Phase decomposition in extruded Zn-Al based alloy

Ageing characteristics of an extruded eutectoid Zn-Al based alloy were investigated using X-ray diffraction and scanning electron microscopy techniques. The extruded alloy consisted of Al rich phase and Zn rich _E and phases. The original cast eutectoid Zn-Al alloy was extruded at 250 °C. Both supersaturated _s and _s phase decomposed during extrusion and appeared as fine and coarse lamellar structures. The _E and phases particles formed in the original interdendritic region. It was found that two Zn rich phases _E and decomposed sequentially during ageing at 170, 140 °C. The decomposition of the _E phase occurred as a discontinuous precipitation in the early stage of ageing and the decomposition of the phase took place in a four phase transformation: + T + in the prolonged ageing. Two typical morphologies of the decomposition of the Zn rich phases _E and were distinctive in back-scattered scanning electron microscopy.     

Shear viscosity of liquid4He and3He-4He mixtures,especially near the superfluid transition

High-resolution measurements of are reported for liquid⁴He and³He-⁴He mixtures at saturated vapor pressures between 1.2 and 4.2 K with particular emphasis on the superfluid transition. Here is the mass density, the shear viscosity, and in the superfluid phase both and are the contributions from the normal component of the fluid ( _n and _n ). The experiments were performed with a torsional oscillator operating at 151 Hz. The mole fraction X of³He in the mixtures ranged from 0.03 to 0.65. New data for the total density and data for _n by various authors led to the calculation of . For⁴He, the results for are compared with published ones, both in the normal and superfluid phases, and also with predictions in the normal phase both over a broad range and close to T. The behavior of and of in mixtures if presented. The sloped/dT near T and its change at the superfluid transition are found to decrease with increasing³He concentration. Measurements at one temperature of versus pressure indicate a decreasing dependence of on molar volume asX(³He) increases. Comparison of at T, the minimum of _n in the superfluid phase and the temperature of this minimum is made with previous measurements. Thermal conductivity measurements in the mixtures, carried out simultaneously with those of , revealed no difference in the recorded superfluid transition, contrary to earlier work. In the appendices, we present data from new measurements of the total density for the same mixtures used in viscosity experiments. Furthermore, we discuss the data for _n determined for⁴He and for³He-⁴He mixtures, and which are used in the analysis of the data.     

On the kinds of motion in the gravitational escape of loose materials

The kinematics of the escape process of granular materials from vessels with escape holes located in a horizontal flat bottom is investigated. By using moving pictures, the boundaries of the zones of the different state and the motion of the loose material are determined.Notation A size of the side of a square hole - A_c size of the side of the cross section of a prismatic vessel - a greatest dimension of a loose material particle (length) - b width of a loose material particle - C experimental coefficient dependent on the physicomechanical properties of the loose material - c thickness of a loose material particle - D diameter of the cylindrical vessel - d diameter of the escape hole - H height of the beginning of funnel formation on the free surface of loose material - h₀ height of slopes of fixed material - h₁ dome height - h_ell height of the upper point of the intensive motion ellipsoid above the escape hole plane - S displacement of a loose material particle per unit time - W humidity - _h volume mass of loose material in the hopper - _b bulk weight (nature of the grain) - _sp specific gravity of the loose material - angle of repose of filling - _b angle of repose of shattering Translated from Inzhenerno-Fizicheskii Zhurnal, vol. 20, No. 5, pp. 815–821, May, 1971.     

