Preparation of rod-shaped BaTiO3 powder

Rod-shaped BaTiO₃ powder particles have been prepared from rod-shaped TiO₂ ·nH₂O and BaCO₃ in molten chloride. The morphology of BaTiO₃ particles was studied referring to the effects of the chemical species of the starting titanium compound, amount of chloride, particle size of the titanium compound and reaction conditions, and the preparation condition of rod-shaped BaTiO₃ has been determined: i.e., large TiO₂ ·nH₂O particles were heated at 700°C in molten salt with an equal amount of BaTiO₃. This condition was effective in suppressing the formation of BaTiO₃ by a solution-precipitation process as well as the deformation of either TiO₂ ·nH₂O or BaTiO₃, which are responsible for the formation of equiaxed BaTiO₃ particles. The obtained rod-shaped BaTiO₃ particles had a cubic symmetry. Electron diffraction analysis showed that the following topotactic relation is retained; 0 1 0_{potassium tetratitanate} 0 1 0_{hydrated titania} 1 0 0_anatase 1 0 0_{barium titanate}     

Importance of initial surface film in the degradation of stainless steels by atmospheric exposure

The surface compositions of stainless steels types 304, 316, 430, and 444 combined with four types of surface finishes, 2B finish, hairline polishing, mirror polishing, and bright annealing, were measured by ICP-AES, EPMA, and XPS before exposure. The surface finish that most enriched the chromic species in the surface film was mirror polishing, followed by bright annealing, 2B finish, and hairline polishing. The order of corrosion-resistance was type 444, type 316, type 304, and type 430. The surface compositions were correlated with the rating number and pitting depth after exposure to atmospheric environments. The rating number had a high positive correlation with the concentration of Cr in the surface film, and had a slight correlation with the near-surface composition measured by EPMA at 12 kV, but did not show any correlation with bulk composition within the composition range covered in the present work. This same trend was observed for pitting depth. It was concluded that the cationic concentration of Cr in the surface film before atmospheric exposure is the prime factor in controlling the resistance of stainless steels to atmospheric corrosion.     

Formation of Small-Sized CdSxSe1-x Crystals in Sol-Gel-Derived SiO2 Glasses

Silica glasses doped with small-sized CdS_x-Se_1-x crystals were prepared by the sol-gel method. Gels synthesized by the hydrolysis of Si(OC₂H₅)₄, in the presence of CdSeO₄ with NH₄SCN dissolved in HNO₃ or NH₄OH, were heated in H₂-N₂ atmosphere. The pH value of solutions for CdSeO⁴ and NH⁴SCN primarily determined the fraction of anions in CdS^xSe^1-x crystals. The anion content in crystals was dependent on the pH value of the solvent and/or heat-treatment temperature, and the sulfur fraction changed from 0.1 to 0.6. The optical absorption spectra were red-shifted as the selenium content and the crystal size increased, and the emission spectra showed a sharp band near the absorption edge position and a broad tail extending into the long wavelength. The optical band gap energies increased reciprocally proportional to the square of the crystal size.     

Studies on the nuclear magnetic resonance spectra of olefinic protons of conjugated fatty acid methyl esters

The NMR spectra of olefinic protons in the four representative conjugated fatty acid methyl esters, methylcis-9,trans-11-octadecadienoate, methyltrans-9,trans-11-octadecadienoate, methyl α eleostearate, and methyl β eleostearate, were studied. The chemical shift of each olefinic proton in these compounds was determined by considering their intramolecular environment. Coupling constants were also obtained as the results of spectral analysis.     

Fate of the chlorine and fluorine in a sub-bituminous coal during pyrolysis and gasification

The fate of the chlorine and fluorine present in a sub-bituminous coal from Indonesia during pyrolysis and gasification has been studied with fixed and entrained bed reactors. The rate profile for HCl evolved in the temperature programmed pyrolysis exhibits the main and shoulder peaks at 480 and 600 °C, respectively. Model experiments and subsequent Cl 2p XPS measurements show that HCl reacts with metal impurities and carbon active sites at 500 °C to be retained as inorganic and organic chlorine forms, from which HCl evolves again at elevated temperatures. It is suggested that the HCl observed in the coal pyrolysis may originate from the above-mentioned chlorine functionalities formed by secondary reactions involving the nascent char. In the CO₂ gasification of the 900 °C char at 1000 °C and 2.5 MPa, any measurable amounts of HCl and HF could not be detected even at a high conversion of 75 wt% (daf), suggesting the accumulation of these halogens in the residual char. When the coal is injected into an O₂-blown, entrained bed gasifier at 1200-1400 °C under 2.6 MPa, the partial oxidation proceeds to a larger extent at a higher O₂/coal ratio, whereas the chlorine and fluorine are enriched in the remaining char, and the extent of the enrichment at the latter stage of gasification is larger with the fluorine. The XPS measurements of the chars reveal the presence of the broad F 1 s peak, which can cover a wide range of binding energies attributable to inorganic and organic fluorine. The halogen enrichment during gasification is discussed in terms of secondary reactions of HCl and HF with char.     

