Failure mechanism of EB-PVD thermal barrier coatings on NiAl substrate

Yttria stabilized zirconia（YSZ） was deposited on the line cut β-NiAl substrate by electron-beam physical vapour deposition（EB-PVD）, and the cyclic oxidation behaviors of thermal barrier coatings on β-NiAl substrate were investigated in 1 h thermal cycles at 1 200 ℃ in air. The results show that the samples fail after 80-100 cycles. Sub-interface cavitations in the substrate develop due to depletion of Al in forming thermally grown oxides（TGOs）. The collapse and closing up of cavities result in the ragged YSZ/TGO/substrate interface. Since the specific crack trajectories are quite sensitive to local geometry, cracks along the YSZ/TGO/substrate interfaces ultimately lead to YSZ spallation.     

基于交会技术的碳酸盐岩多矿物处理新方法

基于塔里木油田碳酸盐岩储层的特点,建立了适合各油田的测井解释模型和单矿物处理程序,对比分析了现有的各种多矿物处理方法,提出基于交会图技术的新的迭代算法,使得程序更稳定,适用性更强;整合油田已建立的各种测井解释模型,形成适合于塔里木油田储层特征的碳酸盐岩多矿物处理软件。通过实际生产应用,在精细处理与储层评价方面效果良好。     

多元稀土氧化物掺杂二氧化锆基陶瓷材料的热物理性能

稀土氧化物(RE)掺杂氧化钇稳定二氧化锆(YSZ)是提高传统YSZ热障涂层隔热性能和高温稳定性的有效途径之一。在1500 ℃高温固相反应烧结24 h制得Gd₂O₃和Yb₂O₃多元稀土氧化物掺杂的YSZ(含3.5%Y₂O₃(摩尔分数))(GY-YSZ)陶瓷材料。采用XRD研究了GY-YSZ 陶瓷材料的晶体结构和物相组成; 采用激光脉冲法研究了Gd₂O₃和Yb₂O₃掺杂对GY-YSZ 陶瓷材料的热物理性能的影响规律。研究发现, 掺杂2.0%~3.0%Gd₂O₃和Yb₂O₃(摩尔分数)后GY-YSZ的热导率为0.90~1.15 W·(m·K)-1, 比YSZ降低30%以上, 显示了良好的隔热性能。稀土氧化物掺杂对YSZ陶瓷材料热物理性能的影响机制为: 掺杂Gd₂O₃和Yb₂O₃导致YSZ中单斜相(M)、 四方相(T)和立方相(C)含量发生变化, 同时YSZ晶格发生畸变。      

一个多快好省的风电建设项目——记辽宁昌图风电场的建设

介绍了在风电场建设中,依据风场的风资源状况和拟采购机组的适应性,提出了增加轮毂高度和叶轮直径的改进方案;根据当地的气候特点,充分利用最佳施工期和当地的风速日变化特点,采取"滚动吊装"等措施,取得了在高寒地区的近50MW风电项目,当年开工、当年投产运营的好成绩.     

电子束物理气相沉积热障涂层技术研究进展

介绍了电子束物理气相沉积设备的原理、结构及其工艺特点,并在此基础上综述了EB-PVD热障涂层近年来的研究进展。