Thermal conductivity of hydrocarbons in the naphthene group under high pressures

The thermal conductivity of hydrocarbons in the naphthene group has been experimentally determined. An equation is now proposed for calculating the thermal conductivity over the given temperature and pressure ranges.Notation thermal conductivity - ₂₀ and ₃₀ values of the thermal conductivity at 20 and 30°C, respectively - t₀,P₀ thermal conductivity at t₀, p₀ - _t p thermal conductivity at temperature t and under pressure P - change in thermal conductivity - P pressure - P_melt melting pressure - P₀ atmospheric pressure - t₀ 20°C temperature - T, t temperature - T_cr critical temperature - temperature coefficient of thermal conductivity - ₂₀ temperature coefficient of density - density - ₂₀ density at 20°C - _cr critical density - M molar mass - =T/T_cr referred temperature - v specific volume - v₀ specific volume at 20°C - v change in specific volume - _{3 0} a coefficient - B (t) a function of the temperature - S a quadratic functional - W_i, weight of the i-th experimental point - _i error of the i-th experimental value of thermal conductivity - B _{y, =0.6} value of B (t) at T = 0.6T_cr - B = B (t)/B_{, =0.6} referred value of coefficient B (t) Translated from Inzhenerno-Fizicheskii Zhurnal, Vol. 41, No. 3, pp. 491–499, September, 1981.     

Vibrational properties of wood along the grain

The dynamic Young's modulus (E_L) and loss tangent (tan _L ) along the grain, dynamic shear modulus (G_L) and loss tangent (tan _S) in the vertical section, and density () of a hundred spruce wood specimens used for the soundboards of musical instruments were determined. The relative acoustic conversion efficiency ( ) and a ratio reflecting the anisotropy of wood (, (E_L/G_L)(tan _S/tan _L)) were defined in order to evaluate the acoustic quality of wood along the grain. There was a positive correlation between and , and the variation in was larger than that in . It seemed logical to evaluate the acoustic quality of spruce wood by a measure of . By using a cell wall model, those acoustic factors were expressed with the physical properties of the cell wall constituents. This model predicted that the essential requirement for an excellent soundboard is smaller fibril angle of the cell wall, which yields higher and higher . On the other hand, the effects of chemical treatments on the and of wood were clarified experimentally and analyzed theoretically. It was suggested that the and of wood cannot be improved at the same time by chemical treatment.     

Thermal Conductivity of the Accidental Degeneracy and Enlarged Symmetry Group Models for Superconducting UPt3

We present theoretical calculations of the thermal conductivity for the accidental degeneracy and enlarged symmetry group models that have been proposed to explain the phase diagram of UPt ₃ . The order parameters for these models possess point nodes or cross nodes, reflecting the broken symmetries of the ground state. These broken symmetries lead to robust predictions for the ratio of the low-temperature thermal conductivity for heat flow along the axis and in the basal plane. The anisotropy of the heat current response at low temperatures is determined by the phase space for scattering by impurities. The measured anisotropy ratio, _c/ _b, provides a strong constraint on theoretical models for the ground state order parameter. The accidental degeneracy and enlarged symmetry group models based on no spin-orbit coupling do not account for the thermal conductivity of UPt ₃. The models for the order parameter that fit the experimental data for the and directions of the heat current are the 2D E_1g and E _2u models, for which the order parameters possess line nodes in the ab-plane and point nodes along the axis, and the A_1gE _1g model of Zhitomirsky and Ueda. This model spontaneously breaks rotational symmetry in the ab-plane below T_c2 and predicts a large anisotropy for the ab-plane heat current.     

Mössbauer studies of α″-Fe16N2 and α′-Fe8N films

Conversion-electron Mössbauer spectra of epitaxial -Fe₁₆N₂ and -Fe₈N films have been studied and their differences are discussed in detail. The Mössbauer spectrum of -Fe₁₆N₂ can be decomposed into three subspectra, which correspond to the 4d, 8h and 4c sites. The Mössbauer spectrum of -Fe₈N can be fitted using four spectra based on a nitrogen-atom-random-distribution model. The average hyperfine field is larger (3%) for -Fe₁₆N₂ than for -Fe₈N, which is approximately consistent with a 4.1% enhancement of the magnetic moments for -Fe₁₆N₂. The iron moments tend to locate in the film plane for -Fe₁₆N₂ and to arrange perpendicularly to the film plane for -Fe₈N.     

