value and controllable temperature coefficient in the microwave region. However, the sintering temperature was relatively higher (above 1100 °C) for practical application. In this study, dielectric properties of Li_(1+x−y)Nb_(1−x−3y)Ti_(x+4y)O₃ solid solution were studied with different x and y contents and among them, the Li_1.0Nb_0.6Ti_0.5O₃ composition (x = 0.1, y = 0.1) was selected, due to its reasonable dielectric properties to determine the possibility of low temperature sintering. The effects of 0.17Li₂O–0.83V₂O₅, as a sintering agent, on sinterability and microwave dielectric properties of Li_1.0Nb_0.6Ti_0.5O₃ ceramics were investigated as a function of the sintering agent content and sintering temperature. With addition of 0.17Li₂O–0.83V₂O₅ above 0.5 wt%, the specimens were well densified at a relatively lower temperature of 850 °C. Only slight decrease in apparent density was observed with increasing 0.17Li₂O–0.83V₂O₅ content above 0.75 wt%. In the case of 0.5 wt% 0.17Li₂O–0.83V₂O₅ addition, the values of dielectric constant and Q × f reached maximum. Further addition caused inferior microstructure, resulting in degraded dielectric properties. For the specimens with 0.5 wt% 0.17Li₂O–0.83V₂O₅ sintered at 850 °C, dielectric constant, Q × f and TCF values were 64.7, 5933 GHz and 9.4 ppm per °C, respectively.     

Dielectric properties of barium titanate–molybdenum composite

The barium titanate–molybdenum composites were prepared through solid state reaction method in argon atmosphere. The microstructure, resistivity, and dielectric properties of the composites were investigated. XRD results indicated that chemical reactions between barium titanate (BaTiO₃:BT) and molybdenum (Mo) have taken place during sintering, resulting in the formation of BaMoO₄ (BM) and BaTi₂O₅ (BT₂). The resistivity decreased with the increasing amount of Mo in the composites. The composites (when x = 5 and 20 wt.%) showed lower dielectric constant than pure BaTiO₃, especially, the dielectric constant (when x = 20 wt.%) reached a minimum value (<10⁴), while composites (when x = 10 and 15 wt.%) showed rather high dielectric constant at temperatures range from 25 °C to 160 °C. The dielectric constant of the composite gradually decreased with increase in frequency at the room temperature. The dielectric constant of composite (when x = 5 wt.%) comes up to 10⁴, and the T_c (Curie temperature) of the composite was relatively higher than that of BT (120 °C).     

Microstructure,ferroelectric and piezoelectric properties of Bi0.5K0.5TiO3-modified BiFeO3–BaTiO3 lead-free ceramics with high Curie temperature

The effects of composition, sintering temperature and dwell time on the microstructure and electrical properties of (0.75 ? x)BiFeO₃–0.25BaTiO₃–xBi_0.5K_0.5TiO₃ + 1 mol% MnO₂ ceramics were studied. The ceramics sintered at 1000 °C for 2 h possess a pure perovskite structure and a morphotropic phase boundary of rhombohedral and pseudocubic phases is formed at x = 0.025. The addition of Bi_0.5K_0.5TiO₃ retards the grain growth and induces two dielectric anomalies at high temperatures (T₁ ～ 450–550 °C and T₂ ～ 700 °C, respectively). After the addition of 2.5 mol% Bi_0.5K_0.5TiO₃, the ferroelectric and piezoelectric properties of the ceramics are improved and very high Curie temperature of 708 °C is obtained. Sintering temperature has an important influence on the microstructure and electrical properties of the ceramics. Critical sintering temperature is 970 °C. For the ceramic with x = 0.025 sintered at/above 970 °C, large grains, good densification, high resistivity and enhanced electrical properties are obtained. The weak dependences of microstructure and electrical properties on dwell time are observed for the ceramic with x = 0.025.     

