Thermoelectric Properties of CexCo4Sb12 Prepared by MA-SPS 总被引:1,自引:1,他引:0
Starting with elementary powders, thermoelectric materials CexCo4Sb12 were prepared by mechanical alloying and spark plasma sintering (MA-SPS). XRD analyses reveal that the expected major phase, named skutterudite was formed in MA process and was kept after SPS. The thermoelectric properties of MA-SPS samples including resistivity, Seebeck coefficient, power factor, thermal conductivity and the dimensionless figure of merit (ZT) were studied by varying Ce content and temperature. Depending on Ce levels, both P and N types of thermoelectric semiconductors were obtained. MA-SPS sintered Ce1.0Co4Sb12 exhibits the highest ZT in the range of 100-500℃ and the maximum ZT is found at x=1.0 and 400℃. 相似文献
33.
以Ni作为添加元素,利用放电等离子技术制备了NixCo4-xSb12(x=0-0.35)化合物热电材料.通过先进的性能表征手段,深入探讨了NixCo4-xSb12化合物的热电性能,为n型热电材料的研究提供了有价值的参考.实验结果表明,一定量Ni的添加,能有效改善材料热电性能,提高热电优值;在Ni添加量x=0.2时,Ni0.2Co3.8Sb12化合物在温度T=773K时具有最大的热电性能优值ZTmax=0.45. 相似文献
34.
35.
36.
N型La0.9NixCo4-xSb12化合物的制备及热电性能研究 总被引:2,自引:0,他引:2
采用放电等离子烧结(SPS)方法制备了N型La0.9NixCo4-xSb12(x=0.05-1.0)化合物热电材料.借助于先进的结构和性能表征手段,系统研究了Ni含量对化合物热电性能的影响规律.实验结果表明,随着Ni含量增加,La0.9NixCo4-xSb12化合物的电阻率和Seebeck系数减小.当Ni含量x<0.6时,化合物的热导率随Ni含量增大而降低,说明加入一定量的Ni能很好地降低材料的热导率.N型La0.9Ni0.4Co3.6Sb12化合物在温度773K时具有最大的热电性能优值(ZT)0.4558. 相似文献
37.
利用电沉积的方法制备氧化亚铜薄膜,研究了络合剂的种类、浓度、后处理工艺及沉积时间对薄膜成相的影响。研究表明,络合剂柠檬酸钠有利于形成氧化亚铜薄膜;随着柠檬酸钠的浓度增加,薄膜中氧化亚铜含量降低,铜单质含量升高;沉积薄膜后,后处理对薄膜成相影响很大,烘干前不清洗薄膜中含有溶液中物质;随着沉积时间变长,薄膜变厚,然后出现掉膜现象。实验结果表明,选用柠檬酸钠为络合剂,柠檬酸钠的浓度为0.015 mol/L,沉积t为30 min,沉积薄膜后用蒸馏水清洗,制备出结晶良好,表面呈均匀纯相的氧化亚铜薄膜。 相似文献
38.
39.
水泵轴的断裂失效分析 总被引:3,自引:0,他引:3
通过宏观和微观的断口形貌观察、理化检验 ,认为水泵轴的断裂属于疲劳断裂 ,原因是强度不足 ,并提出了有关设计、生产和维修的建议。改进了设计后 ,没有再出现水泵轴在使用中断裂的事故。 相似文献
40.
CuInSe2薄膜太阳能电池是当前可再生能源领域的研究热点之一.掺杂在一定程度上起到提高薄膜电池光电性能及降低薄膜电池成本的作用.从元素掺杂角度出发,对元素掺杂的种类、方式,掺杂元素在薄膜电池光电性能和相互作用机制上的影响进行了重点综述,最后提出了当前CuInSe2薄膜电池存在的主要问题和发展方向. 相似文献