Synthesis and characterization of biocompatible hydroxyapatite coated ferrite

Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

Synthesis of amphiphilic magnetic microspheres by dispersion copolymerization of styrene and poly(ethylene oxide) macromonomer

Amphiphilic magnetic microspheres ranging in diameter from 5 to 100 µm were prepared by dispersion copolymerization of styrene and poly(ethylene oxide) vinylbenzyl (PEO‐VB) macromonomer (MPEO) in the presence of Fe₃O₄ magnetic fluid. The effects of various polymerization parameters on the average particle size were systematically investigated. The average particle size was found to increase with increasing styrene concentration and initiator concentration. It also increased with decreasing stabilizer concentration and molecular weight of MPEO. The content of the hydroxyl groups localized in the microspheres ranged from 0.01 to 0.2 mmol g^?1. © 2003 Society of Chemical Industry     

Electrochemical synthesis and characterization of chloride doped polyaniline

Chloride doped polyaniline conducting polymer films have been prepared in a protic acid medium (HCl) by potentiodynamic method in an electrochemical cell and studied by cyclic voltammetry and FTIR techniques. The FTIR spectra confirmed Cl^- ion doping in the polymers. The polymerization rate was found to increase with increasing concentration of aniline monomer. But the films obtained at high monomer concentration were rough having a nonuniform flaky polyaniline distribution. Results showed that the polymerization rate did not increase beyond a critical HCl concentration. Cyclic voltammetry suggested that, the oxidation-reduction current increased with an increase in scan rate and that the undoped polyaniline films were not hygroscopic whereas chloride doped polyaniline films were found to be highly hygroscopic.     

Degree-of-polarization and eye-closure penalty associated with optical signals with orthogonal polarizations

We perform a systematic measurement of the degree-of-polarization (DOP) and eye-closure penalty for optical signals with orthogonal polarizations. We find that the symmetry of DOP is maintained for the orthogonal polarizations under both first and higher order polarization-mode dispersion (PMD), whereas the symmetry of eye-closure penalty is broken under second-order PMD. An orthogonal polarization pair can have large disparity of eye-closure penalty despite an identical DOP. We also demonstrate a novel approach to estimate the maximum eye-closure penalty asymmetry with three orthogonal polarizations on the Poincare/spl acute/ sphere.     

On-demand learning for a wireless campus

The current Internet and wireless networks are harsh environments for transporting high-bandwidth multimedia data. We examine the technical issues involved, and describe an end-to-end solution to support a Web-based learn-on-demand system that operates in a wireless campus environment.     

A new Pd-oxide-Al/sub 0.3/Ga/sub 0.7/As MOS hydrogen sensor

A new and interesting Pd-oxide-Al/sub 0.3/Ga/sub 0.7/As MOS hydrogen sensor has been fabricated and studied. The steady-state and transient responses with different hydrogen concentrations has been measured at various temperatures. Based on the large Schottky barrier height and presence of oxide layer, the studied device exhibits a high hydrogen detection sensitivity and wide temperature operating regime. The studied device exhibits the low-leakage current and obvious current changes when exposed to hydrogen-contained gas. Even at room temperature, a very high hydrogen detection sensitivity of 155.9 is obtained when a 9090 ppm H/sub 2//air gas is introduced. Furthermore, when exposed to hydrogen-contained gas at 95/spl deg/C, both the forward and reverse currents are substantially increased with increased hydrogen concentration. In other words, the studied device can be used as a hydrogen sensor under the applied bidirectional bias. Under the applied voltage of 0.35 V and 9090 ppm H/sub 2//air hydrogen ambient, a fast adsorption response time about 10 s is found. The transient and steady-state characteristics of hydrogen adsorption are also investigated.     

深层搅拌桩防渗墙质量通病及防治

深层搅拌桩防渗漏墙技术可靠,工序简单、易于操作和控制,造价低廉,因而在堤防工程建设中得到了广泛的应用。文章简述了该技术的施工过程,并分析了该技术的质量通病,提出了防治措施,得出实际应用效果。     

A novel InP/InGaAs TEBT for ultralow current operations

A novel InP/InGaAs tunneling emitter bipolar transistor (TEBT) is fabricated and demonstrated. The studied device exhibits a very small collector-emitter offset voltage of 40 mV and an extremely wide operation regime. The operation region is larger than 11 decades in magnitude of collector current (10/sup -12/ to 10/sup -1/A). A current gain of 3 is obtained even if the device is operated at an ultralow collector current of 3.9 /spl times/ 10/sup -12/A (1.56 /spl times/ 10/sup -7/A/cm/sup 2/). Furthermore, the common-emitter breakdown voltage of the studied device is higher than 2 V. Consequently, the studied device shows a promise for low supply voltage, and low-power consumption circuit applications.     

高抗挤厚壁套管的性能及应用效果评价

中原油田套管损坏的主要原因是现有套管强度不够,无法抵抗盐膏层段的巨大外挤力。开发了TP130TT型高抗挤厚壁套管,其强度能很好地抵抗盐膏层巨大外挤力。实验室试验表明,各项性能指标达到了设计要求,现场使用取得了很好的效果,解决了中原油田盐膏层段套管强度不足的难题。     

A fully soft-switched extended-period quasi-resonantpower-factor-correction circuit

This paper presents the design criteria, procedure, and implementation of a soft-switched power-factor-correction (PFC) circuit based on the extended-period quasi-resonant (EPQR) principles. All power electronic devices including switches and diodes in the circuit are fully soft switched. The design method is demonstrated in a prototype circuit. The operating principles are confirmed with computer simulation and experimental results. A comparison of the EP-QR operation and zero-voltage-transition (ZVT) pulse-width modulation (PWM) method