柠檬酸盐对阳极箔形成速度与比电容的影响

为了提高铝电解电容器用高压阳极箔形成速度与比电容,将水合处理后的腐蚀箔在95℃、2 g/L柠檬酸钠去离子水溶液中浸泡5 min,在530 V电压化成时,形成时间缩短约2 min,化成箔比电容由0.556×10–6 F.cm–2提高至0.584×10–6 F.cm–2,阳极氧化铝膜的结构与性能得到改善。     

缓蚀剂在高压阳极箔电解扩孔中的作用机理

将高压阳极发孔铝箔在70℃、质量分数为3%的硝酸液中阳极电解扩孔,研究了添加大分子缓蚀剂聚苯乙烯磺酸(PSSA)后高压阳极箔的腐蚀机理。结果显示:添加PSSA后,腐蚀箔减薄量明显降低,质量损失率减小,并孔率降低,520 V化成的比容提高了约23%。隧道孔由孔口大、孔内小的锥子状转变为孔口小、孔内大的垒球棒状。铝箔表面的电位显著上升,而隧道孔内的电位基本保持不变,从而证明了,大分子缓蚀剂PSSA提高了铝箔表面和隧道孔口附近的电化学反应的阻力,电流主要分布到孔内,加速了孔内的扩孔过程。     

Al2O3/Au/Al2O3层状阻氚薄膜

采用磁控溅射法在316L不锈钢基体上分别沉积单层Al2O3膜、单层Au膜以及Al2O3/Au/Al2O3层状薄膜。采用气相渗透法在500℃,氘分压为0.06 MPa条件下测试了薄膜的阻氘性能。结果表明,3种薄膜氘渗透后,薄膜的形貌良好,无开裂、无剥落的现象,氘渗透率减低因子均比316L不锈钢基材增大一个数量级以上,阻氘效能按单层Al2O3膜、单层Au膜以及Al2O3/Au/Al2O3层状薄膜依次递升。Al2O3/Au/Al2O3层状薄膜的优异阻氘效能可归因于,延性的Au夹层使层状薄膜的力学性能得到显著提高;Al2O3层能阻止Au与基体间互扩散,使Au能充分发挥阻氘效能。本研究表明,由贵金属与陶瓷阻氚材料构成的层状薄膜是发展阻氚涂层的新途径。     

复合料浆热压滤法制备空间网络复合涂层及其高温氧化行为

采用复合料浆热压滤法制备出厚度在数十微米到数百微米之间可控的YSZ/YSZ、Al2O3/YSZ、Al2O3/YSZ-Al2O3和Al2O3/Al2O3复合涂层。微观形貌显示复合涂层由具有空间网络结构的YSZ或Al2O3包覆颗粒状YSZ或/和Al2O3组成。高温氧化实验结果显示,含有适量YSZ颗粒的Al2O3/YSZ-Al2O3复合涂层具有优异的抗高温氧化性能。为通过氧元素在复合涂层中的扩散行为深入分析其抗高温氧化性能,本文还基于复合涂层的微观结构及高温氧化行为表现,建立与之相对应的简化模型。     

Fe20Cr4.5Al微晶和含Y2O3弥散氧化物微晶涂层的高温氧化性能

采用自行研制的高频电脉冲沉积(HFESD)设备在Fe20Cr4.5Al合金表面分别制备了Fe20Cr4.5Al微晶涂层与Fe20Cr4.5Al-Y2O3弥散氧化物微晶涂层.在1000℃和1100℃静态空气中,对合金基体和施加涂层试样进行了200 h的恒温氧化实验.结果表明在两种实验温度条件下,含有Y2O3弥散氧化物颗粒的微晶涂层,完全消除了Al2O3氧化膜中的凸脊,细化了氧化膜的晶粒,抑制了氧化膜的剥落,大大地提高了氧化膜的致密性和粘附性.单一的微晶涂层则部分抑制了凸脊状氧化膜的形成,氧化膜由脊状氧化物和细晶氧化物混杂组成.涂层对氧化增重的影响则与氧化温度-氧化膜的生长速率有关,在1000℃下,涂层试样的氧化增重均有所降低,其中弥散氧化物微晶涂层试样的氧化增重最低;在1100℃下,施加微晶涂层和弥散氧化物涂层对氧化增重影响很小.微晶和Y2O3弥散氧化物颗粒在提高Al2O3氧化膜保护性方面具有"协同效应".     

