Microstructure Development of Oxycarbide Composites during Active-Filler-Controlled Polymer Pyrolysis

The microstructure development of a ceramic composite material fabricated by active-filler-controlled polymer pyrolysis (AFCOP) was investigated. During heating of a polysiloxane precursor mixed with titanium powder in argon atmosphere up to 1400°C, thermally induced decomposition of the polymer phase is combined with simultaneous carburization of the transition metal filler. Precipitation of nanocrystalline titanium carbide at the filler particle surface starts above 400°C, and larger, faceted carbide particles have growth above 800°C. A skeleton of turbostratic carbon is formed above 800°C in the polymer-derived silicon oxycarbide matrix from which b-silicon carbide and cristobalite crystallize above 1000°C. A pronounced reduction in linear shrinkage involved in polymer–ceramic conversion is observed. The shrinkage reduction ranges from more than 25% for the filler-free precursor to less than 10% in the presence of 30 vol% of the titanium filler. Thus, active-filler-controlled pyrolysis offers the possibility of controlling shrinkage and porosity formation during polymer–ceramic conversion in order to fabricate bulk components from organometallic polymer precursor systems.     

Spherical sample holders to improve the susceptibility measurement of superparamagnetic materials

The design of two custom sample holders with a spherical cavity for commercial vibrating sample magnetometer systems is described. For such cavities, the magnetization M[over ->] and the internal magnetic field H(i)[over ->] of a sample are both homogeneous. Consequently, the material parameter M(H(i)) of a sample can be determined even for liquids and powders with a high magnetic susceptibility.     

Perinatal Obesity Induces Hepatic Growth Restriction with Increased DNA Damage Response,Senescence, and Dysregulated Igf-1-Akt-Foxo1 Signaling in Male Offspring of Obese Mice

Maternal obesity predisposes for hepato-metabolic disorders early in life. However, the underlying mechanisms causing early onset dysfunction of the liver and metabolism remain elusive. Since obesity is associated with subacute chronic inflammation and accelerated aging, we test the hypothesis whether maternal obesity induces aging processes in the developing liver and determines thereby hepatic growth. To this end, maternal obesity was induced with high-fat diet (HFD) in C57BL/6N mice and male offspring were studied at the end of the lactation [postnatal day 21 (P21)]. Maternal obesity induced an obese body composition with metabolic inflammation and a marked hepatic growth restriction in the male offspring at P21. Proteomic and molecular analyses revealed three interrelated mechanisms that might account for the impaired hepatic growth pattern, indicating prematurely induced aging processes: (1) Increased DNA damage response (γH2AX), (2) significant upregulation of hepatocellular senescence markers (Cdnk1a, Cdkn2a); and (3) inhibition of hepatic insulin/insulin-like growth factor (IGF)-1-AKT-p38-FoxO1 signaling with an insufficient proliferative growth response. In conclusion, our murine data demonstrate that perinatal obesity induces an obese body composition in male offspring with hepatic growth restriction through a possible premature hepatic aging that is indicated by a pathologic sequence of inflammation, DNA damage, senescence, and signs of a possibly insufficient regenerative capacity.     

Monomolecular and Bimolecular Recombination of Electron–Hole Pairs at the Interface of a Bilayer Organic Solar Cell

While it has been argued that field‐dependent geminate pair recombination (GR) is important, this process is often disregarded when analyzing the recombination kinetics in bulk heterojunction organic solar cells (OSCs). To differentiate between the contributions of GR and nongeminate recombination (NGR) the authors study bilayer OSCs using either a PCDTBT‐type polymer layer with a thickness from 14 to 66 nm or a 60 nm thick p‐DTS(FBTTh₂)₂ layer as donor material and C₆₀ as acceptor. The authors measure JV‐characteristics as a function of intensity and charge‐extraction‐by‐linearly‐increasing‐voltage‐type hole mobilities. The experiments have been complemented by Monte Carlo simulations. The authors find that fill factor (FF) decreases with increasing donor layer thickness (L_p) even at the lowest light intensities where geminate recombination dominates. The authors interpret this in terms of thickness dependent back diffusion of holes toward their siblings at the donor–acceptor interface that are already beyond the Langevin capture sphere rather than to charge accumulation at the donor–acceptor interface. This effect is absent in the p‐DTS(FBTTh₂)₂ diode in which the hole mobility is by two orders of magnitude higher. At higher light intensities, NGR occurs as evidenced by the evolution of s‐shape of the JV‐curves and the concomitant additional decrease of the FF with increasing layer thickness.     

