Facile modifications of polyimide via chloromethylation: II. Synthesis and characterization of thermocurable transparent polyimide having methylene acrylate side groups

From chloromethylated polyimide, a useful starting material for modification of aromatic polyimides, a thermocurable transparent polyimide having acrylate side groups was prepared. In the presence of 1,8‐diazabicyclo[5,4,0]undec‐7‐ene, chloromethylated polyimide was esterified with acrylic acid to synthesize poly(imide methylene acrylate). The polymer was soluble in organic solvent, which makes it possible to prepare a planar film by spin coating. The polymer film became insoluble after thermal treatment at 230 °C for 30 min. Optical transparency of the film at 400 nm (for 1 µm thickness) was higher than 98 % and not affected by further heating at 230 °C for 250 min. Adhesion properties measured by the ASTM D3359‐B method ranged from 4B to 5B. Preliminary results of planarization testing showed a high degree of planarization (DOP) value (>0.53). These properties demonstrate that poly(imide methylene acrylate) could be utilized as a thermocurable transparent material in fabricating display devices such as TFT‐LCD. Copyright © 2004 Society of Chemical Industry     

Holographic polymer‐dispersed liquid crystal fabrication under electric field

The transmission mode of holographic polymer‐dispersed liquid crystals (HPDLCs) was developed an under electric field. It is reported that orientation of LC molecules under an electric field induces orientation of oligomer molecules giving rise to low off‐state diffraction and small grating shrinkage. Copyright © 2005 Society of Chemical Industry     

The relationship between photo-catalytic performance and optical property over Si-incorporated TiO2

This study focuses on the relationship between photo-catalytic performance and optical property over Si-incorporated TiO₂. The Si-incorporated TiO₂ particles exhibited a pure structure of anatase having a particle size of less than 20 nm and surface area of more than 190 m²/g. The absorbance did not shift to a higher wavelength in spite of the incorporation of the Si ions, but the intensity of the photoluminescence (PL) curve was the smallest in the case of the 2.0 mol% Si-TiO₂, which was related to the recombination between the excited electrons and holes. Based on these results, the photodecomposition of methyl orange in the liquid reaction was enhanced over the 2.0 mol% Si-incorporated TiO₂ compared with that over pure TiO₂: Methyl orange at 10.0 ppm was completely decomposed after 100 min when 1.0 g of the 2.0 mol% Si-incorporated TiO₂ was used.     

Modified atmosphere packaging of a mixed prepared vegetable salad dish

The aim of this study was to design a modified atmosphere package for a mixed vegetable salad consisting of 75 g of cut carrot, 55 g of cut cucumber, 20 g of sliced garlic and 50 g of whole green pepper. Respiration data of all the components were combined with film permeability data to predict package atmospheres and design optimal packages for experimental testing for improved shelf-life of the produce. The optimal package avoided minimum O₂ and maximum CO₂ tolerance limits, and chilling injury temperatures for any component. A pouch form package made of 27 mm low density polyethylene developed a modified atmosphere of 2.0–2.1% O₂ and 5.5–5.7% CO₂, which was beneficial for all components and provided better quality retention than other test packages.     

Acidogenic fermentation of blended food‐waste in combination with primary sludge for the production of volatile fatty acids

The performance of a laboratory‐scale anaerobic acidogenic fermenter fed with a mixture of blended kitchen food‐waste and primary sludge from a sewage treatment plant was investigated for the production of volatile fatty acids (VFA). The operating variables for acidogenic fermentation were kitchen food‐waste content (10 and 25 wt %), hydraulic retention time (HRT: 1, 3 and 5 days), temperature (ambient: 18 ± 2 °C, and mesophilic: 35 ± 2 °C) and pH (varied from 5.2 to 6.7). The experimental results indicated that effluent VFA concentrations and VFA production rates were higher at ambient temperature than at mesophilic conditions. The net amount of VFA with 10 wt % food‐waste increased up to 920 mg dm^?3 with an increase of HRT, but contrasting results (a decrease of 2610 mg dm^?3) were found due to the conversion of VFA into biogas in the case of 25 wt % food‐waste, which increased significantly at HRT of 3–5 days. In terms of biogas composition (CO₂ and CH₄), the organic matter was converted into CO₂ through the oxidative pathway by facultative species at low temperature while mesophilic temperature and optimum pH (6.3–7.8) played a pivotal role in increasing rate of conversion of VFA into biogas by methanogenesis. Rates of VFA production and their conversion are dependent on the food‐waste content in the mixture. Yet, the higher concentration of food‐waste (25% compared with 10%) did not produce VFA proportionally due to the increased rate of conversion of VFA into gaseous products. The maximum VFA production rate (0.318 g VFA_produced g^?1 VS_fed day^?1) was achieved in the 10 wt % food‐waste at ambient temperature and at a 5‐day HRT. Copyright © 2005 Society of Chemical Industry     

Neue Entwicklungen beim Hohlkatoden‐Gasflusssputtern. New Developments in Hollow Cathode Gas Flow Sputtering

The gas flow sputter technique was invented a few years ago particularly for the inexpensive fabrication of sophisticated ceramic layers. Meanwhile, it has matured and become increasingly powerful. Today it is on the verge of being applied in industrial fabrication processes. The present article gives an overview over the method, its characteristics and the numerous applications.     