New high Q microwave dielectric ceramics with rock salt structures: (1 − x)Li2TiO3 + xMgO system (0 ≤ x ≤ 0.5)

The structural evolution and microwave dielectric properties of (1 ? x)Li₂TiO₃ + xMgO system (0 ≤ x ≤ 0.5) have been investigated in this paper. The ordering degree decreased with the increase of MgO content. The microcracks and cleavage on (0 0 1) due to the weak Li–O bonds disappeared with the increase of MgO content. The dielectric constant and temperature coefficient of resonant frequency decreased with the increase of MgO content. The Q × f value increased with x up to x = 0.2 and then decreases with the further increase of x. An excellent combined microwave dielectric properties could be obtained when x = 0.24, ?_r = 19.2, Q × f = 106,226 GHz and τ_f = 3.56 ppm/°C.     

Magneto-dielectric laminated Ba(Fe0.5Nb0.5)O3-Bi0.2Y2.8Fe5O12 composites with high dielectric constant and high permeability

Magneto-dielectric laminated ceramic composites of xBa(Fe_0.5Nb_0.5)O₃-(1-x)Bi_0.2Y_2.8Fe₅O₁₂(BFN-BYIG) with high volume fractions of the giant dielectric constant material BFN (x=10, 30, 50, 70 wt%) were fabricated by the solid-state sintering method. Microstructure, dielectric and magnetic properties of the composites were investigated. The composites possess stable dielectric properties in the frequency range from 100 Hz to 1 MHz with high dielectric constant and low dielectric loss. The maximum permeability of the magneto-dielectric laminated composites reaches up to about 25. And the magnetic behaviors are strongly dependent on the mass ratio of BYIG. The results indicate that such multilayer structures of BFN/BYIG can enhance the permeability and decrease the dielectric and magnetic loss efficiently.     

Enhancement of pyroelectric properties of lead-free 0.94Na0.5Bi0.5TiO3-0.06BaTiO3 ceramics by La doping

Lead-free 0.94NBT-0.06BT-xLa ceramics at x = 0.0–1.0 (%) were synthesized by a conventional solid-state route. XRD shows that the compositions are at a morphotropic phase boundary where rhombohedral and tetragonal phases coexist. With increasing La³⁺ content pyroelectric coefficient (p) and figures of merits greatly increase; however, the depolarization temperature (T_d) decreases. p is 7.24 × 10⁻⁴C m⁻² °C⁻¹ at RT at x = 0.5% and 105.4 × 10⁻⁴C.m^−2 °C⁻¹ at T_d at x = 0.2%. F_i and F_v show improvements at RT from 1.12 (x = 0%) to 2.65 (x10 ⁻¹⁰ m v⁻¹) (x = 0.5%) and from 0.021 to 0.048 (m².C⁻¹) respectively. F_i and F_v show a huge increase to 37.6 × 10⁻¹⁰ m v⁻¹ and 0.56 m² C⁻¹ respectively at T_d at x = 0.2%. F_C shows values of 2.10, 2.89, and 2.98 (x10⁻⁹C cm⁻² °C⁻¹) at RT at 33, 100 and 1000 (Hz) respectively. Giant pyroelectric properties make NBT-0.06BT-xLa at x = 0.2% and 0.5% promising materials for many pyroelectric applications.     

Dielectric behavior and impedance spectroscopy in lead-free BNT–BT–NBN perovskite ceramics for energy storage

The dielectric behavior, impedance spectroscopy and energy-storage properties of 0.85[(1−x)Bi_0.5Na_0.5TiO₃–xBaTiO₃]–0.15Na_0.73Bi_0.09NbO₃ [(BNT–xBT)–NBN] ternary ceramics were investigated. Temperature dependent permittivity curves displayed two depressed anomalies, resulting in significantly improved dielectric temperature stability. (BNT–9BT)–NBN showed a permittivity of 1680 at 150 °C with Δε/ε_150 °C varying no more than ±10% up to 340 °C. From the complex impedance analysis, grain and grain boundary shared the same time constant. The high temperature resistivity followed the Arrhenius law with E_a=1.7–2.0 eV, suggesting intrinsic band-type electronic conduction. The maximum energy-storage density of all the samples reached 1.1–1.4 J/cm³, accompanied with good temperature stability in the range of 25–140 °C. These results indicate that (BNT–xBT)–NBN system should be a promising lead-free material for energy-storage capacitor applications.     

