Synthesis of amphiphilic magnetic microspheres by dispersion copolymerization of styrene and poly(ethylene oxide) macromonomer

Amphiphilic magnetic microspheres ranging in diameter from 5 to 100 µm were prepared by dispersion copolymerization of styrene and poly(ethylene oxide) vinylbenzyl (PEO‐VB) macromonomer (MPEO) in the presence of Fe₃O₄ magnetic fluid. The effects of various polymerization parameters on the average particle size were systematically investigated. The average particle size was found to increase with increasing styrene concentration and initiator concentration. It also increased with decreasing stabilizer concentration and molecular weight of MPEO. The content of the hydroxyl groups localized in the microspheres ranged from 0.01 to 0.2 mmol g^?1. © 2003 Society of Chemical Industry     

Evaluating the impact of CASE: an empirical comparison of retrospective and cross-sectional survey approaches

The purpose of this paper is to evaluate two methods of assessing the productivity and quality impact of Computer Aided Software Engineering (CASE) and Fourth Generation Language (4GL) technologies: (1) by the retrospective method; and (2) the cross-sectional method. Both methods involve the use of questionnaire surveys. Developers' perceptions depend on the context in which they are expressed and this includes expectations about the effectiveness of a given software product. Consequently, it is generally not reliable to base inferences about the relative merits of CASE and 4GLs on a cross-sectional comparison of two separate samples of users. The retrospective method that requires each respondent to directly compare different products is shown to be more reliable. However, there may be scope to employ cross-sectional comparisons of the findings from different samples where both sets of respondents use the same reference point for their judgements, and where numerical rather than verbal rating scales are used to measure perceptions.     

The organisational learning effects of management accounting information under advanced manufacturing technology

This study empirically examined the organisational learning effects of the nonfinancial performance information provided by management accounting information systems (MAISs) under advanced manufacturing technology (AMT). In this study, a target costing system and the frequent and quick reporting of information were considered the facilitators of learning. First, we examined the relationships between AMT level and the amount of nonfinancial performance information produced by MAISs. The empirical results showed that there are significant positive relationships between the level of AMT and nonfinancial performance information. With a systems approach, we also proved the impact of the relationships among AMT levels, nonfinancial performance information and learning facilitators on the organisational performance of a firm. The results of our research suggest that under a high level of AMT, for the provision of information to result in an increase of performance through organisational learning, a target costing system must be introduced and a large amount of information should be provided frequently and quickly. The results of this study also showed that although AMT level may be low, fairly well-arranged facilitators and a moderately large amount of information may be necessary for the improvement of performance. In conclusion, effective organisational learning depends on the provision of relevant information as well as efficient learning support mechanisms.     

Structure and properties of CE/CTBN/EP blends: II. Effect of EP on the mechanical properties and thermostability of the CE/CTBN system

Carboxyl‐terminated butadiene‐acrylonitrile rubber (CTBN) has often been used to improve the toughness of cyanate ester (CE) resin while sacrificing modulus and thermostability. In this paper, the addition of the appropriate amount of epoxy resin (EP) to the CE/CTBN system is shown to not only increase the modulus and thermostability of the blend, but also improve the toughness. The values of impact strength showed a maximum for the CE/CTBN/EP 100/5/5 blend. The temperature of 10 % weight loss (T₁₀) improves from 376 °C for CE/CTBN 100/5 to 407 °C for the CE/CTBN/EP 100/5/2.5 blend. It is proposed that addition of the appropriate amount of EP can decrease the mobility and increase the stability of CTBN via the reaction between the terminal carboxyl group of CTBN and the hydroxyl group of EP. But a very high EP concentration will decrease the crosslinking density of CE, consequently reducing the mechanical properties and thermostability of the blends. Copyright © 2004 Society of Chemical Industry     

Facile modifications of polyimide via chloromethylation: II. Synthesis and characterization of thermocurable transparent polyimide having methylene acrylate side groups

From chloromethylated polyimide, a useful starting material for modification of aromatic polyimides, a thermocurable transparent polyimide having acrylate side groups was prepared. In the presence of 1,8‐diazabicyclo[5,4,0]undec‐7‐ene, chloromethylated polyimide was esterified with acrylic acid to synthesize poly(imide methylene acrylate). The polymer was soluble in organic solvent, which makes it possible to prepare a planar film by spin coating. The polymer film became insoluble after thermal treatment at 230 °C for 30 min. Optical transparency of the film at 400 nm (for 1 µm thickness) was higher than 98 % and not affected by further heating at 230 °C for 250 min. Adhesion properties measured by the ASTM D3359‐B method ranged from 4B to 5B. Preliminary results of planarization testing showed a high degree of planarization (DOP) value (>0.53). These properties demonstrate that poly(imide methylene acrylate) could be utilized as a thermocurable transparent material in fabricating display devices such as TFT‐LCD. Copyright © 2004 Society of Chemical Industry     

Global practical stabilization of planar linear systems in the presence of actuator saturation and input additive disturbance

In this note, we revisit the problem of global practical stabilization for planar linear systems subject to actuator saturation and input additive disturbances. A parameterized linear state feedback law is designed such that, by tuning the value of the parameter, all trajectories of the closed-loop system converge to an arbitrarily small neighborhood of the origin in a finite time and remain in there.