Ti_3Al-Nb合金的有序转变

研究了Ti_3Al-Nb合金在高温下的有序化,冷却过程高温β相转变及时效过程亚稳定β相分解的行为,结果指出,在1060℃固溶处理时,合金形成初生α_2和β高温有序相;在固溶处理后的冷却过程中,合金发生β→α_2+ω型转变;在700℃时效过程中,合金发生(β+ω型)亚稳→(α_2+β)稳定分解。     

氯化物介质矿浆电解法浸出硫化铜精矿

研究了在ＦｅＣｌ３ＨＣｌＮａＣｌ体系中直接电解浸出硫化铜精矿矿浆制取铜粉的工艺条件及机理。试验表明，在阳极初始溶液含Ｆｅ３＋６０ｇ／Ｌ、ＨＣｌ３０ｇ／Ｌ、ＮａＣｌ１５０ｇ／Ｌ，阴阳极电流密度分别为３５０和６００Ａ／ｍ２，１００℃的条件下浸出５ｈ，可获得铜浸出率９８．８％、渣含铜０．３４％、铜粉纯度９７．５％的结果；Ｆｅ３＋浓度是影响铜浸出率最显著的因素，阳极上发生的主要反应是Ｆｅ２＋的氧化；元素硫产生的机理是酸直接分解黄铜矿生成Ｈ２Ｓ，Ｈ２Ｓ溶解后再被Ｆｅ３＋氧化。     

VIRALL复合板的振动阻尼特性

采用悬臂粱横向弯曲自由振动方法，研究了单向增强VIRALL(vinylon reinforced aluminum laminates)复合板及相应的单一铝合金板的振动阻尼性能，结果表明，前者的振动衰减系数高于后者，还发现VIRALL复合板的阻尼性能受其纤维取向影响。     

Resistance welding of carbon fibre reinforced polyetheretherketone composites using metal mesh and PEI film

Weldability of polyetheretherketone( PEEK) with polyetherimide( PEI) is tested. And carbon fiber reinforced PEEK laminates are resistance welded using stainless steel mesh heating element. The effects of the welding time and welding pressure on the lap shear strength of joints are investigated. Results show that PEEK can heal with PEI well in welding condition and the lap shear strength of PEEK/CF(carbon fibre) joint increases linearly with welding time, but reaches a maximum value when welding pressure ranging from 0.3 MPa to 0.5 MPa with constant welding time. The fracture characteristics of surface are analyzed by SEM techniques, and four types of fracture modes of lap shear joints are suggested.     

Process of friction-stir welding high-strength aluminum alloy and mechanical properties of joint

The process of friction-stir welding 2A12CZ alloy has been studied. And strength and elongation tests have been performed, which demonstrated that the opportunity existed to manipulate friction-stir welding parameters in order to improve a range of material properties. The results showed that the joint strength and elongation arrived at their maximums ( 331 MPa and 4% ) at 37. 5 mm/min and 300 rpm. As welding parameters changing, joint tensile strength and elongation had similar development. Hardness measurement indicated that the weld was softened. However, there was considerable difference in softening degree for different joint zone. The weld top had lower hardness and wider softening zone than other zone of the weld. And softening zone at advancing side was wider than that at retreating side.     

CORRELATION BETWEEN STRUCTURE AND MAONETIC PROPERTIES OF AMORPHOUS Gd-Co FILMS

本文用电子衍射方法研究了非晶态Gd-Co薄膜(400—700A)的结构,测定了五个试样的径向分布函数,并把其中两个试样的径向分布函数与它们的磁性(一为垂直膜面单轴各向异性,另一为平面各向异性)联系,发现Gd-Co薄膜的垂直膜面磁各向异性可能与膜中异类原子的最近邻配位数较大有关。     

流动液体中夹杂物超声去除的影响因素

以高密度聚乙烯（HDPE）颗粒和水形成的悬浮液为研究体系。考察了有无超声波作用下。介质流量、夹杂物数量以及夹杂物的粒径对总去除率、上浮去除率、壁面粘附去除率的影响。实验结果表明，在短时间内（30s)超声波对流动液体中的夹杂物具有明显的去除效果。总去除率达93％。夹杂物的总去除率随着超声波输入电功率的增大而提高；超声波对较多数量或较大粒径的夹杂物去除效果更显著。超声波作用下流动液体中的夹杂物比静止液体中的更容易去除。超声波对流动液体中夹杂物去除效果的去除机理主要是通过气泡捕获夹杂物，超声空化效应产生直接包裹夹杂物的气泡以及通过夹杂物碰撞凝聚使夹杂物容易上浮实现去除。     

A SIMPLIFIED EXPRESSION OF m-n-δ RELATIONS FOR MATERIALS WITH PLASTICITY OR SUPERPLASTICITY

以Hart的微分型本构关系为基础,本文推导出了一个既包含应变硬化效应(n)又包含应变速率敏感效应(m)的m-n-δ关系式δ=[1/(1-(1-α(0))~(1/m))]~m×e~n-1当n=0时,它吻合于Ghosh和Ayres的现代分析,当m=0时,吻合于Considère的经典分析.该公式的计算结果和实验结果一致.     

TiAl/Ti/V/Cu/40Cr钢扩散连接界面组织结构对接头强度的影响

研究了TiAl/Ti/V/Cu/40Cr钢的扩散连接，结果显示：在TiAl/Ti界面处形成了对接头强度有利的Ti3Al TiAl双相层及Ti固溶体层，而Ti/V/Cu/40Cr界面处未出现金属间化合物及其它脆性相，接头最高拉伸强度可达420MPa，接近TiAl母材。     

Au-Ni-Kovar合金系统基底元素表面偏聚的SAM和XPS研究SCIEI

本文采用SAM和XPS对实用Au-Ni-Kovar合金系统热处理样品(250—350℃,0.5—1.5h)进行了基底元素穿透Au层的表面偏聚研究,给出了这一复杂系统中Ni,Co表面偏聚机理的直观证据,即Ni,Co主要是通过晶界扩散穿透Au层而后以表面扩散覆盖镀Au表面的;表面偏聚元素化学态的研究则不仅表明,氧的吸附和氧化反应是Ni,Co表面偏聚的驱动力,而且发现,上述偏聚会引起样品表面吸水的现象。