o′-β′ sialon ceramics

Powders of Si₃N₄, Al₂O₃ and SiO₂ were mixed with Y₂O₃ as sintering aid and hot-pressed to form o- sialon. During sintering, the o phase preferentially precipitated in the temperature region of 1550 to 1600 °C, and the phase precipitated at temperatures of 1700 °C and above. The resultant microstructure consisted of dual phases of o and . The mechanical properties of o- sialon were improved with increasing amount of the phase. When SiO₂ required for the formation of the o phase was all included in the grain boundary phase, o- sialon exhibited a three-point bending strength as much as 1400 MPa. The oxidation resistance of o- sialon is expected to improve due to the presence of the o phase, but actually was not so good due to the presence of the grain-boundary glassy phase and impurities.     

The tensile strength and ductility of continuous fibre composites

The plastic instability approach has been applied to the tensile behaviour of a continuous fibre composite. It is shown that the combination of two components with different strengths and degrees of work-hardening produces a new material with a new degree of work-hardening, which may be determined by the present analysis. Expressions for the elongation at rupture and the strength of a composite have been obtained and the results of the calculation are compared with some experimental data.List of symbols V _f volume fraction of fibres in composite - , , true strain of fibre, matrix and composite - s true stress - , , nominal stress on fibre, matrix and composite - _*, _*, _* critical stress of fibre, matrix and composite (ultimate tensile strength) - _*, _* critical strain of separate fibre and matrix - _* critical strain of composite - Q external load - A cross-sectional area - A ₀ initial value of area     

Dielectric Dispersion in Yttrium and Erbium Formate Dihydrate Crystals

The dielectric properties of Y(HCOO)₃ · 2H₂O and Er(HCOO)₃ · 2H₂O are studied. The frequency dependences (0.01 Hz to 20 kHz) of the real () and imaginary () parts of dielectric permittivity ( = – i) are shown to follow a fractal scaling law for the dielectric response of solids. In the tan versus temperature curves, a number of maxima are revealed in a narrow temperature range. The experimental data are used to evaluate the activation energies of relaxation processes. The observed anomalies are assumed to be associated with changes in the dynamics of protons in hydrogen bonds.     

High-frequency dielectric properties of Mg-Al-Si,Ca-Al-Si and Y-Al-Si oxynitride glasses

Recently developed coaxial line techniques [1] have been used to determine, at room temperature, the values of the real () and imaginary (') parts of the dielectric constants for some Mg-Al-Si, Ca-Al-Si and Y-Al-Si oxynitride glasses over the frequency range 500 MHz to 5 GHz. The frequency dependencies of and ' are consistent with the universal law of dielectric response in that (-_t8)^(n–1) and '^(n–1) for all glass compositions; the high experimental value of the exponent (n=1.0±0.1) suggests the limiting form of lattice loss [2] situation. In this frequency range, as previously reported [3] at longer wavelengths, the addition of nitrogen increases the dielectric constant, (); in both the oxide and oxynitride glasses is also influenced by the cation, being increased with cation type in the order magnesium, yttrium, calcium as at lower frequencies.     

Influence of stabilizers on Na-β′′-Al2O3 phase formation in Li2O(MgO)-Na2O-Al2O3 ternary systems

The influences of stabilizers on - and -Al2O3 phase formations in Li2O(MgO)-Na2O-Al2O3 systems were investigated. When stabilized with 4MgCO3Mg(OH)25H2O, most of the -Al2O3 phase formed below 1200°C and further - to -Al2O3 transformation with an increase of temperature was not observed. On the other hand, when stabilized with Li2CO3,-Al2O3 formation occurred by two steps. First, -Al2O3 was partly formed below 1200°C, and, second, noticeable transformation from -Al2O3 to -Al2O3 occurred at higher temperature ranges. It was shown that transient eutectic liquid in the Li2O-Na2O-Al2O3 system promoted the - to -Al2O3 transformation at higher temperatures. Uniform distribution of both Mg2+ and Li+ stabilizing ions enhanced -Al2O3 formation at low temperatures. In the Li-stabilized systems, however, homogeneous distribution of Li+ ions hindered both the formation of transient eutectic liquid and the second - to -Al2O3 phase transformation at high temperatures.     

