Study on the machinability of resulfurized composite free-cutting steels

The machinability of S, S-Ca, S-RE, and S-RE-Ca system resulfurized composite free-cutting steels were investigated, where RE is rare earths, mostly cerium. The experimental results showed that in the low cutting speed range (≤35 m/min), the S-RE system free-cutting steel had better machinability than the others and that the S-RE-Ca system free-cutting steel exhibited the best machinability at high cutting speeds. A protective layer capable of preventing diffusion wear was formed on the rake face of a P30 tool when S-RE-Ca system free-cutting steel was machined in the cutting speed range of 120 to 160 m/min.     

SBTV铁电材料的制备和微观组织结构

采用固相反应法合成了SrBi2Ta2O9(简称SBT)和V掺杂SrBi2Ta2O9(简称SBTV)陶瓷,通过TG-DTA、XRD、SEM、TEM等技术手段研究了材料的烧结工艺、相组成和微观组织结构.研究表明V2O5是一种很好的助烧剂,掺杂后材料的烧结温度可降低200℃烧结后纯SBT均为单一的钙钛矿相SBT;掺杂后2种成型工艺所制备的SBTV除了生成少量Bi4(V2O11)外,仍主要由钙钛矿相组成;同时所有的材料都发生了一定程度的择优取向.掺杂后材料的晶粒形态发生变化棒状转化为片状.同时V掺杂后引起了晶格畸变,产生应变,SBTV材料在透射中观察到具有α-边界特征的90°畴.     

34CrNiMo钢齿轮轴开裂原因分析

对34CrNiMo钢齿轮轴的化学成分、金相组织及断口分析表明，其淬火开裂的主要原因是由于锻造温度过高，导致过热缺陷所致。     

肥料防结块缓释概况及性能快速表征方法探讨

介绍了颗粒肥料结块的原因机理、影响因素和传统的处理方法。简述了缓释肥料的特点、类型、加工方法以及国内外的研究发展状况。模拟肥料贮存、运输和施用环境以及设计装置，对颗粒肥料防结块、缓释性能快速表征方法进行了有益的探讨。对不同包膜尿素的测试结果表明，所设计的肥料养分释放模拟装置具有较好的应用前景。     

低翘曲玻纤增强PET复合材料的制备和性能研究

依据降低翘曲的机理，选用不同降低翘曲的方法，制备了系列翘曲玻纤增强PET复合材料，结果表明，具有较高形状对称性的填料，如滑石粉，云母粉和玻璃微珠都能不同程度地降低玻纤增强PET体系的翘曲，非晶聚合物也能有效改进该体系的翘曲性能。     

固体超强酸合成乙酸丁酯

本文讨论了固体超强酸催化剂合成乙酸丁酯的方法，比较了各类固体超强酸的优劣，为工业化生产乙酸丁醋筛选超强酸催化剂提供极具价值的参考依据。     

碱式硫酸镁晶须的合成及应用

以一定浓度的MgSO4和NaOH溶液为原料,在常温下混合,在160℃,0.5 MPa的条件下用水热法反应8 h,制备出增强阻燃材料MgSO4.5Mg(OH)2.3H2O型碱式硫酸镁晶须(MOS),探讨了反应条件对产物形貌、结构及组成的影响,初步确立了制备MOS的工艺条件。经过对复合材料的拉伸性能测试得出结论,采用MOS填充改性的聚丙烯,优于市售纳米氢氧化镁和阻燃级氢氧化镁。     

D-HPG废水的预处理

D-对羟基苯甘氨酸制药废水 COD高 ,成分复杂。采用 Fe粉及 Fenton试剂预处理 ,COD总去除率高达98%以上。小试确定了 Fe粉加入量为 14 0 g/ L、曝气时间为 7h、Fenton法预处理 D- HPG废水的最佳反应条件 :H2 O2 质量浓度为 2 1.5 g/ L,Fe SO4 质量浓度为 3.8g/ L,氧化时间为 4 h,p H为 5     

基于分形理论的陶瓷材料显微组织模拟

利用VB开发工具,开发出基于二维和三维系统单相、复相陶瓷材料显微组织及其演变的仿真模拟软件,其主要包括三个模块:二维系统仿真模块、三维系统仿真模块和显微结构定量分析模块;可实现二维和三维的显微组织仿真图像输出,并且可方便地观察空间任意角度截面显微组织及其演变;应用分形理论、拓扑学等方法,对显微结构进行了定量分析,得到晶粒数及平均体积等参数与仿真时间MCS的变化关系。     

Effects of sulfate-reducing bacteria on the corrosion behavior of carbon steel

The influences of the growing process of sulfate-reducing bacteria (SRB) in seawater system on the medium state and corrosion behavior of carbon steel were studied by detecting solution state parameters and using corrosion electrochemical methods. The growing process of SRB in the seawater shows the three stages of growing, death and residual phases. The solution state parameters of the concentration of sulfide, the pH value and the redox potential changed during the three stages of the SRB growing process. And the corrosion rate of D36 carbon steel was accelerated during the growing phase and stable during the death and residual phases. The results indicate that the medium state and the corrosion rate of the steel do not depend on the number of active SRB, but depend on the accumulation of the metabolism products of SRB.