P 型氮化镓层生长压力对InGaN/GaN基发光二极管性能的影响

The advantages of In Ga N/Ga N light emitting diodes(LEDs) with p-Ga N grown under high pressures are studied.It is shown that the high growth pressure could lead to better electronic properties of p-Ga N layers due to the eliminated compensation effect.The contact resistivity of p-Ga N layers are decreased due to the reduced donor-like defects on the p-Ga N surface.The leakage current is also reduced,which may be induced by the better filling of V-defects with p-Ga N layers grown under high pressures.The LED efficiency thus could be enhanced with high pressure grown p-Ga N layers.     

采用AlN缓冲层在Si(111)衬底上生长GaN的形貌

针对Si衬底上生长GaN具有的特有形貌进行了研究,分析采用扫描电镜(SEM)、X射线能谱仪(EDS)、原子力显微镜(AFM)等手段,研究了使用AlN作为缓冲层的GaN的生长模式、缺陷形成机理、应力释放机制.并且发现缓冲层厚度和外延层生长温度对裂纹和表面缺陷的形成有很大的影响.     

基于InP衬底的GaAsSb/InP异质结晶体管

采用金属有机化学气相沉积生长了InP/GaAs0.5Sb0.5/InP 双异质结晶体三极管(DHBT)材料,研究了材料质量对器件性能的影响.制备的器件不但具有非常好的直流特性,而且还表现出良好的微波特性,其结果与能带理论的预言一致,DHBT集电结和发射结的电流理想因子分别为1.00和1.06,击穿电压高达15V,电流放大增益截止频率超过100GHz.     

基于InP衬底的GaAsSb/InP异质结晶体管

采用金属有机化学气相沉积生长了InP/GaAs0.5Sb0.5/InP 双异质结晶体三极管(DHBT)材料,研究了材料质量对器件性能的影响.制备的器件不但具有非常好的直流特性,而且还表现出良好的微波特性,其结果与能带理论的预言一致,DHBT集电结和发射结的电流理想因子分别为1.00和1.06,击穿电压高达15V,电流放大增益截止频率超过100GHz.     

LFMCW雷达运动目标高精度检测方法

LFMCW雷达检测运动目标，可以采用对称三角LFMCW信号，通过频域配对实现动目标距离、速度的去耦合。但是在实现时，如果只采用传统的FFT作为核心算法就会引起较大的测距、测速误差。本文采用FFT-CZT两级处理方法，从而在运算量增加不多的情况下，显著提高LFMCW雷达的动目标测距、测速精度。仿真结果表明，本方法适用于各种带宽的LFMCW雷达，具有通用性。     

插入n-AlGaN/GaN超晶格改善GaN基LED的droop效应

在GaN基LED的n-GaN和InGaN/GaN发光区之间插入n-AlGaN/GaN超晶格来改善其droop效应。注入电流低于100mA时,插入n-AlGaN/GaN超晶格的LED的流明效率低于没有插入层的LED。注入电流高于100mA时,插入n-AlGaN/GaN超晶格的LED的流明效率高于没有插入层的LED。插入n-AlGaN/GaN超晶格后,GaN基LED在-5V的反向电压下,漏电由2.568029μA减少到0.070543μA。人体模式下,插入n-AlGaN/GaN超晶格的LED在2000V的静电电压下的通过率从60%提高到了90%。LED droop效应的改善是因为n-AlGaN/GaN超晶格过滤了穿透位错并改善了电流扩展能力。     

