胶体石墨对低温金属树脂复合结合剂性能的影响

在铝基金属树脂复合结合剂中添加质量分数为0～0.4%的微量胶体石墨,研究复合结合剂的强度、硬度、微观组织及其反应结合机理。结果表明:在烧结温度为360 ℃,保温时间为5 min,保温压力为2 100 N/cm2条件下,随着胶体石墨质量分数增加,复合结合剂的密度先下降再上升随后又下降; 硬度、强度和弹性模量都是先上升再下降。在胶体石墨添加质量分数为0.2%时,复合结合剂的硬度和强度达最大值,分别为61.5 HRB和250 MPa,且复合结合剂的密度和弹性模量适中。微量胶体石墨可以和复合结合剂中的Al生成少量Al₄C₃,促进三维交叉网状结构形成,提高低温金属树脂复合结合剂性能。      

Preparation and properties of β-tricalcium phosphate porous bloceramlc

Porous β-tricalcium phosphate bioceramic (PTCP) has important roles in surgical implants because of good biocompatibility. But the low compressive strength of the ceramic limits its application. The preparation of PTCP was improved with the adjustment of the constituents and the sintering-process. A new type of PTCP material with high compressive strength was made. The compositions, microstructure and properties of PTCP were analyzed by TG-DSC, XRD, TEM, SEM and so on. The result indicates that stearic acid burns sufficiently and gives out carbon dioxide and water vapor when slowly heated between 200℃ and 400℃ so that the porous structure like coral in β-TCP bioceramic is formed. Through crystallization at 470℃ and 570℃, more CaO-P2O3 glass-cement is converted into crystallite-glass, which is beneficial for improving the compressive strength of β-TCP bioceramic. PTCP can form a support action in bone imperfect section with good solubility.     

正暖和倒暖启动对汽轮机组寿命的影响研究

汽轮机转子是机组最脆弱的设备,其使用寿命代表了整个机组的寿命,而在启动过程中转子所承受的等效应力最大,因此掌握不同启动方式下机组寿命的情况尤为重要。将某电厂汽轮机组作为仿真算例,对以冷态正暖和背压倒暖2种方式启动的机组进行三维建模、网格划分以及温度场和应力场的模拟分析,并进行寿命评估计算,得出2种启动方式下的机组寿命损耗,比较2种启动方式的优劣,为不同机组选择合适的启动方式提供合理的建议。     

含蜡原油热输管道轴向温降计算及其应用

根据含蜡原油在三个不同温度区域的比热表达式,从能量平衡关系式出发,推导出了含蜡原油热输管道轴向温降的计算公式,并与苏霍夫温降公式进行了比较.结果表明:实际运行情况下,原有的外输油起点温度范围已不再是最佳的选择.应用推导出的计算公式计算并调整外输起点温度,可以大大降低不必要的能量消耗,每年可节约燃料费29.2×104RMB$.     

STUDY ON THE STRUCTURE OF ARTIFICIAL SILICA FUME AND THE ACTIVITY OF VOLCANIC ASH

The present experimental technique is usedto study the image,crystal phase,pore structure and mi-crostructure of artificial silica fume,and the experimentalresults show that artificial silica fume is a non-crystallineand porous matter with a high specific surface area andthe high activity of volcanic ash.Therefore,it is a type ofideal material which can replace silica fume.     

粉煤灰增强MC尼龙复合材制备与性能研究

为提高MC尼龙的综合性能,在己内酰胺熔融单体中加入粉煤灰,通过碱催化阴离子聚合反应制备粉煤灰增强尼龙复合材料(FMCPA),采用扫描电镜和拉伸实验对复合材料的显微组织进行了观察和分析,并对其力学性能和摩擦性能进行了测试.结果表明,原状粉煤灰经活化处理后变得均匀细小,但与基体间存在明显的界面空隙,而经活化偶联处理的粉煤灰均匀分布在复合材料中,与尼龙基体的界面结合良好.复合材料的拉伸断面有明显的牵引痕迹,粉煤灰颗粒起到钉紧作用.粉煤灰质量分数较低时,尼龙复合材料以粘着磨损为主,伴有磨粒磨损;随着粉煤灰质量分数的增加,磨粒磨损加重.粉煤灰的加入提高了复合材料的力学性能,同时改善其耐磨损性能,当粉煤灰质量分数为20%时复合材料的综合性能最好.     

粉煤灰—石灰混合湿磨原理研究

本文运用图象分析的方法,从统计角度研究了粉煤灰与石灰混合干磨与混合湿磨制品显微结构的差别,提出了有效托贝莫来石及有效托贝莫来石系数的定量表达式。在对比实验和晶体生长理论的基础上,指出了混合湿磨过程中生成的水化硅酸钙具有“晶核”作用。由于生长的晶核对离子具有“优先吸附”的界面作用和“优先沉淀”的结晶中心作用,克服了水热合成产物优先在孔中生长的局部化现象,减少了无效托贝莫来石数量;缓和了高浓度屏蔽作用及界面近程析晶作用,从而加速了粉煤灰、石灰、石膏的水热反应,提高了制品强度。     

POLYMER-SUPPORTED β-CYCLODEXTRIN CATALYST FOR SELECTIVE SYNTHESISOF 4-H YDROXYBENZOIC ACID

4-hydroxybenzoic acid was synthesized by one pot method using polymer-bonded β-amino prop ionic acid-2-β-cyclodextrin as a catalyst.by which the selectivity for 4-hydroxybenzoic acid is 87%. A possible carboxylation mechanism in the presence of the title catalyst is discussed. Also.the recovery and reusage of the catalyst is studied.     

蒸压硅酸盐陶粒混凝土梁受弯性能研究

为探究新型蒸压硅酸盐陶粒在桥梁结构中应用的可行性,进行了蒸压硅酸盐陶粒混凝土梁的静力受弯试验,研究了梁的受力过程和变形规律,并分析了其正截面弯曲承载力以及挠度。结果表明：随着蒸压硅酸盐陶粒掺量的增加,混凝土梁的正截面抗弯承载力最大提升了20%;使用普通混凝土梁的计算公式对蒸压硅酸盐陶粒混凝土梁的承载力进行计算,得到的实测值均高于理论值,安全系数可达1.1倍以上;蒸压硅酸盐陶粒混凝土梁的裂缝发展和破坏规律与普通混凝土梁一致,可以安全地用于桥梁结构,减轻桥梁自重;采用现行规范中关于正截面受弯承载力和挠度的计算公式对蒸压硅酸盐陶粒混凝土梁进行设计,其结果安全可靠。