Abnormal variation of microwave dielectric properties in A/B site co-substituted (Ca1−0.3xLa0.2x)[(Mg1/3Ta2/3)1−xTix]O3 complex perovskite ceramics

A/B site co-substituted (Ca_1?0.3xLa_0.2x)[(Mg_1/3Ta_2/3)_1?xTi_x]O₃ ceramics (0.1 ≤ x ≤ 0.5) were prepared by solid state reaction and the structures, microstructures and dielectric properties were investigated. B site 1:2 cation ordering and oxygen octahedra tilting lead to monoclinic symmetry with space group P2₁/c for x = 0.1. For x above 0.1, the ordering was destroyed and the crystal structure became orthorhombic with space group Pbnm. The B site 1:2 cation ordering tended to be destroyed to form 1:1 ordering by the A site La³⁺ substitution. The dielectric constant increased linearly with increasing content of Ti⁴⁺ as the increasing second Jahn–Teller distortion enhanced the B site cation rattling. The temperature coefficient of resonant frequency and Qf values showed abnormal variations, which were refined to be caused by the increasing A site cation vacancy and diffused distribution of small size ordering domains respectively. Good combination of microwave dielectric properties was obtained at x = 0.5, where ?_r = 48, Qf = 21,000 GHz and τ_f = 2.2 ppm/°C.     

Dependence of dielectric properties on structural characteristics of (Zn1/3A2/3)0.5 (Ti1−xBx)0.5O2 (A = Nb5+, Ta5+, B = Ge4+, Sn4+) ceramics at microwave frequencies

The effects of structural characteristics on the dielectric properties of (Zn_1/3A_2/3)_0.5(Ti_1?xB_x)_0.5O₂ (A = Nb⁵⁺, Ta⁵⁺, B = Ge⁴⁺, Sn⁴⁺) (0.1 ≤ x ≤ 0.3) ceramics were investigated at microwave frequency. The sintered specimens showed solid solutions with a tetragonal rutile structure within the solid solution range of compositions. With an increase of BO₂, the temperature coefficient of resonant frequency (TCF) and dielectric constant (K) decreased with a decrease of oxygen octahedral distortion and dielectric polarizabilites, respectively. However, the quality factor (Qf) of the sintered specimens was increased with BO₂ due to the reduction of Ti⁴⁺ ions. The Qf value of the specimens with A = Ta was higher than that of the specimens with A = Nb.     

Microwave dielectric properties of (Zn1/3B2/3)0.5(Ti0.8M0.2)0.5O2 (B = Nb5+, Ta5+, M = Sn4+, Ge4+) ceramics

Dielectric properties of (Zn_1/3Nb_(2?x)/3Ta_x/3)_0.5(Ti_0.8Sn_0.1Ge_0.1)_0.5O₂ (x = 0, 1, 2) and/or (Zn_1/3Nb_1/3Ta_l/3)_0.5(Ti_0.8Sn_0.2(l?y)Ge_0.2y)_0.5O₂ (y = 0, 0.5, 1) were investigated at the microwave frequencies. For the compositions with single phase of rutile structure, the dielectric constant (K) of specimens was not only dependent on the dielectric polarizabilities, but also on the bond length ratio of apical bond (d_apical) to equatorial bond (d_equatorial) of oxygen octahedron in the unit cell. Temperature coefficients of the resonant frequencies (TCF) of the specimens with B = Nb⁵⁺ and/or M = Sn⁴⁺ was larger than those with B = Ta⁵⁺ and/or M = Ge⁴⁺. These results could be attributed to the changes of the degree of oxygen octahedral distortion. Quality factors (Qf) of the specimens with B = Ta⁵⁺ and/or M = Sn⁴⁺ were larger than those with B = Nb⁵⁺ and/or M = Ge⁴⁺.     

