Active,passive and transpassive dissolution of a nickel base super alloy in concentrated acid mixture solution

The electrochemical and corrosion behaviour of a nickel base super alloy (C-263) has been investigated in the deaerated binary and ternary solution mixture of concentrated phosphoric acid, acetic acid, sulphuric acid, nitric acid or water using potentiostatic technique at 35°C. The possibilities of electropolishing of this alloy in these solution mixtures have been also explored. The alloy showed distinct active, passive and transpassive behaviour in the experimental solutions. The alloy remained active and turned passive in the negative potential region. Transpassive dissolution of the alloy is observed and electropolishing is achieved in this region. The best electropolishing is obtained in 50% H₃PO₄ + 40% CH₃COOH + 10% H₂SO₄. Higher content of water in the electrolytic solution is not useful for electropolishing of the alloy The experimental results also suggest that a current plateau in the transpassive potential region is not a sufficient condition to achieve electropolishing.     

Physicochemical and Functional Properties of Freeze-Dried and Oven Dried Corn Gluten Meals

The physicochemical and functional properties of convection oven- and freeze-dried gluten meals of two corn varieties were evaluated. The physicochemical properties (water solubility index, water absorption index, Hunter color parameters, and bulk density) and functional properties (water absorption, oil absorption, least gelation concentration, protein solubility, and emulsification properties) of convection-oven and freeze-dried corn gluten meals were compared with each other and soy flour. Freeze-dried corn gluten meals was observed to have lower bulk density (0.244-0.263 kg/m³) and was lighter in color (high L and ΔE) compared to their counterpart convection oven-dried gluten meals. Freeze-dried gluten meals from both corn varieties showed significantly higher oil absorption, water absorption, pH, emulsification, and protein solubility compared to oven-dried corn gluten meals. The gluten meals from both corn varieties had lower water absorption and bulk density but higher oil absorption than soy flour, suggesting the hydrophobic nature of corn proteins. Corn gluten meals formed thin (pourable) emulsions compared to soy flour emulsions, which were thick salad dressing type. Freeze- and convection oven-dried corn gluten meals showed significantly lower protein solubility measured at different pH than soy flour.     

A comparison of leaf-spring with aircushion trailer suspensions in the transport environment

Packaging engineers need to be able to accurately determine the forces present in the shipping environment in order to protect packaged goods. The purpose of this study was to determine the vertical vibration levels measured in three separate truck-trailer suspension systems; conventional leaf-spring, conventional air-ride and damaged air-ride. The main conclusion reached in this study is that the air-ride suspension when maintained gives lower power density (PD) levels on all road surfaces studied. A damaged air-ride suspension and leaf-spring suspension are very similar in response frequencies, although the damaged air-ride produces higher vibration levels at lower frequencies.     

Response spectrum analysis of piping systems with elastic-plastic gap supports

A new seismic support device and its application in piping systems is described. The device, E-BAR (patented), can be cost effectively used for snubber replacement programs, mitigation of hydraulic transients, pipe whip and as a thermal stop. The device has pre-set gaps to allow free thermal movement. During a seismic or other dynamic load event, if the pipe movement exceeds the gap dimension, the device acts as an elastic or elastic-plastic restraint. The device also has a unique design feature for not exceeding the restraint force beyond a specified limit design value. To analyze piping systems with gap supports having elastic-plastic characteristics, modal analysis procedures for both response spectrum and time history methods are developed. The comparison of responses obtained from the procedures with nonlinear time history analysis and test results available in the literature shows excellent correlation. A pilot program conducted for snubber replacement with E-BARs demonstrates that the limit force feature of E-BAR makes them very attractive for snubber replacement. This is because a particular E-BAR with a specified limit design force can be selected, such that, the E-BAR replacing the snubber does not require any modifications be made to the existing support steel and hardware.     

A high-current and high-temperature 6H-SiC thyristor

A 6H-SiC thyristor has been fabricated and characterized. A forward breakover voltage close to 100 V and a pulse switched current density of 5200 A/cm² have been demonstrated. The thyristor is shown to operate under pulse gate triggering for turn-on and turn-off, with a rise time of 43 ns and a fall time of less than 100 ns. The forward breakover voltage is found to decrease by only 4% when the operating temperature is increased from room temperature to 300°C. It is found that anode ohmic contact resistance dominates the device forward drop at high current densities     

What decides: high mortality in paediatric acute renal failure?

Forty paediatric cases of A.R.F. (Acute Renal Failure) of various aetiology were included in the study. 60% of patients were less than 4 years of age with male predominance. 80% cases reported to us very late with oligoanuria of more than 24 hours (2-7 days). Diarrhoea, vomiting and fever were other dominant symptoms. Maximum cases were severely anaemic (87.5%) with mean Hb 7.73 +/- 1.9 gm%. 40% cases were of underweight while only one case (2.5%) was of over weight, inspite of volume excess in 40% cases. All 24 cases, who were estimated for serum albumin, found to have marked hypoalbuminemia. Mortality was found to be as high as 65% inspite of effective peritoneal dialysis in all cases. High mortality seems to be due to profound anuria of many days (because of marked delay in reaching the hospital), fever and malnutrition besides other factors as aetiology.     

Electrical conductivity in iodine-doped ethyl cellulose

The electrical conductivity of solution-grown ethyl cellulose (EC) films, 5–30 μm thick, has been studied in the sandwich configuration (metal–EC–metal) as a function of iodine concentration from 0.5 to 5.0 wt% ratio. The studies were conducted in the temperature range 333–383 K, while the field was varied over the range (3.0–5.5) × 10⁴V/cm. Aluminium was used as the lower electrode, while the upper electrode was of Al, Ag, Cu, Au or Sn. Certain transient effects such as a large burst of current immediately after the application of field were observed. An attempt was made to identify the nature of the current by comparing the observed dependence on electric field, electrode material and temperature with the respective characteristic features of the existing theories of electrical conduction. The results show that the electrical conduction follows Ohm's law at lower fields, while at higher fields, space-charge limited current (SCLC) was observed. It was also found that Richardson–Schottky emission was responsible, to some extent, for the transport of charge carriers in the polymer. The conductivity of the films increased on doping with iodine. The dopant molecules are considered to act as additional trapping centes and provide links between the polymer molecules in the amorphous region, thus resulting in the formation of charge transfer complexes.     

One-step oxidation of cyclohexane to adipic acid

Liquid-phase oxidation of cyclohexane with Co(III) catalyst and gaseous oxygen was found to be influenced by reaction temperature, catalyst concentration and the duration. Maximum adipic acid product selectivity (77%) with about 85% cyclohexane conversion was attained at 100°C using catalyst: cyclohexane molar ratio 0·08. Under these conditions more than 80% cyclohexane was converted in the first hour, although selectivity to adipic acid continued to increase for the next 5 h. Cyclohexyl acetate and cyclohexyl monoadipate were identified as important intermediates. This study supports the mechanism proposed by Schultz, J. G. D. and Opchenko, A., J. Org. Chem., 38 (21) (1973) 3729.