Advanced Characterization and Optimization of NiOx:Cu-SAM Hole-Transporting Bi-Layer for 23.4% Efficient Monolithic Cu(In,Ga)Se2-Perovskite Tandem Solar Cells

The performance of five hole-transporting layers (HTLs) is investigated in both single-junction perovskite and Cu(In, Ga)Se₂ (CIGSe)-perovskite tandem solar cells: nickel oxide (NiO_x,), copper-doped nickel oxide (NiO_x:Cu), NiO_x+SAM, NiO_x:Cu+SAM, and SAM, where SAM is the [2-(3,-6Dimethoxy-9H-carbazol-9yl)ethyl]phosphonic acid (MeO-2PACz) self-assembled monolayer. The performance of the devices is correlated to the charge-carrier dynamics at the HTL/perovskite interface and the limiting factors of these HTLs are analyzed by performing time-resolved and absolute photoluminescence ((Tr)PL), transient surface photovoltage (tr-SPV), and X-ray/UV photoemission spectroscopy (XPS/UPS) measurements on indium tin oxide (ITO)/HTL/perovskite and CIGSe/HTL/perovskite stacks. A high quasi-Fermi level splitting to open-circuit (QFLS-V_oc) deficit is detected for the NiO_x-based devices, attributed to electron trapping and poor hole extraction at the NiO_x-perovskite interface and a low carrier effective lifetime in the bulk of the perovskite. Simultaneously, doping the NiO_x with 2% Cu and passivating its surface with MeO-2PACz suppresses the electron trapping, enhances the holes extraction, reduces the non-radiative interfacial recombination, and improves the band alignment. Due to this superior interfacial charge-carrier dynamics, NiO_x:Cu+SAM is found to be the most suitable HTL for the monolithic CIGSe-perovskite tandem devices, enabling a power-conversion efficiency (PCE) of 23.4%, V_oc of 1.72V, and a fill factor (FF) of 71%, while the remaining four HTLs suffer from prominent V_oc and FF losses.     

Nanoimprint Lithography Facilitated Plasmonic-Photonic Coupling for Enhanced Photoconductivity and Photocatalysis

Imprint lithography has emerged as a reliable, reproducible, and rapid method for patterning colloidal nanostructures. As a promising alternative to top-down lithographic approaches, the fabrication of nanodevices has thus become effective and straightforward. In this study, a fusion of interference lithography (IL) and nanosphere imprint lithography on various target substrates ranging from carbon film on transmission electron microscope grid to inorganic and dopable polymer semiconductor is reported. 1D plasmonic photonic crystals are printed with 75% yield on the centimeter scale using colloidal ink and an IL-produced polydimethylsiloxane stamp. Atomically smooth facet, single-crystalline, and monodisperse colloidal building blocks of gold (Au) nanoparticles are used to print 1D plasmonic grating on top of a titanium dioxide (TiO₂) slab waveguide, producing waveguide-plasmon polariton modes with superior 10 nm spectral line-width. Plasmon-induced hot electrons are confirmed via two-terminal current measurements with increased photoresponsivity under guiding conditions. The fabricated hybrid structure with Au/TiO₂ heterojunction enhances photocatalytic processes like degradation of methyl orange (MO) dye molecules using the generated hot electrons. This simple colloidal printing technique demonstrated on silicon, glass, Au film, and naphthalenediimide polymer thus marks an important milestone for large-scale implementation in optoelectronic devices.     

2D van der Waals Heterojunction of Organic and Inorganic Monolayers for High Responsivity Phototransistors

Van der Waals (vdW) heterostructures composing of organic molecules with inorganic 2D crystals open the door to fabricate various promising hybrid devices. Here, a fully ordered organic self-assembled monolayer (SAM) to construct hybrid organic–inorganic vdW heterojunction phototransistors for highly sensitive light detection is used. The heterojunctions, formed by layering MoS₂ monolayer crystals onto organic [12-(benzo[b]benzo[4,5]thieno[2,3-d]thiophen-2-yl)dodecyl)]phosphonic acid SAM, are characterized by Raman and photoluminescence spectroscopy as well as Kelvin probe force microscopy. Remarkably, this vdW heterojunction transistor exhibits a superior photoresponsivity of 475 A W⁻¹ and enhanced external quantum efficiency of 1.45 × 10⁵%, as well as an extremely low dark photocurrent in the pA range. This work demonstrates that hybridizing SAM with 2D materials can be a promising strategy for fabricating diversified optoelectronic devices with unique properties.