Grain size control of lead-free Li0.06(Na0.5K0.5)0.94NbO3 piezoelectric ceramics by Ba and Ti doping

In this study, Ba- and Ti-doped Li_0.06(Na_0.5K_0.5)_0.94NbO₃ [(1 ? x)Li_0.06(Na_0.5K_0.5)_0.94NbO₃–xBaTiO₃ (x = 0–0.07)] ceramics were prepared by using conventional solid state reaction method, and the microstructure and electric properties of these samples were investigated. The grain size distribution of non-doped Li_0.06(Na_0.5K_0.5)_0.94NbO₃ ceramics was relatively wide. The microstructure was composed of grains ranging 1.1–5.0 μm in size. However, with increasing Ba and Ti content, the grain size distribution became narrow and the average grain size decreased from 2.0 to 0.9 μm in size. In particular, the microstructure of x = 0.07 sample was composed of grains ranging 0.5–2.2 μm in size. As a result, the frequency dispersion of dielectric constant for the (1 ? x)Li_0.06(Na_0.5K_0.5)_0.94NbO₃–xBaTiO₃ (x = 0–0.07) ceramics was reduced and the mechanical quality factor Q_m was enhanced with increasing Ba and Ti content.     

Temperature-insensitive dielectric and piezoelectric properties in (1-x)K0.5Na0.5Nb0.997Cu0.0075O3-xSrZrO3 ceramics

Systematic investigation on phase transition, dielectric and piezoelectric properties of (1-x)K_0.5Na_0.5Nb_0.997Cu_0.0075O₃-xSrZrO₃ (x = 0, 0.03, 0.06, 0.09, 0.12, 0.15, abbreviated as KNNC-100xSZ) ceramics was carried out. Due to the coexistence of orthorhombic and tetragonal phase in a wide temperature range, a diffused polymorphic phase transition (PPT) region was achieved in KNNC with x ≥ 0.06. KNNC-12SZ ceramics exhibited high dielectric permittivity (∼1679), low dielectric loss (∼0.02) and small variation (Δe'/ε'_25 °C ≤ 15%) in dielectric permittivity from −78 °C to 237.3 °C. KNNC-6SZ ceramic possessed a high level of unipolar strain (∼0.15%) and maintained a smaller variation of ±12% under the corresponding electric field of 60 kV cm⁻¹ at 10 Hz from 25 °C to 175 °C. d₃₃^*, which was calculated according to the unipolar strain at 60 kV cm⁻¹, was 230 pm V⁻¹ and remained stable below 100 °C. Therefore, our work provided a new promising candidate for temperature-insensitive capacitors and piezoelectric actuators.     

Enhanced microstructure and electrical properties of Mn-modified Bi0.5(Na0.65K0.35)0.5TiO3 ferroelectric ceramics

Bi_0.5(Na_0.65K_0.35)_0.5TiO₃ (BNKT) and Mn-modified Bi_0.5(Na_0.65K_0.35)_0.5(Mn_xTi_1−x)O₃ (BNKMT-10³x), (x=0.0–0.5%) ferroelectric ceramics were synthesized by solid-state reaction method. Optimization of calcination temperature in Mn-doped ceramics was carried out for the removal of secondary phases observed in XRD analysis. BNKMT ceramics sintered at 1090 °C showed enhanced dielectric, piezoelectric and ferroelectric properties in comparison to pure BNKT. The average grain size was found to increase from 0.35 μm in BNKT to 0.52 μm in Bi_0.5(Na_0.65K_0.35)_0.5(Mn_0.0025Ti_0.9975)O₃ (BNKMT-2.5) ceramics. The dielectric permittivity maximum temperature (T_m) was increased to a maximum of 345 °C with Mn-modification. AC conductivity analysis was performed as a function of temperature and frequency to investigate the conduction behavior and determine activation energies. Significant high value of piezoelectric charge coefficient (d₃₃=176 pC/N) was achieved in BNKMT 2.5 ceramics. Improved temperature stability of ferroelectric behavior was observed in the temperature dependent P–E hysteresis loops as a result of Mn-incorporation. The fatigue free nature along with enhanced dielectric and ferroelectric properties make BNKMT-2.5 ceramic a promising candidate for replacing lead based ceramics in device applications.     

