In vivo setting behaviour of fast-setting calcium phosphate cement

The in vivo setting behaviour of fast-setting calcium phosphate cement (FSCPC) between femoral muscles of the rat was investigated to evaluate the possible value of FSCPC for medical and dental application. Conventional CPC (c-CPC) and FSCPC were implanted between femoral muscles, and various aspects of the setting behaviour such as setting time, mechanical strength and conversion ratio of cement into hydroxyapatite (HAP: Ca10(PO4)6(OH)2) were measured by the Vicat needle method, diametral tensile strength (DTS) measurement, and quantitative powder X-ray diffraction (XRD) analysis, respectively. The setting time of FSCPC in vivo was 5-7 min, in contrast to 48 min for c-CPC. As a result of its fast setting, set specimens of FSCPC showed higher mechanical strength from the initial stage than c-CPC. Higher DTS values were observed in FSCPC than c-CPC implanted after 24 h. Powder XRD analysis revealed faster conversion of FSCPC than c-CPC into HAP, which was responsible both for the faster setting and higher mechanical strength from the initial stage. We concluded, therefore, that FSCPC may be used for a wide range of clinical applications, i.e. fields where fast setting is required such as orthopaedic, plastic and reconstructive, and oral and maxillofacial surgery.     

Improved analysis of a bearingless switched reluctance motor

Bearingless switched reluctance motors, which can control rotor radial positions with magnetic force, have been proposed. Bearingless switched reluctance motors have combined characteristics of switched reluctance motors and magnetic bearings. Production of radial force for rotor shaft magnetic suspension is explained with differential stator windings. Mathematical relations between motor currents and radial force are derived by considering cross coupling and fringing fluxes. Theoretical relationships are verified with experimental results at partial overlap positions