Influence of mixed-mode loading on fatigue-crack propagation

The subject of fatigue which comprises crack nucleation, crack propagation and final failure or fracture has, over the years, been the subject of numerous theoretical and experimental studies. These studies have highlighted the extrinsic influence of mixed-mode loading in governing the fatigue behavior of a wide spectrum of engineering materials and structures. In this paper we review the basic criteria and models that have been proposed and used to predict crack behavior and response for structures containing large cracks and subject to mixed-mode loading. Since the aspect of crack growth is the focus of this review, the effects or contributions from intrinsic microstructural effects are largely excluded. Specific criteria discussed are the maximum tangential stress, minimum strain-energy density and the maximum energy-release rate criteria. The use of these criteria to predict the behavior of structures is examined based on results published in the open literature. The characteristics and implications of each criterion are examined and discussed with particular relevance to threshold conditions on crack growth, direction of crack growth and crack-growth rate. The limitations of each criterion are highlighted.     

Stress function with finite magnitude of stress concentration around an interface crack

A new mathematical model for study of an interface crack between two dissimilar elastic half planes is proposed. A process zone is formed along the interface between the physical crack and the continuous part. Both the crack opening (and sliding) displacement with a smooth shape and the finite magnitude of stress concentration appear in this zone. The analytical model is expressed by closed elastic solutions using complex variables, but with no oscillations at the crack tip.     

13SiMnNiCrMoV钢切口疲劳裂纹萌生门槛值

本文研究在13SiMnNiCrMoV 结构钢中用尖裂纹的应力强度因子来反映三点弯曲缺口试样的疲劳裂纹萌生规律。当 R=0.1,f=100Hz,试样尺寸 B×W×L=12.5×25×117mm 时,缺口名义应力幅的门槛值为Δσ_(th)=3315ρ~(0.352) MPa,0.5mm≤ρ≤5mmΔK_(th)=250ρ~(0.352) MPam~(1/2)门槛值与ρ有关。同时得到缺口裂纹萌生的循环次数 N_i 与名义应力幅Δσ、缺口曲率半径ρ的定量关系是N_i=3.98×10~(22)ρ~(1.62)/Δσ~(4.85),N_i≤10~(5.5)并讨论了(ΔK_1/ρ~(1/2))_(th)与ρ无关的结论。     

热泵型一拖二变频空调器的开发

将国内外最新的变容量控制、电子膨胀阀控制、室内外机独立解耦控制和智能旁通除霜控制等控制方法与计算机仿真优化设计应用于热泵型变频一拖二空调系统的开发,给出了系统的原理、结构,并进行了实验研究。结果表明,系统运行稳定可靠,性能系数达到国内同类产品的领先水平,并超过了国家单元分体热泵空调器的节能标准。也为多元变容量空调系统奠定了理论与实验基础。     

模拟光耦SLC800在转台系统中的应用

在大功率转台控制系统中．存在着较大的电压干扰和电磁兼容问题。在转台的控制精度和驱动功率不断提高的情况下．本文使用模拟光耦隔离器件SLC800重新设计了转台中的某部分模拟电路．将功率放大电路和控制电路隔开，来增强系统的抗干扰能力和运行的可靠性。实验结果的分析和转台的运行表明：应用模拟光耦进行隔离，有效地消除了转台控制中的干扰和电磁兼容。     

嘉陵江渠化开发浅析

渠化开发是对国家内河水运基础设施建设的探索性实践,文章阐述了嘉陵江流域航电工程开发的特点和开发现状,对流域开发的必要性以及嘉陵江渠化开发带来的显著社会经济效益进行了分析,对嘉陵江渠化开发的建设模式进行了积极探索和总结,列出了开发过程中存在的一些问题,并提出了解决问题的具体建议,对其他河流的开发有一定的借鉴价值。     

建筑安装与装饰工程施工监理工作的体会

结合对建筑安装和装饰工程施工特点的分析 ,从加大质量控制中事前控制的力度、合理制定进度计划等方面 ,针对性地提出了施工监理工作的重点 ,以确保监理工作的顺利开展。     

薄层反射波非零炮检距的属性特征

 本文从薄层顶、底界面反射波的走时入手，研究了薄层反射波在非零炮检距集上出现的干涉现象，导出了薄层反射波在出现干涉时的炮检距计算公式，说明薄层干涉出现的炮检距是多变量函数，即随着埋藏深度h、地层速度v、薄层厚度Δh以及地震波的主频f*的变化而改变。本文重点分析了地层厚度Δh和地震子波主频f*对反射波振幅特性和频率特性的影响。在充分分析薄层反射的振幅、频谱随炮检距变化关系的基础上，指出在应用叠前信息（如AVO分析）进行储层预测等方面的研究时，应充分考虑薄层反射波的干涉和调谐现象带来的振幅和频率特征的变化。     

-50℃用20MnMoD钢锻件及其焊接接头性能

研究了-50℃的20MnMoD钢锻件及其焊接接头在不同热处理状态时的综合力学性能。结果表明,-50℃的20MnMoD钢锻件具有良好的低温韧性,可与-50℃级正火型低温压力容器钢15MnNiNbDR配套使用。     

抽油机减速器齿轮的失效分析

找出了人字齿轮减速器在工作中右端齿轮出现严重磨损的原因并进行了分析。提出在国内现有制造技术的条件下，对于37kN·m以下的减速器应推广使用斜齿轮传动。