改性吸附剂对水中Cu(Ⅱ)的去除效果研究

以改性有机肥为吸附剂吸附水中Cu(Ⅱ),探究了Cu(Ⅱ)初始浓度、吸附时间、吸附温度、吸附剂用量、转速和溶液初始pH值等因素的影响。结果表明,pH=5、温度30 ℃、转速150 r/min时,改性吸附剂吸附Cu(Ⅱ)在2 h达到吸附平衡;吸附剂用量为8 g/L时,吸附量最大;吸附过程符合准二级动力学方程,等温吸附曲线符合Langmuir方程,说明其吸附为单层吸附。     

钛白石膏对重金属Pb（II）的吸附特性研究

利用工业废弃物钛白石膏作为吸附剂,研究了其对重金属Pb(II)的吸附特性。采用BET、XRD、SEM对钛白石膏进行了表征,研究了介质pH值、温度、接触时间、投加量以及离子强度对Pb(II)在钛白石膏上吸附特性的影响。结果表明,钛白石膏对Pb(II)的吸附速率较快,在70 min时就达到吸附平衡,去除率达到99.8%。升高温度和增大吸附剂的投加量,均有助于去除率的提高,表明该吸附过程为吸热反应,最适宜pH值为5.7左右。吸附动力学特征更符合准二级动力学模型,Langmuir等温模型可较好的拟合钛白石膏吸附Pb(II)的等温过程。     

膨润土负载壳聚糖对水中Cu(II)的吸附特性研究

通过水热振荡法制备了膨润土-壳聚糖复合吸附剂,并对废水中铜(Cu(II))进行吸附。通过傅立叶变换红外光谱(FT-IR)和扫描电子显微镜(SEM)对复合吸附剂进行了表征。研究结果表明,膨润土-壳聚糖复合吸附剂对铜的吸附性能优于单一膨润土。与膨润土相比,膨润土-壳聚糖复合吸附剂的形状不规则,表面粗糙疏松。在Cu(II)初始浓度为50 mg/L、pH值为7、吸附温度为30℃、接触时间为15 min的条件下,膨润土-壳聚糖复合吸附剂对Cu(II)的去除效率可达95%以上,吸附量可达到20.12 mg/g。此外,Langmuir和Freundlich模型都能很好地拟合Cu(II)在两种吸附剂上的等温吸附。膨润土壳聚糖复合吸附剂对Cu(II)的吸附过程符合准二级动力学方程。     

天然沸石负载壳聚糖去除废水中Cr(Ⅵ)研究

将80目天然沸石与90%脱乙酰度壳聚糖的O.5%醋酸溶液按1∶1.2质量比混合,使壳聚糖负载在天然沸石上,制成固体复合吸附剂,用于去除水中Cr(Ⅵ)。最佳工艺条件是:壳聚糖与天然沸石质量比为0.04,吸附剂用量为8.0g/L,废水中Cr(VI)质量浓度不大于10mg/L,pH值为4～6,吸附平衡时间为40min,Cr(VI)去除率为80%。与活性炭吸附法相比,天然沸石-壳聚糖复合吸附剂吸附效果相近,吸附平衡时间短,成本仅为其1/6。与单一的天然沸石或壳聚糖相比,该吸附剂对Cr(VI)离子的吸附速度快、吸附能力强,成本低。     

碳羟基磷灰石对废水中Zn2+的吸附性能及机理研究

利用废弃蛋壳制备碳羟基磷灰石,并利用其对废水中的Zn2 进行吸附作用研究.对影响吸附效果的几个因素,包括pH值、吸附时间、温度、吸附剂用量以及Zn2 初始浓度等进行试验,结果表明,碳羟基磷灰石对Zn2 的吸附效果很好.当废水中Zn2 初始浓度为50 mg/L、CHAP用量为3 g/L、pH为6、温度为35℃、作用时间为1 h时,Zn2 吸附率高达98.75%,其吸附容量达16.5mg/g.吸附试验还表明,该吸附符合Langmuir和Freundlich方程,对Zn2 吸附比较稳定.     

