Carbon supported bimetallic Ru‐Co catalysts for H2 production through NaBH4 and NH3BH3 hydrolysis

This work investigates the effect of the addition of small amounts of Ru (0.5‐1 wt%) to carbon supported Co (10 wt%) catalysts towards both NaBH₄ and NH₃BH₃ hydrolysis for H₂ production. In the sodium borohydride hydrolysis, the activity of Ru‐Co/carbon catalysts was sensibly higher than the sum of the activities of corresponding monometallic samples, whereas for the ammonia borane hydrolysis, the positive effect of Ru‐Co systems with regard to catalytic activity was less evident. The performances of Ru‐Co bimetallic catalysts correlated with the occurrence of an interaction between Ru and Co species resulting in the formation of smaller ruthenium and cobalt oxide particles with a more homogeneous dispersion on the carbon support. It was proposed that Ru^°, formed during the reduction step of the Ru‐Co catalysts, favors the H₂ activation, thus enhancing the reduction degree of the cobalt precursor and the number of Co nucleation centers. A subsequent reduction of cobalt and ruthenium species also occurs in the hydride reaction medium, and therefore the state of the catalyst before the catalytic experiment determines the state of the active phase formed in situ. The different relative reactivity of the Ru and Co active species towards the two investigated reactions accounted for the different behavior towards NaBH₄ and NH₃BH₃ hydrolysis.     

The Role of Excitation Photons Energy in the Photoinduced Carrier Dynamics in InGaAs/InAlAs Superlattice Heterostructures

Technical Physics Letters - The influence of excitation photons energy on the relaxation times of photoexcited carriers is studied. The involved relaxation mechanisms are evaluated and the...     

Phase-Structural and Electrochemical Properties of La2MgNi9 Alloys

Powder Metallurgy and Metal Ceramics - Multiphase La 2 MgNi 9 alloys are synthesized by induction melting. The crystalline structures of all phases in the alloys are determined with X-ray...     

Linear friction welding of Ti6Al4V: experiments and modelling

Linear friction welding of the Ti6Al4V alloy is studied. A new definition of the energy input rate is proposed, based on an integration over time of the in-plane force and velocity; a strong correlation with the upset rate is then found. The effective friction coefficient is estimated to be 0·5±0·1 for varying frequencies and amplitudes, with only a weak dependence on the processing conditions displayed. A model is proposed that accounts for both the conditioning and equilibrium stages of the process, which is shown to be in good agreement with the experimental data. The model is used to study the mechanism by which the flash is formed. A criterion is proposed by which the rippled nature of its morphology can be predicted.     

Temperature cycling and its effect on mechanical behaviours of highporosity chalks

Temperature history can have a significant effect on the strength of water-saturated chalk.In this study,hydrostatic stress cycles are applied to understand the mechanical response of chalk samples exposed to temperature cycling between each stress cycle,compared to the samples tested at a constant temperature.The total accumulated strain during a stress cycle and the irreversible strain are reported.Chalk samples from Kansas(USA)and Mons(Belgium),with different degrees of induration(i.e.amount of contact cementation),were used.The samples were saturated with equilibrated water(polar)and nonpolar Isopar H oil to quantify water weakening.All samples tested during 10 stress cycles with varying temperature(i.e.temperature cycled in between each stress cycle)accumulated more strain than those tested at constant temperatures.All the stress cycles were performed at 30℃.The two chalk types behaved similarly when saturated with Isopar H oil,but differently when saturated with water.When saturated with water,the stronger Kansas chalk accumulated more total strain and more irreversible strain within each stress cycle than the weaker Mons chalk.     

Matrix Transformation in Boron Containing High-Temperature Co–Re–Cr Alloys

An addition of boron largely increases the ductility in polycrystalline high-temperature Co–Re alloys. Therefore, the effect of boron on the alloy structural characteristics is of high importance for the stability of the matrix at operational temperatures. Volume fractions of ε (hexagonal close-packed—hcp), γ (face-centered cubic—fcc) and σ (Cr₂Re₃ type) phases were measured at ambient and high temperatures (up to 1500 °C) for a boron-containing Co–17Re–23Cr alloy using neutron diffraction. The matrix phase undergoes an allotropic transformation from ε to γ structure at high temperatures, similar to pure cobalt and to the previously investigated, more complex Co–17Re–23Cr–1.2Ta–2.6C alloy. It was determined in this study that the transformation temperature depends on the boron content (0–1000 wt. ppm). Nevertheless, the transformation temperature did not change monotonically with the increase in the boron content but reached a minimum at approximately 200 ppm of boron. A probable reason is the interplay between the amount of boron in the matrix and the amount of σ phase, which binds hcp-stabilizing elements (Cr and Re). Moreover, borides were identified in alloys with high boron content.