燃煤火电厂锅炉“四管”的高温腐蚀

燃煤火电厂锅炉的高温腐蚀主要发生在受热面的“四 管”,即水冷壁管、过热器管、再热器管和省煤器管.腐蚀的主要类型是硫腐蚀、氯腐蚀、 水蒸汽腐蚀和钒腐蚀.本文综述了燃煤火电厂锅炉存在的典型高温腐蚀现象和机理,并简要 的介绍了一般防腐蚀措施.     

Corrosion-erosion resistance of Zn-Al co-cementation coatings on carbon steels in aqueous media

A novel Zn-Al co-cementation coating was obtained by a pack cementation method,This coating possesses a two-layered structure,The outer layer is mainly composed of Fe2Al3 and FeAl intermetallics with a small amount of Zn,and the inner layer consists of Zn,Fe and a small amount of Al.The corrosion-erosion resistance of Zn-Al con-cementation coatings on carbon steel was studied by a rotary corrosion method in various NaCl and H2S containing solutions and relevant SiO2 containing media,The experimental results are compared with those of carbon steels and the sherardizing and aluminizing coating ,showing that the Zn-Al co-cementation coating have excellent corrosion-erosion resistance in various aqueous media.     

Controlling limiting length of tunnels on Al foil electroetched in HCl-H2SO4 solution

The limiting length of tunnels, llim, of Al foil electro-etched in HCl-H2SO4 solution and the corresponding anodic polarization curves in the same solution were measured. It is found that there is a dependence of llim on the potential difference, △φ, between the pitting potential, φpit, and the corrosion potential, φcorr, of Al foil, when the temperature and H2SO4 concentration of HCl-H2SO4 electrolyte are changed. The dynamic equation on the tunnel growing and the linear equation between llim and △φ were deduced by analyzing the relationship among the over-potential on Al foil surface, the transport over-potential in tunnel solution and the over-potential at tunnel tip during the electro-etching. The results show that the growing velocity of tunnels decreases with their extending in length and the changing trend of llim can be judged by measuring △φ, which supplies a convenient access to explore new kinds of etchants.     

化学镀镍凝汽器黄铜管工业应用试验研究

试验研究了凝汽器黄铜管的化学镀镍技术,并将该技术成功应用于下花园发电厂3号机组凝汽器上。对化学镀镍加工的凝汽器黄铜管进行了性能检测,镀镍管镀层各项性能指标均达到了相关的技术标准。采用SEM观察了镀镍黄铜管工业应用前后的内表面和断面形貌,测量了镀镍黄铜管工业应用前后在循环冷却水中的极化电阻。试验结果表明该技术在黄铜管表面可获得耐蚀性好、结合力强、性能稳定、质量可靠的均匀阳极性镀层。实际应用证明化学镀镍黄铜管在凝汽器上具有较高的推广应用价值。     

铝电解电容器高压电子箔点蚀机理的研究

采用极化曲线和场发射扫描电镜等方法,研究了铝电解电容器高压电子箔在高温强酸性溶液中的点蚀机理.结果表明:在开路状态下铝光箔在硫酸盐酸发孔溶液中可以产生点蚀,测到自腐蚀电位就是点蚀电位;形成隧道孔后,阳极极化曲线出现点蚀电位,且点蚀过电位与隧道孔长度之间存在线性关系.根据点蚀的微电池模型及其在阳极极化下微电池的腐蚀极化图,提出产生上述现象的原因是阳极极化时带孔铝箔的表面由阴极向阳极转变,其转变的临界点即所测到的点蚀电位.