重金属离子在改性蛭石表面的竞争吸附及其动力学研究

分别利用蛭石原矿和改性蛭石为吸附剂,对水溶液中的Cu2+、Zn2+、Cd2+进行等温吸附试验,研究了吸附剂用量、溶液pH值、重金属离子浓度、吸附时间、吸附温度等环境因素对单一离子在蛭石表面吸附性能的影响,分析了蛭石吸附三种金属离子动力学机理。试验结果表明,蛭石原矿经900℃的高温膨胀及2%的CTMAB改性后,其吸附容量较蛭石原矿有明显增加。当吸附剂用量为0.3 g、pH值为5~6、金属离子初始浓度为150 mg/L、吸附时间60 min、吸附温度为室温时,改性蛭石对Cu2+、Zn2+、Cd2+三种金属离子的最大吸附率均可达90%以上。      

坡缕石黏土吸附水中Zn2+的实验研究

研究了白银坡缕石黏土对水中Zn2+的吸附效果及吸附平衡的热力学特征.结果表明,在Zn2+质量浓度为50 mg/L和100 mg/L时坡缕石用量为8.0 g/L,吸附平衡时间约为60 min,吸附量随pH值的升高而增加,随离子强度的减小而增大；吸附平衡同时符合Langmuir和Freundlich方程,由Langmuir...     

钛柱撑蒙脱石对钴离子的吸附研究

本研究将聚合阳离子Ti4+通过溶胶-凝胶法柱撑插入提纯钠化蒙脱石层间,合成钛柱撑蒙脱石(Ti-pmnt)。X射线衍射分析表明合成材料具有较大的晶面间距(d(001)=2.94 nm)。采用Ti-pmnt合成材料对钴离子进行吸附,研究了pH值、吸附剂用量、温度、吸附时间及初始浓度对Ti-pmnt吸附钴离子的影响。结果表明：最佳吸附pH值为4,吸附平衡时间为120 min,去除率达到99.97%,饱和吸附量为41.94 mg/g,且升温不利于吸附反应进行。Ti-pmnt对钴离子吸附动力学遵循拟二级动力学方程,吸附等温线符合Langmuir等温模型。     

天祝褐煤腐殖酸对Mn(Ⅱ)吸附性能的研究

采用天祝褐煤中提取的腐殖酸对Mn(Ⅱ)进行吸附性能的研究,确定了Mn(Ⅱ)的吸附平衡时间、pH值及吸附速率方程,讨论了腐殖酸用量和Mn(Ⅱ)初始浓度与吸附率和吸附量的关系。     

黄铁矿表面氰根离子的吸附规律研究

以黄铁矿为吸附剂、CN-为吸附质,考察了吸附时间、溶液pH值、黄铁矿用量等因素对吸附效果的影响,同时采用红外光谱检测法分析了黄铁矿表面吸附CN-前后的差异,并对吸附结果进行了Langmuir吸附模型拟合。结果表明,黄铁矿对氰化钠的吸附很快,1 min即达到吸附平衡,最大吸附负载达3.81 mg/g,吸附受pH影响很小;氰根离子与黄铁矿有很强的键合吸附作用;黄铁矿颗粒对氰根离子的吸附是以单分子层化学吸附为主的吸附过程。     

活化斜发沸石吸附除水中氟的研究

采用静态吸附法研究了盐酸活化斜发沸石的吸附除氟性能，研究了活化酸浓度、pH值、接触时间、吸附剂量等对吸附的影响。结果表明，活化斜发沸石的吸附性能随活化酸浓度的增加而提高。活化斜发沸石吸附氟在2h内可以接近达到吸附平衡。溶液pH对吸附性能影响很大，吸附的最佳pH值约为4。吸附等温线可用Freundich吸附等温线方程描述，吸附速率可用拟二级动力学方程描述。     

硅胶负载二氧化锰吸附重金属的研究

该文以原位合成法制得S-MnO₂吸附剂,并采用XRD、FT-IR、SEM、BET/BJH等方法进行表征。考察了吸附反应时间、吸附剂用量、水浴温度、反应溶液酸碱度对S-MnO₂吸附重金属离子的影响。结果表明,S-MnO₂的吸附效果良好,去除率近100%,尤其是Cu2+、Pb2+、Zn2+等重金属离子都达到了饮用水标准。As5+在5 min内即可达到吸附平衡且S-MnO₂几乎不受溶液酸碱度的影响,可在大范围pH（2~10）条件下使用。该材料成本低、效率高、使用范围广、固液分离快、无二次污染,在未来的矿山废水处理领域中有着广泛的应用前景。      

Removal of Mn2+ from aqueous solution by manganese oxide coated zeolite

The preparation, characterization, and adsorption properties of Mn²⁺ by manganese oxide coated zeolite (MOCZ) and its ability in removing Mn²⁺ by adsorption were investigated. Characterization analyses were used to monitor the surface properties (and their changes) of the coated layer and metal adsorption sites on the surface of MOCZ. The adsorption experiments were carried out as a function of solution pH, adsorbent concentration and contact time. Binding of Mn²⁺ ions onto MOCZ was highly pH dependent with an increase in the extent of adsorption with the pH of the media investigated. After the Mn²⁺ adsorption by MOCZ, the medium pH decreased and enhanced with increasing adsorbent concentration. The pseudo-second-order model fitted better among all the kinetic models suggesting that the adsorption mechanism might be a chemisorption process. The equilibrium data showed excellent correlation for both Langmuir and Freundlich isotherm model and this implies both monolayer adsorption and a heterogeneous surface existence in MOCZ. At pH = 6, the Mn²⁺ uptake by MOCZ attained as high as 1.1 meq Mn²⁺ g^?1 at equilibrium. The results suggested that MOCZ presents a fairly good potential as an adsorbent for an efficient removal of Mn²⁺ ions from aqueous solution.     

