Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

Fabrication of direct Z-scheme FeIn2S4/Bi2WO6 hierarchical heterostructures with enhanced photocatalytic activity for tetracycline hydrochloride photodagradation

A series of direct Z-scheme FeIn₂S₄/Bi₂WO₆ hierarchical heterostructures with intimate interface contacts were synthesized by in-situ growth route and characterized by systematical analyses. All as-prepared FeIn₂S₄/Bi₂WO₆ nanocomposites showed significantly enhanced photocatalytic activity towards photodegradation for the removal of tetracycline hydrochloride (TCH) in comparison with individual FeIn₂S₄ and Bi₂WO₆. Meanwhile, the highest photocatalytic degradation activity can be achieved by modulating adding amount of FeIn₂S₄ in FeIn₂S₄/Bi₂WO₆ nanocomposites and the optimized component ratio of FeIn₂S₄ to Bi₂WO₆ is determined to be 10 wt%. The enhanced photocatalytic activity could be ascribed to efficient separation between photogenerated holes and electrons based on the construction of direct Z-scheme system. The high photocatalytic stability of resultant 10 wt% FeIn₂S₄/Bi₂WO₆ nanocomposites was revealed through six successive recycling reactions. The main intermediate generated during TCH photodegradation was explored by HPLC-MS. Besides, the direct Z-scheme photocatalytic mechanism was confirmed by band position analysis, electron spin resonance (ESR) and active species capture experiment.     

Stabilizing temperature-capacitance dependence of (Sr,Pb, Bi)TiO3-Bi4Ti3O12 solutions for energy storage

(1-x)Sr_0.7Pb_0.15Bi_0.1TiO₃-xBi₄Ti₃O₁₂ ((1-x)SPBT-xBIT, x = 0-0.125) bulk ceramics were developed and calcined via the solid-state method, aimed at the application of pulsed power capacitors. The phase structures, temperature stability, hysteresis loop, and discharge properties were systematically investigated. Considering both the temperature stability and dielectric properties, 0.925SPBT-0.075BIT bulk ceramics with a capacitance variation satisfying the X7R specification were developed for pulsed power capacitors. The energy storage density was 0.252 J/cm³, and the ceramics showed high temperature stability at 80 kV/cm. The discharge current waveforms of the 0.925SPBT-0.075BIT ceramics were recorded. A high discharge power density of approximately 1.01 × 10⁸ W/kg with an 8 Ω load resistor and short discharge period of 84 ns were achieved at 50 kV/cm. The good temperature stability properties and high power density show that the 0.925SPBT-0.075BIT ceramics are well suited for pulsed power capacitors with a wide temperature range.     

Experimental study on the permeability and self-healing capacity of geosynthetic clay liners in heavy metal solutions

Geosynthetic clay liners (GCLs), which have a very low permeability to water and a considerably high self-healing capacity, are widely used in liner systems of landfills. In this study, a series of experimental tests were carried out under complex conditions on typical commercial GCLs from China. In particular, the effects of pH values and lead ions (Pb²⁺) were tested in addition to other factors. The swelling properties of natural bentonite encapsulated between geotextile components in the GCLs were tested first. The swelling capacity was reduced rapidly at pH values < 3 and concentrations of Pb²⁺ >40 mM. Permeability tests on GCLs with different concentrations of lead ions were then performed by using the self-developed multi-link flexible wall permeameter, and data showed that increases in lead ion concentrations greatly improved the permeability. Finally, self-healing capacity tests were conducted on needle-punched GCLs under different levels of damage. Results showed that the GCLs have a good self-healing capacity with small diameter damage holes (2 mm, close to three times the original aperture), but with a damage aperture larger than 15% of the sample area, the self-healing capacity could not prevent leakage; hence, in certain situations it will be necessary to repair the damage to meet the anti-seepage requirement.     

Decoder side information generation techniques in Wyner-Ziv video coding: a review

Multimedia Tools and Applications - In Wyner-Ziv (WZ) video coding, decoder side information (SI) takes a key role in a WZ video codec among other building blocks. In this paper, we review the...