Growth and corrosion resistance of molybdate modified zinc phosphate conversion coatings on hot-dip galvanized steel

The modified zinc phosphate conversion coatings（ZPC） were formed on hot-dip galvanized（HDG） steel when 1.0 g/L sodium molybdate were added in a traditional zinc phosphate solution. The growth performance and corrosion resistance of the modified ZPC were investigated by SEM, open circuit potential（OCP）, mass gain, potentiodynamic polarization and electrochemical impedance spectroscopy（EIS） measurements and compared with those of the traditional ZPC. The results show that if sodium molybdate is added in a traditional zinc phosphate solution, the nucleation of zinc phosphate crystals is increased obviously; zinc phosphate crystals are changed from bulky acicular to fine flake and a more compact ZPC is obtained. Moreover, the mass gain and coverage of the modified ZPC are also boosted. The corrosion resistance of ZPC is increased with an increase in coverage, and thus the corrosion protection ability of the modified ZPC for HDG steel is more outstanding than that of the traditional ZPC.     

水性丙烯酸树脂作为金属表面钝化剂的研究现状

水性丙烯酸树脂作为金属表面处理剂已经有广泛的研究和应用。综述了水性丙烯酸树脂作为主要成膜物质在金属基体钝化成膜的方法、种类及其研究进展,指出其钝化膜的耐蚀性与铬酸盐钝化膜相当,有些甚至超过了铬酸盐钝化膜,具有替代铬酸盐钝化膜的潜力。     

热浸镀锌铝系列合金镀层的研究进展

综述了近15年来国内外学者对热浸镀Zn-Al系列镀层研究的新成果。重点介绍了Galfan(Zn-5%AlRE)、Zn-23%Al-0.3%Si和Galvalume(Zn-55%Al-1.6%Si)镀层的组织结构和性能以及Zn-Al系列镀层应用在批量热镀锌中所遇到的问题及解决办法。     

镀锌层钼酸盐钝化膜腐蚀行为的研究

钼酸盐钝化能够显著提高镀锌层的耐腐蚀能力。一定工艺下获得的钼酸盐钝化膜的耐蚀性与铬酸盐钝化膜的耐蚀性相当,在酸性腐蚀介质下甚至可优于铬酸盐钝化。钼酸盐钝化中存在裂纹会降低钝化膜在中性盐雾腐蚀或盐水浸泡腐蚀中的耐蚀能力,而在酸性盐雾腐蚀下钝化膜的耐蚀能力则主要取决于钝化膜厚度。钼酸盐钝化膜能阻滞锌层在5％NaCl水溶液中腐蚀的阴极过程,使腐蚀电流显著减小。     

低合金高强度结构钢预镀镍后热镀锌的镀层组织研究

研究了含0.38%Si(质量分数)的Q345钢预镀镍后热镀锌时镀层的生长和组织形成。结果表明:预镀一薄层镍可有效抑制含Si>0.3%的低合金高强度结构钢热镀锌时生成超厚、表面灰暗的锌层,镍层越厚,锌层生长越慢。在浸锌时,镀镍层先与Zn反应生成Ni Zn合金相γ,和γ,镍层消耗完后,出现Fe Zn合金相δ和Ni Zn合金相δ2,最后Ni Zn相消失,镀层为连续的δ相和分散在η相中的块状ζ相;Ni Zn相形成连续致密的层状组织是抑制锌层快速生长的主要原因。     

热镀锌钢表面硅烷/硅酸盐复合膜的耐蚀性能研究

为了改善硅烷膜的耐蚀性,将硅烷化热镀锌钢板用硅酸钠溶液封闭后处理,获得了硅烷/硅酸盐复合膜.采用中性盐雾试验(NSS)、湿热试验、盐水全浸试验和电化学交流阻抗谱(EIS)评价了膜层的耐蚀性能.结果表明,与单一硅烷膜相比,复合膜的耐蚀性能明显提高,超过了常规铬酸盐钝化膜.尤其是在5%NaCl溶液中,复合膜的低频阻抗数值随浸泡时间的增加先增大后减小,表明其具有一定的"自修复"能力.     

含硅钢表面因素对热浸镀锌反应活性的影响

综述了含硅钢材表面状态因素对热浸镀锌反应活性的影响,这些因素包括亚表面氧化、表面粗糙度、表面残余应力、表面晶粒位向及表面组织结构等.结果表明,对于热轧状态的含硅钢材,亚表面氧化和表面粗糙度对热浸镀锌有明显的影响.对于其它因素的影响,目前尚无统一看法.     

硅对活性钢热镀锌组织的影响

将高硅活性钢板(0.37wt%Si)表面预镀纯Fe层后浸入450℃熔融锌中,研究热浸锌层组织的变化,特别是α-Fe/Г界面附近组织的变化规律.结果表明:钢中的Si会在钢基表面富集;随着钢基/镀层界面向钢基方向移动,富Si的α-Fe破碎成粒子或絮状物,以类似克根达尔效应中惰性标记物的方式穿过Г层进入δ层,从而促进δ向钢基方向生长并吞并附近的Г相,令Г相逐渐消失;与此同时,原来正常的镀层很快就转变为典型的高硅活性钢镀层.     

热浸镀锌性能及质量要求

根据镀锌层的防腐蚀作用及国家标准中对热镀锌层质量的规定,参照美、英、日等国及ＩＳＯ热镀锌标准中的有关规定和说明,对热镀锌层的质量要求问题进行了探讨。     

锌浴温度对0.49%Si活性钢热浸镀锌层组织的影响

研究了高硅钢(0.49%Si,质量分数)在不同浸镀温度(440,480,520,560,600℃)和不同浸镀时间(1,3,5,10min)下的热镀锌试样镀层组织,探讨了浸镀温度和浸锌时间对镀层组织的影响。SEM/EDS结果表明:440℃和480℃热镀锌,镀层由薄而连续δ层和破碎的块状ζ相组成,无Γ相。ζ相生长过快,镀层过厚、灰暗、黏附性差,镀层生长主要由界面反应机制控制;520℃热镀锌时,镀层由极薄的Γ层、致密δk层和疏松的δp层组成,镀层生长主要受扩散机制控制;560℃和600℃镀锌时,镀层为Γ层和致密的δ相层,部分δ粒子弥散分布在η层中,镀层生长为扩散机制控制并伴随有显著的δ溶解过程。最佳高温镀锌温度应在520~560℃。