用Mn3O4吸附水中Cr(Ⅲ)的试验研究

以合成的Mn₃O₄为吸附剂,研究了pH、吸附时间、Mn₃O₄投加量和Cr(Ⅲ)浓度对Cr(Ⅲ)吸附效果的影响,并测定了吸附等温线。结果表明：当Cr(Ⅲ)初始浓度为10 mg/L时,发生吸附的pH范围为3.0～7.2, pH=6.5时吸附率达到93.7%,pH＞7.2时容易出现Cr(OH)₃沉淀;在25 ℃及pH=5.5的条件下,Mn₃O₄对Cr(Ⅲ)的吸附量经历一个先快速上升,后逐渐增大并达到平衡的过程,达到平衡的时间为17 h;Cr(Ⅲ)的吸附量随Mn₃O₄投加量和Cr(Ⅲ)浓度的增加而增大,吸附等温线符合Freundlich方程。     

新疆中低品位膨润土在炼油碱渣废液处理中的应用

以新疆中低品位膨润土为原料,制备出具有良好吸附能力的膨润土环境修复材料,同时研究了其作吸附剂对于炼油碱渣中挥发酚及硫离子的吸附效果及影响因素。结果表明,在吸附剂量为40g/L、振荡时间为15m in、吸附pH值为8的条件下,其对挥发酚的去除率最高可达94%。25℃常温下,膨润土环境修复材料吸附炼油碱渣废液中挥发酚的等温吸附模型满足Freund lich方程,回归方程为:Q=0.204Ce0.485。当吸附剂量为60g/L、振荡时间为30m in、pH=8时,其对炼油碱渣废液中硫离子的去除率可达53.8%。     

褐煤活性焦处理含铜、铅、砷工业废水的研究

采用褐煤活性焦吸附剂对污水中的Cu,Pb,As进行处理并回收利用.研究不同型号活性焦吸附剂对废水的处理效果影响,选取最佳的吸附剂.通过静态吸附试验对吸附时间、pH、吸附剂用量做了最终的确定.结果表明,最佳的吸附条件是选取C型吸附剂,吸附时间为120 min、废水pH约为5.0、吸附用量为1 t废水需20 kg吸附剂,Cu、Pb、As的吸附率分别可达93.09％,97.49％,98.47％.这为褐煤活性焦作为水处理吸附材料提供了有利的证实.     

交联壳聚糖吸附处理低浓度含铀废水

以天然高分子化合物壳聚糖(CTS)为原料,在碱性条件下用环氧氯丙烷对壳聚糖进行化学改性,制得不溶水的交联壳聚糖(CCTS),用作含铀废水的吸附剂,探讨了pH值、吸附剂用量、铀初始浓度、粒径对吸附的影响及其对铀的吸附动力学规律。结果表明,当废水pH=3～5左右,交联壳聚糖用量为10 mg,铀初始浓度为50 mg/L,经160 min后可达吸附平衡,铀的吸附去除率最高可达98.0%以上,交联壳聚糖对铀的吸附规律较好地符合Langmuir吸附等温式,吸附动力学模型可用准二级速率方程来描述。初始铀浓度为50 mg/L,壳聚糖和交联壳聚糖对铀的吸附去除率分别为87.4%,98.0%,交联壳聚糖对铀的吸附能力得到明显的提高。     

粉煤灰对二价金属离子的吸附特性

考察了粉煤灰对二价金属离子的吸附性能.结果表明，粉煤灰可有效吸附水溶液中的重金属离子.吸附由易到难次序为：Pb>Cu>Cd>Zn.随pH升高，去除率增加.吸附在约60 min内达到平衡.等温吸附数据符合Freundlich模型，但在pH=4.5时表现为单一线性区，而在pH= 6和pH=8时表现为2个线性区.粉煤灰对金属离子的吸附明显受到其它共存离子的影响，Cd与Pb之间存在较强的协同吸附作用.对实际废水的测试表明，粉煤灰可同时有效去除工业废水中多种金属离子.