住宅建筑结构中隔震技术的应用和经济评价

对当前隔震系统做了简单介绍 ,介绍了基础隔震的技术和施工方法等。讨论在住宅结构中推广隔震技术的方法 ,对各种类型的住宅结构做经济评价 ,讨论推广的可能性和难点。     

分割电极片状压电致动器——(二)位移特性及狭缝宽度对其影响的实验研究

研究了悬臂梁式分割电极片状压电致动器的位移特性。理论分析表明，分割电极狭缝宽度会减小致动器自由端的位移输出，但当狭缝宽度小于致动器电极宽度的１０％时，可忽略狭缝宽度的影响。致动器端部位移的测试结果大于理论计算值。与现有磁头悬浮臂尺寸相近的致动器，在２０Ｖ～５０Ｖ的电压驱动下均可获得１μｍ～２μｍ的致动位移。对９８５０道／厘米的密度磁盘，该位移能覆盖至少一个磁道宽度，满足磁头定位两级伺服系统对第二级致动器位移的基本要求。     

Synthesis, characteristics and oxygen-sensitive properties of SrMgxTi 1 − xO3 nanocrystals

SrMg_xTi_{1 - x}O₃ nanocrystals (x = 0.1–0.6) were synthesized by the stearic acid gel method. Powder samples were characterized by X-ray diffraction and X-ray photoelectron (XP) spectroscopy. The results showed that the lattice parameter a and the O 1s XP spectrum changed not only with the Mg content x but also with the grain size d of the samples. The conductivity of a thick film specimen fabricated on an aluminium oxide wafer was investigated in a nitrogen—oxygen atmosphere.     

Pore size control of porous silica by sol-gel process

Porous silica glass was prepared by sol-gel process from tetraethoxysilane (TEOS). The effects of solvents (water, ethanol), drying condition, heat treatment temperature on specific surface area and pore size distribution of porous silica were investigated. Gelation process accelerates with an increase of H₂O content, while retards with the increase of ethanol amount. Structure changes during heat treatment were studied by means of DTA, XRD. TEM micrographs show that the gel particles shrink after heated at 500°C, thus the average pore size decreases.     

A method to estimate entropies and heat capacities applied to alkali oxides

We present a method that is useful in the estimate and assessment of heat capacity data. The approach is based on an analysis of the logarithmic average of the phonon frequencies. In this quantity, that may be easily derived from experimental data on the vibrational entropy, the influence of atomic masses can be exactly accounted for even in polyatomic solids. Our method is applied to Li₂O, Na₂O, K₂O, Rb₂O, and Cs₂O. In particular, literature data for K₂O are critically examined.     

辐射制备缓释抗癌药阿糖胞苷的研究

报告了甲基丙烯酸酯类在室温下进行辐射聚合制备缓释抗癌药阿糖胞苷（Ａｒａ－Ｃ）的研究结果。结果表明，不仅亲水性单体，而且疏水性单体（包括ＭＭＡ、ＥＭＡ和ＢＭＡ等）都可用于辐射固化。加入到亲水性基质中的疏水性单体可以延缓药物的离体释放，其顺序是ＭＭＡ＜ＥＭＡ＜ＢＭＡ，央ＭＭＡ－ＨＥＭＡ共聚物中，Ａｒａ－Ｃ释放率随着基质中的ＭＭＡ含量增加而降低。药物的离体释放还受许多困素的控制，结果显示：药物释放量随着     

Preparation and optical properties of CdxHg1-xTe doped silica glass

In this paper, the Cd_xHg_1-xTe (x=1-0.7) doped silica glass was prepared through two step sol-gel process and in-situ growth technique from tetraethoxysilane (TEOS), cadmium acetate, mercury acetate and telluric acid. The influence of various factors on the glass was studied. The structure of the microcrystals was investigated by XRD. The absorption and transmittance spectrum of the composite showed that the shift of absorption edge was in conformity with the quantum size effect. The third-order nonlinear optical susceptibility χ⁽³⁾ was measured by the degenerate four wave mixing (DFWM). The values of χ⁽³⁾ was in the range of 10^-11-10^-12 MO esu at wavelength of 1.06 μm.     

A polymerizable photoredox initiation system for vinyl photopolymerization

A polymerizable photoredox system consisting of 4-methacryl oxbenzophenone (MABP) and N,N-dimethlaminoethyl methacrylate (DMAEMA) used for the photopolymerization of acrylonitrile (AN) was studied. It was found that the polymerization rate is proportional to the 0.93th power for the AN concentration, the 0.28th power for the MABP concentration, and the 0.25th power for the DMAEMA concentration. The overall activation energy of the polymerization obtained is 30.43 kJ/mol. The recorded ESR spectrum indicates that the excited-state MABP abstraets hydrogen mainly from the methyl group of the dimethylamino moiety. The comparison of the initiation ability of polymeric MABP or polymeric DMAEMA with their monomeric forms has also been done and the results indicate that in good solvents P (MABP) has a much higher initiation ability than that of monomeric MABP, but monomeric DMAEMA and P (DMAEMA) display almost the same initiation ability. In poor solvent, the initiation ability of P (MABP) is not so obviously higher than that in good solvents. The result of UV analysis of P (AN) initiated by the MABP–DMAEMA system indicates that both MABP and DMAEMA not only initiate the photopolymerization of AN, but also enter into P (AN) polymer chains. © 1994 John Wiley & Sons, Inc.     

Using thermally stimulated currents to find defective capacitors

BaTiO₃ multilayer capacitors with a nominal capacitance of 3.5nF have been carefully measured using the thermally stimulated current (TSC) technique. When a 300V polarization voltage is applied at room temperature, a new TSC peak appeared in defective sample A after it has been immersed in water. No new peak was found in good-quality sample B after a similar treatment. The accelerated life test shows that sample A hasa much shorter life than sample B in terms of insulation resistance.     

TEM method for rapid and precise evaluation of continuous recrystallization

With the aid of a double-tilt holder in a transmission electron microscope, a new method for a rapid and precise determination of the misorientations of a large number of subgrain or grain boundaries is given in this article. By use of the method, the continuous recrystallization can be rapidly and precisely evaluated when compared to the other conventional methods.