Characteristics of nitrogen and phosphorus removal in SBR and SBBR with different ammonium loading rates

Laboratory scale experiments were conducted to study the deterioration of enhanced biological phosphorus removal (EBPR) due to influent ammonium concentration, and to compare the performance of two types of sequencing batch reactor (SBR) systems, a conventional SBR and sequencing batch biofilm reactor (SBBR). Both in SBR and SBBR, the total nitrogen removal efficiency decreased from 100% to 53% and from 87.5% to 54.4%, respectively, with the increase of influent ammonium concentration from 20 mg/l to 80 mg/l. When the influent ammonium concentration was as low as 20 mg/l (C: N: P=200: 20: 15), denitrifying glycogen-accumulating organisms (DGAOs) were successfully grown and activated by using glucose as a sole carbon source in a lab-scale anaerobic-oxic-anoxic (A₂O) SBR. In the SBR, due to the effect of incomplete denitrification and pH drop, the nitrogen and phosphorus removal efficiency decreased from 77% to 33.3% when the influent ammonium concentration increased from 20 mg/l to 80 mg/l. However, in the SBBR, simultaneous nitrification/denitrification (SND) occurred, and the nitrification rate in the aerobic phase did not change remarkably in spite of the increase in influent ammonium concentration. Phosphorus removal was not affected by the increase of influent ammonium concentration.     

A positive‐working photosensitive polyimide based on thermal cross‐linking and acidolytic cleavage

A novel positive‐working photosensitive polyimide (PSPI) based on a poly(hydroxyimide) (PHI), a crosslinking agent having vinyl ether groups, and a photoacid generator (PAG) was prepared. The PHI as a base resin of the three‐component PSPI was synthesized from 4,4′‐oxydiphthalic anhydride and 2,2′‐bis(3‐amino‐4‐hydroxyphenyl)hexafluoropropane through ring‐opening polymerization and subsequent thermal cyclization. 2,2′‐bis(4‐(2‐(vinyloxy)ethoxy)phenyl)propane (BPA‐DEVE) was used as a vinylether compound and diphenyliodonium 5‐hydroxynaphthalene‐1‐sulfonate was used as a PAG. The phenolic hydroxyl groups of the PHI and the vinyl ether groups of BPA‐DEVE are thermally crosslinked with acetal structures during prebake step, and the crosslinked PHI becomes completely insoluble in an aqueous basic solution. Upon exposure to UV light (365 nm) and subsequent postexposure bake (PEB), a strong acid generated from the PAG cleaves the crosslinked structures, and the exposed area is effectively solubilized in the alkaline developer. The dissolution behavior of the PSPI containing each 11.5 wt % of BPA‐DEVE and of the PAG was studied after UV exposure (365 nm) and PEB. It was found that the difference in dissolution rates between exposed and unexposed areas was enough to get high resolution. A fine positive pattern with a resolution of 5 μm in a 3.7‐μm‐thick film was obtained from the three‐component PSPI. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Polyaniline-multiwalled carbon nanotube composites: Characterization by WAXS and TGA

Polyaniline/carboxylated multi-walled carbon nanotube (PAni/c-MWNT) nanocomposites have been synthesized by micellar aided emulsion polymerization with various c-MWNTs compositions, viz., 0.5, 1, 5, and 10 wt %. The microcrystalline parameters such as the nanocrystal size (〈N〉), lattice strain (g), interplanar distance (d_hkl), width of the crystallite size distribution, surface weighted crystal size (D_s), and volume of the ordered regions were calculated from the X-ray data by using two mathematical models, namely the Exponential distribution and Reinhold distribution methods. The effects of heat ageing on the microcrystalline parameters of the PAni/c-MWNT nanocomposites were also studied and the results are correlated. The thermal stability and electrical resistivity of the PAni/c-MWNT nanocomposites were examined with thermogravimetric analysis (TGA) and a conventional two-probe method. The TGA data indicate that the thermal stability of the nanocomposites improved after the incorporation of c-MWNTs. The influence of temperature on the resistivity of the nanocomposites was also measured. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci 2008