薄板坯连铸连轧工艺对铌微合金化高强度钢组织和性能的影响

首先建立薄板坯连铸连轧工艺的试验室模拟技术，并运用该模拟技术，研究薄板坯连铸连轧工艺(CSP)和传统板坯再加热工艺(TRP)两种工艺对铌微合金化高强度钢的显微组织和力学性能的影响。研究结果表明：CSP钢的晶粒细化效果不如TRP钢，两者的平均铁素体晶粒尺寸分别为8．17μm和6．30μm。在CSP试验钢板中铌的析出量较大，特别是在铁素体中细小颗粒的铌的析出物较多，沉淀强化效果较强。CSP试验钢的σ0.5和σb分别较TRP工艺低约40MPa和约25MPa，同时其低温冲击韧性较好，FATT温度较低。     

The thermal behavior of mechanically activated galena by thermogravimetry analysis

The thermal decompositions of mechanically activated and nonactivated galenas were studied by thermogravimetry analysis (TGA) at the heating rate of 10 K min⁻¹ in argon. Results indicate that the initial temperature of thermal decomposition (abbreviated as T _di) in the TGA curves for different galenas decreases gradually with increased grinding time. The specific granulometric surface area (S _G), the structural disorder, and the content of elemental sulfur of mechanically activated galenas were analyzed by an X-ray diffraction (XRD) laser particle-size analyzer, XRD analysis, and the gravimetric method, respectively, which shows that the specific granulometric surface area of mechanically activated galenas remains almost constant after a certain grinding time, but the lattice distortions (ε) rise, the crystallite sizes (D) decrease, and the elemental sulfur contents of mechanically activated galenas increase with increased grinding time. The results imply that the decrease of the initial temperature of thermal decomposition in the TGA curves for mechanically activated galenas is mainly caused by the increase of lattice distortions, and the formation of new dangling bonds resulted from the production of elemental sulfur of mechanically activated galenas with increased grinding time. Finally, the differences in the thermal-decomposition reactivity between nonactivated and mechanically activated galenas were also discussed.     

自蔓延高温合成TiNi多孔体合金

为了开发新型的生体材料，本文对自蔓延高温合成TiNi多孔体合金——人造骨材料进行了研究。以单质钛粉和镍粉作原料，在氩气保护条件下，采用预热点燃模式和热爆模式制得了不同形态的多孔TiNi形状记忆合金。采用SEM和XRD分析了样品的孔洞特征和相组成，测试了其力学性能，并研究了合成条件参数与样品表面形貌和孔隙状态之间的关系。结果表明，用SHS法制备TiNi多孔体合金是可行的。     

微电量测量中信号的拾取和放大

本文介绍了静电计级运算放大器在工业微电量测量中的应用,并且给出了实际的电路结构和相关的噪声解决办法。     

Improved method for HgI2 crystal growth and detector fabrication

Instead of the temperature oscillation method (TOM), a modified vapor growth method was applied in this paper to grow large HgI₂ crystals with fewer lattice defects by providing a relatively stable temperature field during growth. And a new processing technique of HgI₂ crystals was developed for detector fabrication by merging solution string-sawing and hand-cleaving. The lattice deformations caused during cleaving were reduced greatly by eliminating passivated layers on the sawed crystal platelets before cleaving.     

聚吡咯导电材料合成方法的进展

本文对聚吡咯及聚吡咯导电复合物的合成方法进行了综述。     

A theory for the formation of tetrahedral amorphous carbon including deposition rate effects

A theoretical model is presented to describe the effect of ion beam bombardment rate on the formation of tetrahedral amorphous carbon (ta-C) films. The critical ion energy, E_c, corresponding to a 50% sp³ content in the films, is found to be dependent on both the effective thermal resistance and the ion beam bombardment rate. In the model, the ‘window’ width in the ion energy scale for the formation of ta-C material increases with decreasing deposition rate and with a reduction in the effective thermal resistance, until limited by lower and upper boundary thresholds. Experimental data are reproduced by the model. The plasmon energy, which correlates with sp³ fraction, is found experimentally of be higher for lower deposition rate and smaller effective thermal resistance. Data points for high sp³ content ta-C films deposited on silicon substrates at room temperature occupy a region in the ion energy-deposition rate (E-r) diagram similar to that predicated from the theory.     

关于最优等效替代法的实质及其应用条件的研究

本文研究了经济分析基本方法之一最优等效替代法的实质,系统地导出了被评价方案的绝对经济指标与相对经济指标的关系,并结合典型案例分析指出了该方法的应用条件,对正确进行建设项目的经济评价具有现实意义。     

TEM study of PLZT ceramics

The microscopic structures of PLZT(7.9/70/30 and x/65/35, x = 7 or 8) ceramics were studied by means of transmission electron microscopy. The presence of micro-regions in PLZTs was first verfied.     

热力除氧器运行特性实验研究

在热力除氧器实验装置上，对研制的新型除氧器进行了稳态运行特性和动态运行特性实验，得到了除氧器的各种运行特性曲线。研究结果表明，由于对喷嘴和填料进行改进，建立起有利于除氧的传热传质条件，使所研制的除氧器具有良好的稳态及动态运行特性，除氧效果优良。