Catalytic oxidative desulfurization of gasoline using phosphotungstic acid supported on MWW zeolite

Catalysts for the desulfurization of gasoline samples were synthesized via the immobilization of well-dispersed phosphotungstic acid (HPW) on Mobil composition of matter-twenty-two (MWW) zeolite. Characterization results indicated that these catalysts possess a mesoporous structure with the retention of the Keggin structure of immobilized HPW. Relevant reaction parameters influencing sulfur removal were systematically investigated, including HPW loading, catalyst dosage, temperature, initial S-concentration, molar ratio of oxidant to sulfide (O/S), volume ratio of MeCN to model oil (Ext./oil), and sulfide species. The 40 wt-% HPW/MWW catalyst exhibited the highest catalytic activity with 99.6% dibenzothiophene sulfur removal from prepared samples. The 40 wt-% HPW/MWW catalyst was recycled four times and could be easily regenerated. Finally, as an exploratory study, straight-run-gasoline and fluid catalytic cracking gasoline were employed to accurately evaluate the desulfurization performance of 40 wt-% HPW/MWW. Our research provides new insights into the development and application of catalysts for desulfurization of gasoline.     

Egg shell waste as an activation agent for the manufacture of porous carbon

Egg shell waste was used as an activation agent directly for the manufacture of a biomass-derived porous carbon,which possessed a surface area of 626 m~2·g~(-1) and was rich in nitrogen, sulfur and oxygen functionalities. The activation mechanism was proposed, and the carbon showed its potential to act as an adsorbent for the adsorptive removal of various contaminants from both aqueous and non-aqueous solutions, possessing maximum adsorption capacities of 195.9, 185.1, 125.5 and 44.6 mg·g~(-1) for sulfamethoxazole, methyl orange, diclofenac sodium and dibenzothiophene, respectively. Through the utilization of egg shell waste as a sustainable activation agent, this work may help to make the widely applied biomass-derived porous carbons more economical and ecological.     

The effects of thermoresponsive microgel density on cell adhesion,proliferation, and detachment

In recent years, poly(N-isopropylacrylamide)-based microgels have been emerged as a new thermoresponsive coating for cell/cell sheet harvesting, yet few work reports their effect on cell attachment, morphology, activity, and proliferation in details. In this work, poly(N-isopropylacrylamide-co-styrene) (pNIPAAmSt) microgel was selected as the model to study its density on NIH3T3 cell adhesion, morphology, activity, and detachment. Results showed that 0.5 wt % pNIPAAmSt microgel density leads to more cells adhesion, higher cell activity yet lower cell proliferation. Moreover, cell adhesion location can be well controlled either by manipulating the sub-cellular scale distances between microgels or by fabricating large scale surface patterns of the microgels on higher microgel density. By temperature stimuli, similar ratio cells detached from the microgel density surface from 0.5 to 1.5 wt %. The results in this article are worthy for the application of thermoresponsive microgels in cell regulation. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020 , 137, 48773.     

Morphology and properties of HDPE/zinc-neutralized sulfonated EPDM blends

The compatibility of zinc-neutralized sulfonated EPDM (Zn-SEPDM) and its effect on crystallizing behavior of high-density polyethylene (HDPE) as well as the morphology of the blend were studied through wide-angle X-ray diffractomer (WAXD), differential scannign calorimetry (DSC), transition electron micrography.(TEM), scanning electron micrography (SEM), a capillary rheometer, and mechanical property test. The results show that addition of Zn-SEPDM decreases both the melting point and the crystallizing temperature of HDPE. The apparent viscosity of the blend decreases with increasing of shear rate and stress. As Zn-SEPDM content exceeds 20%, Zn-SEPDM in the blend becomes continuous and an abrupt change in impact strength occurs. Owing to the incorporation of ionic groups into EPDM, the strong interaction between the chains make the impact strength of HDPE incredibly increased without sacrificing much of its tensile strength.     

塑料基TiO2电致变色薄膜制备及性能研究

采用溶胶-凝胶法分别在镀有ITO透明电极的玻璃和塑料基体上制备了TiO2电致变色薄膜,对比研究了不同基体上溶胶的成膜性及薄膜的电致变色性能.结果表明:在相对湿度低于15%的环境中,采用0.4mol/L的溶胶可以通过多次提拉制得表面光洁的较厚透明TiO2薄膜;随热处理温度的升高,薄膜的电色可逆性变好,循环寿命变大,但离子储存能力下降;塑料基TiO2薄膜与相同条件下制备的玻璃基薄膜具有相似的性能,呈现出较弱的阴极电致变色效应和较强的Li 储存能力,有望用作柔性电致变色器件的对电极.     

芳纶Ⅲ纤维拉伸性能的实验研究

测试了芳纶Ⅲ纤维的拉伸性能等,并与F-12和Kevlar-49纤维进行了对比.对由芳纶Ⅲ纤维与环氧树脂基体复合成型的单向纤维增强环形试样,测试了其拉伸强度、弹性模量和层间剪切强度,结果表明:芳纶Ⅲ纤维单向纤维复合材料的拉伸强度和弹性模量与F-12纤维相当,分别比Kevlar-49纤维要高出约25.7%和24.7%;但早期的芳纶Ⅲ纤维与环氧树脂基体的界面结合性较差,层间剪切强度仅为32.0～35.2MPa.     

脉冲式气流干燥过程的模拟优化

考察了脉冲式气流干燥过程中不同参数对干燥结果的影响。增大固气流量比,可以增大干燥热效率和降低最终产品的湿含量;进口气体温度的升高,能降低最终产品的湿含量,但同时也降低了干燥的热效率。粒径的减小,会使颗粒表面水分蒸发速度上升,从而降低产品的最终湿含量,增加干燥的热效率。     

浅谈部分实心预应力混凝土管桩的生产工艺与施工质量控制

部分实心预应力混凝土管桩是一种用于一般工业与民用建筑基础的新型工程桩,其特点是采用工厂预先填芯生产工艺,从而形成部分实心预应力混凝土管桩.施工时采用预应力钢棒作为连接钢筋,并通过六角头穿芯孔螺丝锁定于端板的预应力张拉孔上,保证桩与桩或基础承台的可靠连接.与一般空心PHC管桩相比,能有效减少现场施工工作量、缩短工期、降低...     

玫瑰花露酒的研制

本试验以食用玫瑰为主要原料,以食用酒精为酒基,经过酒精的处理,浸提,调配等过程,开发出芳香四溢的玫瑰露酒.试验结果表明:产品配比为酒精度20V/V,糖10%,柠檬酸0.2%时,质量最佳.     

白水泥闭路粉磨系统选粉机的改造

白水泥作为一种特种水泥,水泥成品要求比表面积高,80μm、45μm筛余细度控制严格.改造前,水泥粗颗粒多,细度不易控制.将原系统中O-Sepa N-1500水平涡流选粉机更改为SLK1500型空气打散涡流选粉机,改善了物料打散效果,提高了选粉机选粉效率和台时产量,解决了粗颗粒窜入成品影响质量的问题.