Effect of crystalline phase, orientation and temperature on the dielectric properties of poly (vinylidene fluoride) (PVDF)

The effect of crystalline phase, uniaxial drawing and temperature on the real () and imaginary () parts of the relative complex permittivity of poly (vinylidene fluoride) (PVDF) was studied in the frequency range between 10² and 10⁶ Hz. Samples containing predominantly and phases, or a mixture of these, were obtained by crystallization from a DMF solution at different temperatures. phase samples were also obtained from melt crystallization and from commercial films supplied by Bemberg Folien. Different molecular orientations were obtained by uniaxial drawing of and phase samples. The results showed that the crystalline phase exerts strong influence on the values of and , indicating that the _a relaxation process, associated with the glass transition of PVDF, is not exclsively related to the amorphous region of the polymer. An interphase region, which maintains the conformational characteristics of the crystalline regions, should influence the process decisively. The molecular orientation increased the values of for both PVDF phases and modified its dependence with temperature over the whole frequency range studied. The influence of the crystallization and molecular orientation conditions on the dc electric conductivity (_dc) were also verified. The value of _dc was slightly higher for samples crystallized from solution at the lowest temperature and decreased with draw ratio.     

Low temperature internal friction on γ-irradiated polyvinylidene fluoride (PVDF)

A least-squares fitting of the below room temperature part of the internal friction spectra, obtained by the torsion pendulum technique on as-received and-irradiated (up to 1 Grad) strips and fibres of polyvinylidene fluoride [-(CH₂-CF₂-) _n -.; PVDF] by a superposition of single Debye functions, reveals that the spectral component features are determined not only by purely amorphous chain characteristics but also by the dosedependence of crystallinity. A careful analysis of the relaxation spectra confirms that at least one relaxation effect (236 K) is created upon irradiation. The analysis of the dose dependence of the characteristics of the (glass transition; 220 K) and _u (apparent upper glass transition; 270 K) relaxations, suggests the probable influence of crystallinity on the molecular motion in the amorphous phase. The increase of the intensity of the relaxation (190 K) is related to the irradiation-induced crystallite degradation.Fellow of the Interuniversitair Instituut voor Kernwetenschappen     

Microstructure and properties of supersaturated ZA27 alloy during natural ageing

The decomposition of the supersaturated solid solution of ZA27 alloy at room temperature has been investigated by X-ray diffraction, TEM and mechanical properties testing. Based on the results obtained, both continuous precipitation and cellular reaction occur during the decomposition process. The continuous precipitation follows the sequence: ₁ + spherical GP zones ₂ + elliptical GP zones ₃ + R + . The cellular reaction can be written: + + . The properties of the alloy depend on the microstructure. After 1 month of ageing, a series of changes of microstructure have taken place. The properties of the alloy are: _b=500 MPa, =13%,H _v=148.     

High-field electrical conduction in m Hgl2

The electrical and dielectric properties of illuminated Hgl₂ were studied at room temperature under various a.c.-signal amplitudes in the frequency range 1 Hz to 10 kHz. Below 40 H, We real part of the dielectric constant, ,was found to vag slightly with voltege for low electric fields (E < 10³V cm^–1, above which it showed a steady increase with the applied voltage. At higher frequencies, no voltage dependence of (or the geometrical capacitance) of the crystal was observed. On the other hand, the imaginary part of the dielectric constant, or the a.c. conductivity, (=_o) was found to decrease considerably with the applied voltage forE < 10³V cm^–1 at all frequencies. For higher fields (E > 10³V cm^–1), exp [C(E/)^1/2], whereC is e constant. Above 40 Hz, this variation was in good agreement with the behaviour of the bulk, resistance of the crystal. Such behaviour is discussed in the view of Richardnon-Schottky and Poole-Frenkel conduction mechanisms, which seem to be operative in Hgl₂ at room temperature.     

