LaCoO_3光催化降解孔雀绿染料的研究

采用硬脂酸溶胶-凝胶法合成出钙钛矿型复合氧化物LaCoO3,用XRD,TEM等手段进行了表征,并以其为催化剂对染料孔雀绿进行降解实验。以高压汞灯为光源,研究了催化时间、催化剂用量、染料起始浓度、溶液pH值以及H2O2加入量对降解率的影响。结果表明,100 mL10 mg/L孔雀绿溶液用0.15 g催化剂降解2 h,降解率达到90.1%,加入适量的H2O2、提高溶液pH值均会提高染料的降解率。     

我国氯酸钠生产技术概况及发展前景分析

概述了我国氯酸钠生产技术进展及推广应用情况。综合国内外氯酸钠生产现状分析了国内应用前景。指出我国氯酸钠工业的发展思路应是：合理利用资源，降低生产成本；利用新技术，降低消耗定额；利用自身氢气资源，发展高附加值化工产品和改变消费结构，扩大氯酸钠消费量。     

海藻酸微胶囊的制备及在药物控释中的研究进展

海藻酸具有相对温和的凝胶条件与良好的生物相容性 ,已广泛应用于药物缓释与生物医学工程。综述了海藻酸微胶囊的制作方法、增加海藻酸微囊的稳定性与控制物质扩散的主要方法及海藻酸凝胶在药物控释研究中的进展     

SiC晶须增强陶瓷基复合材料的研究

用不同的Al_2O_3粉料,采用SiC晶须补强以及加入第三相SiC粒子弥散增韧的方式,研究了SiC晶须Al_2O_3基复合材料的力学性能,得到强度σ_f=780MPa,K_(Ic)=7.6MPa·m~(1/2)的结果。通过不同的分敌途径,对晶须分散效果进行了实验观察和探讨;并讨论了晶须的分散均匀性对力学性能的影响。同时,就晶须团聚体在增韧过程中所起的作用提出了一种新的、可能的增韧机制,合理地解释了实验结果。最后,就三元复合系统中晶须补强和弥散增韧两种途径的迭加效果进行了讨论。     

Synthesis and characterization of poly(butyl acrylate)/silica and poly(butyl acrylate)/silica/poly(methyl methacrylate) composite particles

Poly(butyl acrylate)/poly(methyl methacrylate) (PBA/PMMA) core–shell particles embedded with nanometer‐sized silica particles were prepared by emulsion polymerization of butyl acrylate (BA) in the presence of silica particles preabsorbed with 2,2′‐azobis(2‐amidinopropane)dihydrochloride (AIBA) initiator and subsequent MMA emulsion polymerization in the presence of PBA/silica composite particles. The morphologies of the resulting PBA/silica and PBA/silica/PMMA composite particles were characterized, which showed that AIBA could be absorbed effectively onto silica particles when the pH of the dispersion medium was greater than the isoelectric potential point of silica. The critical amount of AIBA added to have stable dispersion of silica particles increased as the pH of the dispersion medium increased. PBA/silica composite particles prepared by in situ emulsion polymerization using silica preabsorbed with AIBA showed higher silica absorption efficiency than did the PBA/silica composite particles prepared by direct mixing of PBA latex and silica dispersion or by emulsion polymerization in which AIBA was added after the mixing of BA and silica. The PBA/silica composite particles exhibited a raspberrylike morphology, with silica particles “adhered” to the surfaces of the PBA particles, whereas the PBA/silica/PMMA composite latex particles exhibited a sandwich morphology, with silica particles mainly at the interface between the PBA core and the PMMA shell. Subsequently, the PBA/silica/PMMA composite latex obtained had a narrow particle size distribution and good dispersion stability. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 99: 3425–3432, 2006     

Effects of ultrasonic oscillation on processing behaviors of PS,EPDM, and PS/EPDM blend

In this study, the extrusion processing behaviors of polystyrene (PS), ethylene–propylene–diene terpolymer (EPDM), and their blend (PS/EPDM, 80/20) were studied by using a special ultrasonic oscillation extrusion system developed in our laboratory. The die pressure and volume flow rate were measured at different ultrasonic intensities and screw rotation speeds. The dependences on ultrasonic intensity of die pressure, volume flow rate, and apparent viscosity of polymers, as well as die swell at the same screw rotation speed were investigated. The effects of screw rotation speed on the processing behaviors of polymers and their blend at the same ultrasonic intensity were also studied. The experimental results showed that in the presence of ultrasonic irradiation, the processibilities of polymers and their blend were improved. Their possible mechanism is discussed in this article. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 1856–1863, 2006     

SbSn金属间化合物的制备及其脱硫性能

以Sb、Sn为原料,用机械合金化法制备了SbSn金属间化合物,用X射线衍射仪和透射电镜对其进行了表征。实验考察了球料比、球磨时间、球磨转速、原料比以及使用后的清洗方式对SbSn金属间化合物性能的影响;并考察了2种不同性质的乳状液对脱硫的影响。结果表明球料比10∶1、转速270r/min、球磨时间8h为最佳合成条件。在常温常压下对于油品中的噻吩,单程脱除率在9.7%左右,3次循环实验后脱硫率可以达到23%。     

PVAm/PAN复合膜的制备及其对CO2/CH4的分离性能

New polymeric membrane materials——polyvinyl amine (PVAm) with different primary amine contents were synthesized.By covering polyacrylonitrile(PAN) ultrafiltration membranes with PVAm, the PVAm/PAN composite membranes for CO₂/CH₄ separation were prepared. The composite membranes containing more primary amino groups have higher selectivity for CO₂/CH₄.The cross-linking of acid or glutaradehyde could improve the gas permselectivity of the composite membranes. With decreasing CO₂ content in the feed gas, the CO₂/CH₄ separation factor increased.When the feed gas was 25%(vol) CO₂ and 75%(vol) CH₄, the CO₂ permeation rate was 4.1×10^-9cm³(STP) •cm^-2•Pa^-1•s^-1, and the CO₂/CH₄ separation factor was 180.     

微机用于抛物线齿同步带传动强度理论的研究

采用啮合原理与弹性力学复交函数相结合的方法，借助计算机对抛物线齿同步带传动强度理论进行了系统研究，并将整个计算过程编制成ＲＨＤＧＲＡＰＨ软件。利用该软件进行了带齿和轮齿及刀具齿形设计、啮合原理分析、应力和变形计算、刀具可加工最小齿数的确定及加工误差分布计算。