Fabrication of barium titanate ceramics via digital light processing 3D printing by using high refractive index monomer

A digital light processing (DLP) technology has been developed for 3D printing lead-free barium titanate (BTO) piezoelectric ceramics. By comparing the curing and rheological properties of slurries with different photosensitive monomer, a high refractive index monomer acryloyl morpholine (ACMO) was chosen, and a design and preparation method of BTO slurry with high solid content, low viscosity and high curing ability was proposed. By further selecting the printing parameters, the single-layer exposure time was reduced and the forming efficiency has been greatly improved. Sintered specimens were obtained after a nitrogen-air double-step debinding and furnace sintering process, and the BTO ceramics fabricated with 80 wt% slurry shows the highest relative density (95.32 %) and piezoelectric constant (168.1 pC/N). Furthermore, complex-structured BTO ceramics were prepared, impregnated by epoxy resin and finally assembly made into hydrophones, which has significance for the future design and manufacture of piezoelectric ceramic-based composites that used in functional devices.     

High-temperature oxidation behavior of monolithic Zr3[Al(Si)]4C6 and its composite incorporating 30vol% ZrB2-SiC: Providing a basis for broadening the service temperature

To provide a basis for the high-temperature oxidation of ultra-high temperature ceramics (UHTCs), the oxidation behavior of Zr₃[Al(Si)]₄C₆ and a novel Zr₃[Al(Si)]₄C₆-ZrB₂-SiC composite at 1500 °C were investigated for the first time. From the calculation results, the oxidation kinetics of the two specimens follow the oxidation dynamic parabolic law. Zr₃[Al(Si)]₄C₆ exhibited a thinner oxide scale and lower oxidation rate than those of the composite under the same conditions. The oxide scale of Zr₃[Al(Si)]₄C₆ exhibited a two-layer structure, while that of the composite exhibited a three-layer structure. Owing to the volatilization of B₂O₃ and the active oxidation of SiC, a porous oxide layer formed in the oxide scale of the composite, resulting in the degradation of its oxidation performance. Furthermore, the cracks and defects in the oxide scale of the composite indicate that the reliability of the oxide scale was poor. The results support the service temperature of the obtained ceramics.     

煤矸石粉/聚酯纤维沥青混合料盐冻损伤研究EI北大核心CSCD

针对煤矸石粉替代率50%、聚酯纤维掺量0.4%的沥青混合料,开展盐冻耦合作用(NaCl溶液质量分数为0%、7.0%、13.0%、26.5%,冻融循环次数为0、2、4、6、8)下的半圆弯曲(SCB)试验,分析了盐冻耦合作用对SCB试件内部损伤劣化过程的影响.结果表明:NaCl溶液质量分数为13.0%、冻融循环为8次时,盐冻耦合作用对沥青混合料的侵蚀破坏作用最强,试件内部损伤最严重;在煤矸石粉与矿粉质量比为1∶1、聚酯纤维掺量为0.4%的条件下,沥青混合料能够形成高黏性、致密、厚实的沥青膜以及由纤维形成的三维网状结构,从而显著降低盐冻侵蚀对沥青混合料的损伤.通过Poly2D模型对SCB试件的极限拉应力损伤量进行拟合,拟合系数为0.944.     

A cheating immune (k, n) visual cryptography scheme by using the rotation of shares

Multimedia Tools and Applications - Since Noar and Shamir introduced visual cryptography scheme (VCS), the cheating problem of VCS has absorbed much attention of scholars. The current researches on...     

锁紧机构防脱落保持架设计与分析

针对锁紧机构保持架在恶略环境下,反复振动过程中保持架上钢球脱落问题,提出了一种新型防脱落保持架设计方案,重点介绍了锁紧机构中保持架的工作形式,通过ANSYS进行有限元仿真分析,得出新型保持架结构满足刚强度要求以及热变形要求,且在随机振动6.06 g条件位移小,能有效免锁紧机构直线运动时钢球从外部脱落的可能,提高了锁紧机构工作过程中的可靠性与安全性.     

Facile synthesis of MgO–Mg2SiO4 composite ceramics with high strength and low thermal conductivity

The recycling of solid waste is a win-win solution for humans and nature. For this purpose, magnesite tailings and silicon kerf waste were employed to prepare MgO–Mg₂SiO₄ composite ceramics by solid-state reaction synthesis in the present work. Then, effects of sintering temperature and raw material ratio on as-prepared ceramics were systematically studied. As-prepared ceramics showed improvement in their relative density (from 47.55%–68.12% to 90.96%–95.25%) and cold compressive strength (from 7.34–118.66 MPa to 303.39–546.65 MPa) with the increase in sintering temperature from 1300 to 1600 °C. In addition, it was found that Si promoted synthesis process of Mg₂SiO₄ phase through transient liquid phase sintering and Fe₂O₃ accelerated sintering process through activation sintering. Consequently, the presence of Mg₂SiO₄ phase effectively improved the density and strength of MgO–Mg₂SiO₄ composite ceramic, while reducing its thermal conductivity. This work provides a potential reutilization strategy for magnesite tailings, and as-prepared products are expected to be applied in fields of construction, metallurgy, and chemical industry.     

Measuring the disparity among scientific disciplines using Library of Congress Subject Headings

Scientometrics - Examining the relationships among scientific disciplines is important today, but existing methods are limited by the contents and structure of their bibliographic databases. We...     

Microstructure and electric properties of Pr-doped Pb(Zr0.52Ti0.48)O3 ceramics

Improving the piezoelectric activity of lead zirconate titanate (PZT) ceramics is of great importance for practical applications. In this study, the influence of Pr³⁺ doping on the ferroelectric phase composition, microstructure, and electric properties on the A-site of (Pb_1-1.5xPr_x)(Zr_0.52Ti_0.48)O₃ is extensively investigated. A dense and fine microstructural sample is obtained with the introduction of Pr³⁺. The results show that the morphotropic phase boundary (MPB) moves to the rhombohedral phase region. The rhombohedral and tetragonal phases exhibit an ideal coexistence in the 4 mol.% Pr³⁺ doped (PPZT4) samples. Lead vacancy and the reduction of the potential energy barrier are considered to be the key mechanisms for donor doping, which is upheld by the Pr³⁺ doping. Combining the I-E hysteresis loops with the P-E hysteresis loops, it becomes apparent that both contribution maximums of the domain switching and residual polarisation are in PPZT4. Moreover, the thermal aging resistance of PZT is improved by doping, and the temperature stability is optimised from 83% in PZT to 96% in PPZT4. Hence, an appropriate amount of Pr³⁺ doping can effectively improve the piezoelectric activity of PZT ceramics in the MPB area and optimise the performance stability of the material under application temperatures.