13SiMnNiCrMoV钢切口疲劳裂纹萌生门槛值

本文研究在13SiMnNiCrMoV 结构钢中用尖裂纹的应力强度因子来反映三点弯曲缺口试样的疲劳裂纹萌生规律。当 R=0.1,f=100Hz,试样尺寸 B×W×L=12.5×25×117mm 时,缺口名义应力幅的门槛值为Δσ_(th)=3315ρ~(0.352) MPa,0.5mm≤ρ≤5mmΔK_(th)=250ρ~(0.352) MPam~(1/2)门槛值与ρ有关。同时得到缺口裂纹萌生的循环次数 N_i 与名义应力幅Δσ、缺口曲率半径ρ的定量关系是N_i=3.98×10~(22)ρ~(1.62)/Δσ~(4.85),N_i≤10~(5.5)并讨论了(ΔK_1/ρ~(1/2))_(th)与ρ无关的结论。     

内蒙古煤系高岭土作为FCC催化剂基质的研究

研究两种内蒙古煤系高岭土（1^＃、2^＃）的化学组成、晶体结构并与苏州高岭土进行了比较。对三种高岭土进行酸改性，利用BET、吡啶-TPD和微反测试分别研究改性前后高岭土的性能特点。并将内蒙古高岭土1^＃与苏州高岭土采用半合成方法合成了FCC催化剂，测定了其裂化活性。研究结果表明，内蒙古1^＃具有较良好的晶体结构和化学组成，经酸改性后比表面积大大增加，具有合适的孔径分布，裂化活性较好，可以取代苏州高岭土作为FCC催化剂的基质。     

普物光学实验的现代化

为了扩大学生的视野，增加实验的兴趣，充分调动学生学习的积极性和创新精神，我们将一些反映当前光学发展的新内容、新技术引进到普物光学实验中，并在实验教学方法上进行了改革。本文介绍了我们的具体做法和体会。     

兴化市有线电视城乡联网暨系统升级改造方案

在原有1 310 nm系统的基础上,通过增加1 550 nm光发射机、光放大器以及线路扩容、加芯等技术手段来有计划分阶段地实施1 550 nm改造工程,并对回传业务、指标分配、实施步骤等作了简要的论述。     

Ultrasound‐activated Knoevenagel condensation of malononitrile with carbonylic compounds catalysed by alkaline‐doped saponites

α,β‐Unsaturated nitriles have been synthesized by Knoevenagel condensation of a carbonylic compound with malononitrile, assisted by sonochemical irradiation. Two alkaline‐promoted clays (Li⁺‐ and Cs⁺‐exchanged saponites) have been employed as catalysts. The influence of the carbonylic compound (benzaldehyde or cyclohexanone) and the use of a solvent on the catalytic activity have been studied. Remarkable increase in the conversion values has been found when the reaction is activated by ultrasound, as compared with the thermal activation. In this green, solvent‐free procedure, α,β‐unsaturated nitriles have been produced in very high yields (97%) when the Cs⁺‐saponite is used as catalyst. Copyright © 2004 Society of Chemical Industry     

矿用扁平接链环静态电测实验及有限元分析

对φ30的矿用扁平接链环进行静态拉伸电测实验，分析并得出产生最大强度的位置。同时应用ANSYS有限元分析软件对接链环的力学简化模型进行分析，与实验结果相比较，有助于找出齿部破坏规律，对齿形的改进及今后的疲劳分析具有重要意义。     

200kA预焙槽节能降耗的几点尝试

通过对200kA预焙槽节能方面做的几点尝试，探索出了200kA预焙电解槽在节约能源方面的措施，并取得了较好的节能效果。     

Analysis of trace mercury in water by solid phase extraction using dithizone modified nanometer titanium dioxide and cold vapor atomic absorption spectrometry

A new method for analysis of trace mercury in water samples was developed, based on the combination of preconcentration/separation using dithizone-modified nanometer titanium dioxide (TiO2) as a solid phase extractant and determination by cold vapor atomic adsorption spectrometry (CVAAS). Dithizone was dissolved with alcohol and loaded on the surface of nano-sized TiO2 powders by stirring. The static adsorption behavior of Hg2 on the dithizone-modified nanoparticles was investigated in detail. It was found that excellent adsorption ratio for Hg2 could be obtained in the pH range of 7-8 with an oscillation time of 15 min, and a 5 mL of 3.5 mol·L-1 HCl solution could quantitatively elute Hg2 from nanometer TiO2 powder. Common coexisting ions caused no obvious influence on the determination of mercury. The mechanisms for the adsorption and desorption were discussed. The detection limit (3σ) for Hg2 was calculated to be 5 ng·L-1. The proposed method was applied to the determination of Hg2 in a mineral water sample and a Zhujiang River water sample. By the standard addition method, the average recoveries were found to be 94.4%-108.3% with RSD (n = 5) of 2.9%-3.5%.     

山东改造工程旧房质量检测

结合某成品仓库改作商业用房的工程实例,对该建筑进行了详细的检测与分析,并根据结果提出了针对性的加固方案,并对加固效果进行了探讨,为工程改造提供了依据,可供类似工程借鉴。     

Thermal Expansion Behavior of La1—xSrxMn1—yCoyO3—δ Perovskites

The thermal expansion behavior of La1-xSrxMn1-yCoyO3-δ (x=0.2-0.4, y=0.1-0.3) perovskites in air has been investigated. The average linear thermal expansion coefficients increased with increasing Sr content up to 40 mole fraction or Co content up to 30 mole fraction. The expansion is generally attributed to an increase in the average cation radius as some of the cations in the perovskite are reduced in valence when oxygen ions are removed from the structure.