The surface film formed on amorphous Pd-Ti-P alloy by anodic polarization in 2 m NaCl solution

X-ray photoelectron spectroscopy was used to investigate the effect of the composition and thickness of surface film on the electrocatalytic properties for chlorine gas evolution on amorphous Pd-Ti-P alloy in NaCl solution. The amount of charge for gas evolution exhibited a wavy change with an increase in polarization potential. The gas evolution became active with an increase in palladium content of the surface film and slowed down with increases of titanium and phosphorus contents of the film. However, despite the fact that the formation of surface film consisting mainly of titanium as a cation in the potential region higher than 1.6 V (sce), the catalytic activity for gas evolution increased, suggesting the change in the gas evolution mechanism in the higher potential region.     

Anodic characteristics of amorphorous palladium-base alloys in sodium chloride solutions

The anodic characteristics of a variety of amorphous palladium-base alloys were examined with a view to their use for the production of sodium hypochlorite by electrolysis of dilute sodium chloride solutions at ambient temperature. The corrosion resistance of palladium-metalloid alloys was obtained by alloying with platinum group metals and/or valve metals. Among these alloys, rhodium-containing alloys showed high electrocatalytic activities for chlorine evolution. Surface activation treatment was, however, necessary to obtain sufficiently high activities for chlorine evolution at low overpotentials. Surface-activated amorphous alloys possessed considerably higher current efficiency for chlorine evolution in comparison with currently used anodes.     

An X-ray photoelectron spectroscopic study of electrocatalytic activity of platinum group metals for chlorine evolution

A correlation of the catalytic activity for anodic chlorine evolution of platinum group metals to the nature of the surface film formed during chlorine evolution in a sodium chloride solution was studied by X-ray photoelectron spectroscopy. The change in the surface film with increasing potential was found on platinum, including an increase in the cationic valence. This seemed responsible for the decrease in the activity for chlorine evolution on platinum in the high potential region. Increasing potential did not result in the appreciable increase in the cationic valence in the surface film on the other platinum group metals. Replacement of hydroxyl ions in the surface film by chloride ions became easier in the order of rhodium, iridium and palladium, and the activity for anodic chlorine evolution increased in this order due possibly to an increase in the amount of chloride ions in the film which seemed to be one of the reactants in the rate determining electrochemical desorption of adsorbed chlorine atom. Chlorine molecules adsorbed on the surface film were also found. It was assumed that the activity for anodic chlorine evolution might be low when the metal surface was covered by a large amount of molecular chlorine which was the reaction product.     

Organic–silicate hybrid catalysts based on various defined structures for Knoevenagel condensation

Two types of organic–inorganic hybrid base catalysts are prepared. Organic-functionalized molecular sieves (OFMSs), particularly “amine-immobilized porous silicates”, are designed based on common idea to immobilize catalytic active sites on silicate surface. Silicate–organic composite materials (SOCMs), such as “ordered porous silicate–quaternary ammonium composite materials”, are the precursors of ordered porous silicates obtained during the synthesis. Both the OFMS and the SOCM are used as the catalysts for Knoevenagel condensation. Among the OFMSs, there is clear tendency that the use of molecular sieve with larger pore volume and/or surface area gives the product in higher yield. Aminopropylsilyl (AP)-functionalized mesoporous silicates such as AP-MCM-41 gives the product in high yield under mild conditions. No loss of activity is observed after repeated use for three times. The SOCMs are also active for the same reaction. The precursors of the mesoporous silicates are more active than those of microporous silicates. This material can be repeatedly used without significant loss of activity. High activity is not due to the leached species. The active sites of the SOCM catalysts are considered to be SiO⁻ moieties located on the pore-mouth. Activity of the SOCM increases when the reaction is carried out without solvent, whereas decrease in activity of the OFMS is observed in the solvent-free system.     

Synthesis of AlPO4 Molecular Sieves with AFI and AEL Structures by Dry-Gel Conversion Method and Catalytic Application of Their SAPO Counterparts on Isopropylation of Biphenyl

AlPO₄-5 and AlPO₄-11 were synthesized by dry-gel conversion (DGC) method. Steam-assisted conversion (SAC) and vapor-phase transport (VPT) techniques were applied for this purpose. The synthesis was successful in presence of a certain minimum amount of external bulk water, without which the crystallization failed. Crystallization by VPT method was slower than corresponding SAC and HTS method. SAPO analogs of the samples, SAPO-5 and SAPO-11 were also synthesized by DGC method. Samples made by DGC methods had higher yield than the conventional hydrothermal synthesis (HTS); otherwise the samples showed similar characteristics as that made by HTS. XRD, SEM and N₂-adsorption results showed high crystallinity and purity of the samples made by DGC, and ²⁷Al MAS NMR spectra indicated the tetrahedral framework nature of Al. SAPO-5 and SAPO-11 were tested for their catalytic activity in isopropylation of biphenyl, and in terms of conversion and selectivity, SAPO-5 was found to be suitable for this application.