Numerical calculation of a generalized thermal model of radio-electronic apparatus

A method is proposed for numerical calculation of the temperature field of a generalized model of electronic equipment with high component density.Notation x,y,z,x,y spatial coordinates, m - time, sec - L_x, L_v, L_z dimensions of heated zone, m - _x, _y, _z effective thermal-conductivity coefficients of heated zone, W/m·deg - ₂ thermal conductivity of chassis, W/m·deg - a _z thermal diffusivity of heated zone along z axis, m²/sec - c₁ effective specific heat of heated zone, J/kg·deg - ₁ effective density of heated zone, kg/m³ - c₃, ₃, c₂, ₂ thermophysical characteristics of cooling agent and chassis, J/kg·deg·kg/m³ - q_v(x, ), q(x, y) volume heat-source distribution, W/m³ - q_s (x) surface heat-source distribution, W/m² - p number of cooling agent channels - Fo Fourier number - Bi Biot number - Uⁱ coolant velocity in i-th channel, m/sec - T₁(x, ), T₂(x, ), T₃(x, ) temperature distribution of heated zone, chassis, and coolant, °K - T₃₀, T₁₀(x), T₂₀(x) initial temperatures, °K - T_3in coolant temperature at input to channel, °K - T_T(x) effective temperature distribution of heat loss elements, °K - T_C temperature of external medium, °K - dimensionless heated zone temperature - _v(x) local volume heat exchange coefficient, W/m³·deg - ₁₂(x), _1C(x), _1T(x) heat liberation coefficients - W/m²·sec; ₂₁(x, y), _2c(x, y), _2T(x, y) volume heat-exchange coefficients of chassis with heated zone, medium, and cooling elements, W/m³·deg Translated from Inzhenerno-Fizicheskii Zhurnal, Vol. 40, No. 5, pp. 876–882, May, 1981.     

Investigation of the graphitic microstructure in flake and spheroidal cast irons using Raman spectroscopy

It has been demonstrated that Raman spectroscopy is an excellent technique for the characterisation of the graphite in flake and spheroidal cast irons. The Raman spectrum of graphite is highly sensitive to both structural ordering and residual stresses as can be seen from the position, intensity and shape of the Raman bands. The relative intensities and widths of the G Raman bands for flake and spheroidal graphite have been compared and found to correspond to the degree of graphitisation across the graphite. The two Raman bands of the G doublet (G₁ and G₂) change in intensity and width with distance across a graphite spheroid, although their positions remain approximately constant. In contrast, the change in intensity and width of the two Raman bands of the G doublet for flake graphite shows no discernible pattern leading to the conclusion that there is no systematic change of graphitic ordering along a graphite flake. Finally, the fact that the positions of the G₁ and G₂ Raman bands for both flake and spheroidal graphite remain relatively constant with distance implies that there are no residual stresses in the graphite in flake and spheroidal cast iron.     

On the nucleation ofθ′ and T1 on Al3Zr precipitates in Al-Li-Cu-Zr alloys

Two quaternary Al-Li-Cu-Zr alloys have been investigated using electron microscopy. Ageing at 190° C resulted in the nucleation of precipitates on the Al₃Zr/matrix interface in addition to heterogeneous nucleation on matrix dislocations. In the majority of cases, the broad, coherent face of the plans ms in contact with the Al₃Zr precipitates. Similar evidence showed that nucleation of T₁ precipitates occurred on the Al₃Zr, but to a lesser extent than. Solid-solid nucleation theory has been used to account for the Al₃Zr acting as a nucleation substrate.     

The mechanism of continuous dissolution of the lamellar structure in aged Al 22 at% Zn alloy

The mechanism of continuous dissolution was studied using transmission electron microscopy, X-ray diffraction and hardness measurements. The metastable phase was identified in the first stage of dissolution nucleating at the - boundaries. Interface dislocations at the - boundaries forming a perpendicular net in the 110 directions were identified as of screw character and of Burgers vector b=1/2a 110. During dissolution a change of shape of precipitates occurs leading to their fragmentation and to a change of the direction of boundaries into 110 directions.