Influence of growth conditions on the V-defects in InGaN/GaN MQWs

The influence of the growth temperature,TMIn/TEGa andⅤ/Ⅲratio on the V-defects of InGaN/GaN multi-quantum wells（MQWs） has been investigated and discussed.When the TMIn flow increases from 180 to 200 sccm,the density of V-defects increases from 2.72×10¹⁸ to 5.24×10¹⁸ cm^-2,and the V-defect width and depth increase too.The density also increases with the growth temperature.The densities are 2.05×10⁸,2.72×10¹⁸ and 4.23×10⁸ cm^-2,corresponding to a growth temperature of 748,753 and 758℃respectively.When the NH₃ flows are 5000,6600 and 8000 sccm,the densities of the V-defects of these samples are 6.34×10¹⁸,2.72×10¹⁸ and 4.13×10¹⁸ cm^-2,respectively.A properⅤ/Ⅲratio is needed to achieve step flow growth mode.We get the best quality of InGaN/GaN MQWs at a growth temperature of 753℃TMIn flow at 180 sccm,NH₃ flow at 6600 sccm,a flatter surface and less V-defects density.The depths of these V-defects are from 10 to 30 nm,and the widths are from 100 to 200 nm.In order to suppress the influence of V-defects on reverse current and electro-static discharge of LEDs,it is essential to grow thicker p-GaN to fill the V-defects.     

Improvement of the efficiency droop of GaN-LEDs using an AlGaN/GaN superlattice insertion layer

With an n-AlGaN(4 nm)/GaN(4 nm) superlattice(SL) inserted between an n-GaN and an InGaN/GaN multiquantum well active layer,the efficiency droop of GaN-based LEDs has been improved.When the injection current is lower than 100 mA,the lumen efficiency of the LED with an n-AlGaN/GaN SL is relatively small compared to that without an n-AlGaN/GaN SL.However,as the injection current increases more than 100 mA,the lumen efficiency of the LED with an n-AlGaN/GaN SL surpasses that of an LED without an n-AlGaN/GaN SL. The wall plug efficiency of an LED has the same trend as lumen efficiency.The improvement of the efficiency droop of LEDs with n-AlGaN/GaN SLs can be attributed to a decrease in electron leakage due to the enhanced current spreading ability and electron blocking effect at high current densities.The reverse current of LEDs at -5 V reverse voltage decreases from 0.2568029 to 0.0070543μA,and the electro-static discharge(ESD) pass yield of an LED at human body mode(HBM)-ESD impulses of 2000 V increases from 60%to 90%.     

MOCVD于高温AlN模板上生长的AlGaN材料

A high temperature AlN template was grown on sapphire substrate by metalorganic chemical vapor deposition.AFM results showed that the root mean square of the surface roughness was just 0.11 nm.Optical transmission spectrum and high resolution X-ray diffraction（XRD）characterization both proved the high quality of the AlN template.The XRD（002）rocking curve full width at half maximum（FWHM）was about 53.7 arcsec and（102）FWHM was about 625 arcsec.The densities of screw threading dislocations（TDs）and edge TDs wereestimated to be - 6 × 10^6 cm^-2 and - 4.7 ×10^9 cm^-2. AlGaN of Al composition 80.2% was further grown on the AlN template. The RMS of the surface roughness was about 0.51 nm. XRD reciprocal space mapping was carried out to accurately determine the Al composition and relaxation status in the AlGaN epilayer. The XRD （002） rocking curve FWHM of the AIGaN epilayer was about 140 arcsec and （102） FWHM was about 537 arcsec. The density of screw TDs was estimated to be - 4 × 10^7 cm^-2 and that of edge TDs was - 3.3 × 10^9 cm^-2. These values all prove the high quality of the AlN template and AlGaN epilayer.     

在复合衬底γ-Al2O3/Si(001)上生长GaN

采用分子束外延(MBE)生长方法,使用γ-Al2O3材料作为新型过渡层,在Si(∞1)衬底上获得了没有裂纹的GaN外延层,实验结果表明使用γ-Al2O3过渡层有效地缓解了外延层中的应力.通过生长并测试分析几种不同结构的外延材料,研究了复合衬底γ-Al2O3/Si(001)生长GaN情况,得到了六方相GaN单晶材料,实现了GaN c面生长.预铺薄层Al及高温AlN层可以提高GaN晶体质量,低温AlN缓冲层可以改善GaN表面的粗糙度.为解决Si(001)衬底上GaN的生长问题提供了有益的探索.