Synthesis of Na0.5Bi0.5TiO3 whiskers and their nanoscale piezoelectricity

The perovskite structured lead-free system Na_0.5Bi_0.5TiO₃ (NBT) whiskers were synthesized from whiskers of layered tunnel structured Na₂Ti₆O₁₃ (NT), using a topochemical route. Both NT and NBT whiskers show high aspect ratios with an average length of 15 µm and diameter of 1 µm. By prolonging the reaction time from 2 h to 6 h at 900 °C, NT whiskers with monoclinic phase completely transformed to NBT whiskers with pseudocubic phase. Typical strip-like nanodomains are observed in a NBT whisker, which are parallel to each other. The piezoelectric response amplitude for a NBT whisker indicates a large electric field induced strain, corresponding to a S_max/E_max value of as high as 300 pm/V. This work provides an in-depth instruction to prepare pure NBT whiskers, and gives the detailed piezoelectricity of NBT whiskers to promote their applications in energy harvesting and micro-electromechanical systems.     

Microwave dielectric properties of low loss microwave dielectric ceramics: A0.5Ti0.5NbO4 (A = Zn,Co)

The microwave dielectric properties of low-loss A_0.5Ti_0.5NbO₄ (A = Zn, Co) ceramics prepared by the solid-state route had been investigated. The influence of various sintering conditions on microwave dielectric properties and the structure for A_0.5Ti_0.5NbO₄ (A = Zn, Co) ceramics were discussed systematically. The Zn_0.5Ti_0.5NbO₄ ceramic (hereafter referred to as ZTN) showed the excellent dielectric properties, with ɛ_r = 37.4, Q × f = 194,000 (GHz), and τ_f = −58 ppm/°C and Co_0.5Ti_0.5NbO₄ ceramic (hereafter referred to as CTN) had ɛ_r = 64, Q × f = 65,300 (GHz), and τ_f = 223.2 ppm/°C as sintered individually at 1100 and 1120 °C for 6 h. The dielectric constant was dependent on the ionic polarizability. The Q × f and τ_f are related to the packing fraction and oxygen bond valence of the compounds. Considering the extremely low dielectric loss, A_0.5Ti_0.5NbO₄ (A = Zn and Co) ceramics could be good candidates for microwave or millimeter wave device application.     

Temperature-independent permittivity of xBaTiO3–(1−x)(0.5Bi(Mg1/2Ti1/2)O3–0.5BiScO3) ceramics

xBaTiO₃–(1−x)(0.5Bi(Mg_1/2Ti_1/2)O₃-0.5BiScO₃) or xBT–(1−x)(0.5BMT–0.5BS) (x=0.45–0.60) ceramics were prepared by using the conventional mixed oxide method. Perovskite structure with pseudo-cubic symmetry was observed in all the compositions. Dielectric measurement results indicated that all the samples showed dielectric relaxation behavior. As the content BaTiO₃ was decreased from 0.60 to 0.45, temperature coefficient of permittivity (TCε) in the range of 200–400 °C was improved from −706 to −152 ppm/°C, while the permittivity at 400 °C was increased from 1208 to 1613. The temperature stability of permittivity was further improved by using 2 mol% Ba-deficiency. It was found that lattice parameter and grain size of the 2 mol% Ba-deficient ceramics were smaller than those of their corresponding stoichiometric (S) counterparts, with TCε in the range of 200–400 °C to be improved noticeably. For example, TCε of the Ba-deficiency sample with x=0.45 was −75 ppm/°C in the temperature range of 200–400 °C and the permittivity was 1567 at 400 °C. The results obtained in this work indicated that xBT–(1−x)(0.5BMT–0.5BS) ceramics are very promising candidates for high temperature capacitor applications.